Metals and alloys - Atmospheric corrosion testing - General requirements (ISO 8565:2011)

Metals and alloys - Atmospheric corrosion testing - General requirements (ISO 8565:2011)

ISO 8565:2011 establishes general requirements for stationary corrosion testing of metals and metallic and other inorganic coatings under atmospheric conditions carried out in the open air or under shelters. It can also be applied for testing of complex specimens and assemblies of metallic materials.

Metalle und Legierungen - Korrosionsversuche in der Atmosphäre - Allgemeine Anforderungen (ISO 8565:2011)

In dieser Internationalen Norm sind allgemeine Anforderungen an stationäre Korrosionsversuche von Metallen und metallischen sowie anderen anorganischen Überzügen bei Freibewitterung oder unter Überdachungen festgelegt. Diese Anforderungen können auch auf Korrosionsversuche für komplexe Proben und fertig montierte Baugruppen aus metallischen Werkstoffen angewendet werden.

Métaux et alliages - Essais de corrosion atmosphérique - Exigences générales (ISO 8565:2011)

L'ISO 8565:2011 établit des exigences générales pour les essais de corrosion statique des métaux, revêtements métalliques et autres revêtements inorganiques en milieu extérieur naturel, à ciel ouvert ou sous abri. Elle est également applicable aux essais d'éprouvettes et assemblages de matériaux métalliques complexes.

Kovine in zlitine - Korozijski preskusi v atmosferi - Splošne zahteve (ISO 8565:2011)

Ta mednarodni standard vzpostavlja splošne zahteve za stacionarne korozijske preskuse kovin in kovinskih in drugih anorganskih premazov v atmosferskih pogojih, ki se izvajajo na odprtem ali v zaščitenem prostoru. Lahko se uporabi pri preskušanju kompleksnih vzorcev in sklopov kovinskih materialov.

General Information

Status
Published
Publication Date
30-Jun-2011
Withdrawal Date
30-Jan-2012
ICS
77.060 - Corrosion of metals
Technical Committee
CEN/TC 262 - Metallic and other inorganic coatings
Drafting Committee
CEN/TC 262 - Metallic and other inorganic coatings
Current Stage
6060 - Definitive text made available (DAV) - Publishing
Start Date
01-Jul-2011
Completion Date
01-Jul-2011
Ref Project
SIST EN ISO 8565:2012 - Metals and alloys - Atmospheric corrosion testing - General requirements (ISO 8565:2011)

Relations

Replaces
EN ISO 8565:1995 - Metals and alloys - Atmospheric corrosion testing - General requirements for field tests (ISO 8565:1992)
Effective Date
11-Jul-2011

Buy Standard

EN ISO 8565:2012EN ISO 8565:2012
PreviousNext
Standard
EN ISO 8565:2012
English language
19 pages
sale 10% off
Preview
sale 10% off
Preview
e-Library read for
1 day

Standards Content (Sample)

SLOVENSKI STANDARD
SIST EN ISO 8565:2012
01-januar-2012
1DGRPHãþD
SIST EN ISO 8565:1999
Kovine in zlitine - Korozijski preskusi v atmosferi - Splošne zahteve (ISO
8565:2011)
Metals and alloys - Atmospheric corrosion testing - General requirements (ISO
8565:2011)
Metalle und Legierungen - Korrosionsversuche in der Atmosphäre - Allgemeine
Anforderungen (ISO 8565:2011)
Métaux et alliages - Essais de corrosion atmosphérique - Exigences générales (ISO
8565:2011)
Ta slovenski standard je istoveten z: EN ISO 8565:2011
ICS:
77.060 Korozija kovin Corrosion of metals
SIST EN ISO 8565:2012 en,fr,de
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.

