ISO 36:2017

Rubber, vulcanized or thermoplastic — Determination of adhesion to textile fabrics

ISO 36:2017 specifies a method of test for measuring the force required to separate, by stripping, two plies of fabric bonded with rubber, or a rubber layer and a fabric ply bonded together. The method is applicable when the ply surfaces are approximately plane or when they are in the form of a cylinder having an internal diameter greater than approximately 50 mm. The method is not applicable when the ply surfaces contain sharp bends, angles or other gross irregularities which cannot be excluded when cutting out test pieces. ISO 36:2017 does not apply to coated fabrics, which are tested in accordance with ISO 2411, or textile conveyor belts, which are tested in accordance with ISO 252.

Caoutchouc vulcanisé ou thermoplastique — Détermination de l'adhérence aux textiles

ISO 36:2017 spécifie une méthode d'essai de mesurage de la force nécessaire pour séparer, par pelage, deux plis de textile unis par du caoutchouc ou une couche de caoutchouc liée à un pli de textile. La méthode est applicable lorsque les surfaces des plis sont approximativement planes ou de forme cylindrique, à condition que le diamètre intérieur soit au minimum de l'ordre de 50 mm. La méthode n'est pas applicable lorsque les surfaces des plis comportent des coudes, des angles vifs ou d'autres irrégularités qui ne peuvent être évitées lors de la découpe des éprouvettes. ISO 36:2017 ne s'applique pas aux textiles revêtus soumis à essai conformément à l'ISO 2411, ou aux courroies transporteuses à carcasse textile soumises à essai conformément à l'ISO 252.

General Information

• Status: Withdrawn
• Publication Date: 28-May-2017
• Withdrawal Date: 28-May-2017
• ICS: 59.080.40 - Coated fabrics
• ICS: 83.060 - Rubber
• Technical Committee: ISO/TC 45/SC 2 - Testing and analysis
• Drafting Committee: ISO/TC 45/SC 2/WG 1 - Physical properties
• Current Stage: 9599 - Withdrawal of International Standard
• Completion Date: 04-Mar-2020

Relations

• Revised: ISO 36:2020 - Rubber, vulcanized or thermoplastic — Determination of adhesion to textile fabrics
• Effective Date: 15-Dec-2017
• Revises: ISO 36:2011 - Rubber, vulcanized or thermoplastic — Determination of adhesion to textile fabrics
• Effective Date: 10-Dec-2016

Standards Content (Sample)

INTERNATIONAL ISO
STANDARD 36
Sixth edition
2017-05
Rubber, vulcanized or
thermoplastic — Determination of
adhesion to textile fabrics
Caoutchouc vulcanisé ou thermoplastique — Détermination de
l’adhérence aux textiles
Reference number
ISO 36:2017(E)
©
ISO 2017

---------------------- Page: 1 ----------------------
ISO 36:2017(E)

COPYRIGHT PROTECTED DOCUMENT
© ISO 2017, Published in Switzerland
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized otherwise in any form
or by any means, electronic or mechanical, including photocopying, or posting on the internet or an intranet, without prior
written permission. Permission can be requested from either ISO at the address below or ISO’s member body in the country of
the requester.
ISO copyright office
Ch. de Blandonnet 8 • CP 401
CH-1214 Vernier, Geneva, Switzerland
Tel. [phone]
Fax [phone]
[e-mail]
www.iso.org
ii © ISO 2017 – All rights reserved

---------------------- Page: 2 ----------------------
ISO 36:2017(E)

Contents Page
Foreword .iv
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Principle . 2
5 Apparatus . 2
6 Calibration . 2
7 Test piece . 2
8 Number of test pieces . 3
9 Time-interval between vulcanization and testing . 3
10 Conditioning of test pieces and temperature of test . 3
11 Procedure. 3
12 Expression of results . 4
13 Test report . 4
Annex A (normative) Calibration schedule . 6
Bibliography . 8
© ISO 2017 – All rights reserved iii

---------------------- Page: 3 ----------------------
ISO 36:2017(E)

Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www .iso .org/ directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www .iso .org/ patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation on the voluntary nature of standards, the meaning of ISO specific terms and
expressions related to conformity assessment, as well as information about ISO’s adherence to the
World Trade Organization (WTO) principles in the Technical Barriers to Trade (TBT) see the following
URL: w w w . i s o .org/ iso/ foreword .html
This document was prepared by Technical Committee ISO/TC 45, Rubber and rubber products,
Subcommittee SC 2, Testing and analysis.
This sixth edition cancels and replaces the fifth edition (ISO 36:2011), of which it constitutes a minor
revision to update the normative references in Clause 2.
iv © ISO 2017 – All rights reserved

---------------------- Page: 4 ----------------------
INTERNATIONAL STANDARD ISO 36:2017(E)
Rubber, vulcanized or thermoplastic — Determination of
adhesion to textile fabrics
WARNING — Persons using this document should be familiar with normal laboratory practice.
This document does not purport to address all of the safety problems, if any, associated with its
use. It is the responsibility of the user to establish appropriate safety and health practices and to
ensure compliance with any national regulatory conditions.
1 Scope
This document specifies a method of test for measuring the force required to separate, by stripping,
two plies of fabric bonded with rubber, or a rubber layer and a fabric ply bonded together.
The method is applicable when the ply surfaces are approximately plane or when they are in the
form of a cylinder having an internal diameter greater than approximately 50 mm. The method is not
applicable when the ply surfaces contain sharp bends, angles or other gross irregularities which cannot
be excluded when cutting out test pieces.
This document does not apply to coated fabrics, which are tested in accordance with ISO 2411, or textile
conveyor belts, which are tested in accordance with ISO 252.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content
constitutes requirements of this document. For dated references, only the edition cited applies. For
undated references, the latest edition of the referenced document (including any amendments) applies.
ISO 5893:2002, Rubber and plastics test equipment — Tensile, flexural and compression types (constant
rate of traverse) — Specification
ISO 6133:2015, Rubber and plastics — Analysis of multi-peak traces obtained in determinations of tear
strength and adhesion strength
ISO 18899:2013, Rubber — Guide to the calibration of test equipment
ISO 23529, Rubber — General procedures for preparing and conditioning test pieces for physical test methods
3 Terms and definitions
For the purposes of this document, the following terms and definitions apply.
ISO and IEC maintain terminological databases for use in standardization at the following addresses:
— IEC Electropedia: available at http:// www .electropedia .org/
— ISO Online browsing platform: available at http:// www .iso .org/ obp
3.1
adhesion strength
force per unit width required to cause a separation at the interface between the assembled components
Note 1 to entry: Any separation occurring at any other point, for example inside either component under test,
is a failure of the component material, and does not indicate an adhesion strength. In such cases, the adhesion
strength is greater than the strength of the weakest component involved.
© ISO 2017 – All rights reserved 1

---------------------- Page: 5 ----------------------
ISO 36:2017(E)

4 Principle
The stripping force required to separate two plies of fabric bonded with rubber, or a rubber layer and
a fabric ply bonded together, is measured under specified conditions using test pieces of standard
dimensions in the form of a flat strip.
5 Apparatus
5.1 Test machine, power-driven and equipped with a suitable dynamometer; it shall be capable of
maintaining a substantially constant rate of traverse of the moving head during the test and shall be
linked to an autographic recorder or a computer with graphic capabilities for data acquisition and
processing. An inertialess dynamometer (of the electronic or optical type, for example) should preferably
be used.
The ma
...

