SIST EN 12620:2002+A1:2008
(Main)Aggregates for concrete
Aggregates for concrete
This European Standard specifies the properties of aggregates and filler aggregates obtained by processing natural, manufactured or recycled materials and mixtures of these aggregates for use in concrete. It covers aggregates having an oven dried particle density greater than 2,00 Mg/m3 (2 000 kg/m3) for all concrete, including concrete in conformity with EN 206-1 and concrete used in roads and other pavements and for use in precast concrete products. It also covers recycled aggregate with densities between 1,50 Mg/m3 (1 500 kg/m3) and 2,00 Mg/m3 (2 000 kg/m3) with appropriate caveats and recycled fine aggregate (4 mm) with appropriate caveats."
It also specifies that a quality control system is in place for use in factory production control and it provides for the evaluation of conformity of the products to this European Standard.
This standard does not cover filler aggregates to be used as a constituent in cement or as other than inert filler aggregates for concrete.
NOTE 1 Aggregates used in construction should comply with all the requirements of this European Standard. As well as familiar and traditional natural and manufactured aggregates Mandate M/125 "Aggregates" included recycled aggregates and some materials from new or unfamiliar sources. Recycled aggregates are included in the standards and new test methods for them are at an advanced stage of preparation. For unfamiliar materials from secondary sources, however, the work on standardisation has only started recently and more time is needed to define clearly the origins and characteristics of these materials. In the meantime such unfamiliar materials when placed on the market as aggregates must comply fully with this standard and national regulations for dangerous substances (see Annex ZA of the standard) depending upon their intended use. Additional characteristics and requirements may be specified on a case by case basis depending upon experience of use of the product, and defined in specific co
Gesteinskörnungen für Beton
Diese Europäische Norm legt die Eigenschaften von Gesteinskörnungen und Füllern (Gesteinsmehlen) fest, die durch Aufbereitung natürlicher, industriell hergestellter oder rezyklierter Materialien und Mischungen daraus für die Verwendung als Betonzuschlag gewonnen werden. Sie deckt Gesteinskörnungen mit einer Kornrohdichte nach Trocknung im Wärmeschrank größer 2,00 Mg/m3 (2 000 kg/m3) für alle Betonarten ab, einschließlich Beton nach EN 206 1 und Beton zur Verwendung in Straßen und anderen Deckschichten und für die Verwendung in Betonfertigteilen. !Die Norm behandelt ebenfalls rezyklierte Gesteinskörnungen mit einer Korndichte zwischen 1,50 Mg/m³ (1 500 kg/m³) und 2,00 Mg/m³ (2 000 kg/m³) sowie rezyklierte feine Gesteinskörnungen (4 mm),
wobei in beiden Fällen die entsprechenden Vorbehalte gelten."
Sie legt auch ein System zur Qualitätssicherung für die Anwendung in der werkseigenen Produktionskontrolle fest, und sie ist für den Nachweis der Konformität der Produkte mit dieser Europäischen Norm vorgesehen.
Diese Norm deckt keine Füller (Gesteinsmehle) ab, die zur Verwendung als Bestandteil von Zement oder als andere als inerte Füller (Gesteinsmehle) für Beton vorgesehen sind.
!ANMERKUNG 1 Gesteinskörnungen für das Bauwesen sollten sämtlichen Anforderungen dieser Europäischen Norm genügen. Neben den bekannten und traditionellen natürlichen und hergestellten Gesteinskörnungen sind rezyklierte Gesteinskörnungen sowie einige Rohstoffe aus Vorkommen, über die noch keine oder nur wenige Erfahrungen vorliegen, im Mandat M/125 „Gesteinskörnungen“ aufgeführt. Rezyklierte Gesteinskörnungen sind in den Normen enthalten und die entsprechenden neuen Prüfverfahren werden bald vorliegen. Mit den Normungsarbeiten für Sekundärrohstoffe, zu denen nur wenige Erfahrungen vorliegen, wurde jedoch erst vor kurzer Zeit begonnen. Mehr Zeit wird benötigt, um die Herkunft und die Eigenschaften dieser Rohstoffe eindeutig festzulegen.
Granulats pour béton
La présente Norme européenne spécifie les caractéristiques des granulats et des fillers élaborés à partir de matériaux
naturels, artificiels ou recyclés et des mélanges de ces granulats qui sont utilisés dans la fabrication du béton.
Elle s’applique aux granulats dont la masse volumique réelle après séchage est supérieure à 2 Mg/m3 (2 000 kg/m3)
pour tous bétons, y compris les bétons conformes à l’EN 206-1 et les bétons utilisés dans la fabrication des routes et
chaussées ainsi que les granulats entrant dans la composition des produits préfabriqués en béton. !Cela couvre
également les gravillons recyclés de masses volumiques entre 1,50 Mg/m3 (1 500 kg/m3) et 2,00 Mg/m3
(2 000 kg/m3) avec les avertissements appropriés et les sables recyclés (4 mm) avec les avertissements
appropriés.
Elle spécifie également les caractéristiques relatives à un système de maîtrise de la production de granulats et à
l’évaluation de la conformité des produits avec la présente Norme européenne.
La présente norme ne traite pas des fillers utilisés comme composant de ciment ou pour un usage autre que celui de
fillers inertes pour bétons.
NOTE 1 Il convient que les granulats utilisés dans la construction respectent toutes les exigences de la présente Norme
européenne. Le mandat M/125 «Granulats» traite, outre des granulats naturels et artificiels courants et traditionnels, des
granulats recyclés ainsi que de certains matériaux d’origine nouvelle ou moins courante. Les granulats recyclés sont inclus
dans les normes et de nouvelles méthodes d’essai, à un stade avancé d’élaboration, leur sont destinées. Les travaux de
normalisation ne font, en revanche, que commencer pour des matériaux moins courants de source secondaire et davantage
de temps sera nécessaire pour définir clairement l’origine et les caractéristiques de ces matériaux.
Agregati za beton
Ta evropski standard določa lastnosti agregatov in polnilnih agregatov, pridobljenih s predelavo naravnih, umetnih ali recikliranih materialov in mešanic teh agregatov, za uporabo v betonu. Obravnava agregate s prostorninsko maso suhih zrn nad 2,0 Mg/m3 (2 000 kg/m3) za vse betone, vključno z betonom, skladnim z EN 206-1, in betonom, ki se uporablja za ceste in druge tlake ter za predizdelane betonske izdelke. 1 Obravnava tudi reciklirani agregat s prostorninsko maso med 1,50 Mg/m3 (1 500 kg/m3) in 2,00 Mg/m3 (2 000 kg/m3) z ustreznimi svarili ter reciklirani drobni agregat (4 mm) z ustreznimi svarili. 1 . Določa tudi, da mora biti za potrebe kontrole proizvodnje v obratu vpeljan sistem kontrole kakovosti, in predpisuje vrednotenje skladnosti proizvodov s tem evropskim standardom. Ta standard ne zajema polnilnih agregatov, ki se uporabljajo kot dodatek k cementu, ter tudi ne tistih, ki se uporabljajo v kakršne koli druge namene, razen kot inertni polnilni agregati za beton.
OPOMBA 1: Agregati, ki se uporabljajo pri gradnji, naj ustrezajo vsem zahtevam tega evropskega standarda. Mandat M/125 "Agregati" je poleg znanih in tradicionalnih naravnih in umetnih agregatov vključil tudi reciklirane agregate ter nekatere materiale iz novih in neobičajnih virov. Reciklirani agregati so vključeni v standarde,
priprava novih preskusnih metod zanje je v zaključni fazi. Za neobičajne materiale iz sekundarnih virov pa se je delo pri standardiziranju začelo šele pred kratkim in bo potrebnega več časa, da se jasno opredelijo viri ter lastnosti teh materialov. V tem času morajo takšni neobičajni materiali pri dajanju na trg glede na njihovo predvideno uporabo v celoti ustrezati temu standardu in nacionalnim predpisom za nevarne snovi (glej dodatek ZA standarda). Od primera do primera in odvisno od izkušenj pri uporabi proizvoda se lahko predpišejo dodatne lastnosti in zahteve ter se opredelijo v posebnih pogodbenih dokumentih.
