ISO 13469:2014

Mechanical joining — Form-fit blind rivets and (lock) bolt joints — Specifications and qualification of testing procedures

ISO 13469:2014 specifies the requirements for the testing procedures for interference-fit/form-fit blind rivet joints and lock bolt joints made of metallicand non-metallic materials. The tests required for a particular joint depend upon the performance requirements of the component/assembly and shall be established before any testing is undertaken. The term sheet as used in ISO 13469:2014 includes extrusions, cast material, plastics, and fibre-reinforced plastics, e. g. carbon and glass fibre-reinforced plastics. ISO 13469:2014 does not apply to civil engineering applications such as metal building and steel construction which are covered by other applicable International Standards.

Assemblage mécanique — Rivets aveugles et boulons à filetage autofreinant — Spécifications et qualification des modes opératoires d'essai

General Information

• Status: Published
• Publication Date: 30-Jun-2014
• ICS: 25.160.10 - Welding processes
• ICS: 25.160.40 - Welded joints and welds
• Technical Committee: ISO/TC 44/SC 6 - Resistance welding and allied mechanical joining
• Drafting Committee: ISO/TC 44/SC 6/WG 4 - Joint ISO/TC 44/SC 6 - ISO/TC 2 WG: Mechanical joining of sheet materials
• Current Stage: 9020 - International Standard under periodical review
• Start Date: 15-Jul-2024
• Completion Date: 15-Jul-2024

Standards Content (Sample)

INTERNATIONAL ISO
STANDARD 13469
First edition
2014-07-01
Mechanical joining — Form-fit
blind rivets and (lock) bolt joints —
Specifications and qualification of
testing procedures
Assemblage mécanique — Rivets aveugles et boulons à filetage
autofreinant — Spécifications et qualification des modes opératoires
d’essai
Reference number
©
ISO 2014
© ISO 2014
All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized otherwise in any form
or by any means, electronic or mechanical, including photocopying, or posting on the internet or an intranet, without prior
written permission. Permission can be requested from either ISO at the address below or ISO’s member body in the country of
the requester.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail [e-mail]
Web www.iso.org
Published in Switzerland
ii © ISO 2014 – All rights reserved

Contents Page
Foreword .iv
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Technical contents of the joining procedure specification (JPS) . 2
4.1 General . 2
4.2 Related to the fastener manufacturer . 3
4.3 Related to parent materials . 3
4.4 Common to all joining processes . 3
5 Requirements for joints . 4
5.1 General . 4
5.2 Test specimen . 4
5.3 Joining of assembly components, test pieces, or test specimens. 4
6 Testing and examinations . 4
6.1 General . 4
6.2 Visual examination . 4
6.3 Macro-section/macroscopic examination . 4
6.4 Tensile shear test . 6
6.5 Cross tension test . 8
6.6 Mechanized peel test . 8
6.7 Fatigue and/or endurance tests . 8
7 Re-testing .10
8 Evaluation of the test results .11
9 Single joint specimen test report .11
Annex A (informative) Examples of joining procedures for blind rivets and lock bolts .12
Annex B (informative) Example of a test report .15
Bibliography .17
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out
through ISO technical committees. Each member body interested in a subject for which a technical
committee has been established has the right to be represented on that committee. International
organizations, governmental and non-governmental, in liaison with ISO, also take part in the work.
ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of
electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are
described in the ISO/IEC Directives, Part 1. In particular the different approval criteria needed for the
different types of ISO documents should be noted. This document was drafted in accordance with the
editorial rules of the ISO/IEC Directives, Part 2 (see www.iso.org/directives).
Attention is drawn to the possibility that some of the elements of this document may be the subject of
patent rights. ISO shall not be held responsible for identifying any or all such patent rights. Details of
any patent rights identified during the development of the document will be in the Introduction and/or
on the ISO list of patent declarations received (see www.iso.org/patents).
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation on the meaning of ISO specific terms and expressions related to conformity
assessment, as well as information about ISO’s adherence to the WTO principles in the Technical Barriers
to Trade (TBT) see the following URL: Foreword - Supplementary information
The committee responsible for this document is ISO/TC 44, Welding and allied processes, Subcommittee
SC 6, Resistance welding and allied mechanical joining.
iv © ISO 2014 – All rights reserved

