EN ISO 9017:2013
(Main)Destructive tests on welds in metallic materials - Fracture test (ISO 9017:2001)
Destructive tests on welds in metallic materials - Fracture test (ISO 9017:2001)
This European Standard specifies the sizes of test specimen and the procedures for carrying out fracture tests in order to obtain information about types, sizes and distribution of internal imperfections such as porosities, cracks, lacks of fusion, lacks of penetration and solid inclusions on the fracture surface. This European Standard applies to metallic materials in all form of product with joints made by any fusion welding process with a thickness greater or equal to 2 mm. This European Standard is used if required by the application standard or by the agreement between the contracting parties.
Zerstörende Prüfung von Schweißverbindungen an metallischen Werkstoffen - Bruchprüfung (ISO 9017:2001)
Diese Internationale Norm legt die Größe der Proben und die Verfahren zur Durchführung der Bruchprüfungen fest, um Informationen über die Art, Größe und Verteilung von inneren Unregelmäßigkeiten wie Porositäten, Risse, Bindefehler, ungenügende Durchschweißungen und feste Einschlüsse auf der Bruchfläche zu erlangen.
Diese Internationale Norm gilt für metallische Werkstoffe aller Erzeugnisarten mit Verbindungen, die eine Dicke gleich oder größer 2 mm aufweisen und durch einen Schmelzschweißprozess hergestellt wurden.
Essais destructifs des soudures sur matériaux métalliques - Essai de texture (ISO 9017:2001)
Porušitveni preskusi zvarov na kovinskih materialih - Prelomni preskus (ISO 9017:2001)
Ta mednarodni standard določa velikosti preskusnega vzorca in postopke za izvajanje prelomnih preskusov, da bi pridobili informacije o vrstah, velikostih in porazdelitvi notranjih nepravilnosti, kot so poroznosti, razpoke, preslaba spojitev, preslaba prevaritev in trdni delci na površini zloma. Ta mednarodni standard se uporablja za kovinske materiale v vseh oblikah izdelkov s spoji, ki so izdelani s postopkom talilnega varjenja in katerih debelina je večja ali enaka 2 mm.
General Information
Relations
Standards Content (Sample)
SLOVENSKI STANDARD
01-december-2013
1DGRPHãþD
SIST EN 1320:1998
Porušitveni preskusi zvarov na kovinskih materialih - Prelomni preskus (ISO
9017:2001)
Destructive tests on welds in metallic materials - Fracture test (ISO 9017:2001)
Zerstörende Prüfung von Schweißverbindungen an metallischen Werkstoffen -
Bruchprüfung (ISO 9017:2001)
Essais destructifs des soudures sur matériaux métalliques - Essai de texture (ISO
9017:2001)
Ta slovenski standard je istoveten z: EN ISO 9017:2013
ICS:
25.160.40 Varjeni spoji in vari Welded joints
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.
EUROPEAN STANDARD
EN ISO 9017
NORME EUROPÉENNE
EUROPÄISCHE NORM
August 2013
ICS 25.160.40 Supersedes EN 1320:1996
English Version
Destructive tests on welds in metallic materials - Fracture test
(ISO 9017:2001)
Essais destructifs des soudures sur matériaux métalliques - Zerstörende Prüfung von Schweißverbindungen an
Essai de texture (ISO 9017:2001) metallischen Werkstoffen - Bruchprüfung (ISO 9017:2001)
This European Standard was approved by CEN on 8 August 2013.
CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European
Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national
standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN member.
This European Standard exists in three official versions (English, French, German). A version in any other language made by translation
under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management Centre has the same
status as the official versions.
CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia,
Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania,
Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and United
Kingdom.
EUROPEAN COMMITTEE FOR STANDARDIZATION
COMITÉ EUROPÉEN DE NORMALISATION
EUROPÄISCHES KOMITEE FÜR NORMUNG
Management Centre: Avenue Marnix 17, B-1000 Brussels
© 2013 CEN All rights of exploitation in any form and by any means reserved Ref. No. EN ISO 9017:2013: E
worldwide for CEN national Members.
Contents Page
Foreword .3
Foreword
The text of ISO 9017:2001 has been prepared by Technical Committee ISO/TC 44 “Welding and allied
processes” of the International Organization for Standardization (ISO) and has been taken over as EN ISO
9017:2013 by Technical Committee CEN/TC 121 “Welding” the secretariat of which is held by DIN.
This European Standard shall be given the status of a national standard, either by publication of an identical
text or by endorsement, at the latest by February 2014, and conflicting national standards shall be withdrawn
at the latest by February 2014.
Attention is drawn to the possibility that some of the elements of this document may be the subject of patent
rights. CEN [and/or CENELEC] shall not be held responsible for identifying any or all such patent rights.
This document supersedes EN 1320:1996.
According to the CEN-CENELEC Internal Regulations, the national standards organizations of the following
countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech
Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece,
Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal,
Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and the United Kingdom.
Endorsement notice
The text of ISO 9017:2001 has been approved by CEN as EN ISO 9017:2013 without any modification.