OPOMBA 2: Lastnosti lahkih agregatov so predpisane v EN 13055-1:2002 1 .
General Information
Relations
Standards Content (Sample)
SLOVENSKI STANDARD
SIST EN 12620:2002+A1:2008
01-september-2008
Agregati za beton
Aggregates for concrete
Gesteinskörnungen für Beton
Granulats pour béton
Ta slovenski standard je istoveten z: EN 12620:2002+A1:2008
ICS:
91.100.15 Mineralni materiali in izdelki Mineral materials and
products
91.100.30 Beton in betonski izdelki Concrete and concrete
products
SIST EN 12620:2002+A1:2008 en,fr,de
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.
---------------------- Page: 1 ----------------------
SIST EN 12620:2002+A1:2008
---------------------- Page: 2 ----------------------
SIST EN 12620:2002+A1:2008
EUROPEAN STANDARD
EN 12620:2002+A1
NORME EUROPÉENNE
EUROPÄISCHE NORM
April 2008
ICS 91.100.15; 91.100.30 Supersedes EN 12620:2002
English Version
Aggregates for concrete
Granulats pour béton Gesteinskörnungen für Beton
This European Standard was approved by CEN on 1 August 2002 and includes Corrigendum 1 issued by CEN on 26 May 2004 and
Amendment 1 approved by CEN on 16 February 2008.
CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European
Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national
standards may be obtained on application to the CEN Management Centre or to any CEN member.
This European Standard exists in three official versions (English, French, German). A version in any other language made by translation
under the responsibility of a CEN member into its own language and notified to the CEN Management Centre has the same status as the
official versions.
CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Cyprus, Czech Republic, Denmark, Estonia, Finland,
France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal,
Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.
EUROPEAN COMMITTEE FOR STANDARDIZATION
COMITÉ EUROPÉEN DE NORMALISATION
EUROPÄISCHES KOMITEE FÜR NORMUNG
Management Centre: rue de Stassart, 36 B-1050 Brussels
© 2008 CEN All rights of exploitation in any form and by any means reserved Ref. No. EN 12620:2002+A1:2008: E
worldwide for CEN national Members.
---------------------- Page: 3 ----------------------
SIST EN 12620:2002+A1:2008
EN 12620:2002+A1:2008 (E)
Contents
page
Foreword.4
1 Scope .5
2 Normative references .5
3 Terms and definitions .6
4 Geometrical requirements .8
4.1 General.8
4.2 Aggregate sizes.8
4.3 Grading .9
4.4 Shape of coarse aggregate.13
4.5 Shell content of coarse aggregate.14
4.6 Fines content.14
4.7 Fines quality.14
5 Physical requirements .15
5.1 General.15
5.2 Resistance to fragmentation of coarse aggregate.15
5.3 Resistance to wear of coarse aggregate.16
5.4 Resistance to polishing and abrasion of coarse aggregate to be used for surface courses.16
5.5 Particle density and water absorption.17
5.6 Bulk density.17
5.7 Durability .18
5.8 !Classification of the constituents of coarse recycled aggregates.19
6 Chemical requirements .20
6.1 General.20
6.2 Chlorides .20
6.3 Sulfur containing compounds.21
6.4 Other constituents.22
6.5 Carbonate content of fine aggregates for concrete pavement surface courses .23
7 Evaluation of conformity.23
7.1 General.23
7.2 Initial type tests.23
7.3 Factory production control.23
8 Designation .23
8.1 Designation and description .23
8.2 Additional information for the description of an aggregate.24
9 Marking and labelling .24
Annex A (informative) Illustration of grading requirements for most commonly used sizes for graded
coarse aggregates .25
Annex B (informative) Guidance on the description of coarseness/fineness of fine aggregates .27
Annex C (normative) Reduced grading tolerances on producer’s declared typical grading for fine
aggregate.28
Annex D (normative) Assessment of fines.29
Annex E (informative) Guidance on the use of aggregates in concrete.30
Annex F (informative) Notes for guidance on the freezing and thawing resistance of aggregates .31
2
---------------------- Page: 4 ----------------------
SIST EN 12620:2002+A1:2008
EN 12620:2002+A1:2008 (E)
Annex G (informative) Guidance on the effects of some chemical constituents of aggregates on the
durability of concrete in which they are incorporated.33
Annex H (normative) Factory production control.36
Annex ZA (informative) Clauses of this European Standard addressing essential requirements or
other provisions of EU Directives.44
Bibliography.56
3
---------------------- Page: 5 ----------------------
SIST EN 12620:2002+A1:2008
EN 12620:2002+A1:2008 (E)
Foreword
This document (EN 12620:2002+A1:2008) has been prepared by Technical Committee CEN/TC 154 "Aggregates",
the secretariat of which is held by BSI.
This European Standard shall be given the status of a national standard, either by publication of an identical text or
by endorsement, at the latest by October 2008 and conflicting national standards shall be withdrawn at the latest by
October 2008.
This document includes Amendment 1, approved by CEN on 2008-02-16.
This document supersedes EN 12620:2002.
The start and finish of text introduced or altered by amendment is indicated in the text by tags
! ".
The modifications of the related CEN Corrigendum have been implemented at the appropriate places in the text
and are indicated by the tags ˜ ™.
This document has been prepared under a mandate given to CEN by the European Commission and the European
Free Trade Association, and supports essential requirements of EU Directive(s).
For relationship with EU Directive(s), see informative Annex ZA, which is an integral part of this document.
!This amendment introduces clauses for recycled aggregates. The clauses call up new test methods,
prEN 933-11, EN 1744-5, EN 1744-6 and EN 1367-4. These standards are at an advanced stage of
preparation."
Annexes A, B, E, F and G are informative. Annexes C, D and H are normative.
This standard includes a Bibliography.
Requirements for other end uses of aggregates will be specified in the following European Standards:
EN 13043 Aggregates for bituminous mixtures and surface treatments for roads, airfields and
other trafficked areas
EN 13055-1 Lightweight aggregates - Part 1 : Lightweight aggregates for concrete, mortar and grout
prEN 13055-2 Lightweight aggregates - Part 2 : Lightweight aggregates for unbound and bound applications
EN 13139 Aggregates for mortar
prEN 13242 Aggregates for unbound and hydraulically bound materials for use in civil engineering
work and road construction
EN 13383-1 Armourstone - Part 1: Specification
prEN 13450 Aggregates for railway ballast
According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following
countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Cyprus, Czech Republic,
Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania,
Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden,
Switzerland and United Kingdom.
4
---------------------- Page: 6 ----------------------
SIST EN 12620:2002+A1:2008
EN 12620:2002+A1:2008 (E)
1 Scope
This European Standard specifies the properties of aggregates and filler aggregates obtained by processing natural,
manufactured or recycled materials and mixtures of these aggregates for use in concrete. It covers aggregates
3 3
having an oven dried particle density greater than 2,00 Mg/m (2 000 kg/m ) for all concrete, including concrete in
conformity with EN 206-1 and concrete used in roads and other pavements and for use in precast concrete products.
3 3 3
!It also covers recycled aggregate with densities between 1,50 Mg/m (1 500 kg/m ) and 2,00 Mg/m
3
(2 000 kg/m ) with appropriate caveats and recycled fine aggregate (4 mm) with appropriate caveats."