INTERNATIONAL STANDARD ISO 13469:2014(E)
Mechanical joining — Form-fit blind rivets and (lock)
bolt joints — Specifications and qualification of testing
procedures
1 Scope
This International Standard specifies the requirements for the testing procedures for
interference-fit/form-fit blind rivet joints and lock bolt joints made of metallic
and non-metallic materials.
The tests required for a particular joint depend upon the performance requirements of the
component/assembly and shall be established before any testing is undertaken.
The term sheet as used in this International Standard includes extrusions, cast material, plastics, and
fibre-reinforced plastics, e. g. carbon and glass fibre-reinforced plastics.
NOTE Specific service, material, or manufacturing conditions can require more comprehensive testing
than specified in this International Standard. Such tests can include macro and micro sections, fatigue, and/or
endurance tests.
This International Standard does not apply to civil engineering applications such as metal building and
steel construction which are covered by other applicable International Standards.
2 Normative references
The following documents, in whole or in part, are normatively referenced in this document and are
indispensable for its application. For dated references, only the edition cited applies. For undated
references, the latest edition of the referenced document (including any amendments) applies.
ISO 12996, Mechanical joining — Destructive testing of joints — Specimen dimensions and test procedure
for tensile shear testing of single joints
ISO 14588, Blind rivets — Terminology and definitions
ISO 16237, Mechanical joining — Destructive testing of joints — Specimen dimensions and test procedure
for cross-tension testing of single joints
3 Terms and definitions
For the purposes of this document, the terms and definitions given in ISO 14588 and the following apply.
3.1
interference-fit joint
form-fit joint
property of a joint in which the transmission of external forces, in particular shear forces, is effected by
geometrical elements which prevent the movement of the components relative to one another
Note 1 to entry: This condition is frequently achieved by the fastener’s outer diameter surface having complete
contact with the joint’s component holes.
[SOURCE: ISO 12996:2013, 3.12 modified — Figure 1 has been added.]
a) Blind rivet joint with b) Blind rivet joint with flaring c) Lock bolt joint
bulbing blind head blind head
Figure 1 — Examples of interference-fit/form-fit joints
3.2
clearance-fit joint
force-fit joint
property of a joint in which external forces, in particular shear forces, are transmitted through friction
and, if the force to be transmitted is greater than the frictional force, then frictional locking is overcome
and the components move relative to one another
Note 1 to entry: This condition is frequently achieved by the fastener’s outer diameter surface having incomplete
contact with the joint’s component holes.
[SOURCE: ISO 12996:2013, 3.13 modified — Figure 2 has been added.]
a) Blind rivet joint with b) Blind rivet joint with flaring c) Lock bolt joint
bulbing head blind head
Figure 2 — Examples of clearance-fit/force-fit joints
3.3
clearance bridging capability
ability to fill the clearance between the rivet and the work piece to eliminate displacement in the shear
plane
4 Technical contents of the joining procedure specification (JPS)
4.1 General
The performance of at least two samples of the joint to be tested shall be evaluated in accordance with
the tests specified in this International Standard and the results recorded.
2 © ISO 2014 – All rights reserved

The following variables affect the performance of the joints and shall be agreed upon by the contracting
parties before testing:
— hole diameters in sheets;
— nominal and measured diameters of blind rivets and lock bolts;
— sheets thicknesses;
— mechanical properties of sheets, blind rivets, and lock bolts;
— degree of clearance in the rivet or lock bolt joint (see Figure 1 and Figure 2);
— percentages of the sheet thickness over which the clearances are bridged;
— methods of assembly of the joints.
The joining procedure specification (JPS) shall provide the necessary information required to make the
joint. The minimum information required in a JPS for riveting processes is listed in 4.2 to 4.4.
For some applications, it might be necessary to supplement the list. All relevant information shall be
specified in the JPS.
Permissible tolerance ranges shall be specified.
An example of a JPS form is shown in Annex B; these forms should be modified according to actual
practice.
4.2 Related to the fastener manufacturer
— identification of the fastener manufacturer;
— identification of JPS.
4.3 Related to parent materials
4.3.1 Composition and characteristics of parent materials
— designation and type(s) of the material(s) and referenced standard(s);
— in the case of coating(s), material(s), types, thicknesses, location, single- or double-sided.
4.3.2 Dimension of parent materials/test pieces
— thickness of material(s);
— dimensions and cross section(s) of profile(s) or extrusion(s).
4.4 Common to all joining processes
4.4.1 Joining process
— Joining process(es) specified shall be designated as manual, mechanized, automated, or robotic.
4.4.2 Machine specification
— type of setting machine/equipment used and appropriate identification.
4.4.3 Joint design
The overlap, edge distance, distance between two hole axes, sequence and pattern, rivet or bolt design,
type, and manufacturer shall be specified and comply with the appropriate standards and/or application,
as applicable.
NOTE A sketch can be used showing the joint design/configuration.
5 Requirements for joints
5.1 General
The following tests for the joints shall be carried out in accordance with the design requirements.
5.2 Test specimen
The dimensions of the test specimens for tensile shear tests shall be in accordance with ISO 12996,
for cross
...

