ASTM D3528-96(2008)

Standard Test Method for Strength Properties of Double Lap Shear Adhesive Joints by Tension Loading

SIGNIFICANCE AND USE
This test method is designed to produce shear property data for the process control and specification of adhesives. This test method may also be useful for research and development of adhesives.
Lap shear properties vary with specimen configuration preparation, speed, and environment of testing. Consequently, where precise comparative results are desired, these factors must be carefully controlled and reported.
SCOPE
1.1 This test method covers the determination of the tensile shear strengths of adhesives for bonding metals when tested in an essentially peel-free standard specimen that develops adhesive stress distribution representative of that developed in a typical low-peel production-type structural joint. The reproducibility of the strengths achieved are directly related to conformance with specified conditions of preparation and testing.
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

General Information

• Status: Historical
• Publication Date: 31-Mar-2008
• ICS: 83.180 - Adhesives
• Technical Committee: D14 - Adhesives
• Drafting Committee: D14.80 - Metal Bonding Adhesives

Relations

• Replaces: ASTM D3528-96(2002) - Standard Test Method for Strength Properties of Double Lap Shear Adhesive Joints by Tension Loading
• Effective Date: 01-Apr-2008
• Replaced By: ASTM D3528-96(2016) - Standard Test Method for Strength Properties of Double Lap Shear Adhesive Joints by Tension Loading
• Effective Date: 01-May-2016
• Referred By: ASTM D6465-99(2016) - Standard Guide for Selecting Aerospace and General Purpose Adhesives and Sealants
• Effective Date: 01-Apr-2008
• Referred By: ASTM D4896-01(2016) - Standard Guide for Use of Adhesive-Bonded Single Lap-Joint Specimen Test Results
• Effective Date: 01-Apr-2008

Standards Content (Sample)

NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation: D3528 − 96(Reapproved 2008)
Standard Test Method for
Strength Properties of Double Lap Shear Adhesive Joints by
1
Tension Loading
This standard is issued under the fixed designation D3528; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
INTRODUCTION
The accuracy of the results of strength tests of adhesive bonds will depend on the conditions under
whichthebondingprocessiscarriedout.Unlessotherwiseagreeduponbetweenthemanufacturerand
the purchaser, the bonding conditions should be prescribed by the manufacturer of the adhesive. In
order to ensure that complete information is available to the individual conducting the tests, the
manufacturer of the adhesive should furnish numerical values and other specific information for each
of the following variables:
(1) Surface preparation
(2) Mixing directions
(3) Adhesive application
(4) Assembly conditions
(5) Curing conditions
(6) Testing conditions
Arangemaybeprescribedforanyvariablebythemanufactureroftheadhesiveifitcanbeassumed
by the test operator that any arbitrarily chosen value within such a range or any combination of such
values for several variables will be acceptable to both the manufacturer and the purchaser of the
adhesive.
1. Scope 2. Referenced Documents
2
1.1 This test method covers the determination of the tensile 2.1 ASTM Standards:
shear strengths of adhesives for bonding metals when tested in A167 Specification for Stainless and Heat-Resisting
an essentially peel-free standard specimen that develops adhe- Chromium-Nickel Steel Plate, Sheet, and Strip (With-
3
sive stress distribution representative of that developed in a drawn 2014)
typical low-peel production-type structural joint. The repro- B36/B36M Specification for Brass Plate, Sheet, Strip, And
ducibility of the strengths achieved are directly related to Rolled Bar
conformance with specified conditions of preparation and B152/B152M Specification for Copper Sheet, Strip, Plate,
testing. and Rolled Bar
B209 Specification for Aluminum and Aluminum-Alloy
1.2 The values stated in SI units are to be regarded as the
Sheet and Plate
standard. The values given in parentheses are for information
B265 Specification for Titanium and Titanium Alloy Strip,
only.
Sheet, and Plate
1.3 This standard does not purport to address all of the
D618 Practice for Conditioning Plastics for Testing
safety concerns, if any, associated with its use. It is the
D907 Terminology of Adhesives
responsibility of the user of this standard to establish appro-
E4 Practices for Force Verification of Testing Machines
priate safety and health practices and determine the applica-
E122 Practice for Calculating Sample Size to Estimate,With
bility of regulatory limitations prior to use.
1 2
This test method is under the jurisdiction of ASTM Committee D14 on For referenced ASTM standards, visit the ASTM website, www.astm.org, or
Adhesives and is the direct responsibility of Subcommittee D14.80 on Metal contact ASTM Customer Service at [e-mail]. For Annual Book of ASTM
Bonding Adhesives Standards volume information, refer to the standard’s Document Summary page on
Current edition approved April 1, 2008. Published April 2008. Originally the ASTM website.
3
approved in 1976. Last previous edition approved in 2002 as D3528 – 96 (2002). The last approved version of this historical standard is referenced on
DOI: 10.1520/D3528-96R08. www.astm.org.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
D3528 − 96 (2008)
T =1.6mm
1
T =3.2mm
2
T =1.6mm
A = Test Gluelines
1
T =3.2mm
B = Spacer = T 2
2
A = Test Gluelines
C = Area in Test Grips
B = Area in Test Grips
D Shear Area
C = Shear areas
FIG. 1 Form and Dimensions of Type A Specimens
FIG. 2 Form and Dimensions of Type B Specimen
Specified Precision, the Average for a Characteristic of a
Cut the specimens from the appropriate test panels that have
Lot or Process
been prepared as prescribed in Section 7. For aluminum-alloy
E171 Practice for Conditioning and Testing Flexible Barrier
specimens the recommended thickness of the sheet is 3.24 6
Packaging
0.125 mm (0.125 6 0.005 in.). The recommended test overlap
length (L) for most metals, with adherends of the prescribed
3. Terminology
metal thickness and arranged as shown in Figs. 1 and 2, is 12.7
3.1 Definitions—Many terms in this test method are defined
6 0.25 mm (0.5 6 0.01 in.).
in Terminology D907.
NOTE 1—Since it is undesirable to exceed the yield point of the metal
4. Significance and Use
in tension duri
...