Non-destructive testing of welded joints in thermoplastics semi-finished products - Part 2: X-ray radiographic testing

Non-destructive testing of welded joints in thermoplastics semi-finished products - Part 2: X-ray radiographic testing

This document specifies fundamental radiographic techniques which enable repeatable results to be obtained economically.
This document applies to the X-ray radiographic examination of heated tool, electrofusion, extrusion and hot gas joints in plastics materials.
It applies to joints in single wall pipes and plates with a range of thicknesses from 5 mm to 100 mm. It only applies to pipes containing air or other gases at the time of X-ray testing.
This document does not specify acceptance levels of the indications.

Zerstörungsfreie Prüfung von Schweißverbindungen thermoplastischer Kunststoffe - Teil 2: Röntgenprüfung

Dieses Dokument legt die grundlegenden Regeln für Durchstrahlungstechniken mit dem Ziel fest,
vergleichbare Ergebnisse in wirtschaftlicher Weise zu erreichen.
Dieses Dokument gilt für die Durchstrahlungsprüfung von Heizelement-, Heizwendel-, Extrusions- und
Warmgasverbindungen an Kunststoffmaterialien.
Es gilt für Verbindungen an Einwandrohren und Platten im Dickebereich von 5 mm bis 100 mm. Es ist nur
anwendbar für Rohre, die während der Durchstrahlungsprüfung Luft oder andere Gase enthalten.
Dieses Dokument legt keine Zulässigkeitsgrenzen für die Angaben fest.

Essais non destructifs des assemblages soudés sur produits semi-finis en thermoplastiques - Partie 2: Contrôle radiographique par rayons X

La présente Norme européenne spécifie les techniques radiographiques de base qui permettent d'obtenir des résultats répétitifs de manière économique.
La présente norme s'applique au contrôle par radiographie aux rayons X d'assemblages de matières plastiques réalisés par soudage par élément chauffant, par électrofusion, par extrusion et au gaz chaud.
Elle s'applique aux assemblages de tubes à paroi simple et de plaques avec une épaisseur se situant dans la plage de 5 mm à 100 mm. Elle ne s'applique qu'aux tubes contenant de l'air ou un autre gaz au moment du contrôle par radiographie aux rayons X.
La présente norme ne spécifie aucun niveau d'acceptation pour les indications.

Neporušitveno preskušanje zvarjenih spojev plastomernih polizdelkov - 2. del: Rentgensko (radiografsko) preskušanje

General Information

Status
Withdrawn
Publication Date
23-Nov-2004
Withdrawal Date
03-Sep-2019
ICS
25.160.40 - Welded joints and welds
Technical Committee
CEN/TC 249 - Plastics
Drafting Committee
CEN/TC 249/SC 5/WG 2 - Testing of welded joints
Current Stage
9960 - Withdrawal effective - Withdrawal
Completion Date
04-Sep-2019
Ref Project
SIST EN 13100-2:2005 - Non-destructive testing of welded joints in thermoplastics semi-finished products - Part 2: X-ray radiographic testing

Relations

Replaced By
EN 13100-2:2019 - Non-destructive testing of welded joints in thermoplastics semi- finished products - Part 2: X-ray radiographic testing
Effective Date
08-Nov-2017
Parent
EN 13100-1:1999 - Non destructive testing of welded joints of thermoplastics semi-finished products - Part 1: Visual examination
Effective Date
22-Dec-2008

Buy Standard

EN 13100-2:2005EN 13100-2:2005
PreviousNext
Standard
EN 13100-2:2005
English language
17 pages
sale 10% off
Preview
sale 10% off
Preview
e-Library read for
1 day

Standards Content (Sample)


