A04.01 - Grey and White Iron Castings

ABSTRACT
This guide covers standard specification for three classes of gray iron for castings intended for use as valve pressure retaining parts, pipe fittings, and flanges. Chemical analysis shall be performed in each lot and shall conform to the required chemical composition for phosphorous and sulfur. Tension test shall be conducted on each class of gray iron castings and shall conform to the specified values of tensile strength. Tension test specimens shall have threaded ends and shall conform to the prescribed dimensions.
SCOPE
1.1 This specification covers three classes of gray iron for castings intended for use as valve pressure-retaining parts, pipe fittings, and flanges.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.
Note 1: The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers gray iron castings that are statically cast in permanent molds. Castings under this specification are classified into a number of grades (A-SA, A-SB, A-SC, A-SS, A-CA, A-CB, A-CC, N-SA, N-SB, N-SC,N-SS, N-CA, N-CB and N-CC) based on the properties of separately cast test bars. The grades are designated A for annealed or N for normalized; followed by an S or a C to designate a solid or a cored casting; followed by an A, B, C, or S to designate the test bar to be poured with the castings. The cast test bar shall be selected on the basis of the controlling section size of the casting and shall have the specified dimensions (diameter and length). Castings may be produced in the as cast state provided the tensile strength and Brinell hardness requirements are met. The chemical composition and heat treatment shall be such as to produce these mechanical requirements as well. A suitable permanent mold design for separately cast test bars is described and the tension test requirements are detailed.
SCOPE
1.1 This specification covers gray iron castings that are statically cast in permanent molds.  
1.2 No precise quantitative relationship can be stated between the properties of the iron in various locations of the same casting or between the properties of a casting and those of a test specimen cast from the same iron (see Appendix X1).  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification deals with abrasion-resistant cast irons used for mining, milling, earth-handling, and manufacturing industries. These alloys may be made by melting process and shall have microstructures that consist of carbides, martensite, bainite, austenite, and in exceptional cases, minor amounts of graphite or pearlite. The following conditions for casting will be supplied: as-cast, as-cast and stress relieved, hardened, hardened and stress relieved, or softened for machining. Heat treatment shall be done. The chemical composition of a class and type (that is, Class I, Type A) shall conform to the range of values specified for carbon, manganese, silicon, nickel, chromium, molybdenum, copper, phosphorus, and sulfur. Hardness test shall also be made.
SCOPE
1.1 This specification covers a group of white cast irons that have been alloyed to secure high resistance to abrasive wear in the applications of the mining, milling, earth-handling, and manufacturing industries.  
1.2 Simple and low-alloy white cast irons that consist essentially of iron carbides and pearlite are specifically excluded from this specification.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers centrifugally cast cylinders with an outer layer of white cast iron and the remainder of the material of gray cast iron. These castings are suitable for pressure containing parts of the design strength of which is based on the gray iron portion of the cylinder. The white iron portion of the cylinder shall be made to a minimum hardness and the casting process shall be controlled to produce a metallurgical bond between the two metal layers. All surfaces shall be machined prior to the cylinders being placed into service. The tensile strength of the cast irons shall be measured by tension testing while the thickness of the white cast iron shall be determined by ultrasonic testing.
SCOPE
1.1 This specification2 covers centrifugally cast cylinders with an outer layer of white cast iron and the remainder of the material of gray cast iron. These castings are suitable for pressure-containing parts, the design strength of which is based on the gray iron portion of the cylinder. These castings are suitable for service at temperatures up to 450 °F [230 °C].  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 The following safety hazards caveat pertains only to the test method portion, Section 8, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers double pour, centrifugally cast, abrasion-resistant roll shells for general application. The outer layer is white iron and the inner layer is gray iron and there shall be no gradient of mottled iron these layers. Both the white and the gray irons may be melted by any suitable melting process. The white iron portion of the casting shall be produced by chemistry rather than chilling. A chemical analysis of the white and gray irons shall be taken and the chemical compositions shall be controlled to obtain the required mechanical properties. The white iron (Types I, II, III, and IV) shall conform to the specified Brinell hardness and the gray iron (Class Nos. 20, 25, 30, and 35) shall conform to the specified tensile strength. The minimum thickness of the white iron layer is given. Hardness and tension tests of the cast dual metal shall be performed.