NORME ISO
INTERNATIONALE 36
Sixième édition
2017-05
Caoutchouc vulcanisé ou
thermoplastique — Détermination de
l’adhérence aux textiles
Rubber, vulcanized or thermoplastic — Determination of adhesion to
textile fabrics
Numéro de référence
ISO 36:2017(F)
©
ISO 2017

---------------------- Page: 1 ----------------------
ISO 36:2017(F)

DOCUMENT PROTÉGÉ PAR COPYRIGHT
© ISO 2017, Publié en Suisse
Droits de reproduction réservés. Sauf indication contraire, aucune partie de cette publication ne peut être reproduite ni utilisée
sous quelque forme que ce soit et par aucun procédé, électronique ou mécanique, y compris la photocopie, l’affichage sur
l’internet ou sur un Intranet, sans autorisation écrite préalable. Les demandes d’autorisation peuvent être adressées à l’ISO à
l’adresse ci-après ou au comité membre de l’ISO dans le pays du demandeur.
ISO copyright office
Ch. de Blandonnet 8 • CP 401
CH-1214 Vernier, Geneva, Switzerland
Tel. [phone]
Fax [phone]
[e-mail]
www.iso.org
ii © ISO 2017 – Tous droits réservés

---------------------- Page: 2 ----------------------
ISO 36:2017(F)

Sommaire Page
Avant-propos .iv
1 Domaine d’application . 1
2 Références normatives . 1
3 Termes et définitions . 1
4 Principe . 2
5 Appareillage . 2
6 Étalonnage . 2
7 Éprouvette . 2
8 Nombre d’éprouvettes . 3
9 Délai entre vulcanisation et essai . 3
10 Conditionnement des éprouvettes et température d’essai . 3
11 Mode opératoire. 4
12 Expression des résultats. 4
13 Rapport d’essai . 4
Annexe A (normative) Programme d’étalonnage . 6
Bibliographie . 8
© ISO 2017 – Tous droits réservés iii

---------------------- Page: 3 ----------------------
ISO 36:2017(F)

Avant-propos
L’ISO (Organisation internationale de normalisation) est une fédération mondiale d’organismes
nationaux de normalisation (comités membres de l’ISO). L’élaboration des Normes internationales est
en général confiée aux comités techniques de l’ISO. Chaque comité membre intéressé par une étude
a le droit de faire partie du comité technique créé à cet effet. Les organisations internationales,
gouvernementales et non gouvernementales, en liaison avec l’ISO participent également aux travaux.
L’ISO collabore étroitement avec la Commission électrotechnique internationale (IEC) en ce qui
concerne la normalisation électrotechnique.
Les procédures utilisées pour élaborer le présent document et celles destinées à sa mise à jour sont
décrites dans les Directives ISO/IEC, Partie 1. Il convient, en particulier de prendre note des différents
critères d’approbation requis pour les différents types de documents ISO. Le présent document a été
rédigé conformément aux règles de rédaction données dans les Directives ISO/IEC, Partie 2 (voir www
.iso .org/ directives).
L’attention est appelée sur le fait que certains des éléments du présent document peuvent faire l’objet de
droits de propriété intellectuelle ou de droits analogues. L’ISO ne saurait être tenue pour responsable
de ne pas avoir identifié de tels droits de propriété et averti de leur existence. Les détails concernant
les références aux droits de propriété intellectuelle ou autres droits analogues identifiés lors de
l’élaboration du document sont indiqués dans l’Introduction et/ou dans la liste des déclarations de
brevets reçues par l’ISO (voir www .iso .org/ brevets).
Les appellations commerciales éventuellement mentionnées dans le présent document sont données
pour information, par souci de commodité, à l’intention des utilisateurs et ne sauraient constituer un
engagement.
Pour une explication de la nature volontaire des normes, la signification des termes et expressions
spécifiques de l’ISO liés à l’évaluation de la conformité, ou pour toute information au sujet de l’adhésion
de l’ISO aux principes de l’Organisation mondiale du commerce (OMC) concernant les obstacles
techniques au commerce (OTC), voir le lien suivant: w w w . i s o .org/ iso/ fr/ avant -propos .html
Le présent document a été élaboré par le comité technique ISO/TC 45, Élastomères et produits à base
d’élastomères, sous-comité SC 2, Essais et analyses.
Cette sixième édition annule et remplace la cinquième édition (ISO 36:2011), dont elle constitue une
révision mineure pour mettre à jour les références normatives à l’Article 2.
iv © ISO 2017 – Tous droits réservés

