kSIST-TP FprCEN ISO/ASTM TR 52958:2026

Additive manufacturing of metals - Powder bed fusion (PBF) - In-situ coaxial photodiode monitoring for lack of fusion flaw detection in PBF-LB (ISO/ASTM DTR 52958:2026)

In this document, a workflow that includes experimental procedures and flaw (imperfection) detection algorithms to identify the location of flaws created during the powder bed fusion-laser-based (PBF-LB) process of metals is explained. These flaws may have detrimental effects on the printed part mechanical performance.
In this practice, only guidelines and workflow for coaxial photodiode-based in-situ monitoring as well as the associated statistical and machine learning flaw detection algorithms are provided.
This practice does not address the security risks associated with manufacturing and environmental information. It is the responsibility of the user to follow practices and establish appropriate information technology related security measures.
WARNING - This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.

Additive Fertigung von Metallen - Pulverbettfusion (PBF) - Bewährte Verfahren zur In-Situ-Fehlererkennung und -analyse für laserbasierte PBF (ISO/ASTM DTR 52958:2026)

Fabrication additive de métaux - Fusion sur lit de poudre - Surveillance par photodiode coaxiale in situ pour la détection de défauts de fusion en PBF-LB (ISO/ASTM DTR 52958:2026)

Dodajalna izdelava kovinskih izdelkov - Spajanje prahu na podlagi (PBF) - Sočasno zaznavanje nespojenih mest med procesom PBF-LB s koaksialno nameščenimi fotodiodami (ISO/ASTM DTR 52958:2026)

General Information

• Status: Not Published
• Public Enquiry End Date: 19-Apr-2026
• ICS: 25.030 - Additive manufacturing
• Technical Committee: VAR - Welding
• Current Stage: 5520 - Unique Acceptance Procedure (UAP) (Adopted Project)
• Start Date: 20-Feb-2026
• Due Date: 10-Jul-2026
• Ref Project: FprCEN ISO/ASTM TR 52958 - Additive manufacturing of metals - Powder bed fusion (PBF) - In-situ coaxial photodiode monitoring for lack of fusion flaw detection in PBF-LB (ISO/ASTM DTR 52958:2026)

Standards Content (Sample)

SLOVENSKI STANDARD
01-april-2026
Dodajalna izdelava kovinskih izdelkov - Spajanje prahu na podlagi (PBF) -
Sočasno zaznavanje nespojenih mest med procesom PBF-LB s koaksialno
nameščenimi fotodiodami (ISO/ASTM DTR 52958:2026)
Additive manufacturing of metals - Powder bed fusion (PBF) - In-situ coaxial photodiode
monitoring for lack of fusion flaw detection in PBF-LB (ISO/ASTM DTR 52958:2026)
Additive Fertigung von Metallen - Pulverbettfusion (PBF) - Bewährte Verfahren zur In-
Situ-Fehlererkennung und -analyse für laserbasierte PBF (ISO/ASTM DTR 52958:2026)
Fabrication additive de métaux - Fusion sur lit de poudre - Surveillance par photodiode
coaxiale in situ pour la détection de défauts de fusion en PBF-LB (ISO/ASTM DTR
52958:2026)
Ta slovenski standard je istoveten z: FprCEN ISO/ASTM TR 52958
ICS:
25.030 3D-tiskanje Additive manufacturing
kSIST-TP FprCEN ISO/ASTM TR en,fr,de
52958:2026
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.

FINAL DRAFT
Technical
Report
ISO/ASTM DTR
ISO/TC 261
Additive manufacturing of metals —
Secretariat: DIN
Powder bed fusion (PBF) — In-situ
Voting begins on:
coaxial photodiode monitoring for
2026-01-27
lack of fusion flaw detection in PBF-
Voting terminates on:
LB
2026-04-21
Fabrication additive de métaux — Fusion sur lit de poudre —
Surveillance par photodiode coaxiale in situ pour la détection de
défauts de fusion en PBF-LB
RECIPIENTS OF THIS DRAFT ARE INVITED TO SUBMIT,
WITH THEIR COMMENTS, NOTIFICATION OF ANY
RELEVANT PATENT RIGHTS OF WHICH THEY ARE AWARE
AND TO PROVIDE SUPPOR TING DOCUMENTATION.
IN ADDITION TO THEIR EVALUATION AS
BEING ACCEPTABLE FOR INDUSTRIAL, TECHNO­
ISO/CEN PARALLEL PROCESSING LOGICAL, COMMERCIAL AND USER PURPOSES, DRAFT
INTERNATIONAL STANDARDS MAY ON OCCASION HAVE
TO BE CONSIDERED IN THE LIGHT OF THEIR POTENTIAL
TO BECOME STAN DARDS TO WHICH REFERENCE MAY BE
MADE IN NATIONAL REGULATIONS.
Reference number
ISO/ASTM DTR 52958:2026(en) © ISO/ASTM International 2026

