ASTM A564/A564M-19
(Specification)Standard Specification for Hot-Rolled and Cold-Finished Age-Hardening Stainless Steel Bars and Shapes
Standard Specification for Hot-Rolled and Cold-Finished Age-Hardening Stainless Steel Bars and Shapes
ABSTRACT
This specification covers bars and shapes of age-hardening stainless steels. Hot-finished or cold-finished rounds, squares, hexagons, bar shapes, angles, tees, and channels are included. These shapes may be produced by hot rolling, extruding, or forging. Type 631 and 632 stainless steels contain a large amount of ferrite in the microstructure and can have low ductility in forgings and large diameter bars. Material of types other than XM-16, XM-25, and Type 630 shall be furnished in the solution-annealed condition, or in the equalized and oven-tempered condition. Types 630, XM-16, and XM-25 may be furnished in the solution-annealed or age-hardened condition. Type UNS S46910 shall be furnished in solution annealed, cold-worked or aged-hardened condition. Shapes may be subjected to either Class A or Class C preparation for removal of visible surface imperfections. The material shall be subjected to tension, impact, and hardness tests.
SCOPE
1.1 This specification2 covers bars and shapes of age-hardening stainless steels. Hot-finished or cold-finished rounds, squares, hexagons, bar shapes, angles, tees, and channels are included; these shapes may be produced by hot rolling, extruding, or forging. Billets or bars for reforging may be purchased to this specification.
1.2 These steels are generally used for parts requiring corrosion resistance and high strength at room temperature, or at temperatures up to 600 °F [315 °C]; 700 °F [370 °C] for Type 632; 840 °F [450 °C] for Type UNS S46910. They are suitable for machining in the solution-annealed condition after which they may be age-hardened to the mechanical properties specified in Section 7 without danger of cracking or distortion. Type XM-25 is machinable in the as-received fully heat treated condition. Type UNS S46910 is suitable for machining in the solution-annealed, cold-worked, and aged-hardened condition.
1.3 Types 631 and 632 contain a large amount of ferrite in the microstructure and can have low ductility in forgings and larger diameter bars. Applications should be limited to small diameter bar.
1.4 The values stated in either inch-pound units or SI (metric) units are to be regarded separately as standards; within the text and tables, the SI units are shown in [brackets]. The values stated in each system are not exact equivalents; therefore, each system must be used independent of the other. Combining values from the two systems may result in nonconformance with the specification.
1.5 Unless the order specifies an “M” designation, the material shall be furnished to inch-pound units.
Note 1: For forgings, see Specification A705/A705M.
Note 2: For billets and bars for forging see Specification A314.
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
General Information
Relations
Buy Standard
Standards Content (Sample)
NOTICE: This standard has either been superseded and replaced by a new version or withdrawn.
Contact ASTM International (www.astm.org) for the latest information
Designation:A564/A564M −19
Standard Specification for
Hot-Rolled and Cold-Finished Age-Hardening Stainless Steel
1
Bars and Shapes
This standard is issued under the fixed designationA564/A564M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the U.S. Department of Defense.
NOTE 2—For billets and bars for forging see Specification A314.
1. Scope*
2
1.6 This international standard was developed in accor-
1.1 This specification covers bars and shapes of age-
dance with internationally recognized principles on standard-
hardeningstainlesssteels.Hot-finishedorcold-finishedrounds,
ization established in the Decision on Principles for the
squares, hexagons, bar shapes, angles, tees, and channels are
Development of International Standards, Guides and Recom-
included; these shapes may be produced by hot rolling,
mendations issued by the World Trade Organization Technical
extruding, or forging. Billets or bars for reforging may be
Barriers to Trade (TBT) Committee.
purchased to this specification.
1.2 These steels are generally used for parts requiring
2. Referenced Documents
corrosion resistance and high strength at room temperature, or
3
2.1 ASTM Standards:
at temperatures up to 600 °F [315 °C]; 700 °F [370 °C] for
A314 Specification for Stainless Steel Billets and Bars for
Type 632; 840 °F [450 °C] for Type UNS S46910. They are
Forging
suitable for machining in the solution-annealed condition after
A370 Test Methods and Definitions for Mechanical Testing
which they may be age-hardened to the mechanical properties
of Steel Products
specified in Section 7 without danger of cracking or distortion.
A484/A484M Specification for General Requirements for
Type XM-25 is machinable in the as-received fully heat treated
Stainless Steel Bars, Billets, and Forgings
condition. Type UNS S46910 is suitable for machining in the
A705/A705M Specification for Age-Hardening Stainless
solution-annealed, cold-worked, and aged-hardened condition.
Steel Forgings
1.3 Types 631 and 632 contain a large amount of ferrite in
A751 Test Methods, Practices, and Terminology for Chemi-
the microstructure and can have low ductility in forgings and
cal Analysis of Steel Products
larger diameter bars. Applications should be limited to small
E527 Practice for Numbering Metals and Alloys in the
diameter bar.
Unified Numbering System (UNS)
2.2 Other Documents:
1.4 The values stated in either inch-pound units or SI
SAE J1086 Recommended Practice for Numbering Metals
(metric)unitsaretoberegardedseparatelyasstandards;within
4
and Alloys (UNS)
the text and tables, the SI units are shown in [brackets]. The
values stated in each system are not exact equivalents;
3. Ordering Information
therefore, each system must be used independent of the other.
