ISO 2440:2025

Flexible and rigid cellular polymeric materials — Accelerated ageing tests

This document specifies laboratory procedures which are intended to imitate the effects of naturally occurring reactions such as oxidation or hydrolysis by humidity for flexible and rigid cellular polymeric materials.

Matériaux polymères alvéolaires souples et rigides — Essais de vieillissement accéléré

Le présent document spécifie des méthodes de laboratoire qui ont pour but de reproduire les effets des réactions se produisant naturellement, telles que l’oxydation ou l’hydrolyse causées par l’humidité pour les matériaux polymères alvéolaires souples et rigides.

General Information

• Status: Published
• Publication Date: 02-Jul-2025
• ICS: 83.100 - Cellular materials
• Technical Committee: ISO/TC 45/SC 4 - Products (other than hoses)
• Drafting Committee: ISO/TC 45/SC 4 - Products (other than hoses)
• Current Stage: 6060 - International Standard published
• Start Date: 03-Jul-2025
• Due Date: 10-Jan-2026
• Completion Date: 03-Jul-2025

Relations

• Consolidates: ISO 10802:2020 - Ductile iron pipelines — Hydrostatic testing after installation
• Effective Date: 28-Jan-2023
• Revises: ISO 2440:2019 - Flexible and rigid cellular polymeric materials — Accelerated ageing tests
• Effective Date: 14-Jan-2023

Standards Content (Sample)

International
Standard
ISO 2440
Fifth edition
Flexible and rigid cellular polymeric
2025-07
materials — Accelerated ageing tests
Matériaux polymères alvéolaires souples et rigides — Essais de
vieillissement accéléré
Reference number
© ISO 2025
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on
the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address below
or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: [phone]
Email: [e-mail]
Website: www.iso.org
Published in Switzerland
ii
Contents Page
Foreword .iv
Introduction .v
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Apparatus . 2
4.1 For dry heat ageing .2
4.2 For humidity ageing .2
4.3 For physical property measurements . .2
5 Test pieces . 2
5.1 Number, size and shape .2
5.2 Conditioning.2
6 Procedure . 2
6.1 General .2
6.2 Dry heat ageing .3
6.2.1 Temperature .3
6.2.2 Duration of ageing .3
6.3 Humidity ageing .3
6.3.1 Humidity .3
6.3.2 Temperatures and duration of ageing .3
6.4 Reconditioning.4
7 Calculation and expression of results . 4
7.1 Calculation .4
7.2 Validity .4
7.3 Expression of results . .4
8 Precision data . 4
9 Test report . 4
Annex A (informative) Method for verification of the validity of ageing results . 6
Annex B (informative) Precision data . 7
Bibliography .11

iii
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out through
ISO technical committees. Each member body interested in a subject for which a technical committee
has been established has the right to be represented on that committee. International organizations,
governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely
with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are described
in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the different types
of ISO document should be noted. This document was drafted in accordance with the editorial rules of the
ISO/IEC Directives, Part 2 (see www.iso.org/directives).
ISO draws attention to the possibility that the implementation of this document may involve the use of (a)
patent(s). ISO takes no position concerning the evidence, validity or applicability of any claimed patent
rights in respect thereof. As of the date of publication of this document, ISO had not received notice of (a)
patent(s) which may be required to implement this document. However, implementers are cautioned that
this may not represent the latest information, which may be obtained from the patent database available at
www.iso.org/patents. ISO shall not be held responsible for identifying any or all such patent rights.
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and expressions
related to conformity assessment, as well as information about ISO's adherence to the World Trade
Organization (WTO) principles in the Technical Barriers to Trade (TBT), see www.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 45, Rubber and rubber products, Subcommittee
SC 4, Products (others than hoses), in collaboration with the European Committee for Standardization (CEN)
Technical Committee CEN/TC 249, Plastics, in accordance with the Agreement on technical cooperation
between ISO and CEN (Vienna Agreement).
This fifth edition cancels and replaces the fourth edition (ISO 2440:2019) which has been technically revised.
The main changes are as follows:
— addition of subclause 7.2;
— addition of Clause 9;
— addition of a method for verification in Annex A;
— addition of precision data in Annex B.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www.iso.org/members.html.

iv
Introduction
The measurement of ageing effects, either by oxidation or hydrolysis by humidity, is used to assess the long-
term behaviour of cellular polymeric materials under laboratory conditions. The physical properties of
interest are measured before and after the application of the specified treatments.
Test conditions are given for open cellular latex, open- and closed-cell polyurethane foams, and closed-cell
polyolefin foams.
The effect of the ageing procedures on any of the physical properties of the material can be examined, but
those normally tested are either the elongation and tensile properties, or the compression or indentation
hardness properties.
These tests do not necessarily correlate either with service behaviour or with ageing by exposure to light.
If desired, the ageing conditions contained in this document can be applied to composite structures
containing any of the above types of cellular material. This can be helpful in the investigation of possible
interactions between cellular materials and other substrates. Composite constructions can be in the form of
complete finished products or representative small specimens cut there-from.