FINAL DRAFT
ISO/ASTM DTR 52958:2026(en)
Technical
Report
ISO/ASTM DTR
ISO/TC 261
Additive manufacturing of metals —
Secretariat: DIN
Powder bed fusion (PBF) — In-situ
Voting begins on:
coaxial photodiode monitoring for
lack of fusion flaw detection in PBF-
Voting terminates on:
LB
Fabrication additive de métaux — Fusion sur lit de poudre —
Surveillance par photodiode coaxiale in situ pour la détection de
défauts de fusion en PBF-LB
RECIPIENTS OF THIS DRAFT ARE INVITED TO SUBMIT,
WITH THEIR COMMENTS, NOTIFICATION OF ANY
RELEVANT PATENT RIGHTS OF WHICH THEY ARE AWARE
© ISO/ASTM International 2026
AND TO PROVIDE SUPPOR TING DOCUMENTATION.
All rights reserved. Unless otherwise specified, or required in the context of its implementation, no part of this publication may
IN ADDITION TO THEIR EVALUATION AS
be reproduced or utilized otherwise in any form or by any means, electronic or mechanical, including photocopying, or posting on
BEING ACCEPTABLE FOR INDUSTRIAL, TECHNO­
ISO/CEN PARALLEL PROCESSING
LOGICAL, COMMERCIAL AND USER PURPOSES, DRAFT
the internet or an intranet, without prior written permission. Permission can be requested from either ISO at the address below
INTERNATIONAL STANDARDS MAY ON OCCASION HAVE
or ISO’s member body in the country of the requester. In the United States, such requests should be sent to ASTM International.
TO BE CONSIDERED IN THE LIGHT OF THEIR POTENTIAL
ISO copyright office ASTM International TO BECOME STAN DARDS TO WHICH REFERENCE MAY BE
MADE IN NATIONAL REGULATIONS.
CP 401 • Ch. de Blandonnet 8 100 Barr Harbor Drive, PO Box C700
CH-1214 Vernier, Geneva West Conshohocken, PA 19428-2959, USA
Phone: [phone] Phone: [phone]
Fax: [phone]
Email: [e-mail] Email: [e-mail]
Website: www.iso.org Website: www.astm.org
Published in Switzerland Reference number
ISO/ASTM DTR 52958:2026(en) © ISO/ASTM International 2026

© ISO/ASTM International 2026 – All rights reserved
ii
ISO/ASTM DTR 52958:2026(en)
Contents Page
Foreword .iv
1 Scope . 1
2 Normative references . 1
3 Terms and definitions . 1
4 Significance and use . 2
5 Design of coupons . 3
5.1 General .3
5.2 Intentionally seeded flaws .4
5.3 Randomized/stochastic flaws .6
6 Sensor description . 6
7 Flaw detection algorithms . 7
7.1 General .7
7.2 Statistical algorithms .8
7.2.1 General .8
7.2.2 Absolute limits (AL) .9
7.2.3 Short term fluctuations (STF) .10
7.2.4 Workflow .11
7.3 Machine-learning approach: clustering algorithm . 13
7.3.1 Self-organizing map (SOM) . 13
7.3.2 K-means .14
8 Implementation of customized algorithms to components with randomized flaws and
the associated voxelization thereof .15
9 Case study: procedural implementation and validation results .18
Bibliography .23

