ISO 75-3

Plastics — Determination of temperature of deflection under load — Part 3: High-strength thermosetting laminates and long-fibre-reinforced plastics

ISO 75-3:2004 specifies a method for the determination of the temperature of deflection under load of high-strength thermosetting laminates and compression-moulded long-fibre-reinforced plastics in which the fibre length is greater than 7,5 mm. The flexural stress used is not fixed, as in ISO 75-2, but is a fraction (1/1000) of the initial (room-temperature) flexural modulus of the material under test. This allows the method to be applied to materials with a wide range of flexural moduli.

Plastiques — Détermination de la température de fléchissement sous charge — Partie 3: Stratifiés thermodurcissables à haute résistance et plastiques renforcés de fibres longues

L'ISO 75-3:2004 spécifie une méthode permettant de déterminer la température de fléchissement sous charge de stratifiés thermodurcissables à haute résistance et de plastiques renforcés de fibres longues moulés par compression dans lesquels la longueur de fibre est supérieure à 7,5 mm. La contrainte de flexion utilisée n'est pas fixée, comme dans l'ISO 75-2, mais représente une fraction (1/1 000) du module initial de flexion (à température ambiante) du matériau soumis à essai. La méthode peut ainsi être appliquée à des matériaux caractérisés par une large gamme de modules de flexion.

General Information

• Status: Not Published
• ICS: 83.080.10 - Thermosetting materials
• ICS: 83.120 - Reinforced plastics
• Technical Committee: ISO/TC 61/SC 2 - Mechanical behavior
• Drafting Committee: ISO/TC 61/SC 2 - Mechanical behavior
• Current Stage: 6000 - International Standard under publication
• Start Date: 09-Jul-2025
• Completion Date: 12-Jul-2025

Relations

• Revises: ISO 75-3:2004 - Plastics — Determination of temperature of deflection under load — Part 3: High-strength thermosetting laminates and long-fibre-reinforced plastics
• Effective Date: 22-Oct-2022

Standards Content (Sample)

FINAL DRAFT
International
Standard
ISO/FDIS 75-3
ISO/TC 61/SC 2
Plastics — Determination of
Secretariat: KATS
temperature of deflection under
Voting begins on:
load —
2025-05-13
Part 3:
Voting terminates on:
2025-07-08
High-strength thermosetting
laminates and long-fibre-reinforced
plastics
Plastiques — Détermination de la température de fléchissement
sous charge —
Partie 3: Stratifiés thermodurcissables à haute résistance et
plastiques renforcés de fibres longues
RECIPIENTS OF THIS DRAFT ARE INVITED TO SUBMIT,
WITH THEIR COMMENTS, NOTIFICATION OF ANY
RELEVANT PATENT RIGHTS OF WHICH THEY ARE AWARE
AND TO PROVIDE SUPPOR TING DOCUMENTATION.
IN ADDITION TO THEIR EVALUATION AS
BEING ACCEPTABLE FOR INDUSTRIAL, TECHNO-
ISO/CEN PARALLEL PROCESSING LOGICAL, COMMERCIAL AND USER PURPOSES, DRAFT
INTERNATIONAL STANDARDS MAY ON OCCASION HAVE
TO BE CONSIDERED IN THE LIGHT OF THEIR POTENTIAL
TO BECOME STAN DARDS TO WHICH REFERENCE MAY BE
MADE IN NATIONAL REGULATIONS.
Reference number
ISO/FDIS 75-3:2025(en) © ISO 2025