DRAFT INTERNATIONAL STANDARD
ISO/DIS 13469
ISO/TC 44/SC 6 Secretariat: DIN
Voting begins on: Voting terminates on:
2013-08-23 2013-11-23
Mechanical joining — Form-fit blind rivets and (lock)
bolt joints — Specifications and qualification of testing
procedures
Assemblage mécanique — Rivets aveugles et boulons à filetage autofreinant — Spécifications et
qualification des modes opératoires d’essai
ICS: 25.160.40;25.160.10
THIS DOCUMENT IS A DRAFT CIRCULATED
FOR COMMENT AND APPROVAL. IT IS
THEREFORE SUBJECT TO CHANGE AND MAY
NOT BE REFERRED TO AS AN INTERNATIONAL
STANDARD UNTIL PUBLISHED AS SUCH.
IN ADDITION TO THEIR EVALUATION AS
BEING ACCEPTABLE FOR INDUSTRIAL,
TECHNOLOGICAL, COMMERCIAL AND
USER PURPOSES, DRAFT INTERNATIONAL
STANDARDS MAY ON OCCASION HAVE TO
BE CONSIDERED IN THE LIGHT OF THEIR
POTENTIAL TO BECOME STANDARDS TO
WHICH REFERENCE MAY BE MADE IN
Reference number
NATIONAL REGULATIONS.
ISO/DIS 13469:2013(E)
RECIPIENTS OF THIS DRAFT ARE INVITED
TO SUBMIT, WITH THEIR COMMENTS,
NOTIFICATION OF ANY RELEVANT PATENT
RIGHTS OF WHICH THEY ARE AWARE AND TO
©
PROVIDE SUPPORTING DOCUMENTATION. ISO 2013

ISO/DIS 13469:2013(E)
Copyright notice
This ISO document is a Draft International Standard and is copyright-protected by ISO. Except as
permitted under the applicable laws of the user’s country, neither this ISO draft nor any extract
from it may be reproduced, stored in a retrieval system or transmitted in any form or by any means,
electronic, photocopying, recording or otherwise, without prior written permission being secured.
Requests for permission to reproduce should be addressed to either ISO at the address below or ISO’s
member body in the country of the requester.
ISO copyright office
Case postale 56 • CH-1211 Geneva 20
Tel. + 41 22 749 01 11
Fax + 41 22 749 09 47
E-mail [e-mail]
Web www.iso.org
Reproduction may be subject to royalty payments or a licensing agreement.
Violators may be prosecuted.
ii © ISO 2013 – All rights reserved

ISO/DIS 13469
Contents Page
Foreword . iv
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Technical contents of the joining procedure specification (JPS) . 2
4.1 General . 2
4.2 Related to the fastener manufacturer . 3
4.3 Related to parent materials . 3
4.3.1 Composition and characteristics of parent materials . 3
4.3.2 Dimension of parent materials/ test pieces . 3
4.4 Common to all joining processes . 3
4.4.1 Joining process . 3
4.4.2 Machine specification . 3
4.4.3 Joint design . 4
5 Requirements for joints . 4
5.1 General . 4
5.2 Test specimen . 4
5.3 Joining of assembly components, test pieces or test specimens . 4
6 Testing and examinations . 4
6.1 General . 4
6.2 Visual examination . 4
6.3 Macro-section / Macroscopic examination . 4
6.4 Tensile shear test . 7
6.5 Cross tension test . 7
6.6 Mechanized peel test . 8
6.7 Fatigue and/or endurance tests . 8
6.7.1 General . 8
6.7.2 Cyclic load tests . 9
6.7.3 Failure criterion in fatigue testing . 11
6.8 Re-testing . 11
7 Evaluation of the test results. 11
8 Single Point Joint Test report . 11
Annex A (informative) Examples of joining procedures for blind rivets and lock bolts . 13
A.1 Equipment for the joining . 13
A.2 Joining procedures/ Joining processes . 13
A.2.1 Blind rivets . 13
A.2.2 Lock bolts . 14
A.2.3 Setting operation –clearance fit lock bolts . 14
A.2.4 Setting operation – lock bolts with interference fit /form fit. 14
Annex B (informative) Example for a test report. 16
Bibliography . 17