It also specifies that a quality control system is in place for use in factory production control and it provides for the
evaluation of conformity of the products to this European Standard.
This standard does not cover filler aggregates to be used as a constituent in cement or as other than inert filler
aggregates for concrete.
˜NOTE 1 Aggregates used in construction should comply with all the requirements of this European Standard. As well as
familiar and traditional natural and manufactured aggregates Mandate M/125 “Aggregates” included recycled aggregates and
some materials from new or unfamiliar sources. Recycled aggregates are included in the standards and new test methods for
them are at an advanced stage of preparation. For unfamiliar materials from secondary sources, however, the work on
standardisation has only started recently and more time is needed to define clearly the origins and characteristics of these
materials. In the meantime such unfamiliar materials when placed on the market as aggregates must comply fully with this
standard and national regulations for dangerous substances (see Annex ZA of the standard) depending upon their intended
use. Additional characteristics and requirements may be specified on a case by case basis depending upon experience of use
of the product, and defined in specific contractual documents.™
NOTE 2 Properties for lightweight aggregates are specified in !EN 13055-1:2002".
2 Normative references
This European Standard incorporates by dated or undated reference, provisions from other publications. These
normative references are cited at the appropriate places in the text, and the publications are listed hereafter. For
dated references, subsequent amendments to or revisions of any of these publications apply to this European
Standard only when incorporated in it by amendment or revision. For undated references, the latest edition of the
publication referred to applies (including amendments).
!deleted text"
!EN 196-2:2005, Methods of testing cement — Part 2: Chemical analysis of cement"
EN 932-3, Tests for general properties of aggregates — Part 3: Procedure and terminology for simplified petrographic
description
EN 932-5, Tests for general properties of aggregates — Part 5: Common equipment and calibration
EN 933-1, Tests for geometrical properties of aggregates — Part 1: Determination of particle size distribution - Sieving
method
EN 933-3, Tests for geometrical properties of aggregates — Part 3: Determination of particle shape —
Flakiness index
EN 933-4, Tests for geometrical properties of aggregates — Part 4: Determination of particle shape — Shape index
EN 933-7, Tests for geometrical properties of aggregates — Part 7: Determination of shell content — Percentage of
shells in coarse aggregates
EN 933-8, Tests for geometrical properties of aggregates — Part 8: Assessment of fines — Sand equivalent test
EN 933-9, Tests for geometrical properties of aggregates — Part 9: Assessment of fines — Methylene blue test
5
---------------------- Page: 7 ----------------------
SIST EN 12620:2002+A1:2008
EN 12620:2002+A1:2008 (E)
EN 933-10, Tests for geometrical properties of aggregates — Part 10: Assessment of fines — Grading of fillers (air jet
sieving)
!prEN 933-11, Tests for geometrical properties of aggregates — Part 11: Classification test for the constituents
of coarse recycled aggregates"
EN 1097-1, Tests for mechanical and physical properties of aggregates — Part 1: Determination of the resistance to
wear (micro-Deval)
EN 1097-2:1998, Tests for mechanical and physical properties of aggregates — Part 2: Methods for the
determination of resistance to fragmentation
EN 1097-3, Tests for mechanical and physical properties of aggregates — Part 3: Determination of loose bulk density
and voids
EN 1097-6, Tests for mechanical and physical properties of aggregates — Part 6: Determination of particle density
and water absorption
EN 1097-8:1999, Tests for mechanical and physical properties of aggregates — Part 8: Determination of the polished
stone value
EN 1097-9, Tests for mechanical and physical properties of aggregates — Part 9: Determination of the resistance to
wear by abrasion from studded tyres — Nordic test
!EN 1367-1:2007", Tests for thermal and weathering properties of aggregates — Part 1: Determination of
resistance to freezing and thawing
EN 1367-2, Tests for thermal and weathering properties of aggregates — Part 2: Magnesium sulfate test
EN 1367-4, Tests for thermal and weathering properties of aggregates — Part 4: Determination of drying shrinkage
EN 1744-1:1998, Tests for chemical properties of aggregates — Part 1: Chemical analysis
!EN 1744-5, Tests for chemical properties of aggregates — Part 5: Determination of acid soluble chloride salts
EN 1744-6, Tests for chemical properties of aggregates — Part 6: Determination of the influence of recycled
aggregate extract on the initial setting time of cement"
ISO 565:1990, Test sieves — Metal wire cloth, perforated metal plate and electroformed sheet — Nominal sizes of
openings
3 Terms and definitions
For the purposes of this European Standard, the following terms and definitions apply.
3.1
aggregate
granular material used in construction. Aggregate may be natural, manufactured or re-cycled
3.2
natural aggregate
aggregate from mineral sources which has been subjected to nothing more than mechanical processing
3.3
all-in aggregate
aggregate consisting of a mixture of coarse and fine aggregates
NOTE It can be produced without separating into coarse and fine fractions or it may be produced by combining coarse and
fine aggregate.
6
---------------------- Page: 8 ----------------------
SIST EN 12620:2002+A1:2008
EN 12620:2002+A1:2008 (E)
3.4
manufactured aggregate
aggregate of mineral origin resulting from an industrial process involving thermal or other modification
3.5
recycled aggregate
aggregate resulting from the processing of inorganic material previously used in construction
3.6
filler aggregate
aggregate, most of which passes a 0,063 mm sieve, which can be added to construction materials to provide certain
properties
NOTE See 3.12 for the definition of "fines".
3.7
aggregate size
designation of aggregate in terms of lower (d) and upper (D) sieve sizes expressed as d/D
NOTE This designation accepts the presence of some particles which are retained on the upper sieve (oversize) and some
which pass the lower sieve (undersize).
3.8
fine aggregate
designation given to the smaller aggregate sizes with D less than or equal to 4 mm
NOTE Fine aggregate can be produced from natural disintegration of rock or gravel and/or by the crushing of rock or gravel
or processing of manufactured aggregate.
3.9
coarse aggregate
designation given to the larger aggregate sizes with D greater than or equal to 4 mm and d greater than or equal to
2 mm
3.10
natural graded 0/8 mm aggregate
designation given to natural aggregate of glacial and/or fluvial origin with D less than or equal to 8 mm
NOTE This aggregate can also be produced by blending processed aggregate.
3.11
batch
production quantity, a delivery quantity, a partial delivery quantity (railway wagon-load, lorry-load, ship's cargo) or a
stockpile produced at one time under conditions that are presumed uniform
NOTE With a continuous process the quantity produced during a specified period should be treated as a batch.
3.12
fines
particle size fraction of an aggregate which passes the 0,063 mm sieve
3.13
category
level of a property of an aggregate expressed as a range of values or a limiting value
NOTE There is no relationship between the categories of different properties.
3.14
grading
particle size distribution expressed as the percentages by mass passing a specified set of sieves
7
---------------------- Page: 9 ----------------------
SIST EN 12620:2002+A1:2008
EN 12620:2002+A1:2008 (E)
4 Geometrical requirements
4.1 General
The necessity for testing and declaring all properties specified in this clause shall be limited according to the
particular application at end use or origin of the aggregate. When required, the tests specified in clause 4 shall be
carried out to determine appropriate geometrical properties.
NOTE 1 When the value of a property is required but not defined by specified limits the value should be declared by the
producer as an XX category, e.g., in Table 8 a value of say 55 for the flakiness index corresponds to FI (Declared value).
Declared 55
NOTE 2 When a property is not required, a “No requirement” category can be used.
NOTE 3 Guidance on selection of approriate categories for specific applications can be found in national provisions in the
place of use of the aggregate.
4.2 Aggregate sizes
All aggregates shall be described in terms of aggregate sizes using the designations d/D except for aggregates added
as fillers which shall be specified as filler aggregate and shall comply with the grading requirements specified in 4.3.
