C21.04 - Raw Materials

SIGNIFICANCE AND USE
3.1 This test method is useful to both sellers and purchasers of alumina and quartz powders for determining particle size distributions for materials specifications, manufacturing control, and development and research.
SCOPE
1.1 This test method, one of several found valuable for the measurement of particle size, covers the determination of the particle size distribution of alumina or quartz powders (0.6 μm to 56.0 μm) using electrical sensing zone particle size analyzers. These instruments use an electric current path of small dimensions which is modulated by individual particle passage through an aperture, and produces individual pulses of amplitude proportional to the particle volume.  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
3.1 Sieve analyses are carried out to determine the particle size distribution of powders which, in turn, are used to qualify those materials as to their usefulness in the process under consideration. Since particle size analyses have only relative significance, the results should be considered only where they correlate with process characteristics. The parameter that is being measured in this test is the amount of material that will pass through a cloth having theoretically square openings. It must be remembered that all the holes are not square, nor uniform in size, and the question of whether a given particle will go through is a statistical one. Since each particle size analysis method measures a unique physical parameter, the results from one method may not agree with those from another. Particle size distributions play a role in such properties as bulk density, dustiness, and handling characteristics. Care should be taken, however, when interpretations are made from one or two points (sieves) on the distribution curve.
SCOPE
1.1 This test method covers the determination of the particle size distribution of nonplastic ceramic powders such as alumina, silica, feldspar, pyrophyllite, nepheline syenite, talc, titanates, and zircon using wire cloth sieves.  
1.2 Materials containing a large amount of fines, containing agglomerates, or that are nonfree-flowing, are wet-sieved to remove excessive fines or to disperse agglomerates before performing the test. This technique is not applicable to materials that are, to any degree, water soluble.  
1.3 The values stated in SI units are to be regarded as standard. The values given in parentheses are mathematical conversions to inch-pound units, or are other customary units (in the case of sieve frame diameter and sieve number), that are provided for information only and are not considered standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This test method covers the determination of free moisture in ceramic whiteware clays. Whiteware clays may be shipped as a bulk shipment in lumps, a bulk shipment of shredded or coarsely ground clay, or in bagged lots of ground or airfloated clay. Directions are given in this test method for obtaining representative samples of the clay shipment to be used in subsequent tests for the properties of the clay in the shipment. Percentage of free moisture shall be calculated to the nearest 0.1%.
SCOPE
1.1 This test method covers the determination of free moisture in ceramic whiteware clays. Whiteware clays may be shipped as a bulk shipment in lumps, a bulk shipment of shredded or coarsely ground clay, or in bagged lots of ground or airfloated clay. Directions are given in this test method for obtaining representative samples of the clay shipment to be used in subsequent tests for the properties of the clay in the shipment.  
1.2 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This test method covers the procedures for determining soluble sulfate ions present in water or a filtrate using a photometer to measure the turbidity of precipitated barium sulfate. This test method also details a method for standardizing the photometer to be used. The soluble sulfate ions may be removed from clays or clay-water slurries by leaching with water during mixing and then filter pressing. An impractical number of washings would be needed to remove all sulfate ions, therefore, this test method should be considered only as a control test and not a quantitative analysis for sulfate ions. Test apparatus include a balance, high speed mixer, filter press, glass beakers, transfer pipets, spectrophotometer, measuring spoon, and other laboratory equipment. All reagents to be used should be of the required purity and concentration.
SCOPE
1.1 This test method covers the determination of soluble sulfate ions present in water or a filtrate by means of a photometer measuring the turbidity of precipitated barium sulfate. A method of standardizing the photometer for this test method is also given.  
1.2 Soluble sulfate ions may be removed from clays or clay-water slurries by leaching with water during mixing and subsequent filter pressing. To remove all the sulfate ions would require an impractical number of washings; therefore, this test method should be considered a control test and not a quantitative analysis for SO4 ions.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 Both sellers and purchasers of alumina and quartz will find the test method useful to determine the specific surface area and indirectly as a measure of the particle size for material specifications, manufacturing control, and research and development.
SCOPE
1.1 This test method covers the determination of the specific surface area of aluminas and silicas used in the manufacture of ceramics. The test method is a general one, permitting the use of any modern commercial nitrogen adsorption apparatus but strictly defining the outgassing procedure. Calculations are based on the Brunauer-Emmett-Teller (BET) equation.  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This test method details the standard procedures for the determination of the particle size distribution of alumina or quartz powders using X-ray monitoring of gravity sedimentation. This test procedure shall make use of an X-ray sedimentation apparatus, and ultrasonic probe or bath. An aqueous homogeneous dispersion of the specimen is permitted to settle in a cell. The decrease in particle concentration over a programmed settling distance is monitored by an X-ray beam passing through the sedimenting dispersion to a detector. The specimen concentration at any given sedimentation distance is inversely proportional to the X-ray flux and the equivalent diameter (spherical) is calculated from Stokes' law.
SCOPE
1.1 This test method covers the determination of the particle size distribution of alumina or quartz powders in the range from 0.5 μm to 50 μm and having a median particle diameter from 2.5 μm to 10 μm using a sedimentation method. This test method is one of several found valuable for the measurement of particle size. Instruments used for this test method employ a constant intensity X-ray beam that is passed through a sedimenting dispersion of particles.  