ISO/DIS 13469
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies
(ISO member bodies). The work of preparing International Standards is normally carried out through ISO
technical committees. Each member body interested in a subject for which a technical committee has been
established has the right to be represented on that committee. International organizations, governmental and
non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the
International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2.
The main task of technical committees is to prepare International Standards. Draft International Standards
adopted by the technical committees are circulated to the member bodies for voting. Publication as an
International Standard requires approval by at least 75 % of the member bodies casting a vote.
Attention is drawn to the possibility that some of the elements of this document may be the subject of patent
rights. ISO shall not be held responsible for identifying any or all such patent rights.
ISO 13469 was prepared by Technical Committee ISO/TC 44, Welding and allied processes, Subcommittee
SC 6, Resistance welding and allied mechanical joining.
This second/third/. edition cancels and replaces the first/second/. edition (), [clause(s) / subclause(s) /
table(s) / figure(s) / annex(es)] of which [has / have] been technically revised.
iv © ISO 2013 – All rights reserved

DRAFT INTERNATIONAL STANDARD ISO/DIS 13469

Mechanical joining — Form-fit blind rivets and (lock) bolt
joints — Specifications and qualification of testing procedures
1 Scope
This international standard specifies the requirements for the testing procedures for interference fit/form-fit
blind rivet joints and lock bolt joints made of metallic and non-metallic materials.
The tests required for a particular joint depend upon the performance requirements of the
component/assembly and shall be established before any testing is undertaken.
The term sheet as used in this standard includes extrusions, cast material, plastics and fibre reinforced
plastics, e. g. carbon and glass fibre reinforced plastics.
NOTE Specific service, material or manufacturing conditions may require more comprehensive testing than specified
in this standard. Such tests may include macro and micro sections, fatigue and/or endurance tests.
This International Standard does not apply to civil engineering applications such as metal building and steel
construction which are covered by other applicable standards.
2 Normative references
The following referenced documents are indispensable for the application of this document. For dated
references, only the edition cited applies. For undated references, the latest edition of the referenced
document (including any amendments) applies.
ISO 12996, Mechanical joining — Destructive testing of joints — Specimen dimensions and test procedure for
tensile shear testing of single joints
ISO/DIS 16237, Mechanical joining — Destructive testing of joints — Specimen dimensions and test
procedure for cross-tension testing of single joints
ISO 14588, Blind rivets — Terminology and definitions
3 Terms and definitions
For the purposes of this document, the terms and definitions given in ISO 14588 and the following apply.
3.1
interference fit joint
form fit joint
property of a joint in which the transmission of external forces, in particular shear forces, is effected by
geometrical elements which prevent the movement of the components relative to one another
NOTE 1 This condition is frequently achieved by the fastener's outer diameter surface having complete contact with the
joint's component holes.
[SOURCE ISO 12996 – modified, Figure 1 added]
ISO/DIS 13469
a) blind rivet joint with bulbing b) blind rivet joint with flaring c) lock bolt joint
blind head blind head
Figure 1 — Examples of interference fit /form fit joints
3.2
clearance fit joint
force fit joint
non-interference fit joint
property of a joint in which external forces, in particular shear forces, are transmitted through friction and if the
force to be transmitted is greater than the frictional force, then frictional locking is overcome and the
components move relative to one another
NOTE 1 to entry This condition is frequently achieved by the fastener's outer diameter surface having incomplete
contact with the joint's component holes.
[SOURCE: ISO 12996 – modified, Figure 2 added]