Aggregate sizes shall be specified using a pair of sieve sizes selected from the basic set, or the basic set plus set 1,
or the basic set plus set 2 in Table 1. A combination of sizes from set 1 and set 2 is not permissible.
Aggregate sizes shall have D/d not less than 1,4.
Table 1 — Sieve sizes for specifying aggregate sizes
Basic set Basic set plus set 1 Basic set plus set 2
mm mm mm
0 0 0
1 1 1
2 2 2
4 4 4
– 5,6 (5) –
– – 6,3 (6)
8 8 8
– – 10
– 11,2 (11) –
– – 12,5 (12)
– – 14
16 16 16
– – 20
– 22,4 (22) –
31,5 (32) 31,5 (32) 31,5 (32)
– – 40
– 45 –
63 63 63
NOTE Rounded sizes shown in parentheses can be used as simplified descriptions of
aggregate sizes.
8
---------------------- Page: 10 ----------------------
SIST EN 12620:2002+A1:2008
EN 12620:2002+A1:2008 (E)
4.3 Grading
4.3.1 General
The grading of the aggregate, when determined in accordance with EN 933-1, shall comply with the requirements of
4.3.1 to 4.3.6 as appropriate to its aggregate size d/D.
NOTE When aggregates of significantly different density are blended caution is necessary to avoid segregation.
When assessing aggregates within a system of factory production control at least 90 % of gradings, taken on
different batches within a maximum period of 6 months, shall fall within the limits specified in 4.3.2 to 4.3.6 for
tolerances on producers’ declared typical gradings.
4.3.2 Coarse aggregates
All coarse aggregates shall comply with the general grading requirements specified in Table 2 appropriate to their
size designation d/D and the selected categories from Table 2.
Table 2 — General grading requirements
Aggregate Size Percentage passing by mass Category
d
G
a & b c b a & b
2 D 1,4 D D d d/2
Coarse D/d ≤ 2 or D ≤ 11,2 mm 100 98 to 100 85 to 99 0 to 20 0 to 5 G 85/20
C
G 80/20
100 98 to 100 80 to 99 0 to 20 0 to 5
C
D/d > 2 and D > 11,2 mm 100 98 to 100 90 to 99 0 to 15 0 to 5 G 90/15
C
Fine D ≤ 4 mm and d = 0 100 95 to 100 85 to 99 – – G 85
F
Natural D = 8 mm and d = 0 100 98 to 100 90 to 99 – – G 90
NG
graded 0/8
All-in D ≤ 45 mm and d = 0 100 98 to 100 90 to 99 – – G 90
A
G 85
100 98 to 100 85 to 99
A
a
Where the sieves calculated are not exact sieve numbers in the ISO 565:1990 R 20 series then the next
nearest sieve size shall be adopted.
b
For gap graded concrete or other special uses additional requirements may be specified.
c
The percentage passing D may be greater than 99 % by mass but in such cases the producer shall
document and declare the typical grading including the sieves D, d, d/2 and sieves in the basic set plus set
1 or basic set plus set 2 intermediate between d and D. Sieves with a ratio less than 1,4 times the next
lower sieve may be excluded.
d
Other aggregate product standards have different requirements for categories.
For graded coarse aggregates where:
a) D > 11,2 mm and D/d > 2; or
b) D ≤ 11,2 mm and D/d > 4,
the following additional requirements (i) and (ii) shall apply for the percentage passing the mid-size sieve:
i) all gradings shall comply with the overall limits given in Table 3;
9
---------------------- Page: 11 ----------------------
SIST EN 12620:2002+A1:2008
EN 12620:2002+A1:2008 (E)
ii) the producer shall document and, on request, declare the typical grading passing the mid-size sieve and
tolerances selected from the categories in Table 3.
Table 3 — Overall limits and tolerances for coarse aggregate grading at mid-size sieves
D/d Mid-size Overall limits and tolerances at mid-size sieves Category
sieve mm (percentage passing by mass) G
T
Overall limits Tolerances on producer's
declared typical grading
< 4 D/1,4 25 to 70 ± 15 G 15
T
≥ 4 D/2 25 to 70 ± 17,5 G 17,5
T
Where the mid-size sieve calculated as above is not an exact sieve size in the ISO 565:1990/R20
series then the nearest sieve in the series shall be used.
NOTE Overall limits and tolerances for the most common product sizes are illustrated in annex A.
For single size coarse aggregates where:
a) D > 11,2 mm and D/d ≤ 2; or
b) D ≤ 11,2 mm and D/d ≤ 4,
there shall be no requirements additional to those specified in Table 2.
4.3.3 Fine aggregate
Fine aggregates shall comply with the general grading requirements specified in Table 2 appropriate to their upper
sieve size D.
The following additional requirements shall be applied to control the variability of the fine aggregate.
The producer shall document and, on request, declare the typical grading for each fine aggregate size produced.
Typical grading is expressed as the percentage by mass of aggregate passing through the sieve sizes specified in
Table 4.
NOTE Recommendations for the classification of coarseness of the fine aggregate are given in annex B (Tables B.1
and B.2)
Fine aggregates in regular satisfactory use for most applications shall comply with the requirements specified in
Table 4. When specified for special uses and cases where the variability of grading is reduced, the grading
tolerances shall be applied in accordance with annex C.
10
---------------------- Page: 12 ----------------------
SIST EN 12620:2002+A1:2008
EN 12620:2002+A1:2008 (E)
Table 4 — Tolerances on producer's declared typical grading for general use fine aggregates
Sieve size Tolerances in percentages passing by mass
mm 0/4 0/2 0/1
a
– –
4 ± 5
a
2 – ± 5 –
a
1 ± 20 ± 20 ± 5
0,250 ± 20 ± 25 ± 25
b
0,063 ± 3 ± 5 ± 5
a
Tolerances of ± 5 are further limited by the requirements for the
percentage passing D in Table 2.
b
In addition to the tolerances stated the maximum value of the fines
content for the category selected from Table 11 applies for
the percentage passing the 0,063 mm sieve.
4.3.4 Natural graded 0/8 mm aggregate
Natural graded 0/8 mm aggregate shall comply with the general grading requirements specified in Table 2.
The following additional requirements shall be applied to control the variability of natural graded 0/8 mm aggregate:
a) the producer shall document and, on request, declare the typical grading for each aggregate produced;
b) gradings shall comply with the tolerances given in Table 5.
11
---------------------- Page: 13 ----------------------
SIST EN 12620:2002+A1:2008
EN 12620:2002+A1:2008 (E)
Table 5 — Tolerances on producer's declared typical grading for natural graded 0/8 mm aggregate
Sieve size Tolerances
mm Percentages passing by mass
8 ± 5
2 ± 10
1 ± 10
0,250 ± 10
0,125 ± 3
0,063 ± 2
4.3.5 All-in aggregate
All-in aggregate shall be supplied as a mixture of coarse and fine aggregate with D ≤ 45 mm and d = 0 and shall
comply with the general grading requirements for the category selected from Table 2.
All-in aggregates shall also comply with the requirements for the percentage passing the two intermediate sieves
specified in Table 6 appropriate to their aggregate size.
Table 6 — Grading requirements for all-in aggregates
Aggregate size Overall limits of the sieves
indicated below
mm (Percentage passing by mass)
Basic set plus set 1 Basic set plus set 2 40 ± 20 70 ± 20
For the sieve
mm
- 0/6,3 1 4
0/8 0/8 1 4
- 0/10 1 4
0/11,2 (11) - 2 5,6 (5)
- 0/12,5 (12) 2 6,3 (6)
- 0/14 2 8
0/16 0/16 2 8
- 0/20 2 10
0/22,4 (22) - 2 11,2 (11)
0/31,5 (32) 0/31,5 (32) 4 16
- 0/40 4 20
0/45 - 4 22,4 (22)
NOTE Figures in parentheses can be used to provide simplified descriptions of ag
...