3.1 It is the responsibility of the purchaser to specify all
Combining values from the two systems may result in noncon-
requirements that are necessary for material ordered under this
formance with the specification.
specification. Such requirements may include but are not
1.5 Unless the order specifies an “M” designation, the
limited to the following:
material shall be furnished to inch-pound units.
3.1.1 Quantity (weight or number of pieces),
NOTE 1—For forgings, see Specification A705/A705M.
3.1.2 Type or UNS designation (Table 1),
3.1.3 Specific melt type when required,
3.1.4 Heat treated condition (5.1),
1
'This specification is under the jurisdiction ofASTM Committee A01 on Steel,
Stainless Steel and Related Alloys and is the direct responsibility of Subcommittee
3
A01.17 on Flat-Rolled and Wrought Stainless Steel. For referenced ASTM standards, visit the ASTM website, www.astm.org, or
Current edition approved May 1, 2019. Published June 2019. Originally contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
ε1
approved in 1966. Last previous edition approved in 2013 as A564/A564M – 13 . Standards volume information, refer to the standard’s Document Summary page on
DOI: 10.1520/A0564_A0564M-19. the ASTM website.
2 4
For ASME Boiler and Pressure Vessel Code applications, see related Specifi- Available from Society of Automotive Engineers (SAE), 400 Commonwealth
cation SA-564/SA-564M in Section II of that Code. Dr., Warrendale, PA 15096-0001, http://www.sae.org.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1
---------------------- Page: 1 ----------------------
A564/A564M−19
A
TABLE 1 Chemical Requirements
Comp
...
This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
´1
Designation: A564/A564M − 13 A564/A564M − 19
Standard Specification for
Hot-Rolled and Cold-Finished Age-Hardening Stainless Steel
1
Bars and Shapes
This standard is issued under the fixed designation A564/A564M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the U.S. Department of Defense.
1
ε NOTE—Corrected incomplete sentence in 7.1 editorially in October 2017.
1. Scope*
2
1.1 This specification covers bars and shapes of age-hardening stainless steels. Hot-finished or cold-finished rounds, squares,
hexagons, bar shapes, angles, tees, and channels are included; these shapes may be produced by hot rolling, extruding, or forging.
Billets or bars for reforging may be purchased to this specification.
1.2 These steels are generally used for parts requiring corrosion resistance and high strength at room temperature, or at
temperatures up to 600°F [315°C]; 700°F [370°C] 600 °F [315 °C]; 700 °F [370 °C] for Type 632; 840°F [450°C] 840 °F [450
°C] for Type UNS S46910. They are suitable for machining in the solution-annealed condition after which they may be
age-hardened to the mechanical properties specified in Section 77 without danger of cracking or distortion. Type XM-25 is
machinable in the as-received fully heat treated condition. Type UNS S46910 is suitable for machining in the solution-annealed,
cold-worked, and aged-hardened condition.
1.3 Types 631 and 632 contain a large amount of ferrite in the microstructure and can have low ductility in forgings and larger
diameter bars. Applications should be limited to small diameter bar.
1.4 The values stated in either inch-pound units or SI (metric) units are to be regarded separately as standards; within the text
and tables, the SI units are shown in [brackets]. The values stated in each system are not exact equivalents; therefore, each system
must be used independent of the other. Combining values from the two systems may result in nonconformance with the
specification.
1.5 Unless the order specifies an “M’’“M” designation, the material shall be furnished to inch-pound units.
NOTE 1—For forgings, see Specification A705/A705M.
NOTE 2—For billets and bars for forging see Specification A314.
1.6 This international standard was developed in accordance with internationally recognized principles on standardization
established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued
by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
2. Referenced Documents
3
2.1 ASTM Standards:
A314 Specification for Stainless Steel Billets and Bars for Forging
A370 Test Methods and Definitions for Mechanical Testing of Steel Products
A484/A484M Specification for General Requirements for Stainless Steel Bars, Billets, and Forgings
A705/A705M Specification for Age-Hardening Stainless Steel Forgings
A751 Test Methods, Practices, and Terminology for Chemical Analysis of Steel Products
E527 Practice for Numbering Metals and Alloys in the Unified Numbering System (UNS)
1
'This specification is under the jurisdiction of ASTM Committee A01 on Steel, Stainless Steel and Related Alloys and is the direct responsibility of Subcommittee A01.17
on Flat-Rolled and Wrought Stainless Steel.
Current edition approved May 1, 2013May 1, 2019. Published July 2013June 2019. Originally approved in 1966. Last previous edition approved in 20102013 as
ε1
A564/A564M – 10.A564/A564M – 13 . DOI: 10.1520/A0564_A0564M-13E01.10.1520/A0564_A0564M-19.
2
For ASME Boiler and Pressure Vessel Code applications, see related Specification SA-564/SA-564M in Section II of that Code.
3
For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
*A Summary of Changes section appears at the end of this standard
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1
---------------------- Page: 1 ----------------------
A564/A564M − 19
2.2 Other Documents:
4
SAE J1086 Recommended Practice for Numbering Metals and Alloys (UNS)
3. Ordering Information
3.1 It is the responsibility of t
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.