a) blind rivet joint with bulbing b) blind rivet joint with flaring c) lock bolt joint
head blind head
Figure 2 — Examples of clearance fit/force fit joints
3.3
clearance bridging capability
the ability to fill the clearance between the rivet and the work piece to eliminate displacement in the shear
plane
4 Technical contents of the joining procedure specification (JPS)
4.1 General
The performance of at least two samples of the joint to be tested shall be evaluated in accordance with the
tests specified in this standard and the results recorded.
ISO/DIS 13469
The following variables affect the performance of the joints and shall be agreed upon by the contracting
parties before testing:
 hole diameters in sheets;
 nominal and measured diameters of blind rivets and lock bolt;
 sheets thicknesses;
 mechanical properties of sheets, blind rivets and lock bolts;
 degree of clearance in the rivet or lock bolt joint (see Figure 1 and Figure 2);
 percentages of the sheet thickness over which the clearances are bridged;
 methods of assembly of the joints.
The joining procedure specification (JPS) shall provide the necessary information required to make the joint.
The minimum information required in a JPS for riveting processes is listed in 4.2 to 4.4.
For some applications, it may be necessary to supplement the list. All relevant information shall be specified in
the JPS.
Permissible tolerance ranges shall be specified.
An example of a JPS form is shown in Annex B; these forms should be modified according to actual practice.
4.2 Related to the fastener manufacturer
 Ident
...

МЕЖДУНАРОДНЫЙ ISO
СТАНДАРТ 13469
Первое издание
2014-07-01
Соединения механические.
Соединения с геометрическим
замыканием закладных заклепок с
крепежными болтами-заклепками.
Технические условия и квалификация
процедур испытания
Mechanical joining — Form-fit blind rivets and (lock) bolt joints —
Specifications and qualification of testing procedures

Ответственность за подготовку русской версии несёт GOST R
(Российская Федерация) в соответствии со статьёй 18.1 Устава ISO
Ссылочный номер
©
ISO 2014
ДОКУМЕНТ ЗАЩИЩЕН АВТОРСКИМ ПРАВОМ

© ISO 2014
Все права сохранены. Если не указано иное, без предварительного письменного согласия издателя никакую часть настоящей
публикации нельзя воспроизводить или использовать в какой-либо форме или каким-либо электронным или механическим
способом, включая фотокопирование, а также публикацию в глобальных и внутренних сетях. Для получение разрешения
необходимо обратиться в ISO по нижеуказанному адресу или к представителю комитета-члена ISO в стране нахождения
инициатора запроса.
ISO copyright office
Case postale 56  CH-1211 Geneva 20
Тел.: + 41 22 749 01 11
Факс: + 41 22 749 09 47
Эл. почта: [e-mail]
Веб-сайт: www.iso.org
Опубликовано в Швейцарии
ii © ISO 2014 – Все права сохранены

Содержание Страница
Предисловие . iv
1 Область применения . 1
2 Нормативные ссылки . 1
4 Техническое содержание спецификации процедуры соединения JPS . 3
4.1 Общие положения . 3
4.2 Для изготовителя соединительных деталей, крепежа . 3
4.3 Для исходных (основных) материалов . 3
4.4 Общее для всех процессов сборки . 4
5 Требования к соединениям . 4
5.1 Общие положения . 4
5.2 Испытательный образец . 4
5.3 Соединение компонентов сборки, образцов для испытания или испытываемых
образцов . 4
6 Испытания и исследования . 4
6.1 Общие положения . 4
6.2 Визуальный осмотр . 5
6.3 Макрошлиф/макроскопическое исследование. 5
6.4 Испытание на сдвигание при растяжении . 6
6.5 Испытание на поперечное растяжение . 8
6.6 Испытание на механизированное отслаивание . 8
6.7 Испытание на усталость и/или долговечность . 8
7 Повторное испытание . 11
8 Оценка результатов испытания . 11
9 Протокол испытания образца одиночного соединения . 11
Приложение A (информативное) Примеры процедур соединения для закладных заклепок и
крепежных болтов-заклепок . 13
Приложение B (информативное) Пример протокола испытания . 16
Библиография . 17
Предисловие
Международная организация по стандартизации (ISO) является всемирной федерацией национальных
организаций по стандартизации (комитетов-членов ISO). Разработка международных стандартов
обычно осуществляется техническими комитетами ISO. Каждый комитет-член, заинтересованный в
деятельности, для которой был создан технический комитет, имеет право быть представленным в этом
комитете. Международные правительственные и неправительственные организации, имеющие связи с
ISO, также принимают участие в работах. ISO работает в тесном сотрудничестве с Международной
электротехнической комиссией (IEC) по всем вопросам стандартизации в области электротехники.
Методики, использованные для разработки данного документа и те, которые предназначены для их
дальнейшего сохранения, описаны в Части 1 Директив ISO/IEC. Особенно следует указывать
различные критерии утверждения, необходимые для разных типов документов ISO. Данный документ
составлен в соответствии с редакторскими правилами Части 2 Директив ISO/IEC
(www.iso.org/directives).
Следует иметь в виду, что некоторые элементы этого документа могут быть объектом патентных прав.
Организация ISO не должна нести ответственность за идентификацию какого-либо одного или всех
патентных прав. Детали любого патентного права, идентифицированного при разработке документа
должны находиться во Введении и/или в перечне полученных патентных заявок ISO.
(www.iso.org/patents)
Любое фирменное наименование, используемое в этом документе является информацией для
удобства пользователей и не является одобрением.
О толковании значения специфических терминов ISO и выражений, относящихся к оценке
соответствия, а также информации о строгом соблюдении ISO принципов ВТО в отношении
Технических барьеров в торговле (TBT) см. следующую URL: Предисловие. Дополнительная
информация
Техническим Комитетом, ответственным за данный документ, является ISO/TC 44, Сварка и
родственные процессы, Подкомитет SC 6, Стойкость сварных и родственных механических
соединений.
iv © ISO 2014 – Все права сохраняются