SLOVENSKI SIST EN 12620:2002+A1
STANDARD
september 2008
Agregati za beton
Aggregates for concrete
Granulats pour béton
Gesteinskörnungen für Beton
Referenčna oznaka
ICS 91.100.15; 91.100.30 SIST EN 12620:2002+A1:2008 (sl)
Nadaljevanje na straneh II in III ter od 1 do 53
© 2011-09. Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.
---------------------- Page: 1 ----------------------
SIST EN 12620:2002+A1 : 200812620:2002+A1 : 20082002+A1:2008
NACIONALNI UVOD
Standard SIST EN 12620:2002+A1 (sl), Agregati za beton, 2008, ima status slovenskega standarda in
je istoveten evropskemu standardu EN 12620:2002+A1 (en, de, fr), Aggregates for concrete, 2008.
Standard SIST EN 12620:2002+A1:2008 nadomešča SIST EN 12620:2002.
NACIONALNI PREDGOVOR
Evropski standard EN 12620:2002+A1:2008 je pripravil tehnični odbor Evropskega komiteja za
standardizacijo CEN/TC 154 Agregati. Slovenski standard SIST EN 12620:2002+A1:2008 je prevod
evropskega standarda EN 12620:2002+A1:2008. V primeru spora glede besedila slovenskega
prevoda v tem standardu je odločilen izvirni evropski standard v enem izmed treh uradnih jezikov
CEN. Slovensko izdajo standarda je pripravil tehnični odbor SIST/TC AGR Agregati.
Odločitev za izdajo tega standarda je dne 20. marca 2008 sprejel SIST/TC AGR Agregati.
ZVEZA S STANDARDI
S privzemom tega evropskega standarda veljajo za omenjeni namen referenčnih standardov vsi
standardi, navedeni v izvirniku, razen tistih, ki so že sprejeti v nacionalno standardizacijo:
SIST EN 196-2:2005 Metode preskušanja cementa – 2. del: Kemična analiza cementa
SISTEN 932-3 Preskusi splošnih lastnosti agregatov – 3. del: Postopek in izrazje
poenostavljenega petrografskega opisa
SISTEN 932-5 Preskusi splošnih lastnosti agregatov – 5. del: Splošne zahteve za
opremo in kalibracijo
SIST EN 933-1 Preskusi geometričnih lastnosti agregatov – 1. del: Določevanje zrnavosti
– Metoda sejanja
SIST EN 933-3 Preskusi geometričnih lastnosti agregatov – 3. del: Določevanje oblike
zrn – Modul ploščatosti
SIST EN 933-4 Preskusi geometričnih lastnosti agregatov – 4. del: Določevanje oblike
zrn – Modul oblike
SIST EN 933-7 Preskusi geometričnih lastnosti agregatov – 7. del: Določanje vsebnosti
školjk – Odstotek školjk v grobih agregatih
SIST EN 933-8 Preskusi geometričnih lastnosti agregatov – 8. del: Ugotavljanje finih
delcev – Ekvivalent peska
SIST EN 933-9 Preskusi geometričnih lastnosti agregatov – 9. del: Ugotavljanje finih
delcev – Preskus z metilen modrim
SIST EN 933-10 Preskusi geometričnih lastnosti agregatov – 10. del: Ugotavljanje finih
delcev – Zrnavost kamene moke (sejanje z zračnim curkom)
SIST EN 933-11 Preskusi geometričnih lastnosti agregatov – 11. del: Klasifikacija sestavin
grobega recikliranega agregata
SIST EN 1097-1 Preskusi mehanskih in fizikalnih lastnosti agregatov – 1. del: Določevanje
odpornosti proti obrabi (mikro-Deval)
SISTEN 1097-2:1999 Preskusi mehanskih in fizikalnih lastnosti agregatov – 2. del: Metode
določevanja odpornosti proti drobljenju
SIST EN 1097-3 Preskusi mehanskih in fizikalnih lastnosti agregatov – 3. del: Določevanje
prostorninske mase in votlin v nasutem stanju
SIST EN 1097-6 Preskusi mehanskih in fizikalnih lastnosti agregatov – 6. del: Določevanje
prostorninske mase zrn in vpijanja vode
II
---------------------- Page: 2 ----------------------
SIST EN 12620:2002+A1 : 2008
SISTEN 1097-8:2000 Preskusi mehanskih in fizikalnih lastnosti agregatov – 8. del:
Določevanje vrednosti količnika zaglajevanja kamenih zrn
SIST EN 1097-9 Preskusi mehanskih in fizikalnih lastnosti agregatov – 9. del: Določevanje
odpornosti proti obrabi zaradi gum-ježevk: Nordijski preskus
SISTEN 1367-1:2007 Preskusi lastnosti agregatov zaradi termičnih in vremenskih vplivov –
1. del: Določevanje odpornosti proti zmrzovanju in odtaljevanju
SISTEN 1367-2 Preskusi lastnosti agregatov zaradi termičnih in vremenskih vplivov –
2. del: Preskus z magnezijevim sulfatom
SISTEN 1367-4 Preskusi lastnosti agregatov zaradi termičnih in vremenskih vplivov –
4. del: Določevanje krčenja pri sušenju
SIST EN 1744-1:1999 Preskusi kemičnih lastnosti agregatov – 1. del: Kemijska analiza
SIST EN 1744-5 Preskusi kemičnih lastnosti agregatov – 5. del: Določevanje kloridnih soli,
topnih v kislini
SIST EN 1744-6 Preskusi kemičnih lastnosti agregatov – 6. del: Ugotavljanje vpliva
izlužka recikliranega agregata na začetni čas vezanja cementa
SIST ISO 565:2003 Preskusna sita – Kovinsko pletivo, kovinske perforirane plošče in
električno oblikovane folije - Imenske mere odprtin
OSNOVA ZA IZDAJO STANDARDA
– privzem standarda EN 12620:2002+A1:2008
PREDHODNA IZDAJA
– SIST EN 12620:2002, Agregati za beton
OPOMBE
– Povsod, kjer se v besedilu standarda uporablja izraz “evropski standard”, v SIST EN
12620:2002+A1:2008 to pomeni “slovenski standard”.
– Uvod in nacionalni predgovor nista sestavni del standarda.
– Ta nacionalni dokument je istoveten EN 12620:2002+A1:2008 in je objavljen z dovoljenjem
CEN
Management Centre
Avenue Marnix 17
B-1000 Bruselj
This national document is identical with EN 12620:2002+A1:2008 and is published with the
permission of
CEN
Management Centre
Avenue Marnix 17
B-1000 Bruselj
III
---------------------- Page: 3 ----------------------
SIST EN 12620:2002+A1 : 200812620:2002+A1 : 20082002+A1:2008
(Prazna stran)
IV
---------------------- Page: 4 ----------------------
EVROPSKI STANDARD EN 12620:2002+A1
EUROPEAN STANDARD
NORME EUROPÉENNE
EUROPÄISCHE NORM april 2008
ICS 91.100.15; 91.100.30 Nadomešča EN 12620:2002
Slovenska izdaja
Agregati za beton
Aggregates for concrete Granulats pour béton Gesteinskörnungen für Beton
Ta evropski standard je CEN sprejel 1. avgusta 2002 in vključuje popravek 1, ki ga je CEN izdal
26. maja 2004, in dopolnilo 1, ki ga je CEN sprejel 16. februarja 2008.
Člani CEN morajo izpolnjevati notranje predpise CEN/CENELEC, s katerim je predpisano, da mora
biti ta standard brez kakršnih koli sprememb sprejet kot nacionalni standard. Najnovejši seznami teh
nacionalnih standardov z njihovimi bibliografskimi podatki se na zahtevo lahko dobijo pri Upravnem
centru ali kateri koli članici CEN.