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. For specific hazard statements, see Section 7.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This standard test method covers the rate determination of clay-water paste layer formation from a clay-water slip under pressure filtration. Filter pressing of clay shall be in accordance to the procedure indicated in this specification. Calculation of filtration rate and void fraction shall depend on thickness of wet filter cake and filtration time. Void fraction in the filter cake shall depend on filter cake weight, filter press cross-sectional area, and wet filter cake thickness.
SCOPE
1.1 This test method covers the determination of the rate at which a layer of clay-water paste is formed from a clay-water slip under pressure filtration. The filtration rate is directly related to such whiteware operations as filter pressing, slip casting, and drying of ware in which water permeability through a clay-water paste is the controlling mechanism.  
1.2 A straight-line relationship exists between the time of filter pressing and the square of the thickness of the paste layer. The filtration rate is directly related to the filter press pressure and the void fraction of the paste layer, and is inversely related to the square of the clay surface area, the ratio of solids to liquid in the slip, and the viscosity of water at the testing temperature.  
1.3 The values stated in acceptable metric units are to be regarded as the standard. The values given in parentheses are for information only.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This guide covers the wet sieve analysis of ceramic whiteware clays. This guide is intended for use in testing shipments of clay as well as for plant control tests. The apparatus to be used include stirring device and sieves. The following procedure shall be followed in the analysis of the ceramic whiteware clays: transferring of duplicate portions of the dried clay sample; agitating of the slurry by means of a mechanical stirrer to ensure complete separation of clay from nonplastic impurities; transferring of the slaked and stirred sample, without loss, to the finest sieve to be employed in the test; washing of the residue remaining on the finest sieve into the pan; nesting the top sieve on the pan, which shall contain a certain amount of clear water; refilling of the pan with the proper amount of water, then nesting the top sieve and its residue on the pan; carefully blotting each sieve on its underside with a soft, damp sponge, and placing the sieve either in a drying oven or under infrared lamps until thoroughly dry; nesting the dried residues and sieves in the proper order, with due care to prevent dusting of the residues; and separating the nested sieves and carefully brushing the residue from each onto a weighing paper.
SCOPE
1.1 This guide covers the wet sieve analysis of ceramic whiteware clays. This guide is intended for use in testing shipments of clay as well as for plant control tests.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 The estimation of average particle size has two chief functions: (1) as a guide to the degree of fineness or coarseness of a powder as this, in turn, is related to the flow and packing properties, and (1) as a control test on the uniformity of a product.  
4.2 These test methods provide procedures for determining the envelope-specific surface area of powders, from which is calculated an “average” particle diameter, assuming the particles are monosize, smooth surface, nonporous, spherical particles. For this reason, values obtained by these test methods will be reported as an average particle size or Fisher Number. The degree of correlation between the results of these test methods and the quality of powders in use will vary with each particular application and has not been fully determined.  
4.3 These test methods are generally applicable to alumina and silica powders, for particles having diameters between 0.2 and 75 μm (MIC SAS) or between 0.5 and 50 μm (FSSS). They may be used for other similar ceramic powders, with caution as to their applicability. They should not be used for powders composed of particles whose shape is too far from equiaxed—that is, flakes or fibers. In these cases, it is permissible to use the test methods described only by agreement between the parties concerned. These test methods shall not be used for mixtures of different powders, nor for powders containing binders or lubricants. When the powder contains agglomerates, the measured surface area may be affected by the degree of agglomeration. Methods of de-agglomeration may be used if agreed upon between the parties concerned.  
4.4 When an “average” particle size of powders is determined using either the MIC SAS or the FSSS, it should be clearly kept in mind that this average size is derived from the determination of the specific surface area of the powder using a relationship that is true only for powders of uniform size and spherical shape. Thus, the results of these methods are ...
SCOPE
1.1 These test methods cover the estimation of the average particle size in micrometres of alumina and silica powders using an air permeability method. The test methods are intended to apply to the testing of alumina and silica powders in the particle size range from 0.2 to 75 μm.  
1.2 The values stated in SI units are to be regarded as standard, with the exception of the values for density and the mass used to determine density, for which the use of the gram per cubic centimetre (g/cm3) and gram (g) units is the long-standing industry practice; and the units for pressure, cm H2O—also long-standing practice.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
3.1 Tests run on many clays generally indicate that a straight-line relationship exists between the methylene blue index (MBI) and such fundamental clay properties as cation exchange capacity, dry bond strength, and casting rate. Where the colloidal portion of the clay is kaolinite, there is also a direct correlation with specific surface (as determined by nitrogen adsorption). Where the colloidal portion contains significant amounts of illite or montmorillonite, the same close correlation does not exist. The MBI better correlates with the ceramic-forming properties than does the specific surface.  
3.2 That portion of a clay lying within the colloidal range (generally defined as the 0.5- to 0.001-μm range), determines the strictly colloidal properties of the clay and, together with the amount and type of organic material associated with the clay and the 2- to 0.2-μm fraction, largely determines the properties of the clay when used in ceramic-forming processes. While the specific surface of a clay is a function of the particle size and morphology and a relationship exists between dye adsorption and specific surface, the MBI should not be considered to be a particle size analysis since the value obtained is dominated by the character of only the very fine end of the particle size distribution. This procedure describes the determination of the dye adsorption (in this case, methylene blue) of a clay.
SCOPE
1.1 This test method covers the measurement of the adsorption of methylene blue dye by a clay, which is calculated as a methylene blue index for a clay.  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This test method details the standard procedure for the determination of modulus of rupture of ceramic whiteware clays, both dry and after conditioning at specified relative humidity, or both. The apparatuses needed for this method are a conditioning cabinet, and a testing machine. Extruded, clay-flint, and solid cast specimens shall be prepared accordingly. Specific procedures as to handling, warpage, drying, and storage, and the corresponding calculations are discussed thoroughly.