2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.Neporušitveno preskušanje zvarjenih spojev plastomernih polizdelkov - 2. del: Rentgensko (radiografsko) preskušanjeZerstörungsfreie Prüfung von Schweißverbindungen thermoplastischer Kunststoffe - Teil 2: RöntgenprüfungEssais non destructifs des assemblages soudés sur produits semi-finis en thermoplastiques - Partie 2: Contrôle radiographique par rayons XNon-destructive testing of welded joints in thermoplastics semi-finished products - Part 2: X-ray radiographic testing83.140.01Izdelki iz gume in polimernih materialov na splošnoRubber and plastics products in general25.160.40Varjeni spoji in variWelded jointsICS:Ta slovenski standard je istoveten z:EN 13100-2:2004SIST EN 13100-2:2005en01-marec-2005SIST EN 13100-2:2005SLOVENSKI
STANDARD
EUROPEAN STANDARDNORME EUROPÉENNEEUROPÄISCHE NORMEN 13100-2November 2004ICS 25.160.40English versionNon-destructive testing of welded joints in thermoplastics semi-finished products - Part 2: X-ray radiographic testingEssais non destructifs des assemblages soudés surproduits semi-finis en thermoplastiques - Partie 2: Contrôleradiographique par rayons XZerstörungsfreie Prüfung von Schweißverbindungenthermoplastischer Kunststoffe - Teil 2: RöntgenprüfungThis European Standard was approved by CEN on 14 October 2004.CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this EuropeanStandard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such nationalstandards may be obtained on application to the Central Secretariat or to any CEN member.This European Standard exists in three official versions (English, French, German). A version in any other language made by translationunder the responsibility of a CEN member into its own language and notified to the Central Secretariat has the same status as the officialversions.CEN members are the national standards bodies of Austria, Belgium, Cyprus, Czech Republic, Denmark, Estonia, Finland, France,Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Slovakia,Slovenia, Spain, Sweden, Switzerland and United Kingdom.EUROPEAN COMMITTEE FOR STANDARDIZATIONCOMITÉ EUROPÉEN DE NORMALISATIONEUROPÄISCHES KOMITEE FÜR NORMUNGManagement Centre: rue de Stassart, 36
B-1050 Brussels© 2004 CENAll rights of exploitation in any form and by any means reservedworldwide for CEN national Members.Ref. No. EN 13100-2:2004: ESIST EN 13100-2:2005

Minimum image quality values.14 A.1 Single-wall technique; IQI on source side.14 A.2 Double-wall technique; double image; IQI on source side.15 A.3 Double-wall thickness; single or double image; IQI on film side.15 Annex B (informative)
Recommended number of exposures when using the perpendicular, double-wall, single-image and single-wall off-centre techniques for a circumferential butt weld.16
mm t Nominal thickness mm w Penetrated thickness mm
S Radiation source — F Film — α Inclination angle
SDR Dn/t — 5 General 5.1 Security Measures Local or national or international safety precautions when using ionising radiation shall be strictly applied. WARNING NOTICE - Exposure of any part of the human body to X-rays can be highly injurious to health. Wherever X-ray equipment is in use, appropriate legal requirements shall be applied.
5.2 Surface preparation and stage of manufacture Prior to radiography the joint shall be cleaned to remove all traces of dirt etc. from the component surface, which might later cause difficulty in detecting defects. In the case of heated tool butt welded pipes, the external weld bead shall be removed prior to radiography. SIST EN 13100-2:2005
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

CEN
EN 12814-7:2024(Main)
Testing of welded joints of thermoplastics semi-finished products - Part 7: Tensile test with waisted test specimens
SIST EN 12814-7:2024

This document specifies the dimensions, the method of sampling, the preparation of the test specimens and the conditions for performing the tensile test with waisted test specimens in order to determine the tensile energy welding factor.
A tensile test with waisted specimens can be used in conjunction with other tests (e.g. bend, tensile, tensile creep, macro, etc.) to assess the performance of welded assemblies, made from thermoplastics materials.
The test is applicable to co-axial or co-planar heated tool butt welded assemblies made from thermoplastics materials filled or unfilled, but not reinforced. It is not applicable to tubular assemblies with a nominal outside diameter less than 90 mm.

