Founding - Malleable cast irons

This European Standard defines grades and the corresponding requirements for malleable cast irons.
This European standard specifies five grades of whiteheart malleable cast iron and nine grades of blackheart malleable cast iron, based on mechanical properties measured on cast samples (which are test pieces).
This European Standard specifies Brinell hardness values determined only when these values are requested by the purchaser.
This European Standard does not cover technical delivery conditions for malleable cast iron castings. Reference should be made to EN 1559-1 [3] and EN 1559-3 [4].
This European Standard does not cover chemical composition, except phosphorous (see Clause 6).

Gießereiwesen - Temperguss

Diese Europäische Norm legt die Sorten für und die zugehörigen Anforderungen an Temperguss fest.
Diese Europäische Norm legt, basierend auf den an Probestücken (die Proben sind) gemessenen mechanischen Eigenschaften, fünf Sorten von entkohlend geglühtem Temperguss und neun Sorten von nichtentkohlend geglühtem Temperguss fest.
Diese Europäische Norm legt Werte für die Brinellhärte fest, die nur bestimmt werden, wenn diese Werte vom Käufer verlangt werden.
Diese Europäische Norm enthält nicht die Technischen Lieferbedingungen für Temperguss. Es sollte auf EN 1559-1 [3] und EN 1559-3 [4] Bezug genommen werden.
Diese Europäische Norm enthält keine Angaben über die chemische Zusammensetzung mit Ausnahme von Phosphor (siehe Abschnitt 6).
Die Temperguss-Sorte EN-GJMB-300-6 (5.4100) darf für keinerlei Druckgeräteanwendungen verwendet werden, auch nicht für z. B. Druckgeräteanwendungen, die nicht unter die Druckgeräte-Richtlinie 2014/68/EU fallen.

Fonderie - Fontes malléables

La présente Norme européenne définit les nuances et les exigences correspondantes relatives aux fontes
malléables.
La présente Norme européenne spécifie cinq nuances de fonte malléable à coeur blanc et neuf nuances de fonte
malléable à coeur noir, en se basant sur leurs propriétés mécaniques mesurées sur des échantillons coulés (qui
sont les éprouvettes).
La présente Norme européenne spécifie les valeurs de dureté Brinell, déterminées uniquement lorsqu'elles sont
demandées par l'acheteur.
La présente Norme européenne ne couvre pas les conditions techniques de fourniture de pièces moulées en fonte
malléable. Il convient de se référer à l’EN 1559-1 [3] et l’EN 1559-3 [4].
La présente Norme européenne ne couvre pas les exigences en matière de composition chimique, sauf pour le
phosphore (voir l’Article 6).
La nuance de fonte malléable EN-GJMB-300-6 (5.4100) ne doit être utilisée pour aucune application sous pression,
c’est-à-dire aussi les applications sous pression non couvertes par la Directive Equipements sous Pression
2014/68/EC.

Livarstvo - Temprana litina

Ta evropski standard določa razrede in ustrezne zahteve za temprano litino.
Ta evropski standard določa pet razredov bele temprane litine in devet razredov črne temprane litine na podlagi mehanskih lastnosti, izmerjenih na litih vzorcih (ki so preskusni kosi).
Ta evropski standard določa vrednosti trdote po Brinellu, ki se izmerijo le, kadar te vrednosti zahteva kupec.
Ta evropski standard ne zajema tehničnih dobavnih pogojev za odlitke iz tempranih litin. Sklicevati se je treba na standarda EN 1559-1 [3] in EN 1559-3 [4].
Ta evropski standard ne zajema kemijske sestave, razen fosforjeve (glej točko 6).