Ta evropski standard obstaja v treh izvirnih izdajah (angleški, francoski in nemški). Izdaje v drugih
jezikih, ki jih članice CEN na lastno odgovornost prevedejo in izdajo ter prijavijo pri Upravnem centru
CEN, veljajo kot uradne izdaje.
Člani CEN so nacionalni organi za standarde Avstrije, Belgije, Bolgarije, Cipra, Češke republike,
Danske, Estonije, Finske, Francije, Grčije, Islandije, Irske, Italije, Latvije, Litve, Luksemburga,
Madžarske, Malte, Nemčije, Nizozemske, Norveške, Poljske, Portugalske, Romunije, Slovaške,
Slovenije, Španije, Švedske, Švice in Združenega kraljestva.
CEN
Evropski komite za standardizacijo
European Committee for Standardization
Comité Européen de Normalisation
Europäisches Komitee für Normung
Upravni center: Rue de Stassart, 36 B-1050 Bruselj
© 2008 CEN. Lastnice avtorskih pravic so vse države članice CEN. Referenčna oznaka EN 12620:2002+A1:2008 E
---------------------- Page: 5 ----------------------
SIST EN 12620:2002+A1 : 200812620:2002+A1 : 20082002+A1:2008
VSEBINA Stran
Predgovor .4
1 Področje uporabe .5
2 Zveze s standardi .5
3 Izrazi in definicije .6
4 Geometrijske zahteve.8
4.1 Splošno.8
4.2 Velikosti agregata.8
4.3 Zrnavost.9
4.4 Oblika grobega agregata.12
4.5 Vsebnost školjk v grobem agregatu .13
4.6 Vsebnost finih delcev .13
4.7 Kakovost finih delcev.14
5 Fizikalne zahteve.14
5.1 Splošno.13
5.2 Odpornost grobega agregata proti drobljenju .13
5.3 Odpornost grobega agregata proti obrabi.14
5.4 Odpornost grobega agregata za površinske sloje proti zaglajevanju in obrusu (abraziji) .14
5.5 Prostorninska masa zrn in vpijanje vode.15
5.6 Prostorninska masa v nasutem stanju .15
5.7 Obstojnost .15
1
5.8 Klasifikacija sestavin grobih recikliranih agregatov .17
6 Kemijske zahteve .18
6.1 Splošno.18
6.2 Kloridi.18
6.3 Sestavine, ki vsebujejo žveplo .20
6.4 Druge sestavine.20
6.5 Vsebnost karbonatov v drobnih agregatih za površinske sloje betonskih oblog .22
7 Vrednotenje skladnosti .22
7.1 Splošno .22
7.2 Začetni tipski preskusi .22
7.3 Kontrola proizvodnje v obratu.22
8 Opredeltev .22
8.1 Opredelitev in opis.22
8.2 Dodatne informacije za opis agregata.22
9 Označevanje.23
Dodatek A (informativni): Prikaz zahtev za zrnavost za najobičajnejše velikosti grobega agregata
zvezne zrnavosti.24
Dodatek B (informativni): Navodilo za opredelitev grobosti/finosti drobnih agregatov .26
Dodatek C (normativni): Zmanjšana dovoljena odstopanja za tipično zrnavost drobnega agregata,
ki jo deklarira proizvajalec .27
2
---------------------- Page: 6 ----------------------
SIST EN 12620:2002+A1 : 2008
Dodatek D (normativni): Ocenjevanje finih delcev .28
Dodatek E (informativni): Navodilo za uporabo agregata v betonu .29
Dodatek F (informativni): Opombe glede odpornosti agregata proti zmrzovanju in tajanju.30
Dodatek G (informativni): Navodilo o učinkih nekaterih kemičnih sestavin agregatov na
trajnost betona, katerega sestavljajo.32
Dodatek H (normativni): Kontrola proizvodnje v obratu .35
Dodatek ZA (informativni): Točke tega evropskega standarda, ki se nanašajo na
bistvene zahteve ali druga določila direktiv EU.41
Literatura .53
3
---------------------- Page: 7 ----------------------
SIST EN 12620:2002+A1 : 200812620:2002+A1 : 20082002+A1:2008
Predgovor
Ta dokument (EN 12620:2002+A1:2008) je pripravil tehnični odbor CEN/TC 154 Agregati, katerega
sekretariat vodi BSI.
Ta evropski standard mora dobiti status nacionalnega standarda z objavo istovetnega besedila ali z
razglasitvijo najpozneje do oktobra 2008. Nacionalne standarde, ki so v nasprotju s tem standardom,
je treba umakniti najpozneje do oktobra 2008.
Ta dokument vključuje dopolnilo 1, ki ga je CEN sprejel 16. februarja 2008.
Ta dokument nadomešča EN 12620:2002.
1
Začetek in konec besedila, ki je dodano z dopolnilom ali je z njim spremenjeno, je označeno z 1 .
Spremembe iz popravka CEN so vključene na ustreznih mestih v besedilu in označene z
.
Ta dokument je bil pripravljen na podlagi mandata, ki sta ga Evropska komisija in Evropsko združenje
za prosto trgovino (EFTA) podelila CEN, in podpira bistvene zahteve direktiv(-e) EU.
Zveza z direktivo(-ami) EU je razvidna iz informativnega dodatka ZA, ki je sestavni del tega
dokumenta.
1 dopolnilom so uvedene točke za reciklirane agregate. Točke vključujejo nove preskusne
S tem
metode, prEN 933-11, EN 1744-5, EN 1744-6 in EN 1367-4. Ti standardi so v zaključni fazi
priprave. 1
Dodatki A, B, E, F in G so informativni. Dodatki C, D in H so normativni.
Ta standard vključuje literaturo.
Zahteve za druge končne uporabe agregatov bodo predpisane v naslednjih evropskih standardih:
EN 13043 Agregati za bitumenske zmesi in površinske prevleke za ceste, letališča in druge
prometne površine
EN 13055-1 Lahki agregati – 1. del: Lahki agregati za beton, malto in injekcijsko malto
prEN 13055-2 Lahki agregati – 2. del: Lahki agregati za nevezane in vezane uporabe
EN 13139 Agregati za malto
EN 13242 Agregati za nevezane in hidravlično vezane materiale za uporabo v inženirskih
objektih in za gradnjo cest
EN 13383-1 Kamen za obloge pri vodnih zgradbah in drugih gradbenih delih – 1. del:
Specifikacija
prEN 13450 Agregati za grede železniških prog
Skladno z notranjimi predpisi CEN/CENELEC morajo ta evropski standard obvezno uvesti nacionalne
organizacije za standarde naslednjih držav: Avstrije, Belgije, Bolgarije, Cipra, Češke republike,
Danske, Estonije, Finske, Francije, Grčije, Islandije, Irske, Italije, Latvije, Litve, Luksemburga,
Madžarske, Malte, Nemčije, Nizozemske, Norveške, Poljske, Portugalske, Romunije, Slovaške,
Slovenije, Španije, Švedske, Švice in Združenega kraljestva.
4
---------------------- Page: 8 ----------------------
SIST EN 12620:2002+A1 : 2008
1 Področje uporabe
Ta evropski standard določa lastnosti agregatov in polnilnih agregatov, pridobljenih s predelavo
naravnih, umetnih ali recikliranih materialov in mešanic teh agregatov, za uporabo v betonu.