© ISO/ASTM International 2026 – All rights reserved
iii
ISO/ASTM DTR 52958:2026(en)
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards
bodies (ISO member bodies). The work of preparing International Standards is normally carried out through
ISO technical committees. Each member body interested in a subject for which a technical committee
has been established has the right to be represented on that committee. International organizations,
governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely
with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
The procedures used to develop this document and those intended for its further maintenance are described
in the ISO/IEC Directives, Part 1. In particular, the different approval criteria needed for the different types
of ISO documents should be noted. This document was drafted in accordance with the editorial rules of the
ISO/IEC Directives, Part 2 (see www.iso.org/directives).
ISO draws attention to the possibility that the implementation of this document may involve the use of (a)
patent(s). ISO takes no position concerning the evidence, validity or applicability of any claimed patent
rights in respect thereof. As of the date of publication of this document, ISO had not received notice of (a)
patent(s) which may be required to implement this document. However, implementers are cautioned that
this may not represent the latest information, which may be obtained from the patent database available at
www.iso.org/patents. ISO shall not be held responsible for identifying any or all such patent rights.
Any trade name used in this document is information given for the convenience of users and does not
constitute an endorsement.
For an explanation of the voluntary nature of standards, the meaning of ISO specific terms and expressions
related to conformity assessment, as well as information about ISO's adherence to the World Trade
Organization (WTO) principles in the Technical Barriers to Trade (TBT), see www.iso.org/iso/foreword.html.
This document was prepared by Technical Committee ISO/TC 261, Additive manufacturing, in cooperation
with ASTM Committee F42, Additive Manufacturing Technologies, on the basis of a partnership agreement
between ISO and ASTM International with the aim to create a common set of ISO/ASTM standards on
Additive Manufacturing, and in collaboration with the European Committee for Standardization (CEN)
Technical Committee CEN/TC 438, Additive manufacturing, in accordance with the Agreement on technical
cooperation between ISO and CEN (Vienna Agreement).
Any feedback or questions on this document should be directed to the user’s national standards body. A
complete listing of these bodies can be found at www.iso.org/members.html.

© ISO/ASTM International 2026 – All rights reserved
iv
FINAL DRAFT Technical Report ISO/ASTM DTR 52958:2026(en)
Additive manufacturing of metals — Powder bed fusion (PBF)
— In-situ coaxial photodiode monitoring for lack of fusion
flaw detection in PBF-LB
1 Scope
This document provides a workflow comprising experimental procedures and flaw detection algorithms
aimed at locating flaws in parts produced during the powder bed fusion-laser-based (PBF-LB) process of
metals. It emphasizes the use of coaxial photodiode-based in-situ monitoring and statistical and clustering
machine learning algorithms, particularly for detecting lack of fusion-induced flaws. The workflow
delineates setting thresholds for statistical detection and determining the number of clusters for machine
learning algorithms, utilizing intentional seeded flaws in parts. Validation procedures are provided through
computed tomography scanner data. Hardware limitations and considerations for multi-laser processes are
addressed, with attention to potential issues.
2 Normative references
The following documents are referred to in the text in such a way that some or all of their content constitutes
requirements of this document. For dated references, only the edition cited applies. For undated references,
the latest edition of the referenced document (including any amendments) applies.
ISO/ASTM 52900, Additive manufacturing — General principles — Fundamentals and vocabulary
3 Terms and definitions
For the purposes of this document, the terms and definitions given in ISO/ASTM 52900 and the following
apply:
ISO and IEC maintain terminology databases for use in standardization at the following addresses:
— ISO Online browsing platform: available at https://www.iso.org/obp
— IEC Electropedia: available at https://www.electropedia.org/
3.1
clustering algorithm
unsupervised machine learning methods with unlabelled input data is grouped by similarity
3.2
coaxial photodiode arrangement
type of sensor arrangement on the powder bed fusion-laser-based machine aligned with the laser beam path
3.3
computed tomography
CT
non-destructive examination technique capturing radiographic projections of an object at various rotational
angles followed by mathematically reconstruction to produce a three-dimensional volume data set or one or
more two-dimensional cross-sectional images