FINAL DRAFT
ISO/FDIS 75-3:2025(en)
International
Standard
ISO/FDIS 75-3
ISO/TC 61/SC 2
Plastics — Determination of
Secretariat: KATS
temperature of deflection under
Voting begins on:
load —
Part 3:
Voting terminates on:
High-strength thermosetting
laminates and long-fibre-reinforced
plastics
Plastiques — Détermination de la température de fléchissement
sous charge —
Partie 3: Stratifiés thermodurcissables à haute résistance et
plastiques renforcés de fibres longues
RECIPIENTS OF THIS DRAFT ARE INVITED TO SUBMIT,
WITH THEIR COMMENTS, NOTIFICATION OF ANY
RELEVANT PATENT RIGHTS OF WHICH THEY ARE AWARE
AND TO PROVIDE SUPPOR TING DOCUMENTATION.
© ISO 2025
IN ADDITION TO THEIR EVALUATION AS
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
BEING ACCEPTABLE FOR INDUSTRIAL, TECHNO-
ISO/CEN PARALLEL PROCESSING
LOGICAL, COMMERCIAL AND USER PURPOSES, DRAFT
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on
INTERNATIONAL STANDARDS MAY ON OCCASION HAVE
the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address below
TO BE CONSIDERED IN THE LIGHT OF THEIR POTENTIAL
or ISO’s member body in the country of the requester.
TO BECOME STAN DARDS TO WHICH REFERENCE MAY BE
MADE IN NATIONAL REGULATIONS.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: [phone]
Email: [e-mail]
Website: www.iso.org
Published in Switzerland Reference number
ISO/FDIS 75-3:2025(en) © ISO 2025

ii
ISO/FDIS 75-3:2025(en)
Contents Page
Foreword .iv
Introduction .v
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Principle . 1
5 Apparatus . 2
5.1 Means of producing a flexural stress .2
5.2 Heating equipment .2
5.3 Weights .2
5.4 Temperature-measuring instrument .2
5.5 Deflection-measuring instrument .2
5.6 Micrometers and gauges .2
6 Test specimens . 2
6.1 General .2
6.2 Shape and dimensions .3
6.3 Specimen inspection .3
6.4 Number of test specimens .3
6.5 Test-specimen preparation .3
6.6 Annealing .3
7 Conditioning and drying . 4
8 Procedure . 4
8.1 Calculation of the force to be applied .4
8.2 Initial temperature of the heating equipment .4
8.3 Measurement .4
9 Expression of results . 5
10 Precision . 5
11 Test report . 5
Annex A (informative) Precision data . 6
Bibliography .11

iii
ISO/FDIS 75-3:2025(en)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out through
ISO technical committees. Each member body interested in a subject for which a technical committee
has been established has the right to be represented on that committee. International organizations,
governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely
with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are described
in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the different types
of ISO document should be noted. This document was drafted in accordance with the editorial rules of the
ISO/IEC Directives, Part 2 (see www.iso.org/directives).
ISO draws attention to the possibility that the implementation of this document may involve the use of (a)
patent(s). ISO takes no position concerning the evidence, validity or applicability of any claimed patent
rights in respect thereof. As of the date of publication of this document, ISO had not received notice of (a)
patent(s) which may be required to implement this document. However, implementers are cautioned that
this may not represent the latest information, which may be obtained from the patent database available at
www.iso.org/patents. ISO shall not be held responsible for identifying any or all such patent rights.
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and expressions
related to conformity assessment, as well as information about ISO's adherence to the World Trade
Organization (WTO) principles in the Technical Barriers to Trade (TBT), see www.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 61, Plastics, Subcommittee SC 2, Mechanical
behavior, in collaboration with the European Committee for Standardization (CEN) Technical Committee
CEN/TC 249, Plastics, in accordance with the Agreement on technical cooperation between ISO and CEN
(Vienna Agreement).
This third edition cancels and replaces the second edition (ISO 75-3:2004), which has been technically
revised.
The main changes are as follows:
— the Introduction, Scope and Principle clauses (Clause 4) have been updated;
— the normative references and the bibliography have been updated;
— the span definition has been changed by using a formula in accordance with ISO 178;
— preferred specimen thickness dimensions have been added;
— examples of initial deflection, error and standard deflection calculations have been added;
— a precision statement has been added as a new Annex A.
A list of all parts in the ISO 75 series can be found on the ISO website.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www.iso.org/members.html.