---------------------- Page: 4 ----------------------
NORME INTERNATIONALE ISO 36:2017(F)
Caoutchouc vulcanisé ou thermoplastique —
Détermination de l’adhérence aux textiles
AVERTISSEMENT — Il convient que l’utilisateur du présent document connaisse bien les
pratiques courantes de laboratoire. Le présent document n’a pas pour but de traiter tous les
problèmes de sécurité qui sont, le cas échéant, liés à son utilisation. Il incombe à l’utilisateur
d’établir des pratiques appropriées en matière d’hygiène et de sécurité, et de s’assurer de la
conformité à la réglementation nationale en vigueur.
1 Domaine d’application
Le présent document spécifie une méthode d’essai de mesurage de la force nécessaire pour séparer, par
pelage, deux plis de textile unis par du caoutchouc ou une couche de caoutchouc liée à un pli de textile.
La méthode est applicable lorsque les surfaces des plis sont approximativement planes ou de forme
cylindrique, à condition que le diamètre intérieur soit au minimum de l’ordre de 50 mm. La méthode
n’est pas applicable lorsque les surfaces des plis comportent des coudes, des angles vifs ou d’autres
irrégularités qui ne peuvent être évitées lors de la découpe des éprouvettes.
Le présent document ne s’applique pas aux textiles revêtus soumis à essai conformément à l’ISO 2411,
ou aux courroies transporteuses à carcasse textile soumises à essai conformément à l’ISO 252.
2 Références normatives
Les documents suivants cités dans le texte constituent, pour tout ou partie de leur contenu, des
exigences du présent document. Pour les références datées, seule l’édition citée s’applique. Pour les
références non datées, la dernière édition du document de référence s’applique (y compris les éventuels
amendements).
ISO 5893:2002, Appareils d’essai du caoutchouc et des plastiques — Types pour traction, flexion et
compression (vitesse de translation constante) — Spécifications
ISO 6133:2015, Caoutchouc et plastiques — Analyse des tracés multi-pics obtenus lors des déterminations
de la résistance au déchirement et de la force d’adhérence
ISO 18899:2013, Caoutchouc — Guide pour l’étalonnage du matériel d’essai
ISO 23529, Caoutchouc — Procédures générales pour la préparation et le conditionnement des éprouvettes
pour les méthodes d’essais physiques
3 Termes et définitions
Pour les besoins du présent document, les termes et définitions suivants s’appliquent.
L’ISO et l’IEC tiennent à jour des bases de données terminologiques destinées à être utilisées en
normalisation, consultables aux adresses suivantes:
— IEC Electropedia: disponible à l’adresse http:// www .electropedia .org/
— ISO Online browsing platform: disponible à l’adresse http:// www .iso .org/ obp
© ISO 2017 – Tous droits réservés 1

---------------------- Page: 5 ----------------------
ISO 36:2017(F)

3.1
adhérence
force par unité de largueur nécessaire pour provoquer une séparation à l’interface des éléments
assemblés
Note 1 à l’article: Toute séparation se produisant en un autre point, par exemple à l’intérieur de l’un ou de l’autre
des éléments soumis à essai, constitue une rupture du matériau constituant cet élément et n’est pas considérée
comme représentative d’une adhérence. Dans de tels cas, l’adhérence est supérieure à la résistance de l’élément le
plus faible impliqué.
4 Principe
La force de pelage nécessaire pour séparer deux plis de textile unis par du caoutchouc ou une couche de
caoutchouc liée à un pli de textile, est mesurée dans des conditions spécifiées au moyen d’éprouvettes
de dimensions normalisées ayant la forme d’une bande plane.
5 Appareillage
5.1 Machine d’essai de traction, mobile et munie d’un dynamomètre approprié; elle doit pouvoir
maintenir une vitesse de translation sensiblement constante de la traverse mobile pendant l’essai et
doit être reliée à un instrument enregistreur ou à un ordinateur équipé d’une interface graphique pour
acquisition et traitement des données. Il convient d’utiliser de préférence un dynamomètre à faible
inertie (de type électronique ou optique par exemple).
La machine doit être conforme aux ex
...