МЕЖДУНАРОДНЫЙ СТАНДАРТ ISO 13469:2014(R)

Механические соединения. Соединения с геометрическим
замыканием закладных заклепок и с крепежными болтами-
заклепками. Технические условия и квалификация
процедур испытания
1 Область применения
Настоящий международный стандарт устанавливает требования к процедурам испытания соединений
из металлических и неметаллических материалов с применением закладных заклепок (с прессовой
посадкой/ с геометрическим замыканием) и крепежных болтов-заклепок.
Испытания необходимые для конкретного соединения зависят от эксплуатационных требований
компонента/узла и устанавливаются перед началом любого испытания.
Основные условия, использованные в данном международном стандарте, включают изделия,
полученные выдавливание, литой материал, пластики, армированные пластмассы, т н угле- и
стекловолоконные армированные пластики.
ПРИМЕЧАНИЕ Специальные услуги, материал или условия производства могут потребовать более
всестороннего испытания, чем установленное в данном международном стандарте. Такие испытания могут
включать испытания макро и микрошлифов, испытания на усталость и/или на долговечность.
Данный международный стандарт не применяется в гражданском строительстве металлических
зданий и стальных конструкций, на которые распространяется действие другого международного
стандарта.
2 Нормативные ссылки
Следующие ссылочные нормативные документы, полностью или частично, являются обязательными
для применения настоящего документа. Для жестких ссылок применяется только цитируемое издание
документа. Для плавающих ссылок необходимо использовать самое последнее издание нормативного
ссылочного документа (включая любые изменения).
ISO 12996, Механические соединения. Разрушающий контроль соединений. размеры образцов и
процедура для проверки сдвигания при испытаниях на растяжение отдельных соединений
ISO 14588, Заклепки потайные. Терминология и определения
ISO 16237, Соединения механические. Разрушающие испытания соединений. Размеры образцов и
методика испытания на поперечное растяжение соединений с одним швом
3 Термины и определения
Для данного документа применяются следующие термины и определения.
3.1
соединение с прессовой посадкой
interference-fit joint
соединение с геометрическим замыканием (по форме)
form-fit joint
свойство соединения, в котором передача внешних усилий, в частности усилий среза, осуществляется
геометрическими элементами, которые предотвращают движение компонентов относительно друг
друга
Примечание 1 к записи: Это условие часто выполняется через поверхность наружного диаметра крепежа,
имеющей полный контакт с отверстиями компонента соединения.
[ИСТОЧНИК: ISO 12996:2013, 3.12 модифицированный — добавлен Рисунок 1.]