iv
ISO/FDIS 75-3:2025(en)
Introduction
The first edition (1993) of this document described a method for the determination of the temperature of
deflection under load (bending stress) of high-strength thermosetting laminates and compression-moulded
long-fibre reinforced plastics. The test load used was not a fixed load, as in ISO 75-2, but a function (1/10) of
the ultimate or specified load applied flatwise on specimen.
In the second edition of (2004) this document, the test load is determined as a fraction of the flexural
modulus of the material under test. This has the advantage that the test load is a fraction of the flexural
strength of the material and allowed the method to be applied to materials with a wide range of flexural
moduli. The test determines the temperature-dependent decrease in the flexural modulus. Because tensile
modulus and tensile strength are not necessarily related, using the flexural modulus to determine the test
load leads to more readily comparable descriptions of material behaviour.
The flexural strain increase at which the temperature of deflection under load is measured had been
increased from 0,1 % to 0,2 % to obtain greater commonality with ISO 75-2.
In this third edition, the calculation of the span value has been updated to conform with a similar and widely
used standard (i.e. ISO 178).
It is also reconfirmed that the determination of the temperature under load method described in the ISO 75
series has a great range of applicability. More in details, this method is suitable for use with the following
range of materials:
— thermosetting moulding materials, reinforced compounds, with fibre length, prior to processing, greater
than 7,5 mm; thermosetting sheets.
Despite the title clearly mention thermosetting based materials, the method has been validated also for:
— thermoplastic moulding, extrusion and casting materials, reinforced compounds, with fibre length, prior
to processing, greater than 7,5 mm; rigid thermoplastics sheets.
The method
...

ISO/FDIS 75-3:2025(en)
ISO/TC 61/SC 2
Secretariat: KATS
Date: 2025-02-04-28
Plastic Plastics — Determination of temperature of deflection under
load — —
Part 3:
High-strength thermosetting laminates and long-fibre-reinforced
plastics
Plastiques — Détermination de la température de fléchissement sous charge —
Partie 3: Stratifiés thermodurcissables à haute résistance et plastiques renforcés de fibres longues
FDIS stage
ISO/FDIS 75-3:2025(en)
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication
may be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying,
or posting on the internet or an intranet, without prior written permission. Permission can be requested from either ISO
at the address below or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: + 41 22 749 01 11
EmailE-mail: [e-mail]
Website: www.iso.orgwww.iso.org
Published in Switzerland
ii
ISO/FDIS 75-3:2025(en)
Contents
Foreword . v
Introduction . vi
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Principle . 2
5 Apparatus . 2
6 Test specimens . 3
7 Conditioning and drying . 4
8 Procedure . 4
9 Expression of results . 5
10 Precision . 5
11 Test report . 5
Annex A (informative) Precision data . 7
Bibliography . 13