SIGNIFICANCE AND USE
3.1 The purpose of this test method is to obtain values of rupture modulus of clays before firing, under various processing conditions (relative humidity).
SCOPE
1.1 This test method covers the determination of the modulus of rupture of ceramic whiteware clays both dry and after conditioning at 50 or 80 % relative humidity, or both.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 Both suppliers and users of pulverized ceramic powders will find this test method useful to determine particle size distributions for materials specifications, manufacturing control, development, and research.  
4.2 The test method is simple, although tedious, uses inexpensive equipment, and will provide a continuous curve with data obtained with standardized woven sieves.
SCOPE
1.1 This guide covers the determination of the particle size distribution of pulverized alumina and quartz for particle sizes from 45 to 5 μm by wet sieving.  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.2.1 The only exception is in the Section 5, Apparatus, 5.1 where there is no relevant SI equivalent.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
5.1 Manufacturers and users of alumina powders will find this test method useful to determine the particle size distribution of these materials for product specification, quality control, and research and development testing.
SCOPE
1.1 This test method covers the determination of the particle size distribution of alumina in the range from 0.1 to 20 μm having a median particle diameter from 0.5 to 5.0 μm.  
1.2 The procedure described in this test method may be successfully applied to other ceramic powders in this general size range. It is the responsibility of the user to determine the applicability of this test method to other material.  
1.3 The values stated in SI units are to regarded as the standard. The values given in parentheses are for information only.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
2.1 The purpose of this test is to obtain values of shrinkage after drying and firing of clays or bodies or both, under various processing conditions to enable designers to determine the proper size of mold or die so as to produce a predetermined size of fired ware.
SCOPE
1.1 This test method covers the determination of linear shrinkage of ceramic whiteware clays, both unfired and fired.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This practice covers procedures for sampling bulk and bagged ceramic whiteware clays. For bulk shipment consisting lumps, samples shall be taken from different parts of the rail car or truck during unloading. Sampling of hopper car or hopper truck shipments is to be done during unloading of the car or truck. For bulk shipment consisting shredded or coarsely ground clay, samples may be taken with a shovel, or with a grain sampler. For bagged lots of ground or air-floated clay, samples may be taken by a grain-sampler or similar sampling instrument. For a clay shipped in slurry form, a sample may be obtained by taking a single grab sample from any portion of the shipment except by skimming the top surface.
SIGNIFICANCE AND USE
2.1 Since many tests are performed using very small amounts of powder, it is most important that the test portions be obtained in a standardized manner. The practices described here take into account the possibility of segregation and variability of the ceramic powder in containers of the various sizes and numbers, both in dry and slurry forms.
SCOPE
1.1 This practice covers procedures for sampling bulk and bagged shipments of ceramic whiteware clays.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This test method covers the determination of free moisture in ceramic whiteware clays. Whiteware clays may be shipped as a bulk shipment in lumps, a bulk shipment of shredded or coarsely ground clay, or in bagged lots of ground or airfloated clay. Directions are given in this test method for obtaining representative samples of the clay shipment to be used in subsequent tests for the properties of the clay in the shipment. Percentage of free moisture shall be calculated to the nearest 0.1%.
SCOPE
1.1 This test method covers the determination of free moisture in ceramic whiteware clays. Whiteware clays may be shipped as a bulk shipment in lumps, a bulk shipment of shredded or coarsely ground clay, or in bagged lots of ground or airfloated clay. Directions are given in this test method for obtaining representative samples of the clay shipment to be used in subsequent tests for the properties of the clay in the shipment.  
1.2 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
3.1 This test method is useful to both sellers and purchasers of alumina and quartz powders for determining particle size distributions for materials specifications, manufacturing control, and development and research.
SCOPE
1.1 This test method, one of several found valuable for the measurement of particle size, covers the determination of the particle size distribution of alumina or quartz powders (0.6 to 56.0 μm) using electrical sensing zone particle size analyzers. These instruments use an electric current path of small dimensions which is modulated by individual particle passage through an aperture, and produces individual pulses of amplitude proportional to the particle volume.  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
3.1 Sieve analyses are carried out to determine the particle size distribution of powders which, in turn, are used to qualify those materials as to their usefulness in the process under consideration. Since particle size analyses have only relative significance, the results should be considered only where they correlate with process characteristics. The parameter that is being measured in this test is the amount of material that will pass through a cloth having theoretically square openings. It must be remembered that all the holes are not square, nor uniform in size, and the question of whether a given particle will go through is a statistical one. Since each particle size analysis method measures a unique physical parameter, the results from one method may not agree with those from another. Particle size distributions play a role in such properties as bulk density, dustiness, and handling characteristics. Care should be taken, however, when interpretations are made from one or two points (sieves) on the distribution curve.
SCOPE
1.1 This test method covers the determination of the particle size distribution of nonplastic ceramic powders such as alumina, silica, feldspar, pyrophyllite, nepheline syenite, talc, titanates, and zircon using wire cloth sieves.  
1.2 Materials containing a large amount of fines, containing agglomerates, or that are nonfree-flowing, are wet-sieved to remove excessive fines or to disperse agglomerates before performing the test. This technique is not applicable to materials that are, to any degree, water soluble.  
