ASTM A941-01
(Terminology)Standard Terminology Relating to Steel, Stainless Steel, Related Alloys, and Ferroalloys
Standard Terminology Relating to Steel, Stainless Steel, Related Alloys, and Ferroalloys
SCOPE
1.1 This standard is a compilation of definitions of terms related to steel, stainless steel, related alloys, and ferroalloys.
1.2 When a term is used in an ASTM document for which Committee A01 is responsible, it is included herein only when judged, after review by Subcommittee A01.92, to be a generally usable term.
1.3 Some definitions include a discussion section, which is a mandatory part of the definition and contains additional information that is relevant to the meaning of the defined term.
1.4 Definitions of terms specific to a particular standard will appear in that standard and will supersede any definitions of identical terms in this standard.
General Information
Relations
Standards Content (Sample)
NOTICE: This standard has either been superceded and replaced by a new version or discontinued.
Contact ASTM International (www.astm.org) for the latest information.
Designation: A 941 – 01
Terminology Relating to
1
Steel, Stainless Steel, Related Alloys, and Ferroalloys
This standard is issued under the fixed designation A 941; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (e) indicates an editorial change since the last revision or reapproval.
1. Scope * manganese, but does not prescribe a minimum limit for
chromium, cobalt, columbium (niobium), molybdenum,
1.1 This standard is a compilation of definitions of terms
nickel, tungsten (wolfram), vanadium, or zirconium.
related to steel, stainless steel, related alloys, and ferroalloys.
1.2 When a term is used in an ASTM document for which
DISCUSSION—Except as required above, it is permissible for carbon
Committee A01 is responsible, it is included herein only when steel specifications to prescribe limits (minimum or maximum, or both)
for each specified alloying element, subject to the following restrictions
judged, after review by Subcommittee A01.92, to be a gener-
for the heat analysis limits in mass percent:
ally usable term.
(a) for wrought carbon steel products, the specified maximum limit is
1.3 Some definitions include a discussion section, which is
not to exceed: 0.10 for aluminum, 0.60 for silicon, and 0.050 for
a mandatory part of the definition and contains additional
titanium;
information that is relevant to the meaning of the defined term.
(b) for carbon steel castings, the specified maximum limit is not to
1.4 Definitions of terms specific to a particular standard will
exceed: 0.10 for aluminum, 1.00 for silicon, and 0.050 for titanium.
appear in that standard and will supersede any definitions of (c) for carbon steels that are required to be rephosphorized, the
specified minimum limit for phosphorus is not to be less than 0.040;
identical terms in this standard.
(d) for carbon steels that are required to be resulfurized, the specified
minimum limit for sulfur is not to be less than 0.060;
2. Referenced Documents
(e) for carbon steels that are not required to be rephosphorized or
2.1 ASTM Standards:
resulfurized, the specified maximum limit is not to exceed: 0.60 for
2
E 112 Test Methods for Determining Average Grain Size
copper, 0.050 for phosphorus, and 0.060 for sulfur; and
(f) for carbon steels that are required to contain boron, copper, or lead,
3. Terminology
the specified minimum limit is not to exceed: 0.0005 for boron, 0.35 for
copper, and 0.25 for lead.
3.1 Definitions of General Terms:
cast analysis—Deprecated term. Use the preferred term heat
alloy steel, n—a steel, other than a stainless steel, that
analysis.
conforms to a specification that requires one or more of the
certificate of compliance, n—in manufactured products,a
following elements, by mass percent, to have a minimum
document that states that the product was manufactured,
content equal to or greater than: 0.30 for aluminum; 0.0008
sampled, tested, and inspected in accordance with the
for boron; 0.30 for chromium; 0.30 for cobalt; 0.06 for
requirements of the specification (including year of issue)
columbium (niobium); 0.40 for copper; 0.40 for lead; 1.65
and any other requirements specified in the purchase order or
for manganese; 0.08 for molybdenum; 0.30 for nickel; 0.60
contract, and has been found to meet such requirements.
for silicon; 0.05 for titanium; 0.30 for tungsten (wolfram);
0.10 for vanadium; 0.05 for zirconium; or 0.10 for any other
DISCUSSION—A single document, containing test report information
alloying element, except sulphur, phosphorus, carbon, and
and certificate of compliance information, may be used.
nitrogen.
certifying organization, n—in product specifications, the
capped steel, n—a rimmed steel in which, during ingot
entity responsible for the conformance and certification of
solidification, the rimming action was limited by mechanical
the product to the specification requirements.
or chemical means.
coarse grain practice, n—a steelmaking practice for other
carbon steel, n—a steel that conforms to a specification that
than stainless steel that is intended to produce a killed steel
prescribes a maximum limit, by heat analysis in mass
in which aluminum, columbium (niobium), titanium, and
percent, of not more than: 2.00 for carbon and 1.65 for
vanadium are residual elements.
cold working, n—mechanical deformation of a metal at
1
temperatures below its recrystallization temperature.
This terminology is under the jurisdiction of ASTM Committee A01 on Steel,
Stainless Steel, and Related Alloys and is the direct responsibility of Subcommittee
defect, n—an imperfection of sufficient magnitude to warrant
A01.92 on Terminology.
rejection based on the specified requirements.
Current edition approved S
...