v
International Standard ISO 2440:2025(en)
Flexible and rigid cellular polymeric materials — Accelerated
ageing tests
WARNING — Persons using this document should be familiar with normal laboratory practice. This
document does not purport to address all of the safety problems, if any, associated with its use. It is
the responsibility of the user to establish appropriate safety and health practices and to determine
the applicability of any other restrictions.
1 Scope
This document specifies laboratory procedures which are intended to imitate the effects of naturally
occurring reactions such as oxidation or hydrolysis by humidity for flexible and rigid cellular polymeric
materials.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content constitutes
requirements of this document. For dated references, only the edition cited applies. For undated references,
the latest edition of the referenced document (including any amendments) applies.
ISO 23529, Rubber — General procedures for preparing and conditioning test pieces for physical test methods
3 Terms and definitions
For the purposes of this document, the following terms and definitions apply.
ISO and IEC maintain terminology databases for use in standardization at the following addresses:
— ISO Online browsing platform: available at https:// www .iso .org/ obp
— IEC Electropedia: available at https:// www .electropedia .org/
3.1
average value of the property after ageing
X
a
average value from multiple determinations of the property to be investigated, measured after application
of an ageing process
Note 1 to entry: The average value of the property after ageing is expressed in the unit foreseen for this property.
3.2
average value of the property before ageing
X
average value from multiple determinations of the property to be investigated, measured before application
of an ageing process
Note 1 to entry: The average value of the property before ageing is expressed in the unit foreseen for this property.
3.3
percentage change
relative difference of a property before and after an ageing process, measured under repeat conditions
Note 1 to entry: Percentage change is expressed in percent (%).

4 Apparatus
4.1 For dry heat ageing
4.1.1 Oven, with forced circulation, capable of maintaining the required temperature to within ±3 °C.
A device should be used to record the temperature, preferably continuously.
4.2 For humidity ageing
4.2.1 Ageing apparatus, of such a size that the total volume of the test pieces does not exceed 10 % of the
free air space, and such that the test pieces are free of strain, freely exposed to the ageing atmosphere on all
sides and not exposed to light.
4.2.2 Steam autoclave or similar vessel, ca
...

Norme
internationale
ISO 2440
Cinquième édition
Matériaux polymères alvéolaires
2025-07
souples et rigides — Essais de
vieillissement accéléré
Flexible and rigid cellular polymeric materials — Accelerated
ageing tests
Numéro de référence
DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2025
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: [phone]
E-mail: [e-mail]
Web: www.iso.org
Publié en Suisse
ii
Sommaire Page
Avant-propos .iv
Introduction .v
1 Domaine d’application . 1
2 Références normatives . 1
3 Termes et définitions . 1
4 Appareillage . 2
4.1 Pour le vieillissement en chaleur sèche .2
4.2 Pour le vieillissement à l’humidité .2
4.3 Pour le mesurage des caractéristiques physiques .2
5 Éprouvettes. 2
5.1 Nombre, forme et dimensions .2
5.2 Conditionnement .2
6 Mode opératoire . 3
6.1 Généralités .3
6.2 Vieillissement en chaleur sèche .3
6.2.1 Température .3
6.2.2 Durée de vieillissement .3
6.3 Vieillissement à l’humidité .3
6.3.1 Humidité .3
6.3.2 Températures et durées de vieillissement .3
6.4 Reconditionnement .4
7 Calcul et expression des résultats . 4
7.1 Calcul .4
7.2 Validité .4
7.3 Expression des résultats .4
8 Données de fidélité . 4
9 Rapport d’essai . 5
Annexe A (informative) Méthode de vérification de la validité des résultats du vieillissement . 6
Annexe B (informative) Données de fidélité . 7
Bibliographie .11

iii
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale d’organismes nationaux
de normalisation (comités membres de l’ISO). L’élaboration des Normes internationales est en général
confiée aux comités techniques de l’ISO. Chaque comité membre intéressé par une étude a le droit de faire
partie du comité technique créé à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec l’ISO participent également aux travaux. L’ISO collabore étroitement avec
la Commission électrotechnique internationale (IEC) en ce qui concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier, de prendre note des différents
critères d’approbation requis pour les différents types de documents ISO. Le présent document a
été rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir
www.iso.org/directives).
L’ISO attire l’attention sur le fait que la mise en application du présent document peut entraîner l’utilisation
d’un ou de plusieurs brevets. L’ISO ne prend pas position quant à la preuve, à la validité et à l’applicabilité de
tout droit de brevet revendiqué à cet égard. À la date de publication du présent document, l’ISO n’avait pas
reçu notification qu’un ou plusieurs brevets pouvaient être nécessaires à sa mise en application. Toutefois,
il y a lieu d’avertir les responsables de la mise en application du présent document que des informations
plus récentes sont susceptibles de figurer dans la base de données de brevets, disponible à l’adresse
www.iso.org/brevets. L’ISO ne saurait être tenue pour responsable de ne pas avoir identifié tout ou partie de
tels droits de brevet.
Les appellations commerciales éventuellement mentionnées dans le présent document sont données pour
information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l’ISO liés à l’évaluation de la conformité, ou pour toute information au sujet de l’adhésion de
l’ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles techniques au
commerce (OTC), voir www.iso.org/avant-propos.
Le présent document a été élaboré par le comité technique ISO/TC 45, Élastomères et produits à base
d’élastomères, sous-comité SC 4, Produits (autres que tuyaux), en collaboration avec le comité technique CEN/
TC 249, Plastiques, du Comité européen de normalisation (CEN), conformément à l’Accord de coopération
technique entre l’ISO et le CEN (Accord de Vienne).
Cette cinquième édition annule et remplace la quatrième édition (ISO 2440:2019), qui a fait l’objet d’une
révision technique.
Les principales modifications sont les suivantes:
— Ajout du paragraphe 7.2;
— Ajout de l’Article 9;
— Ajout d'une méthode de vérification dans l’Annexe A;
— Ajout de données de fidélité dans l’Annexe B.
Il convient que l’utilisateur adresse tout retour d’information ou toute question concernant le présent
document à l’organisme national de normalisation de son pays. Une liste exhaustive desdits organismes se
trouve à l’adresse www.iso.org/fr/members.html.