1.3 The values stated in SI units are to be regarded as standard. The values given in parentheses are mathematical conversions to inch-pound units, or are other customary units (in the case of sieve frame diameter and sieve number), that are provided for information only and are not considered standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This standard test method covers the rate determination of clay-water paste layer formation from a clay-water slip under pressure filtration. Filter pressing of clay shall be in accordance to the procedure indicated in this specification. Calculation of filtration rate and void fraction shall depend on thickness of wet filter cake and filtration time. Void fraction in the filter cake shall depend on filter cake weight, filter press cross-sectional area, and wet filter cake thickness.
SCOPE
1.1 This test method covers the determination of the rate at which a layer of clay-water paste is formed from a clay-water slip under pressure filtration. The filtration rate is directly related to such whiteware operations as filter pressing, slip casting, and drying of ware in which water permeability through a clay-water paste is the controlling mechanism.  
1.2 A straight-line relationship exists between the time of filter pressing and the square of the thickness of the paste layer. The filtration rate is directly related to the filter press pressure and the void fraction of the paste layer, and is inversely related to the square of the clay surface area, the ratio of solids to liquid in the slip, and the viscosity of water at the testing temperature.  
1.3 The values stated in acceptable metric units are to be regarded as the standard. The values given in parentheses are for information only.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SIGNIFICANCE AND USE
4.1 The estimation of average particle size has two chief functions: first, as a guide to the degree of fineness or coarseness of a powder as this, in turn, is related to the flow and packing properties; and, second, as a control test on the uniformity of a product.  
4.2 These test methods provide procedures for determining the envelope-specific surface area of powders, from which is calculated an “average” particle diameter, assuming the particles are monosize, smooth surface, nonporous, spherical particles. For this reason, values obtained by these test methods will be reported as an average particle size or Fisher Number. The degree of correlation between the results of these test methods and the quality of powders in use will vary with each particular application and has not been fully determined.  
4.3 These test methods are generally applicable to alumina and silica powders, for particles having diameters between 0.2 and 75 μm (MIC SAS) or between 0.5 and 50 μm (FSSS). They may be used for other similar ceramic powders, with caution as to their applicability. They should not be used for powders composed of particles whose shape is too far from equiaxed—that is, flakes or fibers. In these cases, it is permissible to use the test methods described only by agreement between the parties concerned. These test methods shall not be used for mixtures of different powders, nor for powders containing binders or lubricants. When the powder contains agglomerates, the measured surface area may be affected by the degree of agglomeration. Methods of de-agglomeration may be used if agreed upon between the parties concerned.  
4.4 When an “average” particle size of powders is determined using either the MIC SAS or the FSSS, it should be clearly kept in mind that this average size is derived from the determination of the specific surface area of the powder using a relationship that is true only for powders of uniform size and spherical shape. Thus, the results of these meth...
SCOPE
1.1 These test methods cover the estimation of the average particle size in micrometres of alumina and silica powders using an air permeability method. The test methods are intended to apply to the testing of alumina and silica powders in the particle size range from 0.2 to 75 μm.  
1.2 Units—With the exception of the values for density and the mass used to determine density, for which the use of the gram per cubic centimetre (g/cm3) and gram (g) units is the long-standing industry practice; and the units for pressure, cm H2O—also long-standing practice; the values in SI units are to be regarded as standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SIGNIFICANCE AND USE
3.1 Sieve analyses are carried out to determine the particle size distribution of powders which, in turn, are used to qualify those materials as to their usefulness in the process under consideration. Since particle size analyses have only relative significance, the results should be considered only where they correlate with process characteristics. The parameter that is being measured in this test is the amount of material that will pass through a cloth having theoretically square openings. It must be remembered that all the holes are not square, nor uniform in size, and the question of whether a given particle will go through is a statistical one. Since each particle size analysis method measures a unique physical parameter, the results from one method may not agree with those from another. Particle size distributions play a role in such properties as bulk density, dustiness, and handling characteristics. Care should be taken, however, when interpretations are made from one or two points (sieves) on the distribution curve.
SCOPE
1.1 This test method covers the determination of the particle size distribution of nonplastic ceramic powders such as alumina, silica, feldspar, pyrophyllite, nepheline syenite, talc, titanates, and zircon using wire cloth sieves.  
1.2 Materials containing a large amount of fines, containing agglomerates, or that are nonfree-flowing, are wet-sieved to remove excessive fines or to disperse agglomerates before performing the test. This technique is not applicable to materials that are, to any degree, water soluble.  
1.3 The values stated in SI units are to be regarded as standard. The values given in parentheses are mathematical conversions to inch-pound units, or are other customary units (in the case of sieve frame diameter and sieve number), that are provided for information only and are not considered standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SIGNIFICANCE AND USE
3.1 This test method is useful to both sellers and purchasers of alumina and quartz powders for determining particle size distributions for materials specifications, manufacturing control, and development and research.
SCOPE
1.1 This test method, one of several found valuable for the measurement of particle size, covers the determination of the particle size distribution of alumina or quartz powders (0.6 to 56.0 μm) using electrical sensing zone particle size analyzers. These instruments use an electric current path of small dimensions which is modulated by individual particle passage through an aperture, and produces individual pulses of amplitude proportional to the particle volume.  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 This standard does not purport to address all of the safety problems, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SIGNIFICANCE AND USE
4.1 Both suppliers and users of pulverized ceramic powders will find this test method useful to determine particle size distributions for materials specifications, manufacturing control, development, and research.  
4.2 The test method is simple, although tedious, uses inexpensive equipment, and will provide a continuous curve with data obtained with standardized woven sieves.