3 3
Obravnava agregate s prostorninsko maso suhih zrn nad 2,0 Mg/m (2 000 kg/m ) za vse betone,
vključno z betonom, skladnim z EN 206-1, in betonom, ki se uporablja za ceste in druge tlake ter za
predizdelane betonske izdelke. 1 Obravnava tudi reciklirani agregat s prostorninsko maso med 1,50
3 3 3 3
Mg/m (1 500 kg/m ) in 2,00 Mg/m (2 000 kg/m ) z ustreznimi svarili ter reciklirani drobni agregat
(4 mm) z ustreznimi svarili. 1 .
Določa tudi, da mora biti za potrebe kontrole proizvodnje v obratu vpeljan sistem kontrole kakovosti, in
predpisuje vrednotenje skladnosti proizvodov s tem evropskim standardom.
Ta standard ne zajema polnilnih agregatov, ki se uporabljajo kot dodatek k cementu, ter tudi ne tistih,
ki se uporabljajo v kakršne koli druge namene, razen kot inertni polnilni agregati za beton.
OPOMBA 1: Agregati, ki se uporabljajo pri gradnji, naj ustrezajo vsem zahtevam tega evropskega standarda. Mandat
M/125 "Agregati" je poleg znanih in tradicionalnih naravnih in umetnih agregatov vključil tudi reciklirane
agregate ter nekatere materiale iz novih in neobičajnih virov. Reciklirani agregati so vključeni v standarde,
priprava novih preskusnih metod zanje je v zaključni fazi. Za neobičajne materiale iz sekundarnih virov pa
se je delo pri standardiziranju začelo šele pred kratkim in bo potrebnega več časa, da se jasno opredelijo
viri ter lastnosti teh materialov. V tem času morajo takšni neobičajni materiali pri dajanju na trg glede na
njihovo predvideno uporabo v celoti ustrezati temu standardu in nacionalnim predpisom za nevarne snovi
(glej dodatek ZA standarda). Od primera do primera in odvisno od izkušenj pri uporabi proizvoda se lahko
predpišejo dodatne lastnosti in zahteve ter se opredelijo v posebnih pogodbenih dokumentih.
OPOMBA 2: Lastnosti lahkih agregatov so predpisane v 1 EN 13055-1:2002 1 .
2 Zveze s standardi
Ta standard vključuje z datiranim ali nedatiranim sklicevanjem določila iz drugih publikacij. Sklicevanja
na standarde so navedena na ustreznih mestih v besedilu, publikacije pa so naštete spodaj. Pri
datiranih sklicevanjih se pri uporabi tega standarda upoštevajo poznejša dopolnila ali spremembe
katere koli od navedenih publikacij le, če so z dopolnilom ali spremembo vključene vanj. Pri
nedatiranih sklicevanjih se uporablja zadnja izdaja publikacije (vključno z dopolnili).
1 zbrisano besedilo 1 .
1 1
EN 196-2:2005 Metode preskušanja cementa – 2. del: Kemična analiza cementa .
EN 932-3 Preskusi splošnih lastnosti agregatov – 3. del: Postopek in izrazje
poenostavljenega petrografskega opisa
EN 932-5 Preskusi splošnih lastnosti agregatov – 5. del: Splošne zahteve za opremo in
kalibracijo
EN 933-1 Preskusi geometrijskih lastnosti agregatov – 1. del: Določevanje zrnavosti –
Metoda sejanja
EN 933-3 Preskusi geometrijskih lastnosti agregatov –- 3. del: Določevanje oblike zrn –
Modul ploščatosti
EN 933-4 Preskusi geometrijskih lastnosti agregatov – 4. del: Določevanje oblike zrn –
Modul oblike
EN 933-7 Preskusi geometrijskih lastnosti agregatov – 7. del: Določevanje vsebnosti
školjk – Odstotek školjk v grobih agregatih
EN 933-8 Preskusi geometrijskih lastnosti agregatov – 8. del: Ugotavljanje finih delcev –
Ekvivalent peska
EN 933-9 Preskusi geometrijskih lastnosti agregatov – 9. del: Ugotavljanje finih delcev –
Preskus z metilen modrim
5
---------------------- Page: 9 ----------------------
SIST EN 12620:2002+A1 : 200812620:2002+A1 : 20082002+A1:2008
EN 933-10 Preskusi geometrijskih lastnosti agregatov – 10. del: Ocenjevanje finih
delcev – Zrnavost kamene moke (sejanje z zračnim curkom)
1 prEN 933-11 Preskusi geometričnih lastnosti agregatov – 11. del: Klasifikacija sestavin
grobega recikliranega agregata 1
EN 1097-1 Preskusi mehanskih in fizikalnih lastnosti agregatov – 1. del: Določevanje
odpornosti proti obrabi (mikro Deval)
EN 1097-2:1998 Preskusi mehanskih in fizikalnih lastnosti agregatov – 2. del: Metode
določevanja odpornosti proti drobljenju
EN 1097-3 Preskusi mehanskih in fizikalnih lastnosti agregatov – 3. del: Določevanje
prostorninske mase in votlin v nasutem stanju
EN 1097-6 Preskusi mehanskih in fizikalnih lastnosti agregatov – 6. del: Določevanje
prostorninske mase zrn in vpijanja vode
EN 1097-8:1999 Preskusi mehanskih in fizikalnih lastnosti agregatov – 8. del: Določevanje
vrednosti količnika zaglajevanja kamenih zrn
EN 1097-9 Preskusi mehanskih in fizikalnih lastnosti agregatov – 9. del: Določevanje
odpornosti proti obrabi z abrazijo zaradi gum ježevk – Nordijski preskus
1 EN 1367-1:2007 1 Preskusi lastnosti agregatov zaradi termičnih in vremenskih vplivov – 1. del:
Določevanje odpornosti proti zmrzovanju in odtaljevanju
EN 1367-2 Preskusi lastnosti agregatov zaradi termičnih in vremenskih vplivov – 2. del:
Preskus z magnezijevim sulfatom
EN 1367-4 Preskusi lastnosti agregatov zaradi termičnih in vremenskih vplivov – 4. del:
Določevanje krčenja pri sušenju
EN 1744-1:1998 Preskusi kemičnih lastnosti agregatov – 1. del: Kemijska analiza
1 EN 1744-5 Preskusi kemičnih lastnosti agregatov – 5. del: Določevanje kloridnih soli,
topnih v kislini
EN 1744-6 Preskusi kemičnih lastnosti agregatov – 6. del: Ugotavljanje vpliva izlužka
recikliranega agregata na začetni čas vezanja cementa 1
ISO 565:1990 Preskusna sita – Pletivo iz kovinske žice, perforirana kovinska plošča in elektro
pločevina – Nazivne velikosti odprtin
3 Izrazi in definicije
V tem standardu veljajo naslednji izrazi in definicije:
3.1
agregat
zrnat material, ki se uporablja pri gradnji. Agregati so lahko naravni, umetni ali reciklirani
3.2
naravni agregat
agregat mineralnega izvora, ki je bil le mehansko predelan
3.3
mešani agregat
agregat iz mešanice grobih in drobnih agregatov
OPOMBA: Proizvede se lahko brez ločevanja na grobe in fine frakcije ali pa s sestavljanjem grobega in drobnega agregata.
6
---------------------- Page: 10 ----------------------
SIST EN 12620:2002+A1 : 2008
3.4
umetni agregat
agregat mineralnega izvora, pripravljen v industrijskem procesu pod vplivom toplotnih ali drugačnih
sprememb
3.5
reciklirani agregat
agregat, ki nastane s predelavo neorganskega materiala, ki je bil pred tem že vgrajen
3.6
polnilni agregat (polnilo, kamena moka)
agregat, katerega pretežni del gre skozi sito 0,063 mm in se lahko dodaja gradbenim materialom za
doseganje določenih lastnosti
OPOMBA: Glej definicijo "finih delcev" v 3.12.