iv
Introduction
Le mesurage des effets du vieillissement, soit par l’oxydation, soit par l’hydrolyse causées par l’humidité, est
utilisée pour évaluer le comportement à long terme des matériaux polymères cellulaires dans des conditions
de laboratoire. Les caractéristiques physiques considérées sont mesurées avant et après l’application des
traitements spécifiés.
Les conditions d’essai sont données pour le latex à alvéoles ouverts, les mousses de polyuréthanne à alvéoles
ouverts et fermés, et les mousses de polyoléfine à alvéoles fermés.
L’effet des méthodes de vieillissement sur l’une quelconque des caractéristiques physiques du matériau
peut être examiné, mais celles qui sont normalement vérifiées par les essais sont les caractéristiques
d’allongement et de traction ou les caractéristiques de compression ou de dureté par indentation.
Ces essais ne sont pas nécessairement en corrélation, soit avec le comportement en utilisation, soit avec le
vieillissement par exposition à la lumière.
Si cela est souhaité, les conditions de vieillissement contenues dans le présent document peuvent être
appliquées à des structures composites contenant l’un des types de matériaux alvéolaires ci-dessus. Cela
peut être utile dans la recherche des interactions possibles entre les matériaux alvéolaires et d’autres
substrats. Les constructions composites peuvent être sous la forme de produits finis complets ou de petits
échantillons représentatifs qui en seraient prélevés.

v
Norme internationale ISO 2440:2025(fr)
Matériaux polymères alvéolaires souples et rigides — Essais
de vieillissement accéléré
AVERTISSEMENT — Il convient que les utilisateurs du présent document connaissent bien les
pratiques courantes de laboratoire. Le présent document n’a pas pour but de traiter tous les
problèmes de sécurité qui sont, le cas échéant, liés à son utilisation. Il incombe à l’utilisateur de
mettre en place des pratiques appropriées en matière d’hygiène et de sécurité, et de déterminer
l'applicabilité de toute autre restriction.
1 Domaine d’application
Le présent document spécifie des méthodes de laboratoire qui ont pour but de reproduire les effets des
réactions se produisant naturellement, telles que l’oxydation ou l’hydrolyse causées par l’humidité pour les
matériaux polymères alvéolaires souples et rigides.
2 Références normatives
Les documents suivants cités dans le texte constituent, pour tout ou partie de leur contenu, des exigences du
présent document. Pour les références datées, seule l’édition citée s’applique. Pour les références non datées,
la dernière édition du document de référence s’applique (y compris les éventuels amendements).
ISO 23529, Caoutchouc — Procédures générales pour la préparation et le conditionnement des éprouvettes pour
les méthodes d'essais physiques
3 Termes et définitions
Pour les besoins du présent document, les termes et définitions suivants s’appliquent.
L’ISO et l’IEC tiennent à jour des bases de données terminologiques destinées à être utilisées en normalisation,
consultables aux adresses suivantes:
— ISO Online browsing platform: disponible à l’adresse https:// www .iso .org/ obp
— IEC Electropedia: disponible à l’adresse https:// www .electropedia .org/
3.1
valeur moyenne de la caractéristique après vieillissement
X
a
valeur moyenne obtenue à partir de plusieurs déterminations de la caractéristique à étudier, mesurée après
l'application d'un processus de vieillissement
Note 1 à l'article: La valeur moyenne de la caractéristique après vieillissement est exprimée dans l'unité prévue pour
cette caractéristique.
3.2
valeur moyenne de la caractéristique avant vieillissement
X
valeur moyenne obtenue à partir de plusieurs déterminations de la caractéristique à étudier, mesurée avant
l'application d'un processu
...