  • Standard
    10 pages
    English language
    sale 10% off
    e-Library read for
    1 day
  • Standard
    10 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN 16296:2021(Main)
Imperfections in thermoplastics welded joints - Quality levels
SIST EN 16296:2021

This document specifies quality levels for imperfections in thermoplastics welded joints that have cooled to ambient temperature and is applicable to material thickness above 2,0 mm.
Three quality levels are specified in order to permit application for a wide range of welded fabrication. They are designated by symbols B, C and D, where B is the most stringent. The quality levels refer to production quality and not to the fitness-for-purpose (see 3.2) of the manufactured product.
The quality level necessary are expected to be defined by the application standard or by the fabricator in conjunction with the user and/or other parties concerned. The level is expected to be prescribed before the start of production, preferably at the enquiry or order stage.
This document applies to the following thermoplastic materials in Table 1:
and to the following welding processes:
-   heated tool welding;
-   electrofusion socket welding;
-   hot gas welding using filler rod only;
-   extrusion welding;
-   solvent welding of pipes.

  • Standard
    22 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN 12814-2:2021(Main)
Testing of welded joints of thermoplastics semi-finished products - Part 2: Tensile test
SIST EN 12814-2:2021

This document specifies the dimensions, the method of sampling, the preparation of the test specimens and the conditions for performing the tensile test in order to determine the short-term tensile welding factor.
A tensile test can be used in conjunction with other tests (e.g. bend, tensile creep, macro) to assess the performance of welded assemblies, made from thermoplastics materials.
The test is applicable to welded semi-finished products made from thermoplastics materials filled or unfilled, but not reinforced, irrespective of the welding process used.

  • Standard
    14 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN 12814-8:2021(Main)
Testing of welded joints of thermoplastics semi-finished products - Part 8: Requirements
SIST EN 12814-8:2021

This document provides the requirements for the tests made on welded thermoplastics semi-finished products.
The selection of the appropriate test method(s) is made in accordance with the particular type and application of welded product.
The test results depend on the conditions of manufacture for the test specimen and on the test conditions. They can therefore only be related to the behaviour of the product or can only be used for designing a structure, if the test conditions can be related to the service conditions.

  • Standard
    17 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN 13100-2:2019(Main)
Non-destructive testing of welded joints in thermoplastics semi- finished products - Part 2: X-ray radiographic testing
SIST EN 13100-2:2019

This document specifies fundamental radiographic techniques with film, which enable repeatable results to be obtained economically.
This document applies to the X-ray radiographic examination of heated tool, electrofusion, extrusion and hot gas joints in plastics materials.
It applies to joints in solid wall pipes and plates with a range of thicknesses from 5 mm to 100 mm. It only applies to pipes containing air or other gases at the time of X-ray testing.
This document does not specify acceptance levels of the indications.

  • Standard
    20 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN 14728:2019(Main)
Imperfections in thermoplastic welds - Classification
SIST EN 14728:2019

This document specifies a system for classifying imperfections that may be encountered in thermoplastic welded joints during manufacture and provides examples of imperfections for the following welding processes:
-   heated tool butt welding;
-   heated tool socket welding;
-   electrofusion socket welding;
-   hot gas welding;
-   extrusion welding;
-   solvent socket welding.
This document does not describe imperfections that may be generated during service or imperfections present before welding, which are due to poor preparation or assembly of components (e.g. fit up). The correct preparation and assembly of components (e.g. fit up) are described in the relevant welding procedure specification (WPS).
This document is also not concerned with the search for the possible influence of these imperfections on the behaviour of joints in relation to the different types of stress to which the latter may be subjected or on methods for preventing such imperfections.
This document can be used in conjunction with EN 16296 [1] to determine the acceptance of welds.
Only imperfections giving rise to discontinuities of materials or changes in shape are taken into consideration in this document, specifying their type, their shape and their positions. This classification can be used to determine the possible origin or causes of the imperfections.