SCOPE
1.1 This guide covers the determination of the particle size distribution of pulverized alumina and quartz for particle sizes from 45 to 5 μm by wet sieving.  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.2.1 The only exception is in the Section 5, Apparatus, 5.1 where there is no relevant SI equivalent.  
1.3 This standard does not purport to address the safety concerns associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SIGNIFICANCE AND USE
2.1 The purpose of this test is to obtain values of shrinkage after drying and firing of clays or bodies or both, under various processing conditions to enable designers to determine the proper size of mold or die so as to produce a predetermined size of fired ware.
SCOPE
1.1 This test method covers the determination of linear shrinkage of ceramic whiteware clays, both unfired and fired.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ABSTRACT
This test method details the standard procedure for the determination of modulus of rupture of ceramic whiteware clays, both dry and after conditioning at specified relative humidity, or both. The apparatuses needed for this method are a conditioning cabinet, and a testing machine. Extruded, clay-flint, and solid cast specimens shall be prepared accordingly. Specific procedures as to handling, warpage, drying, and storage, and the corresponding calculations are discussed thoroughly.
SIGNIFICANCE AND USE
3.1 The purpose of this test method is to obtain values of rupture modulus of clays before firing, under various processing conditions (relative humidity).
SCOPE
1.1 This test method covers the determination of the modulus of rupture of ceramic whiteware clays both dry and after conditioning at 50 or 80 % relative humidity, or both.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SIGNIFICANCE AND USE
5.1 Manufacturers and users of alumina powders will find this test method useful to determine the particle size distribution of these materials for product specification, quality control, and research and development testing.
SCOPE
1.1 This test method covers the determination of the particle size distribution of alumina in the range from 0.1 to 20 μm having a median particle diameter from 0.5 to 5.0 μm.  
1.2 The procedure described in this test method may be successfully applied to other ceramic powders in this general size range. It is the responsibility of the user to determine the applicability of this test method to other material.  
1.3 The values stated in SI units are to regarded as the standard. The values given in parentheses are for information only.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ABSTRACT
This practice covers procedures for sampling bulk and bagged ceramic whiteware clays. For bulk shipment consisting lumps, samples shall be taken from different parts of the rail car or truck during unloading. Sampling of hopper car or hopper truck shipments is to be done during unloading of the car or truck. For bulk shipment consisting shredded or coarsely ground clay, samples may be taken with a shovel, or with a grain sampler. For bagged lots of ground or air-floated clay, samples may be taken by a grain-sampler or similar sampling instrument. For a clay shipped in slurry form, a sample may be obtained by taking a single grab sample from any portion of the shipment except by skimming the top surface.
SIGNIFICANCE AND USE
2.1 Since many tests are performed using very small amounts of powder, it is most important that the test portions be obtained in a standardized manner. The practices described here take into account the possibility of segregation and variability of the ceramic powder in containers of the various sizes and numbers, both in dry and slurry forms.
SCOPE
1.1 This practice covers procedures for sampling bulk and bagged shipments of ceramic whiteware clays.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SIGNIFICANCE AND USE
4.1 Both sellers and purchasers of alumina and quartz will find the test method useful to determine the specific surface area and indirectly as a measure of the particle size for material specifications, manufacturing control, and research and development.
SCOPE
1.1 This test method covers the determination of the specific surface area of aluminas and silicas used in the manufacture of ceramics. The test method is a general one, permitting the use of any modern commercial nitrogen adsorption apparatus but strictly defining the outgassing procedure. Calculations are based on the Brunauer-Emmett-Teller (BET) equation.  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SIGNIFICANCE AND USE
3.1 Tests run on many clays generally indicate that a straight-line relationship exists between the methylene blue index (MBI) and such fundamental clay properties as cation exchange capacity, dry bond strength, and casting rate. Where the colloidal portion of the clay is kaolinite, there is also a direct correlation with specific surface (as determined by nitrogen adsorption). Where the colloidal portion contains significant amounts of illite or montmorillonite, the same close correlation does not exist. The MBI better correlates with the ceramic-forming properties than does the specific surface.  
3.2 That portion of a clay lying within the colloidal range (generally defined as the 0.5- to 0.001-μm range), determines the strictly colloidal properties of the clay and, together with the amount and type of organic material associated with the clay and the 2- to 0.2-μm fraction, largely determines the properties of the clay when used in ceramic-forming processes. While the specific surface of a clay is a function of the particle size and morphology and a relationship exists between dye adsorption and specific surface, the MBI should not be considered to be a particle size analysis since the value obtained is dominated by the character of only the very fine end of the particle size distribution. This procedure describes the determination of the dye adsorption (in this case, methylene blue) of a clay.
SCOPE
1.1 This test method covers the measurement of the adsorption of methylene blue dye by a clay, which is calculated as a methylene blue index for a clay.  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SCOPE
1.1 This test method covers the determination of the average particle size in micrometres of alumina and silica powders using an air permeability method. The test method is intended to apply to the testing of alumina and silica powders in the particle size range from 0.2 to 50 [mu]m.  
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ABSTRACT
This test method details the standard procedures for the determination of the particle size distribution of alumina or quartz powders using X-ray monitoring of gravity sedimentation. This test procedure shall make use of an X-ray sedimentation apparatus, and ultrasonic probe or bath. An aqueous homogeneous dispersion of the specimen is permitted to settle in a cell. The decrease in particle concentration over a programmed settling distance is monitored by an X-ray beam passing through the sedimenting dispersion to a detector. The specimen concentration at any given sedimentation distance is inversely proportional to the X-ray flux and the equivalent diameter (spherical) is calculated from Stokes' law.