© ISO/ASTM International 2026 – All rights reserved
ISO/ASTM DTR 52958:2026(en)
3.4
data alignment
process of transforming different sets of geometrically or temporally related data into a single, global
coordinate system
3.5
data registration
procedure of data alignment and assignation of a persistent identification to the aligned data set
3.6
ex-situ analysis
measurement procedure performed after the completion of the build cycle
3.7
flaw indicator
indicator corresponding to the location of flaws predicted by the flaw detection algorithm
3.8
lack of fusion
type of process-induced porosity with not fully melted or fused powder particles onto the previously
deposited substrate.
[SOURCE: ASTM E3166-20, 3.4.7]
3.9
reference datum feature
notch, groove, or similar feature added to the geometry in a seeded flaw coupon to ease data alignment and
registration of porosity locations for CT-scan ex-situ analysis
3.10
intentionally seeded flaw
act of intentionally creating flaws through computer-aided design or manipulation of designated processing
parameters, resulting in the placement of the anticipated flaw or the act of intentionally creating a flaw
through the insertion of an artificial object
4 Significance and use
A workflow for indirect flaw detection and analysis documentation during PBF-LB is provided by using
the signals received from a coaxial photodiode that can detect flaws, including lack of fusion, in fabricated
components.
These flaws may have detrimental effects on the mechanical performance of fabricated parts. The workflow
of this document provides a procedure to identify the range of upper and lower thresholds required for the
statistical detection algorithms to effectively identify stochastic lack of fusion defects induced during the
process. It provides a procedure to identify the number of clusters required for machine learning detection
algorithms. In the validation procedure, the datasets collected from a CT scanner that are registered and
voxelized can be used. It is noted that the size of detectable flaw, as determined by the procedure outlined in
this document, is contingent upon the resolution and frequency of the hardware employed, specifically a co-
axial photodiode and its associated data acquisition card. For instance, when utilizing a commonly available
photodiode with a frequency of 60 kHz, the procedure and algorithms specified by this document are unable
to detect flaws smaller than 100 μm.
In general, an in situ photodiode installed coaxially provides information from the process signature and
flaws. However, the recorded in situ data needs to be corrected to remove chromatic and monochromatic
distortion. The corrected data analyse by two main algorithms to identify flaws:
a) statistically, and
b) by machine learning.
© ISO/ASTM International 2026 – All rights reserved
ISO/ASTM DTR 52958:2026(en)
These algorithms can be systematically optimized and customized to detect lack of fusion flaws. To this
end, intentionally seeded flaws are first added to the computer-aided design (CAD) of coupons to tune
the parameters of the algorithms. Then, the customized algorithm is tested by detecting randomized/
stochastic flaws created by powder bed fusion-laser based with intentionally decreased energy density.
The comparison of detection results could be analysed by algorithms with the CT data applied through a
volumetric approach to identify the randomized/stochastic flaws. A flowchart illustrating the progression
in this document is shown in Figure 1.
Figure 1 — Schematic for calibration flow needed for detecting the lack of fusion flaw
5 Design of coupons
5.1 General
To customize and calibrate the detection algorithms systematically, two sets of coupons are suggested.
Reference datum features can also be added to the geometry to ease data alignment and data registration
of porosity locations in the ex situ analysis that is CT-scan in this practice. Figure 2 represents some
suggestions for registry notches/grooves.

© ISO/ASTM International 2026 – All rights reserved
ISO/ASTM DTR 52958:2026(en)
a) Added vertical and horizontal registry grooves b) Added inclined notches
Figure 2 — Addition of registry grooves and inclined notches to the geometry of the coupon
5.2 Intentionally seeded flaws
The effect of the lack of fusion flaw can be mimicked by embedding intentional seeds/voids in the coupons.
[1]
According to ISO/ASTM TR 52906 , for creating these seeds, various sizes, distributions, and geometries of
seeds can be added to the computer-aided design. Two forms of spherical and cylindrical intentional seeded
flaws can be considered where the size of spherical flaws is identified by their diameter and the size of
cylindrical flaws is identified by their cross-sectional diameter and height. Note that the minimum size of
the intentional flaw is dictated by the powder bed fusion-laser based machine restrictions. It is, however,
recommended that the feature size of flaws is set in the computer-aided design model to three different
classes:
The minimum size possible to be made by the powder bed fusion-laser based machine (for example 100 µm
for the diameter of spheres and 100 µm for height and diameter of cylinders) depending on the resolution
and laser spot size:
a) the minimum value plus 50 μm (for example 150 µm for the above-mentioned parameters);
b) the minimum value plus 100 µm (for example 200 µm for the above-mentioned parameters).
Note that within the layers in which the intentional flaws are made, an optimum down-skin parameter is
used to endure the mechanical integrity of the intentional flaw. The capping layer, however, can have no
down-skin setting.
Two examples of intentionally seeded flaws are shown in Figure 3. Figure 3 a) and b) represent two
dimensional cross sections of samples showing the distribution of the intentionally seeded flaws (cylindrical
and spherical), respectively. In Figure 3 a), six nominally identical sets of three sizes of cylindrical flaws (Ø,
H = 200 µm, Ø, H = 150 µm, and Ø, H = 100 µm are shown; in Figure 3 b), six nominally identical sets of three
sizes of spherical flaws (Ø = 200 µm, Ø = 150 µm, and Ø = 100 µm) where Ø is the diameter and H is the
height, in microns, are demonstrated; in Figure 3 c), the capping layer of spherical flaws are represented.