---------------------- Page: 1 ----------------------

SIST EN ISO 8565:2012

---------------------- Page: 2 ----------------------

SIST EN ISO 8565:2012


EUROPEAN STANDARD
EN ISO 8565

NORME EUROPÉENNE

EUROPÄISCHE NORM
July 2011
ICS 77.060 Supersedes EN ISO 8565:1995
English Version
Metals and alloys - Atmospheric corrosion testing - General
requirements (ISO 8565:2011)
Métaux et alliages - Essais de corrosion atmosphérique - Metalle und Legierungen - Korrosionsversuche in der
Exigences générales (ISO 8565:2011) Atmosphäre - Allgemeine Anforderungen (ISO 8565:2011)
This European Standard was approved by CEN on 30 June 2011.

CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European
Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national
standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN member.

This European Standard exists in three official versions (English, French, German). A version in any other language made by translation
under the responsibility of a CEN member into its own language and notified to the CEN-CENELEC Management Centre has the same
status as the official versions.

CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia,
Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland,
Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.





EUROPEAN COMMITTEE FOR STANDARDIZATION
COMITÉ EUROPÉEN DE NORMALISATION

EUROPÄISCHES KOMITEE FÜR NORMUNG

Management Centre: Avenue Marnix 17, B-1000 Brussels
© 2011 CEN All rights of exploitation in any form and by any means reserved Ref. No. EN ISO 8565:2011: E
worldwide for CEN national Members.

---------------------- Page: 3 ----------------------

SIST EN ISO 8565:2012
EN ISO 8565:2011 (E)
Contents Page
Foreword .3

2

---------------------- Page: 4 ----------------------

SIST EN ISO 8565:2012
EN ISO 8565:2011 (E)
Foreword
This document (EN ISO 8565:2011) has been prepared by Technical Committee ISO/TC 156 "Corrosion of
metals and alloys" in collaboration with Technical Committee CEN/TC 262 “Metallic and other inorganic
coatings” the secretariat of which is held by BSI.
This European Standard shall be given the status of a national standard, either by publication of an identical
text or by endorsement, at the latest by January 2012, and conflicting national standards shall be withdrawn at
the latest by January 2012.
Attention is drawn to the possibility that some of the elements of this document may be the subject of patent
rights. CEN [and/or CENELEC] shall not be held responsible for identifying any or all such patent rights.
This document supersedes EN ISO 8565:1995.
According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following
countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech
Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia,
Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain,
Sweden, Switzerland and the United Kingdom.
Endorsement notice
The text of ISO 8565:2011 has been approved by CEN as a EN ISO 8565:2011 without any modification.

3

---------------------- Page: 5 ----------------------

SIST EN ISO 8565:2012

---------------------- Page: 6 ----------------------

SIST EN ISO 8565:2012

INTERNATIONAL ISO
STANDARD 8565
Second edition
2011-07-01

Metals and alloys — Atmospheric
corrosion testing — General
requirements
Métaux et alliages — Essais de corrosion atmosphérique — Exigences
générales




Reference number
ISO 8565:2011(E)
©
ISO 2011

---------------------- Page: 7 ----------------------

SIST EN
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

CEN
EN ISO 10062:2022(Main)
Corrosion tests in artificial atmosphere at very low concentrations of polluting gas(es) (ISO 10062:2022)
SIST EN ISO 10062:2023

This document specifies tests which are intended to determine the influence of one or more flowing polluting gas(es) at volume fractions less than or equal to 10−6 on test samples and/or articles of metals and alloys with or without corrosion protection under determined conditions of temperature and relative humidity.
This document is applicable to
a) metals and their alloys,
b) metallic coatings (anodic and cathodic),
c) metals with conversion coatings,
d) metals with anodic oxide coatings, and
e) metals with organic coatings.