SCOPE
1.1 This specification covers double pour, centrifugally cast, abrasion-resistant roll shells for general application. The outer layer is white iron and the inner layer is gray iron. There shall be no gradient of mottled iron between the white iron and the gray iron.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.2.1 Within the text, the SI units are shown in brackets.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers standards for high-silicon iron castings of Grades 1, 2, and 3 intended for severe environment corrosion-resistant services. The alloy shall be produced by any melting and casting process, or combination of processes that will be capable of meeting the specified contents of carbon, manganese, silicon, chromium, molybdenum, and copper. Reference analysis methods are given for each chemical component. Transverse bend test and hydrostatic test shall be performed. Material shall conform to minimum load at center and minimum deflection at center requirements.
SCOPE
1.1 This specification covers high-silicon cast iron castings intended for corrosion-resistant service.  
1.2 This specification covers three grades as shown in Table 1. Selection of grade depends on the corrosive service to be experienced by the casting. All three grades are suited for application in severe corrosive environments. However, Grade 2 is particularly suited for application in strong chloride environments, and Grade 3 is recommended for impressed current anodes.    
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.4 The following safety hazards caveat pertains only to the test method portion, Section 9, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers statically cast dual metal rolls with the outer layer of the roll body being chilled white iron of different chemical composition than the core and journals of the roll which is gray cast iron. The castings are suitable for pressure containing parts such as pressure vessels, the design strength of which is based on the gray iron portion of the cylinder, and for service at the specified temperatures. The melting procedure shall be optional with the foundry and the casting process shall be controlled to produce a metallurgical bond between the chilled white iron exterior and gray iron interior. The chilled white iron exterior shall be made to the specified minimum hardness and the gray iron portion of the roll shall conform to the applicable class as determined by design requirements. The roll shall conform to the tensile strength requirement to be determined by tensile test and shall meet the required thickness. All surfaces shall be machined or ground, or both, prior to the rolls being placed into service.
SCOPE
1.1 This specification covers statically cast dual metal rolls with the outer layer of the roll body being chilled white iron of different chemical composition than the core and journals of the roll which is gray cast iron. The castings are suitable for pressure-containing parts, the design strength of which is based on the gray iron portion of the cylinder. The castings are suitable for service at temperatures up to 450 °F [232 °C].  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 The following safety hazards statement pertains only to the test method portion, Section 9, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers gray iron castings intended for general engineering use where tensile strength is a major consideration. Castings are classified on the basis of the tensile strength of the iron in separately cast test bars. The surface of the casting shall be free of adhering sand, scale, cracks, and hot tears, as determined by visual examination. The test bars are designated into S, A, B, and C categories, according to the thickness of its controlling wall section. The casting shall be subjected to a tension test to determine its tensile strength.
SCOPE
1.1 This specification covers gray iron castings intended for general engineering use where tensile strength is a major consideration. Castings are classified on the basis of the tensile strength of the iron in separately cast test bars.  
1.1.1 This specification subordinates chemical composition to tensile strength.  
1.2 Castings produced to this specification are graded on the basis of minimum tensile strength obtained in special test coupons designed to standardize cooling rate. The tensile strength developed in certain casting sections may vary from test coupon values (see X1.2).  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers gray iron for castings suitable for pressure-containing parts at elevated temperatures. Castings shall be stress-relieved by placing them in a suitable furnace and heating them uniformly to the temperatures and for the times specified. Castings to be used at a particular temperature range shall undergo heat treatment and cooling. Chemical analysis shall be performed on each class of castings and shall meet the maximum requirement for carbon, phosphorus and sulfur. Iron used in supplying castings shall conform to the required tensile strength. Separately cast test bars having the required dimensions shall be poured from the same lot as the castings represented. The test bars shall be cast in dried siliceous sand molds maintained at approximately room temperature. Tension test shall be performed on each lot and materials shall conform to the tensile requirements specified.