General Information

Status
Published
Public Enquiry End Date
31-May-2018
Publication Date
01-Apr-2019
Technical Committee
Current Stage
6060 - National Implementation/Publication (Adopted Project)
Start Date
28-Mar-2019
Due Date
02-Jun-2019
Completion Date
02-Apr-2019

Relations

Buy Standard

Standard
EN 1562:2019
English language
21 pages
sale 10% off
Preview
sale 10% off
Preview
e-Library read for
1 day

Standards Content (Sample)

2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.Livarstvo - Temprana litinaGießereiwesen - TempergussFonderie - Fontes malléablesFounding - Malleable cast irons77.140.80Železni in jekleni ulitkiIron and steel castingsICS:Ta slovenski standard je istoveten z:EN 1562:2019SIST EN 1562:2019en,fr,de01-maj-2019SIST EN 1562:2019SLOVENSKI
STANDARDSIST EN 1562:20121DGRPHãþD



SIST EN 1562:2019



EUROPEAN STANDARD NORME EUROPÉENNE EUROPÄISCHE NORM
EN 1562
March
t r s { ICS
y yä r z rä s r Supersedes EN
s w x tã t r s tEnglish Version
Founding æ Malleable cast irons Fonderie æ Fontes mallßables
Gießereiwesen æ Temperguss This European Standard was approved by CEN on
s x February
t r s {ä
egulations which stipulate the conditions for giving this European Standard the status of a national standard without any alterationä Upætoædate lists and bibliographical references concerning such national standards may be obtained on application to the CENæCENELEC Management Centre or to any CEN memberä
translation under the responsibility of a CEN member into its own language and notified to the CENæCENELEC Management Centre has the same status as the official versionsä
CEN members are the national standards bodies of Austriaá Belgiumá Bulgariaá Croatiaá Cyprusá Czech Republicá Denmarká Estoniaá Finlandá Former Yugoslav Republic of Macedoniaá Franceá Germanyá Greeceá Hungaryá Icelandá Irelandá Italyá Latviaá Lithuaniaá Luxembourgá Maltaá Netherlandsá Norwayá Polandá Portugalá Romaniaá Serbiaá Slovakiaá Sloveniaá Spainá Swedená Switzerlandá Turkey and United Kingdomä
EUROPEAN COMMITTEE FOR STANDARDIZATION COMITÉ EUROPÉEN DE NORMALISATION EUROPÄISCHES KOMITEE FÜR NORMUNG
CEN-CENELEC Management Centre:
Rue de la Science 23,
B-1040 Brussels
9
t r s { CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Membersä Refä Noä EN
s w x tã t r s { ESIST EN 1562:2019



EN 1562:2019 (E) 2 Contents Page European foreword . 3 Introduction . 4 1 Scope . 5 2 Normative references . 5 3 Terms and definitions . 5 4 Designation. 6 5 Order information . 6 6 Manufacture . 7 7 Requirements . 7 7.1 General . 7 7.2 Tensile strength and elongation . 7 7.3 0,2 % Proof strength . 7 7.4 Brinell hardness . 7 7.5 Impact energy . 7 8 Samples . 11 8.1 General . 11 8.2 Cast samples . 11 8.2.1 Size of test pieces . 11 8.2.2 Frequency and number of tests . 12 8.2.3 Separately cast samples . 13 8.2.4 Side-by-side cast samples. 13 9 Test methods . 13 9.1 Tensile test . 13 9.2 0,2 % proof strength . 13 9.3 Brinell hardness . 13 9.4 Impact test . 13 10 Retests . 14 10.1 Need for retests . 14 10.2 Test validity . 14 10.3 Non-conforming test results . 15 10.4 Heat treatment of samples and castings . 15 11 Inspection documentation . 15 Annex A (informative)
Comparison of malleable cast iron material designations according EN 1560 and ISO/TR 15931 [1], [6] . 16 Annex B (informative)
Un-notched impact test . 17 Annex C (informative)
Significant technical changes between this European standard and the previous edition . 19 Annex ZA (informative)
Relationship between this European Standard and the Essential Requirements of Directive 2014/68/EU aimed to be covered . 20 Bibliography . 21
SIST EN 1562:2019



EN 1562:2019 (E) 3 European foreword This document (EN 1562:2019) has been prepared by Technical Committee CEN/TC 190 “Foundry technology”, the secretariat of which is held by DIN. This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by September 2019 and conflicting national standards shall be withdrawn at the latest by September 2019. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN shall not be held responsible for identifying any or all such patent rights. This document supersedes EN 1562:2012. Within its programme of work, Technical Committee CEN/TC 190 requested CEN/TC 190/WG 6 “Malleable cast iron” to revise EN 1562:2012. This document has been prepared under a standardization request given to CEN by the European Commission and the European Free Trade Association, and supports essential requirements of EU Directive(s). For relationship with EU Directive(s), see informative Annex ZA, which is an integral part of this document. Annex C provides details of significant technical changes between this European Standard and the previous edition. According to the CEN-CENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Serbia, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and the United Kingdom. SIST EN 1562:2019