Foreword . 4
Introduction . 5
1 Scope . 6
2 Normative references . 6
3 Terms and definitions . 6
4 Principle . 6
5 Apparatus . 7
5.1 Means of producing a flexural stress . 7
5.2 Heating equipment . 7
5.3 Weights . 7
5.4 Temperature-measuring instrument . 7
5.5 Deflection-measuring instrument . 7
5.6 Micrometers and gauges . 7
6 Test specimens . 7
6.1 General . 7
6.2 Shape and dimensions . 7
6.3 Specimen inspection . 7
6.4 Number of test specimens . 7
6.5 Test-specimen preparation . 7
6.6 Annealing . 8
7 Conditioning . 8
8 Procedure . 8
8.1 Calculation of the force to be applied . 8
8.2 Initial temperature of the heating equipment . 9
© ISO 2025 – All rights reserved
iii
ISO/FDIS 75-3:2025(en)
8.3 Measurement . 9
9 Expression of results . 10
10 Precision . 10
11 Test report . 10
Annex A (informative) Precision data . 11
A.1 General . 11
A.1.1 Interlaboratory tests . 11
A.1.2 Concept of r and R . 11
A.2 Interlaboratory test conditions . 12
A.2.1 Material 1 . 12
A.2.2 Material 2 . 12
A.2.3 Material 3 . 13
A.2.3.1 Material 3 – test 1 . 13
A.2.3.2 Material 3 – test 2 . 13
A.2.4 Material 4 . 13
A.2.4.1 Material 4 – test 1 . 13
A.2.4.2 Material 4 – test 2 . 14
A.2.5 Material 5 . 14
A.2.5.1 Material 5 – test 1 . 14
A.2.5.2 Material 5 – test 2 . 14
A.3 Interlaboratory test results . 16
A.3.1 Test results . 16
Bibliography . 17
iv
ISO/FDIS 75-3:2025(en)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out through
ISO technical committees. Each member body interested in a subject for which a technical committee has been
established has the right to be represented on that committee. International organizations, governmental and
non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the
International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are described
in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the different types of
ISO document should be noted. This document was drafted in accordance with the editorial rules of the
ISO/IEC Directives, Part 2 (see www.iso.org/directives).
ISO draws attention to the possibility that the implementation of this document may involve the use of (a)
patent(s). ISO takes no position concerning the evidence, validity or applicability of any claimed patent rights
in respect thereof. As of the date of publication of this document, ISO had not received notice of (a) patent(s)
which may be required to implement this document. However, implementers are cautioned that this may not
represent the latest information, which may be obtained from the patent database available at
www.iso.org/patents.www.iso.org/patents. ISO shall not be held responsible for identifying any or all such
patent rights.
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and expressions
related to conformity assessment, as well as information about ISO's adherence to the World Trade
Organization (WTO) principles in the Technical Barriers to Trade (TBT), see
www.iso.org/iso/foreword.htmlwww.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 61, Plastics, Subcommittee SC 2, Mechanical
behavior, in collaboration with the European Committee for Standardization (CEN) Technical Committee
CEN/TC 249, Plastics, in accordance with the Agreement on technical cooperation between ISO and CEN
(Vienna Agreement).
This third edition cancels and replaces the second edition (ISO 75-3:2004), which has been technically revised.
The main changes are as follows:
— — the Introduction, Scope and Principle (Clause 4)clauses (4) have been updated;
— — the normative references and the bibliography have been updated;
— — the span definition has been changed by using a formula complyingin accordance with ISO 178;
— — preferred specimen thickness dimensions have been added;
— — examples of initial deflection, error and standard deflection calculations have been added;
— — a precision statement has been added as a new Annex A.Anne
...

PROJET FINAL
Norme
internationale
ISO/FDIS 75-3
ISO/TC 61/SC 2
Plastiques — Détermination de la
Secrétariat: KATS
température de fléchissement sous
Début de vote:
charge —
2025-05-13
Partie 3:
Vote clos le:
2025-07-08
Stratifiés thermodurcissables à
haute résistance et plastiques
renforcés de fibres longues
Plastics — Determination of temperature of deflection under
load —
Part 3: High-strength thermosetting laminates and long-fibre-
reinforced plastics
LES DESTINATAIRES DU PRÉSENT PROJET SONT
INVITÉS À PRÉSENTER, AVEC LEURS OBSERVATIONS,
NOTIFICATION DES DROITS DE PROPRIÉTÉ DONT ILS
AURAIENT ÉVENTUELLEMENT CONNAISSANCE ET À
FOURNIR UNE DOCUMENTATION EXPLICATIVE.
OUTRE LE FAIT D’ÊTRE EXAMINÉS POUR
ÉTABLIR S’ILS SONT ACCEPTABLES À DES FINS
INDUSTRIELLES, TECHNOLOGIQUES ET COM-MERCIALES,
AINSI QUE DU POINT DE VUE DES UTILISATEURS, LES
PROJETS DE NORMES
TRAITEMENT PARALLÈLE ISO/CEN
INTERNATIONALES DOIVENT PARFOIS ÊTRE CONSIDÉRÉS
DU POINT DE VUE DE LEUR POSSI BILITÉ DE DEVENIR DES
NORMES POUVANT
SERVIR DE RÉFÉRENCE DANS LA RÉGLEMENTATION
NATIONALE.
Numéro de référence
ISO/FDIS 75-3:2025(fr) © ISO 2025