SCOPE
1.1 This specification2 covers gray iron for castings suitable for pressure-containing parts for use at temperatures up to 650 °F (350 °C).  
1.2 Classes of Iron:  
1.2.1 Castings of all classes are suitable for use up to 450 °F (230 °C). For temperatures above 450 °F and up to 650 °F, only Class 40, 45, 50, 55, and 60 castings are suitable.  
1.2.2 Castings of all classes are suitable for use up to 230 °C. For temperatures above 230 °C and up to 350 °C, only Class 275, 300, 325, 350, 380, and 415 castings are suitable.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers gray iron castings for products of the automobile, truck, tractor and allied industries. The materials shall be classified into eight grades (G1800, G2500, G3000, G3500, G4000, G2500a, G3500b and G3500c) based on the range of their casting hardness, chemical composition and microstructure. Grades G1800 and G2500 shall be annealed. Alloy gray iron automotive camshafts of grade designation G4000d shall conform to the required values of casting hardness, chemical compositions of chromium, molybdenum, and nickel and microstructure. The cam areas of camshaft casting shall undergo selective hardening by flame or induction hardening and shall conform to the required values of depth and surface hardness.
SCOPE
1.1 This specification applies to gray iron castings, cast in sand molds, used in the products of the automobile, truck, tractor, and allied industries.  
1.2 The values stated in inch-pound units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers the standard common requirements for iron castings to be used for general industrial applications. The castings shall be made in a workman-like manner and shall conform to the dimensions on drawings furnished by the purchaser before manufacture is started. A lot shall consist of one of the following: all the metal from a single heating in a batch-type melting furnace; all the metal poured from two or more batch-type melting furnaces into a single ladle or a single casting; or all the metal poured from a continuous melting furnace for a given period of time between changes in charge, processing conditions, or aim-for chemistry, whichever is the shorter period. Specimens shall undergo tension tests and shall conform to the specified tensile strength requirements. Chemical analysis such as spectrographic methods shall be performed to determine the chemical composition which shall be in accordance to the carbon content requirement of the specimen. Visual inspection shall also be done to ensure that the casting surface is free of adhering sand, scale, cracks, and hot tears.
SCOPE
1.1 This specification covers a group of requirements that are mandatory requirements when used in conjunction with the following iron casting specifications issued by ASTM:    
ASTM Specification2  
A47/A47M  
A48/A48M  
A197/A197M  
A220/A220M  
A278/A278M  
A319  
A395/A395M  
A436  
A439/A439M  
A518/A518M  
A532/A532M  
A536  
A571/A571M  
A823  
A842  
A874/A874M  
A897/A897M  
1.2 This specification also covers a group of supplementary requirements which may be applied to the above specifications as indicated herein. These are provided for use when additional testing or inspection is desired and apply only when specified individually by the purchaser in the order.  
1.3 The requirements of the individual material specification, and this general specification, shall prevail in the sequence named.  
1.4 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers austenitic gray iron castings that are used primarily for their resistance to heat, corrosion, and wear. The types of castings covered here are: Type 1, Type 1b, Type 2, Type 2b, Type 3, Type 4, Type 5, and Type 6. The materials shall be manufactured by melting in any furnace that produces castings which includes cupolas, air furnaces, electric furnaces, crucible furnaces, and so forth. Heat and product analyses shall be performed wherein specimens shall conform to required chemical composition of carbon, silicon, manganese, nickel, copper, chromium, sulfur, and molybdenum. The materials shall undergo a nonmagnetic test which is based on the material's attraction to a small steel horseshoe-type magnet and a magnetic permeability test in the event that nonmagnetic castings are specified. Tension tests shall be performed wherein specimens shall conform to required tensile strength and Brinell hardness.
SCOPE
1.1 This specification covers austenitic gray iron castings that are used primarily for their resistance to heat, corrosion, and wear. Austenitic gray iron is characterized by uniformly distributed graphite flakes, some carbides, and the presence of sufficient alloy content to produce an austenitic structure.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers gray iron castings exposed to elevated temperatures for non-pressure containing parts such as grate bars, stoker links, stoker parts, oil still furnace parts, firebox parts, ingot molds, glass molds, caustic pots, and metal melting pots. The three classes of gray iron covered here are: Class I, possessing superior thermal shock resistance; Class II, possessing average thermal shock resistance and moderately good tensile strength; and Class III, possessing a higher tensile strength than either Classes I or II. It is the intention of this specification to classify the irons in accordance with their carbon content equivalent, wherein the equation for its calculation is given herein.
