IEC 60249-2-2:1985/AMD5:2000

Amendment 5 - Base materials for printed circuits. Part 2: Specifications. Specification No. 2: Phenolic cellulose paper copper-clad laminated sheet, economic quality

Amendement 5 - Matériaux de base pour circuits imprimés. Deuxième partie: Spécifications. Spécification n° 2: Feuille de papier cellulose phénolique recouverte de cuivre, de qualité économique

General Information

• Status: Replaced
• Publication Date: 29-Mar-2000
• ICS: 31.180 - Printed circuits and boards
• Technical Committee: TC 91 - Electronics assembly technology
• Drafting Committee: WG 1 - TC 91/WG 1
• Current Stage: WPUB - Publication withdrawn
• Completion Date: 15-Oct-2004

Relations

• Replaced By: IEC 61249-2-1:2005 - Materials for printed boards and other interconnecting structures - Part 2-1: Reinforced base materials, clad and unclad - Phenolic cellulose paper reinforced laminated sheets, economic grade, copper clad
• Effective Date: 05-Sep-2023

Standards Content (Sample)

NORME CEI
INTERNATIONALE IEC
60249-2-2
INTERNATIONAL
STANDARD
AMENDEMENT 5
AMENDMENT 5
2000-03
Amendement 5
Matériaux de base pour circuits imprimés –
Partie 2:
Spécifications –
Spécification n° 2: Feuille de papier cellulose
phénolique recouverte de cuivre,
de qualité économique
Amendment 5
Base materials for printed circuits –
Part 2:
Specifications –
Specification No. 2: Phenolic cellulose paper
copper-clad laminated sheet, economic quality

 IEC 2000 Droits de reproduction réservés  Copyright - all rights reserved
International Electrotechnical Commission 3, rue de Varembé Geneva, Switzerland
Telefax: [phone] e-mail: [e-mail] IEC web site http://www.iec.ch
CODE PRIX
Commission Electrotechnique Internationale
F
PRICE CODE
International Electrotechnical Commission
Pour prix, voir catalogue en vigueur
For price, see current catalogue

– 2 – 60249-2-2 Amend. 5 © CEI:2000

AVANT-PROPOS
Le présent amendement a été établi par le comité d'études 52 de la CEI: Circuits imprimés.

Cet amendement incorpore l'amendement 3 (1993) et l'amendement 4 (1994).

Le texte de cet amendement est issu des documents suivants:

FDIS Rapport de vote
52/836/FDIS 52/847/RVD
Le rapport de vote indiqué dans le tableau ci-dessus donne toute information sur le vote ayant
abouti à l'approbation de cet amendement.
Une ligne verticale dans la marge indique le texte de l'amendement 5.
___________
Page 8
4 Propriétés électriques
Modifier le tableau I comme suit:
Tableau I
Propriété Méthode d'essai Exigences
(paragraphe de la CEI 60249-1)
Corrosion de surface 2.4 A l'étude
Corrosion de bord 2.5 A l'étude
Permittivité relative après 2.7 La valeur moyenne ne doit pas
chaleur humide et reprise être supérieure à 5,5
Facteur de dissipation 2.7 La valeur moyenne ne doit pas
diélectrique après chaleur être supérieure à 0,1
humide et reprise
Résistance superficielle après 2.2
10 MΩ min.
chaleur humide et reprise
Résistivité transversale après 2.3
10 MΩm min.
chaleur humide et reprise
Page 12
5.3 Courbure et vrillage maximaux
Remplacer le titre par le nouveau titre suivant:
5.3 Courbure et vrillage
60249-2-2 Amend. 5 © IEC:2000 – 3 –

FOREWORD
This amendment has been prepared by IEC technical committee 52: Printed circuits.

This amendment incorporates amendment 3 (1993) and amendment 4 (1994).