PROJET FINAL
ISO/FDIS 75-3:2025(fr)
Norme
internationale
ISO/FDIS 75-3
ISO/TC 61/SC 2
Plastiques — Détermination de la
Secrétariat: KATS
température de fléchissement sous
Début de vote:
charge —
2025-05-13
Partie 3:
Vote clos le:
2025-07-08
Stratifiés thermodurcissables à
haute résistance et plastiques
renforcés de fibres longues
Plastics — Determination of temperature of deflection under load —
Part 3: High-strength thermosetting laminates and long-fibre-
reinforced plastics
LES DESTINATAIRES DU PRÉSENT PROJET SONT
INVITÉS À PRÉSENTER, AVEC LEURS OBSERVATIONS,
NOTIFICATION DES DROITS DE PROPRIÉTÉ DONT ILS
AURAIENT ÉVENTUELLEMENT CONNAISSANCE ET À
FOURNIR UNE DOCUMENTATION EXPLICATIVE.
DOCUMENT PROTÉGÉ PAR COPYRIGHT
OUTRE LE FAIT D’ÊTRE EXAMINÉS POUR
ÉTABLIR S’ILS SONT ACCEPTABLES À DES FINS
© ISO 2025 INDUSTRIELLES, TECHNOLOGIQUES ET COM-MERCIALES,
AINSI QUE DU POINT DE VUE DES UTILISATEURS, LES
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
PROJETS DE NORMES
TRAITEMENT PARALLÈLE ISO/CEN
INTERNATIONALES DOIVENT PARFOIS ÊTRE CONSIDÉRÉS
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
DU POINT DE VUE DE LEUR POSSI BILITÉ DE DEVENIR DES
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
NORMES POUVANT
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
SERVIR DE RÉFÉRENCE DANS LA RÉGLEMENTATION
NATIONALE.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: [phone]
E-mail: [e-mail]
Web: www.iso.org
Publié en Suisse Numéro de référence
ISO/FDIS 75-3:2025(fr) © ISO 2025

ii
ISO/FDIS 75-3:2025(fr)
Sommaire Page
Avant-propos .iv
Introduction .v
1 Domaine d’application . 1
2 Références normatives . 1
3 Termes et définitions . 1
4 Principe. 2
5 Appareillage . 2
5.1 Moyens de produire une contrainte en flexion .2
5.2 Dispositif de chauffage .2
5.3 Poids .2
5.4 Instrument de mesure de la température .2
5.5 Instrument de mesure du fléchissement .2
5.6 Micromètres et comparateurs .2
6 Éprouvettes. 3
6.1 Généralités .3
6.2 Forme et dimensions .3
6.3 Vérification des éprouvettes .3
6.4 Nombre d’éprouvettes .3
6.5 Préparation des éprouvettes .3
6.6 Recuit .4
7 Conditionnement et séchage . 4
8 Mode opératoire . 4
8.1 Calcul de la force à appliquer .4
8.2 Température initiale du dispositif de chauffage .4
8.3 Mesurage .4
9 Expression des résultats . 5
10 Fidélité . 5
11 Rapport d’essai . 5
Annexe A (informative) Données de fidélité . 6
Bibliographie .12