SCOPE
1.1 This test method covers the determination of the particle size distribution of alumina or quartz powders in the range from 0.5 to 50 μm and having a median particle diameter from 2.5 to 10 μm using a sedimentation method. This test method is one of several found valuable for the measurement of particle size. Instruments used for this test method employ a constant intensity X-ray beam that is passed through a sedimenting dispersion of particles.  
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. For specific hazard statements, see Section 7.

ABSTRACT
This guide covers the wet sieve analysis of ceramic whiteware clays. This guide is intended for use in testing shipments of clay as well as for plant control tests. The apparatus to be used include stirring device and sieves. The following procedure shall be followed in the analysis of the ceramic whiteware clays: transferring of duplicate portions of the dried clay sample; agitating of the slurry by means of a mechanical stirrer to ensure complete separation of clay from nonplastic impurities; transferring of the slaked and stirred sample, without loss, to the finest sieve to be employed in the test; washing of the residue remaining on the finest sieve into the pan; nesting the top sieve on the pan, which shall contain a certain amount of clear water; refilling of the pan with the proper amount of water, then nesting the top sieve and its residue on the pan; carefully blotting each sieve on its underside with a soft, damp sponge, and placing the sieve either in a drying oven or under infrared lamps until thoroughly dry; nesting the dried residues and sieves in the proper order, with due care to prevent dusting of the residues; and separating the nested sieves and carefully brushing the residue from each onto a weighing paper.
SCOPE
1.1 This guide covers the wet sieve analysis of ceramic whiteware clays. This guide is intended for use in testing shipments of clay as well as for plant control tests.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ABSTRACT
This test method covers the determination of free moisture in ceramic whiteware clays. Whiteware clays may be shipped as a bulk shipment in lumps, a bulk shipment of shredded or coarsely ground clay, or in bagged lots of ground or airfloated clay. Directions are given in this test method for obtaining representative samples of the clay shipment to be used in subsequent tests for the properties of the clay in the shipment. Percentage of free moisture shall be calculated to the nearest 0.1%.
SCOPE
1.1 This test method covers the determination of free moisture in ceramic whiteware clays. Whiteware clays may be shipped as a bulk shipment in lumps, a bulk shipment of shredded or coarsely ground clay, or in bagged lots of ground or airfloated clay. Directions are given in this test method for obtaining representative samples of the clay shipment to be used in subsequent tests for the properties of the clay in the shipment.  
1.2 This standard does not purport to address all of the safetyconcerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ABSTRACT
This test method covers the procedures for determining soluble sulfate ions present in water or a filtrate using a photometer to measure the turbidity of precipitated barium sulfate. This test method also details a method for standardizing the photometer to be used. The soluble sulfate ions may be removed from clays or clay-water slurries by leaching with water during mixing and then filter pressing. An impractical number of washings would be needed to remove all sulfate ions, therefore, this test method should be considered only as a control test and not a quantitative analysis for sulfate ions. Test apparatus include a balance, high speed mixer, filter press, glass beakers, transfer pipets, spectrophotometer, measuring spoon, and other laboratory equipment. All reagents to be used should be of the required purity and concentration.
SCOPE
1.1 This test method covers the determination of soluble sulfate ions present in water or a filtrate by means of a photometer measuring the turbidity of precipitated barium sulfate. A method of standardizing the photometer for this test method is also given.  
1.2 Soluble sulfate ions may be removed from clays or clay-water slurries by leaching with water during mixing and subsequent filter pressing. To remove all the sulfate ions would require an impractical number of washings; therefore, this test method should be considered a control test and not a quantitative analysis for SO4 ions.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ABSTRACT
This standard test method covers the rate determination of clay-water paste layer formation from a clay-water slip under pressure filtration. Filter pressing of clay shall be in accordance to the procedure indicated in this specification. Calculation of filtration rate and void fraction shall depend on thickness of wet filter cake and filtration time. Void fraction in the filter cake shall depend on filter cake weight, filter press cross-sectional area, and wet filter cake thickness.
SCOPE
1.1 This test method covers the determination of the rate at which a layer of clay-water paste is formed from a clay-water slip under pressure filtration. The filtration rate is directly related to such whiteware operations as filter pressing, slip casting, and drying of ware in which water permeability through a clay-water paste is the controlling mechanism.
1.2 A straight-line relationship exists between the time of filter pressing and the square of the thickness of the paste layer. The filtration rate is directly related to the filter press pressure and the void fraction of the paste layer, and is inversely related to the square of the clay surface area, the ratio of solids to liquid in the slip, and the viscosity of water at the testing temperature.
1.3 The values stated in acceptable metric units are to be regarded as the standard. The values given in parentheses are for information only.
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ABSTRACT
These test methods cover the chemical analysis of clays used in the manufacture of ceramic whitewares. Determine moisture on the sample in its ordinary air-dried condition. Determine all other percentage compositions on moisture-free samples and report accordingly on a moisture-free basis. Make blank determinations on the reagents for each constituent in the whiteware clay and deduct this blank in each case. The sample shall be heated to a constant weight at a given temperature; the loss in weight is recorded as moisture. For the determination of the silica blank, approximately 0.25 g of alumina should be added as aluminium chloride. The procedure for the determination of iron, aluminium, and titanium oxide blank are presented in details. The procedure for the determination of iron oxide, titania, alumina, lime, magnesia, and alkalies blank are discussed and presented in details.