INTERNATIONAL ISO
STANDARD 9017
First edition
2001-04-01
Destructive tests on welds in metallic
materials — Fracture test
Essais destructifs des soudures sur matériaux métalliques — Essai de
texture
Reference number
ISO 9017:2001(E)
©
ISO 2001
ISO 9017:2001(E)
PDF disclaimer
This PDF file may contain embedded typefaces. In accordance with Adobe's licensing policy, this file may be printed or viewed but shall not
be edited unless the typefaces which are embedded are licensed to and installed on the computer performing the editing. In downloading this
file, parties accept therein the responsibility of not infringing Adobe's licensing policy. The ISO Central Secretariat accepts no liability in this
area.
Adobe is a trademark of Adobe Systems Incorporated.
Details of the software products used to create this PDF file can be found in the General Info relative to the file; the PDF-creation parameters
were optimized for printing. Every care has been taken to ensure that the file is suitable for use by ISO member bodies. In the unlikely event
that a problem relating to it is found, please inform the Central Secretariat at the address given below.
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means, electronic
or mechanical, including photocopying and microfilm, without permission in writing from either ISO at the address below or ISO's member body
in the country of the requester.
ISO copyright office
Case postale 56 � CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail copyright@iso.ch
Web www.iso.ch
Printed in Switzerland
ii © ISO 2001 – All rights reserved
ISO 9017:2001(E)
Contents Page
Foreword.iv
1 Scope .1
2 Normative references .1
3 Terms and definitions .1
4 Principle.2
5 Symbols and abbreviated terms .2
6 Dimensions of test pieces .4
7 Removal of test specimens .6
7.1 General.6
7.2 Marking .6
7.3 Extraction .6
7.4 Preparation.6
8 Test procedure.9
8.1 Butt welds.9
8.2 Fillet welds.11
8.3 Special recommendations for ductile weld metals .11
9 Test result.12
10 Test report .12
Annex A (informative) Example of a test report .13
ISO 9017:2001(E)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO
member bodies). The work of preparing International Standards is normally carried out through ISO technical
committees. Each member body interested in a subject for which a technical committee has been established has
the right to be represented on that committee. International organizations, governmental and non-governmental, in
liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical
Commission (IEC) on all matters of electrotechnical standardization.
International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 3.
Draft International Standards adopted by the technical committees are circulated to the member bodies for voting.
Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote.
Attention is drawn to the possibility that some of the elements of this International Standard may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights.
International Standard ISO 9017 was prepared by Technical Committee ISO/TC 44, Welding and allied processes,
Subcommittee SC 5, Testing and inspection of welds.
Annex A of this International Standard is for information only.
iv © ISO 2001 – All rights reserved
INTERNATIONAL STANDARD ISO 9017:2001(E)
Destructive tests on welds in metallic materials — Fracture test
1 Scope
This International standard specifies the sizes of test specimen and the procedures for carrying out fracture tests in
order to obtain information about types, sizes and distribution of internal imperfections such as porosities, cracks,
lack of fusion, lack of penetration and solid inclusions on the fracture surface.
This International Standard applies to metallic materials in all forms of product with joints made by any fusion
welding process with a thickness greater or equal to 2 mm.
2 Normative references
The following normative documents contain provisions which, through reference in this text, constitute provisions of
this International Standard. For dated references, subsequent amendments to, or revisions of, any of these
publications do not apply. However, parties to agreements based on this International Standard are encouraged to
investigate the possibility of applying the most recent editions of the normative documents indicated below. For
undated references, the latest edition of the normative document referred to applies. Members of ISO and IEC
maintain registers of currently valid International Standards.
1)
ISO 5817:— , Welding — Fusion-welded joints in steel, nickel, titanium and their alloys (beam welding
excluded) — Quality levels for imperfections.
ISO 10042, Arc-welded joints in aluminium and its weldable alloys — Guidance on quality levels for imperfections.
EN 970, Non-destructive examination of fusion welds — Visual examination.
3 Terms and definitions
For the purposes of this International Standard, the following terms and definitions apply.
3.1
examination length
L
f
length of the test specimen measured along the weld axis between any side notches
SeeFigure6.
3.2
total examination length
�L
f
sum of the lengths of all the test specimens comprising the test piece, measured along the weld axis, of the fracture
faces between the side notches of the test specimens
SeeFigure6.
1) To be published. (Revision of ISO 5817:1992)
ISO 9017:2001(E)
3.3
examination thickness
a
f
thickness of the fracture area for each test specimen
See Figures 7and 8.
3.4
examination area
A
f
product of the examination length and the examination thickness for each test specimen
3.5
total examination area
�A
f
sum of all examination areas
4Principle
Fracture the joint through the weld metal in order to examine the fracture surface. The fracture can be induced by
bending or tension, static or dynamic loading. Furthermore, notch dimensions and temperature can be varied to
induce the fracture.
Unless otherwise specified, the test shall be carried out at ambient temperature (23� 5) °C.
5 Symbols and abbreviated terms
The symbols and abbreviated terms to be used for fracture tests are specified in Table 1 and represented in
Figures 5 to 8.
Normally, it is sufficient to give the basic denomination, but for special applications, additional denominations about
the notching and test method can be requested.
EXAMPLE 1 Test specimen taken from a fillet weld with an examination length of 40 mm and examination thickness of
10 mm.
Without any requirement about notching and test method:
Basic denomination: FW/(L a )
f f
i.e. for this example:
FW/(40 � 10)
With additional requirement (square face notching and test method):
Comprehensive denomination: FW/(L a )/Fq See Figure 8
f f
i.e. for this example:
FW/(40 � 10)/Fq See Figure 8
2 © ISO 20
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.