ISO 2115:1976

Plastics — Aqueous dispersions of polymers and copolymers — Determination of white point temperature and minimum film-forming temperature

Matières plastiques — Dispersions aqueuses de polymères et copolymères — Détermination de la température de point blanc et de la température minimale de formation de film

General Information

• Status: Withdrawn
• Publication Date: 31-May-1976
• Withdrawal Date: 31-May-1976
• ICS: 83.080 - Plastics
• Technical Committee: ISO/TC 61 - Plastics
• Drafting Committee: ISO/TC 61 - Plastics
• Current Stage: 9599 - Withdrawal of International Standard
• Completion Date: 07-Feb-1996

Relations

• Revised: SIST ISO 2115:1996 - Plastics -- Polymer dispersions -- Determination of white point temperature and minimum film-forming temperature
• Effective Date: 12-May-2008
• Revised: ISO 2115:1996 - Plastics — Polymer dispersions — Determination of white point temperature and minimum film-forming temperature
• Effective Date: 15-Apr-2008

Standards Content (Sample)

INTERNATIONAL STANDARD 211 5
~
INTERNATIONAL ORGANIZATION FOR STANDARDIZATION .MEXilYHAPORHAR OPrAHHlAUHR no CTAHnAFTH3AUHH *ORGANISATION INTERNATIONALE DE NORMALISATION
t
Plastics - Aqueous dispersions of polymers and copolymers -
Determination of white point temperature and minimum
f ilm-forming temperature
Matières plastiques - Dispersions aqueuses de polymères et copolymères - Détermination de la température
de point blanc et de la température minimale de formation de film
Second edition - 1976-06-01
-
Lu
-
UDC 678.518 : 542.636 Ref. No. IS0 2115-1976 (E)
i PI
te
Descriptors : plastics, polymers, copolymers, aqueous dispersions, tests, measurement, temperature, white point temperature.
Ln
r
c
LN
Price based on 4 pages

---------------------- Page: 1 ----------------------
FOREWORD
IS0 (the International Organization for Standardization) is a worldwide federation
of national standards institutes (IS0 Member Bodies). The work of developing
International Standards is carried out through IS0 Technical Committees. Every
Member Body interested in a subject for which a Technical Committee has been set
up has the right to be represented on that Committee. International organizations,
governmental and non-governmental, in liaison with ISO, also take part in the work.
Draft International Standards adopted by the Technical Committees are circulated
to the Member Bodies for approval before their acceptance as International
Standards by the IS0 Council.
International Standard IS0 2115 was drawn up by Technical Committee
ISO/TC 61, Plastics. This second edition was submitted directly to the IS0 Council,
in accordance with clause 6.12.1 of the Directives for the technical work of ISO.
This edition cancels and replaces the first edition (IS0 2215-1974), which
had been approved by the Member Bodies of the following countries :
Australia Hungary Romania
India South Africa, Rep. of
Austria
Belgium Israel
Spain
Canada Italy Sweden
Czechoslovakia Japan Switzerland
Egypt, Arab Rep. of Netherlands Turkey
France New Zealand United Kingdom
Germany Poland U.S.A.
Greece Portugal U.S.S.R.
No Member Body had expressed disapproval of the document.
O International Organization for Standardization, 1976
Printed in Switzerland

---------------------- Page: 2 ----------------------
INTERNATIONAL STANDARD IS0 2115-1976 (E)
Plastics - Aqueous dispersions of polymers and copolymers -
Determination of white point temperature and minimum
f ilm-form ing temperature
1 SCOPE AND FIELD OF APPLICATION 4 APPARATUS
i This International Standard specifies a method for the
4.1 Test apparatus (see figure 1 as an example) consisting
determination of the ”white point” temperature of aqueous
essentially of a rectangular plate, of aluminium, stainless
dispersions of polymers and copolymers, and the minimum
steel or copper, whose surface may either be perfectly level
film-forming temperature.
and polished, or may contain channels (5)’) - four for
L
example - 0.3 mm deep.2)
2 DEFINITION
At one end of the plate is a rheostat-controlled electrical
When an aqueous dispersion of polymers and copolymers is
resistance (2), which constitutes the hot source. At the
spread out on a support, the water evaporates and the
opposite end is the cold source, consisting either of an
polymer particles interact to form
insulated (7) container (3) in which refrigerant is placed or
of a coil inserted into the end of the plate and through
- either an opaque white mass if the temperature
which a refrigerant mixture is circulated.
conditions are unfavourable,
Evenly spaced along the plate are holes (4) into which
- or a continuous transparent film if the temperature
thermometers can be inserted to measure the temperature
conditions are favourable.
gradient of the plate when equilibrium is reached. The first
hole (IO) is positioned at the cold end of the plate at right
2.1 “white point” temperature : The limiting temperature
angles to the beginning of the channels, if the plate has
below which an opaque mass, and above which a
them.
transparent film, is formed.
Provision should be made for placing a glass cover (6) above
L
the plate, leaving a space through which can be directed a
2.2 minimum film-forming temperature : The limiting
slight current of dry air (dried, for example, by passing
temperature above which a continuous homogeneous film
through a column packed with calcium chloride) at room
without cracks is formed.
temperature, from the cold end to the hot end.
3 PRINCIPLE
Application of a suitable temperature gradient between a
4.2 Devices for temperature measurement, having an
hot source and a cold source on a metal plate (aluminium,
accura
...