© ISO/ASTM International 2026 – All rights reserved
ISO/ASTM DTR 52958:2026(en)
a) Cylindrical type b) Spherical type
c) Schematic of spherical flaws showing the capping layer
Key
A sets (clustered intentional voids)
B capping layer
NOTE 1 All dimensions are in SI coordinate system.
NOTE 2 Figures 3 a) and 3 b) are published under an open access CC by 4.0 license.
Figure 3 — Two dimensional cross sections of samples showing the distribution of different types of
intentionally seeded flaws
© ISO/ASTM International 2026 – All rights reserved
ISO/ASTM DTR 52958:2026(en)
5.3 Randomized/stochastic flaws
Randomized/stochastic flaws can be achieved normally because of process anomalies or by altering process
parameters in which the lack of fusion flaws are created by decreasing the energy density during the
fabrication. For creating randomized lack of fusion flaws, four scenarios are recommended:
a) reducing the laser power;
b) increasing the hatching distance;
c) increasing the scanning speed;
d) increasing the layer thickness.
These alterations depend on the material. It is, however, recommended that the produced parts with altered
process parameters exhibit a relative density reduction of around 0,5 % compared to parts fabricated with
nominal process parameters.
6 Sensor description
The sensor embodied in this document is a coaxial photodiode arrangement with a sampling frequency
of equal or more than 60 kHz. The coaxial photodiode arrangement is aligned with the laser beam path
through a beam splitter (see Figure 4).
NOTE 1 Photodiodes can capture light intensity signals from the melt pool in different wavelengths; however, the
preferred wavelength range for most metallic alloys to capture melt pool light intensity is normally in the visible and
near-infrared ranges (between 750 nm to 900 nm).
In addition to the light intensity data, laser modulation and XY scanner position are recorded and stored in
the associated personal computer. Intensity and geometry calibrations of dataset are also required.
NOTE 2 Details of the data calibration routines are out of the scope of this practice.
NOTE 3 The intensity correction for the coaxial data can be implemented because of the chromatic aberration
phenomenon. It is initiated because the wavelength of light intensity recorded by the photodiode is not the same as the
wavelength optimized for the scanner mirror and f-theta lens or dynamic focusing units.
NOTE 4 The intensity and geometry corrections are dependent on the commercial system and are normally
implemented by the original equipment manufacturer’s monitoring system.

© ISO/ASTM International 2026 – All rights reserved
ISO/ASTM DTR 52958:2026(en)
Key
1 laser
2 scanner mirror
3 F-Thena lense
4 roller
5 powder
6 build plate
7 beam splitter
8 inside the optical path
9 co-axial sensor
Figure 4 — Position of the coaxial sensor in the PBF-LB setup
7 Flaw detection algorithms
7.1 General
Two different approaches are recommended for detecting flaws: statistical algorithms and clustering
machine learning-clustering algorithms.
The statistical algorithm works based on the threshold method, and the clustering algorithm distributes
data into different groups. The workflow to detect the flaws was demonstrated in Figure 1 and is the
following:
Step 1: The preferred algorithm can be applied to the data collected during the printing of the samples with
intentionally seeded flaws.
© ISO/ASTM International 2026 – All rights reserved
ISO/ASTM DTR 52958:2026(en)
Step 2: The detection result is compared with the design and CT scan data to customize/calibrate the
algorithm parameters such as moving average windows length and thresholds.
NOTE The setting of CT scan can normally be optimized in terms of resolution.
Step 3: The customized algorithm stemmed from Step 2 can be used for the detection of randomized flaws
in the fabricated samples.
Step 4: The detection results of Step 3 are validated by CT scan through the volumetric approach and
confusion matrix which is explained in Clause 9.
As an example, several statistical and machine-learning algorithms that are suitable for this practice are
discussed in 7.2 and 7.3. Additionally, the volumetric approach is used to compare the result with CT, which
is discussed in Clause 9.
7.2 Statistical algorithms
7.2.1 General
Statistical algorithms work based on the selection of threshold levels, and their central feature is the moving
[2]
average. Thus, it is critical to have an optimized workflow to identify a threshold range and the window
size/length of the moving average by end users. In Figure 5, the application of
...