FINAL DRAFT
International
Standard
ISO/FDIS 2440
ISO/TC 45/SC 4
Flexible and rigid cellular polymeric
Secretariat: DSM
materials — Accelerated ageing
Voting begins on:
tests
2025-03-28
Matériaux polymères alvéolaires souples et rigides — Essais de
Voting terminates on:
vieillissement accéléré
2025-05-23
RECIPIENTS OF THIS DRAFT ARE INVITED TO SUBMIT,
WITH THEIR COMMENTS, NOTIFICATION OF ANY
RELEVANT PATENT RIGHTS OF WHICH THEY ARE AWARE
AND TO PROVIDE SUPPOR TING DOCUMENTATION.
IN ADDITION TO THEIR EVALUATION AS
BEING ACCEPTABLE FOR INDUSTRIAL, TECHNO­
ISO/CEN PARALLEL PROCESSING LOGICAL, COMMERCIAL AND USER PURPOSES, DRAFT
INTERNATIONAL STANDARDS MAY ON OCCASION HAVE
TO BE CONSIDERED IN THE LIGHT OF THEIR POTENTIAL
TO BECOME STAN DARDS TO WHICH REFERENCE MAY BE
MADE IN NATIONAL REGULATIONS.
Reference number
ISO/FDIS 2440:2025(en) © ISO 2025

FINAL DRAFT
ISO/FDIS 2440:2025(en)
International
Standard
ISO/FDIS 2440
ISO/TC 45/SC 4
Flexible and rigid cellular polymeric
Secretariat: DSM
materials — Accelerated ageing tests
Voting begins on:
Matériaux polymères alvéolaires souples et rigides — Essais de
vieillissement accéléré
Voting terminates on:
RECIPIENTS OF THIS DRAFT ARE INVITED TO SUBMIT,
WITH THEIR COMMENTS, NOTIFICATION OF ANY
RELEVANT PATENT RIGHTS OF WHICH THEY ARE AWARE
AND TO PROVIDE SUPPOR TING DOCUMENTATION.
© ISO 2025
IN ADDITION TO THEIR EVALUATION AS
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
BEING ACCEPTABLE FOR INDUSTRIAL, TECHNO­
ISO/CEN PARALLEL PROCESSING
LOGICAL, COMMERCIAL AND USER PURPOSES, DRAFT
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on
INTERNATIONAL STANDARDS MAY ON OCCASION HAVE
the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address below
TO BE CONSIDERED IN THE LIGHT OF THEIR POTENTIAL
or ISO’s member body in the country of the requester.
TO BECOME STAN DARDS TO WHICH REFERENCE MAY BE
MADE IN NATIONAL REGULATIONS.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: [phone]
Email: [e-mail]
Website: www.iso.org
Published in Switzerland Reference number
ISO/FDIS 2440:2025(en) © ISO 2025

ii
ISO/FDIS 2440:2025(en)
Contents Page
Foreword .iv
Introduction .v
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Apparatus . 2
4.1 For dry heat ageing .2
4.2 For humidity ageing .2
4.3 For physical property measurements . .2
5 Test pieces . 2
5.1 Number, size and shape .2
5.2 Conditioning.2
6 Procedure . 2
6.1 General .2
6.2 Dry heat ageing .3
6.2.1 Temperature .3
6.2.2 Duration of ageing .3
6.3 Humidity ageing .3
6.3.1 Humidity .3
6.3.2 Temperatures and duration of ageing .3
6.4 Reconditioning.4
7 Calculation and expression of results . 4
7.1 Calculation .4
7.2 Validity .4
7.3 Expression of results . .4
8 Precision data . 4
9 Test report . 4
Annex A (informative) Method for verification of the validity of ageing results . 6
Annex B (informative) Precision data . 7
Bibliography .11

iii
ISO/FDIS 2440:2025(en)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out through
ISO technical committees. Each member body interested in a subject for which a technical committee
has been established has the right to be represented on that committee. International organizations,
governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely
with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are described
in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the different types
of ISO document should be noted. This document was drafted in accordance with the editorial rules of the
ISO/IEC Directives, Part 2 (see www.iso.org/directives).
ISO draws attention to the possibility that the implementation of this document may involve the use of (a)
patent(s). ISO takes no position concerning the evidence, validity or applicability of any claimed patent
rights in respect thereof. As of the date of publication of this document, ISO had not received notice of (a)
patent(s) which may be required to implement this document. However, implementers are cautioned that
this may not represent the latest information, which may be obtained from the patent database available at
www.iso.org/patents. ISO shall not be held responsible for identifying any or all such patent rights.
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and expressions
related to conformity assessment, as well as information about ISO's adherence to the World Trade
Organization (WTO) principles in the Technical Barriers to Trade (TBT), see www.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 45, Rubber and rubber products, Subcommittee
SC 4, Products (others than hoses), in collaboration with the European Committee for Standardization (CEN)
Technical Committee CEN/TC 249, Plastics, in accordance with the Agreement on technical cooperation
between ISO and CEN (Vienna Agreement).
This fifth edition cancels and replaces the fourth edition (ISO 2440:2019) which has been technically revised.
The main changes are as follows:
— addition of subclause 7.2;
— addition of Clause 9;
— addition of a method for verification in Annex A;
— addition of precision data in Annex B.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www.iso.org/members.html.