SCOPE
1.1 These test methods cover the chemical analysis of clays used in the manufacture of ceramic whitewares.
1.2 The analytical procedures appear in the following order:

SIGNIFICANCE AND USE
This test method is useful to both sellers and purchasers of alumina and quartz powders for determining particle size distributions for materials specifications, manufacturing control, and development and research.
SCOPE
1.1 This test method, one of several found valuable for the measurement of particle size, covers the determination of the particle size distribution of alumina or quartz powders (0.6 to 56.0 μm) using electrical sensing zone particle size analyzers. These instruments use an electric current path of small dimensions which is modulated by individual particle passage through an aperture, and produces individual pulses of amplitude proportional to the particle volume.
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.
1.3 This standard does not purport to address all of the safety problems, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SIGNIFICANCE AND USE
Sieve analyses are carried out to determine the particle size distribution of powders which, in turn, are used to qualify those materials as to their usefulness in the process under consideration. Since particle size analyses have only relative significance, the results should be considered only where they correlate with process characteristics. The parameter that is being measured in this test is the amount of material that will pass through a cloth having theoretically square openings. It must be remembered that all the holes are not square, nor uniform in size, and the question of whether a given particle will go through is a statistical one. Since each particle size analysis method measures a unique physical parameter, the results from one method may not agree with those from another. Particle size distributions play a role in such properties as bulk density, dustiness, and handling characteristics. Care should be taken, however, when interpretations are made from one or two points (sieves) on the distribution curve.
SCOPE
1.1 This test method covers the determination of the particle size distribution of nonplastic ceramic powders such as alumina, silica, feldspar, pyrophyllite, nepheline syenite, talc, titanates, and zircon using wire cloth sieves.
1.2 Materials containing a large amount of fines, containing agglomerates, or that are nonfree-flowing, are wet-sieved to remove excessive fines or to disperse agglomerates before performing the test. This technique is not applicable to materials that are, to any degree, water soluble.
1.3 The values stated in SI units are to be regarded as standard. The values given in parentheses are mathematical conversions to inch-pound units, or are other customary units (in the case of sieve frame diameter and sieve number), that are provided for information only and are not considered standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SIGNIFICANCE AND USE
Manufacturers and users of alumina powders will find this test method useful to determine the particle size distribution of these materials for product specification, quality control, and research and development testing.
SCOPE
1.1 This test method covers the determination of the particle size distribution of alumina in the range from 0.1 to 20 μm having a median particle diameter from 0.5 to 5.0 μm.
1.2 The procedure described in this test method may be successfully applied to other ceramic powders in this general size range. It is the responsibility of the user to determine the applicability of this test method to other material.
1.3 The values stated in SI units are to regarded as the standard. The values given in parentheses are for information only.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SIGNIFICANCE AND USE
The purpose of this test is to obtain values of shrinkage after drying and firing of clays or bodies or both, under various processing conditions to enable designers to determine the proper size of mold or die so as to produce a predetermined size of fired ware.
SCOPE
1.1 This test method covers the determination of linear shrinkage of ceramic whiteware clays, both unfired and fired.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SIGNIFICANCE AND USE
Tests run on many clays generally indicate that a straight-line relationship exists between the methylene blue index (MBI) and such fundamental clay properties as cation exchange capacity, dry bond strength, and casting rate. Where the colloidal portion of the clay is kaolinite, there is also a direct correlation with specific surface (as determined by nitrogen adsorption). Where the colloidal portion contains significant amounts of illite or montmorillonite, the same close correlation does not exist. The MBI better correlates with the ceramic-forming properties than does the specific surface.
That portion of a clay lying within the colloidal range (generally defined as the 0.5- to 0.001-μm range), determines the strictly colloidal properties of the clay and, together with the amount and type of organic material associated with the clay and the 2- to 0.2-μm fraction, largely determines the properties of the clay when used in ceramic-forming processes. While the specific surface of a clay is a function of the particle size and morphology and a relationship exists between dye adsorption and specific surface, the MBI should not be considered to be a particle size analysis since the value obtained is dominated by the character of only the very fine end of the particle size distribution. This procedure describes the determination of the dye adsorption (in this case, methylene blue) of a clay.
SCOPE
1.1 This test method covers the measurement of the adsorption of methylene blue dye by a clay, which is calculated as a methylene blue index for a clay.
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ABSTRACT
This test method details the standard procedure for the determination of modulus of rupture of ceramic whiteware clays, both dry and after conditioning at specified relative humidity, or both. The apparatuses needed for this method are a conditioning cabinet, and a testing machine. Extruded, clay-flint, and solid cast specimens shall be prepared accordingly. Specific procedures as to handling, warpage, drying, and storage, and the corresponding calculations are discussed thoroughly.
SIGNIFICANCE AND USE
3.1 The purpose of this test method is to obtain values of rupture modulus of clays before firing, under various processing conditions (relative humidity).
SCOPE
1.1 This test method covers the determination of the modulus of rupture of ceramic whiteware clays both dry and after conditioning at 50 or 80 % relative humidity, or both.
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SIGNIFICANCE AND USE
Both suppliers and users of pulverized ceramic powders will find this test method useful to determine particle size distributions for materials specifications, manufacturing control, development, and research.  
The test method is simple, although tedious, uses inexpensive equipment, and will provide a continuous curve with data obtained with standardized woven sieves.