EN 1562:2019 (E) 4 Introduction This document classifies malleable cast irons into two groups. The first group is concerned with decarburized irons referred to as whiteheart malleable cast iron. The second group is non-decarburized irons referred to as blackheart malleable cast iron. Both groups, except completely decarburized whiteheart malleable cast iron, contain free carbon as graphite, called temper carbon. Both groups have grades with structures that can range from ferrite to pearlite and/or other transformation products of austenite. Materials are designated in terms of tensile strength and percentage elongation. Weldablility is an important property of malleable cast irons. Malleable cast irons have good impact resistance and ductility at low temperatures. In this document, a designation system by number, as established in EN 1560 [1], is given. NOTE This designation system by number is based on the principles and the structure as set out in EN 10027–2 [2] and so corresponds with the European numbering system for steel and other materials. Some malleable cast iron grades can be used for pressure equipment. The permitted material grades of malleable cast iron for pressure applications and the conditions for their use are given in specific product or application standards. For the design of pressure equipment, specific design rules apply. Annex ZA gives information relating to the conformance of permitted malleable cast iron grades to the Pressure Equipment Directive 2014/68/EU. SIST EN 1562:2019



EN 1562:2019 (E) 5 1 Scope This document defines grades and the corresponding requirements for malleable cast irons. This document specifies five grades of whiteheart malleable cast iron and nine grades of blackheart malleable cast iron, based on mechanical properties measured on cast samples (which are test pieces). This document specifies Brinell hardness values determined only when these values are requested by the purchaser. This document does not cover technical delivery conditions for malleable cast iron castings. Reference can be made to EN 1559-1 [3] and EN 1559-3 [4]. This document does not cover chemical composition, except phosphorus (see Clause 6). 2 Normative references The following documents are referred to in the text in such a way that some or all of their content constitutes requirements of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. EN 764-5:2014, Pressure equipment — Part 5: Inspection documentation of metallic materials and compliance with the material specification EN 10204:2004, Metallic products — Types of inspection documents EN ISO 148-1:2016, Metallic materials — Charpy pendulum impact test — Part 1: Test method (ISO 148-1:2016) EN ISO 6506-1:2014, Metallic materials — Brinell hardness test — Part 1: Test method (ISO 6506-1:2014) EN ISO 6892-1:2016, Metallic materials —Tensile testing — Part 1: Method of test at room temperature (ISO 6892-1:2016) 3 Terms and definitions For the purposes of this document, the following terms and definitions apply. ISO and IEC maintain terminological databases for use in standardization at the following addresses: — IEC Electropedia: available at http://www.electropedia.org/ — ISO Online browsing platform: available at http://www.iso.org/obp 3.1 malleable cast iron cast material, mainly iron and carbon based, which solidifies in the as-cast condition with a graphite-free (white) structure and achieves its final properties after a heat treatment 3.2 whiteheart malleable cast iron cast material, mainly iron and carbon based, which is cast white and then given a heat treatment in a decarburizing atmosphere to produce a material which is partially or entirely decarburized Note 1 to entry: Any remaining graphite is in the form of temper carbon. SIST EN 1562:2019