iv
ISO/FDIS 2440:2025(en)
Introduction
The measurement of ageing effects, either by oxidation or hydrolysis by humidity, is used to assess the long-
term behaviour of cellular polymeric materials under laboratory conditions. The physical properties of
interest are measured before and after the application of the specified treatments.
Test conditions are given for open cellular latex, open- and closed-cell polyurethane foams, and closed-cell
polyolefin foams.
The effect of the ageing procedures on any of the physical properties of the material can be examined, but
those normally tested are either the elongation and tensile properties, or the compression or indentation
hardness properties.
These tests do not necessarily correlate either with service behaviour or with ageing by exposure to light.
If desired, the ageing conditions contained in this document can be applied to composite structures
containing any of the above types of cellular material. This can be helpful in the investigation of possible
interactions between cellular materials and other substrates. Composite constructions can be in the form of
complete finished products or representative small specimens cut there-from.

v
FINAL DRAFT International Standard ISO/FDIS 2440:2025(en)
Flexible and rigid cellular polymeric materials — Accelerated
ageing tests
WARNING — Persons using this document should be familiar with normal laboratory practice. This
document does not purport to address all of the safety problems, if any, associated with its use. It is
the responsibility of the user to establish appropriate safety and health practices and to determine
the applicability of any other restrictions.
1 Scope
This document specifies laboratory procedures which are intended to imitate the effects of naturally
occurring reactions such as oxidation or hydrolysis by humidity for flexible and rigid cellular polymeric
materials.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content constitutes
requirements of this document. For dated references, only the edition cited applies. For undated references,
the latest edition of the referenced document (including any amendments) applies.
ISO 23529, Rubber — General procedures for preparing and conditioning test pieces for physical test methods
3 Terms and definitions
For the purposes of this document, the following terms and definitions apply.
ISO and IEC maintain terminology databases for use in standardization at the following addresses:
— ISO Online browsing platform: available at https:// www .iso .org/ obp
— IEC Ele
...

2025-01-23
ISO/FDIS 2440:2025(en)
ISO/TC 45/SC 4/WG 8
Secretariat: DSM
Date: 2025-03-13
Flexible and rigid cellular polymeric materials — Accelerated ageing
tests
Matériaux polymères alvéolaires souples et rigides — Essais de vieillissement accéléré
FDIS stage
ISO #####-#:####(X/FDIS 2440:2025(en)
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication
may be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying,
or posting on the internet or an intranet, without prior written permission. Permission can be requested from either ISO
at the address below or ISO’s member body in the country of the requester.
ISO copyright office
CP 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Geneva
Phone: + 41 22 749 01 11
EmailE-mail: [e-mail]
Website: www.iso.org
Published in Switzerland
ii
ISO/FDIS 2440:2025(en)
Contents
Foreword . iv
Introduction . v
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Apparatus . 2
4.1 For dry heat ageing . 2
4.2 For humidity ageing . 2
4.3 For physical property measurements . 2
5 Test pieces . 2
5.1 Number, size and shape . 2
5.2 Conditioning . 2
6 Procedure . 2
6.1 General. 2
6.2 Dry heat ageing . 3
6.3 Humidity ageing . 3
6.4 Reconditioning . 4
7 Calculation and expression of results . 4
7.1 Calculation . 4
7.2 Validity . 4
7.3 Expression of results . 4
8 Precision data . 4
9 Test report . 4
Annex A (informative) Method for verification of the validity of ageing results . 6
Annex B (informative) Precision data . 7
Bibliography . 11