  • Standard
    19 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN ISO 9227:2022(Main)
Corrosion tests in artificial atmospheres - Salt spray tests (ISO 9227:2022)
SIST EN ISO 9227:2023

This document specifies the apparatus, the reagents and the procedure to be used in conducting the neutral salt spray (NSS), acetic acid salt spray (AASS) and copper-accelerated acetic acid salt spray (CASS) tests for assessment of the corrosion resistance of metallic materials, with or without permanent or temporary corrosion protection.
It also describes the method employed to evaluate the corrosivity of the test cabinet environment.
It does not specify the dimensions or types of test specimens, the exposure period to be used for a particular product, or the interpretation of results. Such details are provided in the appropriate product specifications.
The salt spray tests are particularly useful for detecting discontinuities, such as pores and other defects, in certain metallic, organic, anodic oxide and conversion coatings.
The NSS test is particularly applicable to:
—    metals and their alloys;
—    metallic coatings (anodic and cathodic);
—    conversion coatings;
—    anodic oxide coatings;
—    organic coatings on metallic materials.
The AASS test is especially useful for testing decorative coatings of copper + nickel + chromium, or nickel + chromium. It has also been found suitable for testing anodic and organic coatings on aluminium.
The CASS test is useful for testing decorative coatings of copper + nickel + chromium, or nickel + chromium. It has also been found suitable for testing anodic and organic coatings on aluminium.
The salt spray methods are all suitable for checking that the quality of a metallic material, with or without corrosion protection, is maintained. They are not intended to be used for comparative testing as a means of ranking different materials relative to each other with respect to corrosion resistance or as means of predicting long-term corrosion resistance of the tested material.

  • Standard
    32 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN ISO 22479:2022(Main)
Corrosion of metals and alloys - Sulfur dioxide test in a humid atmosphere (fixed gas method) (ISO 22479:2019)
SIST EN ISO 22479:2022

This document specifies a method for assessing the resistance of materials or products to a humid atmosphere containing sulfur dioxide.
This method is applicable to testing metals and alloys, metallic and non-organic coatings and organic coatings.

  • Standard
    22 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN ISO 21207:2022(Main)
Corrosion tests in artificial atmospheres - Accelerated corrosion tests involving alternate exposure to corrosion-promoting gases, neutral salt-spray and drying (ISO 21207:2015)
SIST EN ISO 21207:2022

ISO 21207:2015 defines two accelerated corrosion test methods to be used in assessing the corrosion resistance of products with metals in environments where there is a significant influence of chloride ions, mainly as sodium chloride from a marine source or by winter road de-icing salt, and of corrosion-promoting gases from industrial or traffic air pollution.
ISO 21207:2015 specifies both the test apparatus and test procedures to be used in executing the accelerated corrosion tests.
The methods are especially suitable for assessing the corrosion resistance of sensitive products with metals, e.g. electronic components, used in traffic and industrial environments.

  • Standard
    17 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN ISO 16539:2022(Main)
Corrosion of metals and alloys - Accelerated cyclic corrosion tests with exposure to synthetic ocean water salt-deposition process - "Dry" and "wet" conditions at constant absolute humidity (ISO 16539:2013)
SIST EN ISO 16539:2022

This International Standard specifies two accelerated corrosion test procedures, Methods A and B, for the evaluation of corrosion behaviour of surface-treated metals and their alloys with and without paint on them in atmospheric environments. It also specifies the apparatus used. The two tests involve salt deposition and dry/wet conditions at a constant absolute humidity.
Method A applies to:
metals and their alloys (including corrosion-resistance alloys)
Method B applies to:
metals and their alloys
metals and their alloys with coatings [including metallic coatings (anodic or cathodic), organic
coatings, and conversion coatings]

  • Standard
    27 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN ISO 10270:2022(Main)
Corrosion of metals and alloys - Aqueous corrosion testing of zirconium alloys for use in nuclear power reactors (ISO 10270:2022)
SIST EN ISO 10270:2022

This document specifies:
a) the determination of mass gain;
b) the surface inspection of products of zirconium and its alloys when corrosion is tested in water at 360 °C or in steam at or above 400 °C;
c) the performance of tests in steam at 10,3 MPa.
This document is applicable to wrought products, castings, powder metallurgy products and weld metals.
This method has been widely used in the development of new alloys, heat-treating practices and for the evaluation of welding techniques. It is applicable for use in its entirety to the extent specified for a product acceptance test, rather than merely a means of assessing performance in service.