3.7
velikost agregata
oznaka agregata glede na spodnjo (d) in zgornjo (D) velikost sita, izražena z d/D
OPOMBA: Pri tej oznaki se razume, da nekatera zrna ostanejo na zgornjem situ (nadmerna zrna), nekatera pa gredo skozi
spodnje sito (podmerna zrna).
3.8
drobni agregat
oznaka za manjše velikosti agregata, katerih D je manjši ali enak 4 mm
OPOMBA: Drobni agregat (pesek) lahko nastane pri naravnem razpadanju kamnine (hribine) ali proda in/ali z drobljenjem
kamnine (hribine) ali proda ali z industrijsko predelavo umetnega agregata
.
3.9
grobi agregat
oznaka za večje velikosti agregata, pri katerih je D večji ali enak 4 mm, d pa je večji ali enak 2 mm
3.10
naravni odsejani agregat 0/8 mm
oznaka za naravni agregat ledeniškega in/ali rečnega porekla, katerega D je manjši ali enak 8 mm
OPOMBA: Ta agregat se lahko proizvede tudi z mešanjem predelanega (separiranega) agregata.
3.11
šarža
proizvedena količina, dobavljena količina, delna dobavljena količina (tovor na železniškem vagonu,
tovornjaku ali ladji) ali deponija, ki je proizvedena naenkrat pod domnevno enakimi pogoji
OPOMBA: V neprekinjenem procesu naj kot šarža šteje količina, proizvedena v določenem času.
3.12
fini delci
delež zrn v neki velikosti agregata, ki gredo skozi sito 0,063 mm
3.13
kategorija
raven določene lastnosti nekega agregata, izražena z območjem vrednosti ali z mejno vrednostjo
OPOMBA: Med kategorijami različnih lastnosti ni medsebojne povezave.
3.14
zrnavost
porazdelitev velikosti zrn, izražena z masnimi odstotki presevkov skozi predpisani stavek sit
7
---------------------- Page: 11 ----------------------
SIST EN 12620:2002+A1 : 200812620:2002+A1 : 20082002+A1:2008
4 Geometrijske zahteve
4.1 Splošno
Katere od lastnosti, navedenih v tej točki, je treba preskusiti in deklarirati, je odvisno od predvidenega
načina končne uporabe ali izvora agregata. Kadar se zahteva, je treba za določitev ustreznih
geometričnih lastnosti izvesti preskuse, predpisane v točki 4.
OPOMBA 1: Kadar je vrednost neke lastnosti zahtevana, ni pa opredeljena s predpisanimi mejnimi vrednostmi, naj
proizvajalec to vrednost deklarira kot kategorijo XX ; npr. vrednost modula s ploščatostjo 55 v preglednici
deklarirana
8 ustreza kategoriji Fl (deklarirana vrednost).
55
OPOMBA 2: Kadar lastnost ni zahtevana, se lahko uporabi kategorija “ni zahteve”.
OPOMBA 3: Navodilo za izbiro ustreznih kategorij za določeno uporabo je mogoče najti v nacionalnih predpisih, veljavnih v
kraju uporabe agregata.
4.2 Velikosti agregata
Vse agregate je treba označiti z velikostjo agregata, za kar se uporablja oznaka d/D. Izvzeti so
agregati, ki se dodajajo kot polnilo. Te je treba označiti kot polnilni agregat in morajo izpolnjevati
zahteve za zrnavost, predpisane v 4.3.
Velikosti agregata je treba predpisovati s pomočjo dveh velikosti sit iz preglednice 1, ki se izbereta iz
osnovnega stavka ali iz osnovnega in 1. stavka ali iz osnovnega in 2. stavka. Kombinacija velikosti sit
iz 1. in 2. stavka ni dovoljena.
Razmerje D/d pri označitvi velikosti agregata ne sme biti manjše od 1,4.
Preglednica 1: Velikosti sit za določanje velikosti agregata
Osnovni stavek sit Osnovni in Osnovni in
1. stavek sit 2. stavek sit
mm mm mm
0 0 0
1 1 1
2 2 2
4 4 4
– 5,6 (5)
– – 6,3 (6)
8 8 8
– – 10
– 11,2 (11)
– – 12,5 (12)
– – 14
16 16 16
– – 20
– 22,4 (22) –
31,5 (32) 31,5 (32) 31,5 (32)
– – 40
– 45 –
63 63 63
OPOMBA: Zaokrožene številke v oklepajih se lahko uporabljajo za enostavnejše
označevanje velikosti agregata.
8
---------------------- Page: 12 ----------------------
SIST EN 12620:2002+A1 : 2008
4.3 Zrnavost
4.3.1 Splošno
Zrnavost agregata, določena po EN 933-1, mora biti skladna z zahtevami iz 4.3.1 do 4.3.6 glede na
velikost agregata d/D.
OPOMBA: Kadar se mešajo agregati z izrazito različno prostorninsko maso, je treba paziti, da ne pride do segregacije.
Pri ocenjevanju agregatov v sistemu kontrole proizvodnje v obratu mora biti najmanj 90 % zrnavosti,
ugotovljenih za različne šarže v obdobju največ 6 mesecev, v mejah, predpisanih v 4.3.2 do 4.3.6 za
dovoljena odstopanja od proizvajalčevih deklariranih tipičnih zrnavosti.
4.3.2 Grobi agregati
Vsi grobi agregati morajo biti skladni s splošnimi zahtevami za zrnavost, predpisanimi v preglednici 2,
in ustrezati njihovi označeni velikost d/D in izbrani kategoriji iz preglednice 2.
Preglednica 2: Splošne zahteve za zrnavost
Presevek v masnih odstotkih
Velikost Kategorija
Agregat d
mm G
a & b c b a & b
2 D 1,4 D D d d/2
100 98 do 100 85 do 99 0 do 20 0 do 5 G 85/20
C
D/d ≤ 2 ali D ≤ 11,2 mm
100 98 do 100 80 do 99 0 do 20 0 do 5 G 80/20
c
Grobi
100 98 do 100 90 do 99 0 do 15 0 do 5 G 90/15
D/d > 2 in D > 11,2 mm
C
100 95 do 100 85 do 99 – – G 85
D ≤ 4 mm in d = 0 F
Drobni
Naravni
D = 8 mm in d = 0 100 98 do 100 90 do 99 – – G 90
NG
odsejani 0/8
100 98 do 100 90 do 99 – – G 90
A
Mešani D ≤ 45 mm in d = 0
100 98 do 100 85 do 99 G 85
A
a
Kadar izračunana sita niso točno enaka številkam sit iz serije R 20 po ISO 565, je treba upoštevati naslednjo najbližjo
velikost sita.
b
Za betone z nezvezno zrnavostjo ali za druge posebne namene se lahko predpišejo dodatne zahteve.
c
Presevek pri D je lahko večji od 99 masnih odstotkov, vendar mora v takšnih primerih proizvajalec dokumentirati in
deklarirati tipično zrnavost in pri tem vključiti sita D, d in d/2 ter sita med d in D iz osnovnega in 1. stavka ali iz osnovnega in
2. stavka. Sita, ki niso vsaj 1,4-krat večja od najbližjega spodnjega sita, se lahko izvzamejo.
d
Zahteve za kategorije v drugih produktnih standardih za agregat so različne.
Za grobi agregat z zvezno zrnavostjo, kjer sta:
a) D > 11,2 mm in D/d > 2 ali
b) D ≤ 11,2 mm in D/d > 4,
veljata za presevek na sredinskem situ naslednji dodatni zahtevi (i) in (ii):
i) vse zrnavosti morajo ustrezati absolutnim mejam, navedenim v preglednici 3;
ii) proizvajalec mora dokumentirati in na zahtevo deklarirati tipični presevek na sredinskem situ in
dovoljeno odstopanje za izbrano kategor
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.