iii
ISO #####-#:####(X/FDIS 2440:2025(en)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out through
ISO technical committees. Each member body interested in a subject for which a technical committee has been
established has the right to be represented on that committee. International organizations, governmental and
non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the
International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are described
in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the different types of
ISO document should be noted. This document was drafted in accordance with the editorial rules of the
ISO/IEC Directives, Part 2 (see www.iso.org/directives).
ISO draws attention to the possibility that the implementation of this document may involve the use of (a)
patent(s). ISO takes no position concerning the evidence, validity or applicability of any claimed patent rights
in respect thereof. As of the date of publication of this document, ISO [had/had not] received notice of (a)
patent(s) which may be required to implement this document. However, implementers are cautioned that this
may not represent the latest information, which may be obtained from the patent database available at
www.iso.org/patents. ISO shall not be held responsible for identifying any or all such patent rights.
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and expressions
related to conformity assessment, as well as information about ISO's adherence to the World Trade
Organization (WTO) principles in the Technical Barriers to Trade (TBT), see www.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 45, Rubber and rubber products, Subcommittee
SC 4, Products (others than hoses), in collaboration with the European Committee for Standardization (CEN)
Technical Committee CEN/TC 249, Plastics, in accordance with the Agreement on technical cooperation
between ISO and CEN (Vienna Agreement).
This fifth edition cancels and replaces the fourth edition (ISO 2440:2019) which has been technically revised.
The main changes are as follows:
— — addition of subclause 7.2subclause 7.2;;
— — addition of Clause 9Clause 9;;
— — addition of a method for verification in Annex AAnnex A;;
— — addition of precision data in Annex BAnnex B.
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www.iso.org/members.html.
iv
ISO/FDIS 2440:2025(en)
Introduction
The measurement of ageing effects, either by oxidation or hydrolysis by humidity, is used to assess the long-
term behaviour of cellular polymeric materials under laboratory conditions. The physical properties of
interest are measured before and after the application of the specified treatments.
Test conditions are only given for open cellular latex, both open- and closed-cell polyurethane foams, and
closed-cell polyolefin foams. Conditions for other materials will be added as required.
The effect of the ageing procedures on any of the physical properties of the material can be examined, but
those normally tested are either the elongation and tensile properties, or the compression or indentation
hardness properties.
These tests do not necessarily correlate either with service behaviour or with ageing by exposure to light.
If desired, the ageing conditions contained in this document can be applied to composite structures containing
any of the above types of cellular material. This can be helpful in the investigation of possible interactions
between cellular materials and other substrates. Composite constructions can be in the form of complete
finished products or representative small specimens cut there-from.
v
ISO/FDIS 2440:2025(en)
Flexible and rigid cellular polymeric materials — Accelerated ageing
tests
WARNING — Persons using this document should be familiar with normal laboratory practice. This
document does not purport to address all of the safety problems, if any, associated with its use. It is
the responsibility of the user to establish appropriate safety and health practices and to determine the
applicability of any other restrictions.
1 Scope
This document specifies laboratory procedures which are intended to imitate the effects of naturally occurring
reactions such as oxidation or hydrolysis by humidity for flexible and rigid cellular polymeric materials.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content constitutes
requirements of this document. For dated references, only the edition cited applies. For undated references,
the latest edition of the referenced document (including any amendments) applies.
ISO 23529, Rubber — General procedures for preparing and conditioning test pieces for physical test methods
3 Terms and definitions
For the purposes of this document, the following terms and definitions apply.
ISO and IEC maintain terminology databases for use in standardization at the following addresses:
— — ISO Online browsing platform: available at https://www.iso.org/obp
— — IEC Electropedia: available at https://www.electropedia.org/
3.1 3.1
average value of the property after ageing
̅ ¯
𝑿 𝑋
𝒂 𝑎
average value from multiple determinations of the property to be investigated, measured after application of
an ageing process
Note 1 to entry: The average value of the property after ageing is expressed in the unit foreseen for this property.
3.2 3.2
average value of the property before ageing
̅ ¯
𝑿 𝑋
𝟎 0
average value from multiple determinations of the property to be investigated, measured before application
of an ageing process
Note 1 to entry: The average value of the property before ageing is expressed in the unit foreseen for this property.
3.3 3.3
percentage change
the percentage change is the relative difference of a property before and after an ageing process, measured
under repeat conditions.
Note 1 to entry: Percentage change is expressed in percent (%)(%).
ISO/FDIS 2440:2025(en)
4 Apparatus
4.1 For dry heat ageing
4.1.1 4.1.1 Oven, with forced circulation, capable of maintaining the required temperature to
within ±3 °C.
It is recommended that aA device should be used to record the temperature, preferably continuously.
4.2 For humidity ageing
4.2.1 4.2.1 Ageing apparatus, of such a size that the total volume of the test pieces does not exceed 10 %
of the free air space, and such that the test pieces are free of strain, freely exposed to the ageing atmosphere
on all sides and not exposed to light.
4.2.2 4.2.2 Steam autoclave or similar vessel, capable of maintaining the required temperature to
within ±3 °C and of withstanding absolute pressures up to 300 kPa.
4.2.3 4.2.3 Glass vessel, with a suitable closure, and a water-bath or drying oven for heating the vessel,
capable of maintaining the required temperature to within ±3 °C.
4.3 For physical property measurements
Use apparatus appropriate to the measurements of the physical property to be examined.
5 Test pieces
5.1 Number, size and shape
The number of test pieces, and their size and shape, shall be appropriate to the property being examined. They
shall be prepared, before ageing, to the dimensions used in the particular test.
5.2 Conditioning
Material shall not be tested less than 72 h after manufacture, unless at either 16 h or 48 h after manufacture
it can be demonstrated that the mean result does not differ by more than ±10 % from those obtained after
72 h. Testing is permitted at either 16 h or 48 h if, at the specified time, the above criterion has been satisfied.
Prior to the test, the test pieces shall be conditioned, undeflected and undistorted, for at least 16 h in one of
the following atmospheres as specified in ISO 23529:
a) a) 23 °C ± 2 °C, (50 ± 5) % relative humidity;
b) b) 27 °C ± 2 °C, (65 ± 5) % relative humidity.
This period can form the latter part of the period following manufacture.
It is recommended that forFor reference purposes, the test should be performed 7 days or more after the
cellular material has been manufactured.
6 Procedure
6.1 General
After conditioning, the test of the required physical property shall be performed and the test pieces shall be
brought rapidly to the ageing condition. If the test to be performed is destructive, for example the examination
ISO/FDIS 2440:2025(en)
of tensile properties, it is recommended that the tes
...