  • Standard
    33 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN 12814-4:2018/AC:2018(Corrigendum)
Testing of welded joints of thermoplastics semi-finished products - Part 4: Peel test
SIST EN 12814-4:2018/AC:2018

This document specifies the dimensions, the method of sampling and the preparation of the test specimens, and also the conditions for performing the peel test perpendicular to the weld in order to determine the peel resistance and the failure behaviour.
A peel test can be used in conjunction with other tests (e.g. tensile creep, macroscopic examination...) to assess the performance of welded assemblies, made from thermoplastics materials.
Peel tests are applicable to overlap welded assemblies made from thermoplastics materials.
The T-peel test as defined in Clause 5 will be used only for assessing welded sheet assemblies. This test is not applicable to welded test pieces containing sheets of different nominal thickness.
The decohesion test as defined in Clause 6 will be used only for assessing electrofusion joints with nominal thickness of pipe/fitting greater than 10 mm.
For socket fusion and for electrofusion socket joints with nominal outside diameter less than or equal to 90 mm, a crush test will be used, as defined in Clause 7.
The crush test can also be used for electrofusion joints with outside diameters greater than 90 mm.
The crush test for electrofusion saddle joints will be performed in accordance with ISO 13955 [1].
NOTE   A decohesion test is also defined in ISO 13954 [2].
The tests defined in this standard are not intended to be used for assessment and/or qualification of thermoplastic fittings that already have their own requirements, e.g. polyethylene fittings according to EN 1555-3 [3] and EN 12201-3 [4].

  • Corrigendum
    2 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN 12814-4:2018(Main)
Testing of welded joints of thermoplastics semi-finished products - Part 4: Peel test
SIST EN 12814-4:2018

This document specifies the dimensions, the method of sampling and the preparation of the test specimens, and also the conditions for performing the peel test perpendicular to the weld in order to determine the peel resistance and the failure behaviour.
A peel test can be used in conjunction with other tests (e.g. tensile creep, macroscopic examination...) to assess the performance of welded assemblies, made from thermoplastics materials.
Peel tests are applicable to overlap welded assemblies made from thermoplastics materials.
The T-peel test as defined in Clause 5 will be used only for assessing welded sheet assemblies. This test is not applicable to welded test pieces containing sheets of different nominal thickness.
The decohesion test as defined in Clause 6 will be used only for assessing electrofusion joints with nominal thickness of pipe/fitting greater than 10 mm.
For socket fusion and for electrofusion socket joints with nominal outside diameter less than or equal to 90 mm, a crush test will be used, as defined in Clause 7.
The crush test can also be used for electrofusion joints with outside diameters greater than 90 mm.
The crush test for electrofusion saddle joints will be performed in accordance with ISO 13955 [1].
NOTE   A decohesion test is also defined in ISO 13954 [2].
The tests defined in this standard are not intended to be used for assessment and/or qualification of thermoplastic fittings that already have their own requirements, e.g. polyethylene fittings according to EN 1555-3 [3] and EN 12201-3 [4].

  • Standard
    16 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN 13100-1:2017(Main)
Non destructive testing of welded joints of thermoplastics semi-finished products - Part 1: Visual examination
SIST EN 13100-1:2017

This European standard covers the visual examination of welds in thermoplastic materials. It may also be applied to visual testing of the joint prior to and during the welding.

  • Standard
    7 pages
    English language
    sale 10% off
    e-Library read for
    1 day
CEN
EN 12814-3:2014(Main)
Testing of welded joints in thermoplastics semi-finished products - Part 3: Tensile creep test
SIST EN 12814-3:2014

This European Standard specifies the dimensions, the method of sampling and the preparation of the test specimens, and the conditions for performing the tensile creep test perpendicular to the weld in order to determine the long-term tensile welding factor.
A tensile creep test may be used in conjunction with other tests (e.g. bend test, tensile test, macrographic examination,...) to assess the performance of welded assemblies, made from thermoplastics materials.
The test is applicable to welded assemblies made from thermoplastics materials filled or unfilled such as tubes and fittings, sheets, plates and profiles, but not reinforced, irrespective of the welding process used.

  • Standard
    25 pages
    English language
    sale 10% off
    e-Library read for
    1 day