SCOPE
1.1 This specification covers three classes of gray iron suitable for castings exposed to temperatures encountered in such service as grate bars, stoker links, stoker parts, oil still furnace parts, firebox parts, ingot molds, glass molds, caustic pots, and metal melting pots.  
Note 1: This specification is general, covering cast irons normally used for the above types of service, at temperatures as high as 1400 °F (760 °C). It is not intended to imply that all three classes are suitable throughout this entire temperature range without regard to actual service stresses. Some are suitable for long service at the lower temperatures only, unless low stresses are involved.  
1.2 The three classes of gray iron covered by this specification are as follows:  
1.2.1 Class I,  possessing superior resistance to thermal shock,  
1.2.2 Class II,  possessing average resistance to thermal shock and a moderately good tensile strength (tensile strengths above 30 000 psi (207 MPa) may be expected), and  
1.2.3 Class III,  possessing a higher tensile strength than either Class I or II (tensile strengths as high as 40 000 psi (276 MPa) may be expected).  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers gray iron castings intended for general engineering use where tensile strength is a major consideration. Castings are classified on the basis of the tensile strength of the iron in separately cast test bars. The surface of the casting shall be free of adhering sand, scale, cracks, and hot tears, as determined by visual examination. The test bars are designated into S, A, B, and C categories, according to the thickness of its controlling wall section. The casting shall be subjected to a tension test to determine its tensile strength.
SCOPE
1.1 This specification covers gray iron castings intended for general engineering use where tensile strength is a major consideration. Castings are classified on the basis of the tensile strength of the iron in separately cast test bars.  
1.1.1 This specification subordinates chemical composition to tensile strength.  
1.2 Castings produced to this specification are graded on the basis of minimum tensile strength obtained in special test coupons designed to standardize cooling rate. The tensile strength developed in certain casting sections may vary from test coupon values (see X1.2).  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification deals with abrasion-resistant cast irons used for mining, milling, earth-handling, and manufacturing industries. These alloys may be made by melting process and shall have microstructures that consist of carbides, martensite, bainite, austenite, and in exceptional cases, minor amounts of graphite or pearlite. The following conditions for casting will be supplied: as-cast, as-cast and stress relieved, hardened, hardened and stress relieved, or softened for machining. Heat treatment shall be done. The chemical composition of a class and type (that is, Class I, Type A) shall conform to the range of values specified for carbon, manganese, silicon, nickel, chromium, molybdenum, copper, phosphorus, and sulfur. Hardness test shall also be made.
SCOPE
1.1 This specification covers a group of white cast irons that have been alloyed to secure high resistance to abrasive wear in the applications of the mining, milling, earth-handling, and manufacturing industries.  
1.2 Simple and low-alloy white cast irons that consist essentially of iron carbides and pearlite are specifically excluded from this specification.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers gray iron castings that are statically cast in permanent molds. Castings under this specification are classified into a number of grades (A-SA, A-SB, A-SC, A-SS, A-CA, A-CB, A-CC, N-SA, N-SB, N-SC,N-SS, N-CA, N-CB and N-CC) based on the properties of separately cast test bars. The grades are designated A for annealed or N for normalized; followed by an S or a C to designate a solid or a cored casting; followed by an A, B, C, or S to designate the test bar to be poured with the castings. The cast test bar shall be selected on the basis of the controlling section size of the casting and shall have the specified dimensions (diameter and length). Castings may be produced in the as cast state provided the tensile strength and Brinell hardness requirements are met. The chemical composition and heat treatment shall be such as to produce these mechanical requirements as well. A suitable permanent mold design for separately cast test bars is described and the tension test requirements are detailed.