  • Standard
    24 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN ISO 7539-9:2021(Main)
Corrosion of metals and alloys - Stress corrosion testing - Part 9: Preparation and use of pre-cracked specimens for tests under rising load or rising displacement (ISO 7539-9:2021)
SIST EN ISO 7539-9:2021

1.1  This document specifies procedures for designing, preparing and using pre-cracked specimens for investigating the susceptibility of metal to stress corrosion cracking (SCC) by means of tests conducted under rising load or rising displacement. Tests conducted under constant load or constant displacement are dealt with in ISO 7539-6.
The term “metal” as used in this document includes alloys.
1.2  Because of the need to confine plasticity at the crack tip, pre-cracked specimens are not suitable for the evaluation of thin products such as sheet or wire and are generally used for thicker products including plate, bar, and forgings. They can also be used for parts joined by welding.
1.3  Pre-cracked specimens can be stressed quantitatively with equipment for application of a monotonically increasing load or displacement at the loading points.
1.4  A particular advantage of pre-cracked specimens is that they allow data to be acquired from which critical defect sizes, above which stress corrosion cracking can occur, can be estimated for components of known geometry subjected to known stresses. They also enable rates of stress corrosion crack propagation to be determined.
1.5  A principal advantage of the test is that it takes account of the potential impact of dynamic straining on the threshold for stress corrosion cracking.
1.6  At sufficiently low loading rates, the threshold stress intensity factor for susceptibility to stress corrosion cracking, KISCC, determined by this method can be less than or equal to that obtained by constant load or displacement methods and can be determined more rapidly.

  • Standard
    39 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN ISO 8407:2021(Main)
Corrosion of metals and alloys - Removal of corrosion products from corrosion test specimens (ISO 8407:2021)
SIST EN ISO 8407:2021

This document specifies procedures for the removal of corrosion products formed on metal and alloy corrosion test specimens during their exposure in corrosive environments. For the purpose of this document, the term "metals" refers to pure metals and alloys.
The specified procedures are designed to remove all corrosion products without significant removal of base metal. This allows an accurate determination of the mass loss of the metal, which occurred during exposure to the corrosive environment.
In some cases, these procedures are also applicable to metal coatings, providing the possible effects from the substrate are considered.

  • Standard
    18 pages
    English language
    sale 10% off
    e-Library read for
    1 day
  • Draft
    13 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN ISO 11463:2020(Main)
Corrosion of metals and alloys - Guidelines for the evaluation of pitting corrosion (ISO 11463:2020)
SIST EN ISO 11463:2020

This document gives guidelines for the selection of procedures that can be used in the identification and examination of corrosion pits and in the evaluation of pitting corrosion and pit growth rate.

  • Standard
    20 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN ISO 11844-1:2020(Main)
Corrosion of metals and alloys - Classification of low corrosivity of indoor atmospheres - Part 1: Determination and estimation of indoor corrosivity (ISO 11844-1:2020)
SIST EN ISO 11844-1:2020

This document establishes a classification of low corrosivity of indoor atmospheres.
It specifies the reference metals for which a corrosion attack after a defined exposure period is used for determining corrosivity categories of indoor atmospheres of low corrosivity.
It defines corrosivity categories of indoor atmospheres according to corrosion attack on standard specimens.
It indicates important parameters of indoor atmospheres that can serve as a basis for an estimation of indoor corrosivity.
The selection of a method for the determination of corrosion attack, description of standard specimens, exposure conditions and evaluation are given in ISO 11844-2. The measurement of environmental parameters affecting indoor corrosivity is given in ISO 11844-3.

  • Standard
    28 pages
    English language
    sale 10% off
    e-Library read for
    1 day