SCOPE
1.1 This guide covers the determination of the particle size distribution of pulverized alumina and quartz for particle sizes from 45 to 5 μm by wet sieving.
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.
1.2.1 The only exception is in the Section 5, Apparatus, 5.1 where there is no relevant SI equivalent.
1.3 This standard does not purport to address the safety concerns associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SIGNIFICANCE AND USE
Both sellers and purchasers of alumina and quartz will find the test method useful to determine the specific surface area and indirectly as a measure of the particle size for material specifications, manufacturing control, and research and development.
SCOPE
1.1 This test method covers the determination of the specific surface area of aluminas and silicas used in the manufacture of ceramics. The test method is a general one, permitting the use of any modern commercial nitrogen adsorption apparatus but strictly defining the outgassing procedure. Calculations are based on the Brunauer-Emmett-Teller (BET) equation.
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ABSTRACT
This practice covers procedures for sampling bulk and bagged ceramic whiteware clays. For bulk shipment consisting lumps, samples shall be taken from different parts of the rail car or truck during unloading. Sampling of hopper car or hopper truck shipments is to be done during unloading of the car or truck. For bulk shipment consisting shredded or coarsely ground clay, samples may be taken with a shovel, or with a grain sampler. For bagged lots of ground or air-floated clay, samples may be taken by a grain-sampler or similar sampling instrument. For a clay shipped in slurry form, a sample may be obtained by taking a single grab sample from any portion of the shipment except by skimming the top surface.
SIGNIFICANCE AND USE
Since many tests are performed using very small amounts of powder, it is most important that the test portions be obtained in a standardized manner. The practices described here take into account the possibility of segregation and variability of the ceramic powder in containers of the various sizes and numbers, both in dry and slurry forms.
SCOPE
1.1 This practice covers procedures for sampling bulk and bagged shipments of ceramic whiteware clays.
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ABSTRACT
This guide covers the wet sieve analysis of ceramic whiteware clays. This guide is intended for use in testing shipments of clay as well as for plant control tests. The apparatus to be used include stirring device and sieves. The following procedure shall be followed in the analysis of the ceramic whiteware clays: transferring of duplicate portions of the dried clay sample; agitating of the slurry by means of a mechanical stirrer to ensure complete separation of clay from nonplastic impurities; transferring of the slaked and stirred sample, without loss, to the finest sieve to be employed in the test; washing of the residue remaining on the finest sieve into the pan; nesting the top sieve on the pan, which shall contain a certain amount of clear water; refilling of the pan with the proper amount of water, then nesting the top sieve and its residue on the pan; carefully blotting each sieve on its underside with a soft, damp sponge, and placing the sieve either in a drying oven or under infrared lamps until thoroughly dry; nesting the dried residues and sieves in the proper order, with due care to prevent dusting of the residues; and separating the nested sieves and carefully brushing the residue from each onto a weighing paper.
SCOPE
1.1 This guide covers the wet sieve analysis of ceramic whiteware clays. This guide is intended for use in testing shipments of clay as well as for plant control tests.
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SCOPE
1.1 This test method covers the wet sieve analysis of ceramic whiteware clays. This test method is intended for use in testing shipments of clay as well as for plant control tests.
This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ABSTRACT
This test method details the standard procedures for the determination of the particle size distribution of alumina or quartz powders using X-ray monitoring of gravity sedimentation. This test procedure shall make use of an X-ray sedimentation apparatus, and ultrasonic probe or bath. An aqueous homogeneous dispersion of the specimen is permitted to settle in a cell. The decrease in particle concentration over a programmed settling distance is monitored by an X-ray beam passing through the sedimenting dispersion to a detector. The specimen concentration at any given sedimentation distance is inversely proportional to the X-ray flux and the equivalent diameter (spherical) is calculated from Stokes' law.
SCOPE
1.1 This test method covers the determination of the particle size distribution of alumina or quartz powders in the range from 0.5 to 50 m and having a median particle diameter from 2.5 to 10 m using a sedimentation method. This test method is one of several found valuable for the measurement of particle size. Instruments used for this test method employ a constant intensity X-ray beam that is passed through a sedimenting dispersion of particles.
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.
This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. For specific hazard statements, see Section 7.

SIGNIFICANCE AND USE
Manufacturers and users of alumina powders will find this test method useful to determine the particle size distribution of these materials for product specification, quality control, and research and development testing.
SCOPE
1.1 This test method covers the determination of the particle size distribution of alumina in the range from 0.1 to 20 m having a median particle diameter from 0.5 to 5.0 m.
1.2 The procedure described in this test method may be successfully applied to other ceramic powders in this general size range. It is the responsibility of the user to determine the applicability of this test method to other material.
1.3 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.
This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ABSTRACT
This test method covers the determination of free moisture in ceramic whiteware clays. Whiteware clays may be shipped as a bulk shipment in lumps, a bulk shipment of shredded or coarsely ground clay, or in bagged lots of ground or airfloated clay. Directions are given in this test method for obtaining representative samples of the clay shipment to be used in subsequent tests for the properties of the clay in the shipment. Percentage of free moisture shall be calculated to the nearest 0.1%.
SCOPE
1.1 This test method covers the determination of free moisture in ceramic whiteware clays. Whiteware clays may be shipped as a bulk shipment in lumps, a bulk shipment of shredded or coarsely ground clay, or in bagged lots of ground or airfloated clay. Directions are given in this test method for obtaining representative samples of the clay shipment to be used in subsequent tests for the properties of the clay in the shipment.
1.2 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.