EN 1562:2019 (E) 6 3.3 blackheart malleable cast iron cast material, mainly iron and carbon based, which is cast white and then given a non-decarburizing heat treatment, to produce a material in which all graphite is in the form of temper carbon 3.4 primary graphite graphite which precipitates in the flake form during solidification Note 1 to entry: Primary graphite is more correctly referred to as eutectic graphite. 3.5 cast sample quantity of material cast to represent the cast material, including separately cast sample and side-by-side cast sample 3.6 separately cast sample sample cast in a separate sand mould under representative manufacturing conditions and material grade 3.7 side-by-side cast sample sample cast in the mould alongside the casting, with a joint running system 3.8 relevant wall thickness wall thickness representative of the casting, defined for the determination of the size of the cast samples to which the mechanical properties apply 4 Designation The material shall be designated either by a symbol or by a number as given in Tables 1, 2 and 3. NOTE Comparison of EN 1562 grade designations to the grades from ISO 5922:2005 [5] is given in Annex A. 5 Order information The following information shall be supplied by the purchaser: a) the number of this European Standard; b) the designation of the material; c) the relevant wall thickness of the casting; d) any special requirements. All requirements shall be agreed between the manufacturer and the purchaser by the time of acceptance of the order, e.g. technical delivery conditions according to EN 1559-1 [3] and EN 1559-3 [4]. SIST EN 1562:2019



EN 1562:2019 (E) 7 6 Manufacture The method of manufacture of malleable cast iron as well as its chemical composition and heat treatment shall be left to the discretion of the manufacturer, who shall ensure compliance with the property requirements given in this document for the material ordered. NOTE To produce structures such as ferrite, pearlite or other transformation products of austenite, both material types (groups) depend upon either the malleablising heat treatment or the subsequent additional heat treatment and/or additions of alloying elements. For castings intended to be given additional treatment (such as galvanizing) and/or in the case of castings for use at low temperatures to optimize the impact resistance of the material, the phosphorus content should not exceed 0,10 %. For malleable cast iron materials to be used in special applications, the chemical composition and any special heat treatment may be the subject of an agreement between the manufacturer and the purchaser by the time of acceptance of the order. 7 Requirements 7.1 General The property values apply to malleable cast irons cast in sand moulds or moulds of comparable thermal behaviour. Subject to amendments to be agreed upon in the order, they can apply to castings obtained by alternative methods, when agreed between the manufacturer and purchaser at the time of acceptance of the order. The material designation is based on the minimum mechanical properties obtained in cast samples with a diameter of 12 mm. Mechanical properties are wall thickness dependent as shown in Tables 1, 2 and 3. 7.2 Tensile strength and elongation The tensile strength and elongation shall be tested in accordance with 9.1, the values of tensile strength and percentage elongation after fracture (hereafter referred to as elongation) shall be in accordance with the requirements specified in Tables 1, 2 and 3. 7.3 0,2 % Proof strength When requested by the purchaser and agreed at the time of acceptance of the order, 0,2 % proof strength shall be determined in accordance with 9.2 and the values shall be in accordance with the requirements specified in Tables 1, 2 and 3. 7.4 Brinell hardness Brinell hardness and its range values shall only be specified when agreed between the manufacturer and the purchaser at the time of acceptance of the order. Guidance values for Brinell hardness are listed in Tables 1, 2 and 3. The method of testing and sampling shall be agreed in accordance with the method specified in 9.3. 7.5 Impact energy Impact energy testing is normally requested for EN-GJMB-350-10 only. The method of testing shall be in accordance with 9.4. If the purchaser requires impact testing to be performed on other grades of malleable cast irons, then the Charpy un-notched test should be used (see informative Annex B). SIST EN 1562:2019



EN 1562:2019 (E) 8 For the malleable cast iron grades intended for uses covered by pressure equipment European legislation, the impact energy shall be determined in accordance with 9.4. The minimum values of the impact energy for the six pressure equipment permitted grades, measured on V-notched test pieces machined from cast samples, are given in the Table 3 at room temperature. Table 1 — Mechanical properties of whiteheart malleable cast irons without specified minimum impact energy Material designation Relevant wall thickness Nominal diameter of test piece Tensile strength Elongation 0,2 % proof strength Brinell hardness (for information only) t d Rm A3,4 Rp0,2 mm mm MPa % MPa HBW Symbol Number
min. min. min. max. EN-GJMW-350–4 5.4200
230 t
3 6 270 10 — a 3 < t
5 9 310 5 — 5 < t
7 12 350 4 — t > 7 15 360 3 —
EN-GJMW-550–4 5.4204
250 t
3 6 — — — a 3 < t
5 9 490 5 310 5 < t
7 12 550 4 340 t > 7 15 570 3 350
NOTE The figures given in bold indicate the minimum tens
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.