The text of this amendment is based on the following documents:

FDIS Report on voting
52/836/FDIS 52/847/RVD
Full information on the voting for the approval of this amendment can be found in the report
on voting indicated in the above table.
A vertical line in the margin indicates the text of amendment 5.
___________
Page 9
4 Electrical properties
Amend table I as follows:
Table I
Property Test method Requirements
(subclause of IEC 60249-1)
Surface corrosion 2.4 Under consideration
Corrosion at the edge 2.5 Under consideration
Relative permittivity 2.7 The average value
after damp heat and recovery shall not exceed 5,5
Dielectric dissipation factor 2.7 The average value
after damp heat and recovery shall not exceed 0,1
Surface resistance 2.2
10 MΩ min.
after damp heat and recovery
Volume resistivity 2.3
10 MΩm min.
after damp heat and recovery
Page 13
5.3 Maximum bow and twist
Replace the title by the following title:
5.3 Bow and twist
– 4 – 60249-2-2 Amend. 5 © CEI:2000

Remplacer le tableau IV par le nouveau tableau suivant:

Tableau IV – Courbure et vrillage maximaux

PropriétésMéthode d’essai Epaisseur Dimensions du Exigence(s)

nominale panneau Pourcentage maximal

(IEC 61189-2)
Longueur
Feuille de cuivre Feuille de cuivre

maximale
sur une face sur deux faces
mm mm
Courbure et 2M01 ≥0,8 ≤1,2 ≤350 3,0 2,5
vrillage
2,8 2,3
>350 ≤500
2,5 2,0
>500
2,5 2,0
>1,2 ≤1,6 ≤350
2,3 1,8
>350 ≤500
2,0 1,5
>500
>1,6 2,0 1,5
≤ 350
1,8 1,4
>350 ≤500
1,5 1,3
>500
Courbure et 2M02 A l’étude
vrillage après
gravure et
chauffage
NOTE Les exigences pour la courbure et le vrillage ne s’appliquent qu’aux stratifiés recouverts de cuivre sur une
face avec une épaisseur de feuille maximale de 105 μm (915 g/m ) et aux stratifiés recouverts de cuivre sur deux
faces avec une différence d’épaisseur maximale de la feuille de 70 μm (610 g/m ).
Les exigences pour les stratifiés en dehors de ces limites feront l’objet d’un accord entre l’acheteur et le
fournisseur.
Supprimer le tableau V.
Page 14
5.4 Propriétés concernant l’adhérence de la feuille de cuivre
Remplacer la première ligne du tableau VI de la manière indiquée ci-dessous :
Méthode d'essai
Propriété Exigences
(CEI 61189-2)
Force d'arrachement 2M05 Pas inférieure à 25 N
Tableau VI, colonne 1
Supprimer «1,1,1-trichloroéthane» et remplacer «Solvants autres que le trichloroéthane» par
«Solvants après accord entre acheteur et fournisseur».
Colonne 3:
Supprimer la phrase «Après accord entre acheteur et fournisseur».

60249-2-2 Amend. 5 © IEC:2000 – 5 –

Replace table IV by the following new table:

Table IV – Maximum bow and twist

Property Test method Nominal Panel dimension Requirement(s)

(IEC 61189-2) thickness Maximum length % maximum

Copper foil on Copper foil on
mm mm
one side both sides
Bow and twist 2M01 3,0 2,5
≥0,8 ≤1,2 ≤350
2,8 2,3
>350 ≤500
2,5 2,0
>500
2,5 2,0
>1,2 ≤1,6 ≤350
2,3 1,8
>350 ≤500
2,0 1,5
>500
>1,6 ≤350 2,0 1,5
1,8 1,4
>350 ≤500
1,5 1,3
>500
Bow and twist 2M02 Under consideration
after etching
and heating
NOTE The requirements for bow and twist apply only to one sided copper-clad laminates with maximum foil
thickness of 105 μm (915 g/m ) and double sided copper-clad laminates with maximum foil thickness difference of
70 μm (610 g/m ).
Requirements for laminates beyond these limits shall be subject to agreement between purchaser and supplier.
Delete table V.
Page 15
5.4 Properties related to the copper foil bond
Replace the first row of table VI as follows:
Test method
Property Requirement
(IEC 61189-2)
Pull-off strength 2M05 Not less than 25 N

Table VI, column 1
Delete "1,1,1-trichloroethane" and replace "Solvents other than trichloroethane" by "Solvents
as agreed upon between purchaser and supplier".
Column 3:
Delete the sentence "As agreed upon between purchaser and supplier".

----
...