PROJET FINAL
Norme
internationale
ISO/FDIS 2440
ISO/TC 45/SC 4
Matériaux polymères alvéolaires
Secrétariat: DSM
souples et rigides — Essais de
Début de vote:
vieillissement accéléré
2025-03-28
Flexible and rigid cellular polymeric materials — Accelerated
Vote clos le:
ageing tests
2025-05-23
LES DESTINATAIRES DU PRÉSENT PROJET SONT
INVITÉS À PRÉSENTER, AVEC LEURS OBSERVATIONS,
NOTIFICATION DES DROITS DE PROPRIÉTÉ DONT ILS
AURAIENT ÉVENTUELLEMENT CONNAISSANCE ET À
FOURNIR UNE DOCUMENTATION EXPLICATIVE.
OUTRE LE FAIT D’ÊTRE EXAMINÉS POUR
ÉTABLIR S’ILS SONT ACCEPTABLES À DES FINS
INDUSTRIELLES, TECHNOLOGIQUES ET COM-MERCIALES,
AINSI QUE DU POINT DE VUE DES UTILISATEURS, LES
PROJETS DE NORMES
TRAITEMENT PARALLÈLE ISO/CEN
INTERNATIONALES DOIVENT PARFOIS ÊTRE CONSIDÉRÉS
DU POINT DE VUE DE LEUR POSSI BILITÉ DE DEVENIR DES
NORMES POUVANT
SERVIR DE RÉFÉRENCE DANS LA RÉGLEMENTATION
NATIONALE.
Numéro de référence
ISO/FDIS 2440:2025(fr) © ISO 2025

PROJET FINAL
ISO/FDIS 2440:2025(fr)
Norme
internationale
ISO/FDIS 2440
ISO/TC 45/SC 4
Matériaux polymères alvéolaires
Secrétariat: DSM
souples et rigides — Essais de
Début de vote:
vieillissement accéléré
2025-03-28
Flexible and rigid cellular polymeric materials — Accelerated
Vote clos le:
ageing tests
2025-05-23
LES DESTINATAIRES DU PRÉSENT PROJET SONT
INVITÉS À PRÉSENTER, AVEC LEURS OBSERVATIONS,
NOTIFICATION DES DROITS DE PROPRIÉTÉ DONT ILS
AURAIENT ÉVENTUELLEMENT CONNAISSANCE ET À
FOURNIR UNE DOCUMENTATION EXPLICATIVE.
DOCUMENT PROTÉGÉ PAR COPYRIGHT
OUTRE LE FAIT D’ÊTRE EXAMINÉS POUR
ÉTABLIR S’ILS SONT ACCEPTABLES À DES FINS
© ISO 2025 INDUSTRIELLES, TECHNOLOGIQUES ET COM-MERCIALES,
AINSI QUE DU POINT DE VUE DES UTILISATEURS, LES
Tous droits réservés. Sauf prescription différente ou nécessité dans le contexte de sa mise en œuvre, aucune partie de cette
PROJETS DE NORMES
TRAITEMENT PARALLÈLE ISO/CEN
INTERNATIONALES DOIVENT PARFOIS ÊTRE CONSIDÉRÉS
publication ne peut être reproduite ni utilisée sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique,
DU POINT DE VUE DE LEUR POSSI BILITÉ DE DEVENIR DES
y compris la photocopie, ou la diffusion sur l’internet ou sur un intranet, sans autorisation écrite préalable. Une autorisation peut
NORMES POUVANT
être demandée à l’ISO à l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
SERVIR DE RÉFÉRENCE DANS LA RÉGLEMENTATION
NATIONALE.
ISO copyright office
Case postale 401 • Ch. de Blandonnet 8
CH-1214 Vernier, Genève
Tél.: [phone]
E-mail: [e-mail]
Web: www.iso.org
Publié en Suisse Numéro de référence
ISO/FDIS 2440:2025(fr) © ISO 2025

ii
ISO/FDIS 2440:2025(fr)
Sommaire Page
Avant-propos .iv
Introduction .v
1 Domaine d’application . 1
2 Références normatives . 1
3 Termes et définitions . 1
4 Appareillage . 2
4.1 Pour le vieillissement en chaleur sèche .2
4.2 Pour le vieillissement à l’humidité .2
4.3 Pour le mesurage des caractéristiques physiques .2
5 Éprouvettes. 2
5.1 Nombre, forme et dimensions .2
5.2 Conditionnement .2
6 Mode opératoire . 3
6.1 Généralités .3
6.2 Vieillissement en chaleur sèche .3
6.2.1 Température .3
6.2.2 Durée de vieillissement .3
6.3 Vieillissement à l’humidité .3
6.3.1 Humidité .3
6.3.2 Températures et durées de vieillissement .3
6.4 Reconditionnement .4
7 Calcul et expression des résultats . 4
7.1 Calcul .4
7.2 Validité .4
7.3 Expression des résultats .4
8 Données de fidélité . 5
9 Rapport d’essai . 5
Annexe A (informative) Méthode de vérification de la validité des résultats du vieillissement . 6
Annexe B (informative) Données de fidélité . 8
Bibliographie .12