iii
ISO/FDIS 75-3:2025(fr)
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale d’organismes nationaux
de normalisation (comités membres de l’ISO). L’élaboration des Normes internationales est en général
confiée aux comités techniques de l’ISO. Chaque comité membre intéressé par une étude a le droit de faire
partie du comité technique créé à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec l’ISO participent également aux travaux. L’ISO collabore étroitement avec
la Commission électrotechnique internationale (IEC) en ce qui concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier, de prendre note des différents
critères d’approbation requis pour les différents types de documents ISO. Le présent document a
été rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir
www.iso.org/directives).
L’attention est attirée sur le fait que certains des éléments du présent document peuvent faire l’objet de
droits de brevet. L’ISO ne saurait être tenue pour responsable de ne pas avoir identifié tout ou partie de tels
droits de brevet. Les détails concernant les références aux droits de brevet identifiés lors de l’élaboration du
document sont indiqués dans l’Introduction et/ou dans la liste des déclarations de brevets reçues par l’ISO
(voir www.iso.org/brevets).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données pour
information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l’ISO liés à l’évaluation de la conformité, ou pour toute information au sujet de l’adhésion de
l’ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles techniques au
commerce (OTC), voir www.iso.org/avant-propos.
Le présent document a été élaboré par le comité technique ISO/TC 61, Plastiques, sous-comité SC 2,
Comportement mécanique, en collaboration avec le comité technique CEN/TC 249, Plastiques, du Comité
européen de normalisation (CEN), conformément à l’Accord de coopération technique entre l’ISO et le CEN
(Accord de Vienne).
Cette troisième édition annule et remplace la deuxième édition (ISO 75-3:2004), qui a fait l’objet d’une
révision technique.
Les principales modifications sont les suivantes:
— l’Introduction, le Domaine d’application et l’Article Principe (Article 4) ont été mis à jour;
— les références normatives et la bibliographie ont été mises à jour;
— la définition de portée a été modifiée en utilisant une formule conforme à l’ISO 178;
— l’épaisseur d’éprouvette recommandée a été ajoutée;
— des exemples de calculs de fléchissement initial, d’erreur et de fléchissement normalisé ont été ajoutés;
— la déclaration de la fidélité a été ajoutée sous forme d’une nouvelle Annexe A.
Une liste de toutes les parties de la série ISO 75 est disponible sur le site web de l’ISO.
Il convient que l’utilisateur adresse tout retour d’information ou toute question concernant le présent
document à l’organisme national de normalisation de son pays. Une liste exhaustive desdits organismes se
trouve à l’adresse www.iso.org/fr/members.html.

iv
ISO/FDIS 75-3:2025(fr)
Introduction
La première édition (1993) du présent document décrivaient une méthode permettant de déterminer la
température de fléchissement sous charge (contrainte en flexion) de stratifiés thermodurcissables à haute
résistance et de plastiques renforcés de fibres longues moulés par compression. La charge d’essai utilisée
n’était pas une charge fixe, comme dans l’ISO 75-2, mais une fonction (1/10) de la charge ultime ou spécifiée
appliquée à plat sur l’éprouvette.
Dans la deuxième édition (2004) du présent document, la charge d’essai est déterminée comme une fraction
du module en flexion du matériau soumis à essai. L’avantage est que la charge d’essai est une fraction de la
résistance en flexion du matériau, ce qui permet d’appliquer la méthode à des matériaux caractérisés par
une large gamme de modules en flexion. Cet essai détermine la diminution en fonction de la température
du module en flexion. Le module en traction et la résistance en traction n’étant pas nécessairement
corrélés, l’utilisation du module en flexion pour déterminer la charge d’essai conduit à une description plus
comparable du comportement du matériau.
L’accroissement de la déformation en flexion correspondant à la température de fléchissement sous charge a
été majoré de 0,1 % à 0,2 % pour avoir une similitude plus grande avec l’ISO 75-2.
Dans la troisième édition, le calcul de la valeur de la portée a été actualisé pour être conforme à une norme
similaire qui est largement utilisée (à savoir l’ISO 178).
Il est également reconfirmé que le domaine d’application de la méthode de détermination de la tempér
...