a) Соединение закладной b) Соединение закладной c) Соединение крепежным
заклепкой со сферической заклепкой с развальцованной болтом-заклепкой
глухой головкой глухой головкой
Рисунок 1 — Примеры соединений спрессовой посадкой/с геометрическим замыканием
3.2
соединение с подвижной посадкой
clearance-fit joint
соединение прессовое
force-fit joint
свойство соединения, в котором внешние усилия, в частности силы сдвигания передаются трением, и
если передаваемое усилие больше силы трения, то фрикционное блокирование преодолевается и
компоненты перемещаются относительно друг друга
Примечание 1 к записи: Это условие часто выполняется через поверхность наружного диаметра крепежа,
имеющей неполный контакт с отверстиями компонентов соединения
[ИСТОЧНИК: ISO 12996:2013, 3.13 модифицированный — добавлен Рисунок 2.]

a) Соединение закладной b) Соединение закладной c) Соединение крепежным
заклепкой со сферическая заклепкой с развальцованной болтом-заклепкой-
глухой головкой глухой головкой
Рисунок 2—Примеры соединений со свободной посадкой, с прессовой глухой посадкой
2  ISO 2014 – Все права сохраняются

3.3
способность перекрытия зазора
clearance bridging capability
способность заполнить зазор между заклепкой и деталью для исключения перемещения в плоскости
сдвигания
4 Техническое содержание спецификации процедуры соединения JPS
4.1 Общие положения
В соответствии с испытаниями, установленными данным международным стандартом, проводят
оценку рабочих характеристик не менее двух испытательных образцов соединения и регистрируют
результаты.
Следующие переменные действуют на рабочие характеристики соединения и должны быть
согласованы между договаривающимися сторонами перед испытанием:
— диаметры отверстий в листах;
— номинальные и измеренные диаметры закладных заклепок и крепежных болтов-заклепоками-
заклепкамиов-заклепокы-заклепки-заклепкаов-заклепок;
— толщины листов;
— механические свойства листов, закладных заклепок и крепежных болтов-заклепок;
— величина зазора в соединении закладной заклепкой или крепежным болтом-заклепкой (см.
Рисунок 1 и Рисунок 2;
— проценты толщины листа, выше которой зазоры заполняются;
— методы сборки соединений.
В спецификации процедуры соединения JPS представляется необходимая информация для
осуществления соединения. Минимальная информация, требуемая в спецификации процедуры
соединения JPS для процессов клепки, перечислена в 4.2 до 4.4.
Для некоторых случаев применения может потребоваться дополнительный перечень. Вся нужная
информация должна быть установлена в спецификации процедуры соединения JPS.
Устанавливаются диапазоны допустимых допусков.
Пример формы спецификации процедуры соединения JPS показан в Приложении B; эти формы
модифицируются в соответствии с реальной практикой.
4.2 Для изготовителя соединительных деталей, крепежа
— идентификация изготовителя крепежа;
— идентификация спецификации процедуры соединения JPS.
4.3 Для исходных (основных) материалов
4.3.1 Химический состав и характеристики основных материалов
— обозначение и тип(ы) материала(-ов) и ссылки на стандарт(-ы);
 ISO 2014 – Все права сохраняются 3

— в случае покрытия(ий), материал(ы), типы, толщина, расположение, одно- или двустороннее.
4.3.2 Размер основного материала/ испытательных образцов
— толщина материала(-ов);
— размеры и поперечное сечение(я) профиля(ей) или профилей, полученных экструзией
4.4 Общее для всех процессов сборки
4.4.1 Процесс сборки
— Установленный процесс(ы) сборки должен обозначаться как ручной, механизированный,
автоматический или с помощью робота.
4.4.2 Спецификация машины
— используемый тип наладки машины /оборудования и соответствующая идентификация.
4.4.3 Конструкция сборки
Перекрытие, расстояние до края, расстояние между двумя осями отверстий, последовательность и
шаблон, конструкция заклепки или болта-заклепки, тип, и изготовитель должны быть установлены и
подчиняться соответствующим стандартам и/или назначению, по мере применимости.
ПРИМЕЧАНИЕ Допускается эскиз, показывающий конструкцию/конфигурацию сборки.
5 Требования к соединениям
5.1 Общие положения
Следующие испытания соединений выполняются в соответствии с требованиями конструкции.
5.2 Испытательный образец
Размеры образцов для испытаний на сдвигание при растяжении должны соответствовать ISO 12996,
для испытаний на поперечное растяжение ISO/DIS 16237, на механизированное испытания на
расслаивание соединений, см. например ISO 14270, а для усталостных испытаний см. ISO 18592.
Для облегчения испытания предпочтение отдается использованию образцов, а не любых отрезанных
деталей, отобранных из реальных компон
...