iii
ISO/FDIS 2440:2025(fr)
Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale d’organismes nationaux
de normalisation (comités membres de l’ISO). L’élaboration des Normes internationales est en général
confiée aux comités techniques de l’ISO. Chaque comité membre intéressé par une étude a le droit de faire
partie du comité technique créé à cet effet. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec l’ISO participent également aux travaux. L’ISO collabore étroitement avec
la Commission électrotechnique internationale (IEC) en ce qui concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier, de prendre note des différents
critères d’approbation requis pour les différents types de documents ISO. Le présent document a
été rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir
www.iso.org/directives).
L’ISO attire l’attention sur le fait que la mise en application du présent document peut entraîner l’utilisation
d’un ou de plusieurs brevets. L’ISO ne prend pas position quant à la preuve, à la validité et à l’applicabilité de
tout droit de brevet revendiqué à cet égard. À la date de publication du présent document, l’ISO n’avait pas
reçu notification qu’un ou plusieurs brevets pouvaient être nécessaires à sa mise en application. Toutefois,
il y a lieu d’avertir les responsables de la mise en application du présent document que des informations
plus récentes sont susceptibles de figurer dans la base de données de brevets, disponible à l’adresse
www.iso.org/brevets. L’ISO ne saurait être tenue pour responsable de ne pas avoir identifié tout ou partie de
tels droits de brevet.
Les appellations commerciales éventuellement mentionnées dans le présent document sont données pour
information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l’ISO liés à l’évaluation de la conformité, ou pour toute information au sujet de l’adhésion de
l’ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles techniques au
commerce (OTC), voir www.iso.org/avant-propos.
Le présent document a été élaboré par le comité technique ISO/TC 45, Élastomères et produits à base
d’élastomères, sous-comité SC 4, Produits (autres que tuyaux), en collaboration avec le comité technique CEN/
TC 249, Plastiques, du Comité européen de normalisation (CEN), conformément à l’Accord de coopération
technique entre l’ISO et le CEN (Accord de Vienne).
Cette cinquième édition annule et remplace la quatrième édition (ISO 2440:2019), qui a fait l’objet d’une
révision technique.
Les principales modifications sont les suivantes:
— Ajout du paragraphe 7.2;
— Ajout de l’Article 9;
— Ajout d'une méthode de vérification dans l’Annexe A;
— Ajout de données de fidélité dans l’Annexe B.
Il convient que l’utilisateur adresse tout retour d’information ou toute question concernant le présent
document à l’organisme national de normalisation de son pays. Une liste exhaustive desdits organismes se
trouve à l’adresse www.iso.org/fr/members.html.

iv
ISO/FDIS 2440:2025(fr)
Introduction
Le mesurage des effets du vieillissement, soit par l’oxydation, soit par l’hydrolyse causées par l’humidité, est
utilisée pour évaluer le comportement à long terme des matériaux polymères cellulaires dans des conditions
de laboratoire. Les caractéristiques physiques considérées sont mesurées avant et après l’application des
traitements spécifiés.
Les conditions d’essai sont données pour le latex à alvéoles ouverts, les mousses de polyuréthanne à alvéoles
ouverts et fermés, et les mousses de polyoléfine à alvéoles fermés.
L’effet des méthodes de vieillissement sur l’une quelconque des caractéristiques physiques du matériau
peut être examiné, mais celles qui sont normalement vérifiées par les essais sont les caractéristiques
d’allongement et de traction ou les caractéristiques de compression ou de dureté par indentation.
Ces essais ne sont pas nécessairement en corrélation, soit avec le comportement en utilisation, soit avec le
vieillissement par exposition à la lumière.
Si cela est souhaité, les conditions de vieillissement contenues dans le présent document peuvent être
appliquées à des structures composites contenant l’un des types de matériaux alvéolaires ci-dessus. Cela
peut être utile dans la recherche des interactions possibles entre les matériaux alvéolaires et d’autres
substrats. Les constructions composites peuvent être sous la forme de produits finis complets ou de petits
échantillons représentatifs qui en seraient prélevés.

v
PROJET FINAL Norme internationale ISO/FDIS 2440:2025(fr)
Matériaux polymères alvéolaires souples et rigides — Essais
de vieillissement accéléré
AVERTISSEMENT — Il convient que les utilisateurs du présent document connaissent bien les
pratiques courantes de laboratoire. Le présent document n’a pas pour but de traiter tous les
problèmes de sécurité qui sont, le cas échéant, liés à son utilisation. Il incombe à l’utilisateur de
mettre en place des pratiques appropriées en matière d’hygiène et de sécurité, et de déterminer
l'applicabilité de toute autre restriction.
1 Domaine d’application
Le présent document spé
...