NORME INTERNATIONALE 211 5
INTERNATIONAL ORGANIZATION FOR STANDARDIZATION *MEY;IYHAPOLIHAR OPiAHMlAUMR nO CTAHllAPTM3AUMM .ORGANISATION INTERNATIONALE DE NORMALISATION
Matières plastiques - Dispersions aqueuses de polymères et
copolymères - Détermination de la température de point
blanc et de la température minimale de formation de film
Plastics - Aqueous dispersions of polymers and copolymers - Determination of white point temperature and
minimum film- forming temperature
Deuxième édit ion - 1976 -06 -01
~
CDU 678.518 : 542.636 Réf. no : IS0 2115-1976 (FI
Dascripteurs : matière plastique. polymère, copolymere, dispersion aqueuse, essai, mesurage. température, température de point blanc.
Prix base sur 4 pages

---------------------- Page: 1 ----------------------
AVANT-PROPOS
L'ISO (Organisation Internationale de Normalisation) est une fédération mondiale
d'organismes nationaux de normalisation (Comités Membres ISO). L'élaboration des
Normes Internationales est confiée aux Comités Techniques ISO. Chaque Comité
Membre intéressé par une étude a le droit de faire partie du Comité Technique
correspondant. Les organisations internationales, gouvernementales et non
gouvernementales, en liaison avec 1'60, participent également aux travaux.
Les Projets de Normes Internationales adoptés par les Comités Techniques sont
soumis aux Comités Membres pour approbation, avant leur acceptation comme
Normes Internationales par le Conseil de I'ISO.
La Norme Internationale IS0 2115 a été établie par le Comité Technique
lSO/TC 61, Matièresp/astiques. Cette deuxième édition fut soumise directement au
Conseil de I'ISO, conformément au paragraphe 6.12.1 des Directives pour les tra-
vaux techniques de I'ISO.
La présente édition annule et remplace la première édition (IS0 2215-1974),
qui avait été approuvée par les Comités Membres des pays suivants :
Afrique du Sud, Rép. d' Grèce Portugal
Allemagne Hongrie Roumanie
Royaume-Uni
Australie Inde
Autriche Israël Suède
Belgique Italie Suisse
Canada Japon Tchécoslovaquie
Égypte, Rép. arabe d' Nouvelle-Zélande Turquie
Espagne Pays-Bas U.R.S.S.
France Pologne U.S.A.
Aucun Comité Membre n'avait désapprouvé le document.
O Organisation Internationale de Normalisation, 1976 0
Imprimé en Suisse

---------------------- Page: 2 ----------------------
NORME INTERNATIONALE IS0 2115-1976 (F)
Matières plastiques - Dispersions aqueuses de polymères et
copolymères - Détermination de la température de point
blanc et de la température minimale de formation de film
1 OBJET ET DOMAINE D'APPLICATION 4 APPAREILLAGE
La présente Norme Internationale spécifie une méthode de 4.1 Appareil d'essai (voir la figure 1 donnée à titre
détermination de la température de ((point blanc)) (PB) des d'exemple) constitué par une plaque rectangulaire en
dispersions aqueuses de polymères et copolymères, et de la aluminium, acier inoxydable ou cuivre, qui peut être soit
température minimale de formation de film. parfaitement plane et polie, soit comporter des
cannelures (5)' ) quatre par exemple - ayant 0,3 mm de
profondeur.2 )
2 DÉFINITIONS
À l'une des extrémités de la plaque se trouve une résistance
Lorsqu'une dispersion aqueuse de polymères ou de
électrique (2), réglable à l'aide d'un rhéostat et qui
copolymères est étalée sur un support, l'eau s'évapore et les
constitue la source chaude. Du côté opposé se trouve la
particules de polymères se collent les unes aux autres,
source froide constituée soit par un recipient (3)
formant :
calorifugé (7), soit par un serpentin à l'intérieur même de la
plaque, dans lequel se trouve (recipient) ou circule
- soit une masse opaque blanche si les conditions de
(serpentin) un mélange réfrigérant.
température ne sont pas favorables,
Régulièrement espacées le long de la plaque se trouvent des
- soit un film continu transparent si les conditions de
alvéoles (4) permettant de placer des appareils pour mesurer
température le permettent.
la température de la plaque lorsque le gradient de
température est réalisé. Le premier de ces logements (IO)
2.1 température de ((point blanc)) : Température limite
est placé à l'extrémité de la plaque, côté source froide, l'axe
au-dessous de laquelle la masse reste opaque et au-dessus de
étant situé au début des cannelures si la plaque en
laquelle se forme un film transparent.
comporte.
II doit être possible de disposer une plaque en verre (6)
2.2 température minimale de formation de film :
au-dessus de la plaque en laissant, au-dessus de celle-ci, un
Température limite au-dessus de laquelle se forme un film
intervalle qui sera balayé par un léger courant d'air sec
continu, homogène et sans craquelure.
(séché par passage sur une colonne remplie de chlorure de
calcium, par exemple) à la température ambiante, se
propageant de l'extrémité froide vers l'extrémité chaude.
3 PRINCIPE
Réalisation d'un gradient de température convenable, entre
une source chaude et une source froide dans une plaque
4.2 Appareils de mesurage de la température, précis à
métallique (aluminium, acier inoxydable ou cuivre) soit
0,l "C dans la plage comprise entre - 10 et 4- 50 OC, tels
et
...