SCOPE
1.1 This specification covers gray iron castings that are statically cast in permanent molds.  
1.2 No precise quantitative relationship can be stated between the properties of the iron in various locations of the same casting or between the properties of a casting and those of a test specimen cast from the same iron (see Appendix X1).  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This guide covers standard specification for three classes of gray iron for castings intended for use as valve pressure retaining parts, pipe fittings, and flanges. Chemical analysis shall be performed in each lot and shall conform to the required chemical composition for phosphorous and sulfur. Tension test shall be conducted on each class of gray iron castings and shall conform to the specified values of tensile strength. Tension test specimens shall have threaded ends and shall conform to the prescribed dimensions.
SCOPE
1.1 This specification covers three classes of gray iron for castings intended for use as valve pressure-retaining parts, pipe fittings, and flanges.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.
Note 1: The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers standards for high-silicon iron castings of Grades 1, 2, and 3 intended for severe environment corrosion-resistant services. The alloy shall be produced by any melting and casting process, or combination of processes that will be capable of meeting the specified contents of carbon, manganese, silicon, chromium, molybdenum, and copper. Reference analysis methods are given for each chemical component. Transverse bend test and hydrostatic test shall be performed. Material shall conform to minimum load at center and minimum deflection at center requirements.
SCOPE
1.1 This specification covers high-silicon cast iron castings intended for corrosion-resistant service.  
1.2 This specification covers three grades as shown in Table 1. Selection of grade depends on the corrosive service to be experienced by the casting. All three grades are suited for application in severe corrosive environments. However, Grade 2 is particularly suited for application in strong chloride environments, and Grade 3 is recommended for impressed current anodes.    
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.4 The following safety hazards caveat pertains only to the test method portion, Section 9, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers double pour, centrifugally cast, abrasion-resistant roll shells for general application. The outer layer is white iron and the inner layer is gray iron and there shall be no gradient of mottled iron these layers. Both the white and the gray irons may be melted by any suitable melting process. The white iron portion of the casting shall be produced by chemistry rather than chilling. A chemical analysis of the white and gray irons shall be taken and the chemical compositions shall be controlled to obtain the required mechanical properties. The white iron (Types I, II, III, and IV) shall conform to the specified Brinell hardness and the gray iron (Class Nos. 20, 25, 30, and 35) shall conform to the specified tensile strength. The minimum thickness of the white iron layer is given. Hardness and tension tests of the cast dual metal shall be performed.
SCOPE
1.1 This specification covers double pour, centrifugally cast, abrasion-resistant roll shells for general application. The outer layer is white iron and the inner layer is gray iron. There shall be no gradient of mottled iron between the white iron and the gray iron.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.2.1 Within the text, the SI units are shown in brackets.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers statically cast dual metal rolls with the outer layer of the roll body being chilled white iron of different chemical composition than the core and journals of the roll which is gray cast iron. The castings are suitable for pressure containing parts such as pressure vessels, the design strength of which is based on the gray iron portion of the cylinder, and for service at the specified temperatures. The melting procedure shall be optional with the foundry and the casting process shall be controlled to produce a metallurgical bond between the chilled white iron exterior and gray iron interior. The chilled white iron exterior shall be made to the specified minimum hardness and the gray iron portion of the roll shall conform to the applicable class as determined by design requirements. The roll shall conform to the tensile strength requirement to be determined by tensile test and shall meet the required thickness. All surfaces shall be machined or ground, or both, prior to the rolls being placed into service.
SCOPE
1.1 This specification covers statically cast dual metal rolls with the outer layer of the roll body being chilled white iron of different chemical composition than the core and journals of the roll which is gray cast iron. The castings are suitable for pressure-containing parts, the design strength of which is based on the gray iron portion of the cylinder. The castings are suitable for service at temperatures up to 450 °F [232 °C].  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 The following safety hazards statement pertains only to the test method portion, Section 9, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers centrifugally cast cylinders with an outer layer of white cast iron and the remainder of the material of gray cast iron. These castings are suitable for pressure containing parts of the design strength of which is based on the gray iron portion of the cylinder. The white iron portion of the cylinder shall be made to a minimum hardness and the casting process shall be controlled to produce a metallurgical bond between the two metal layers. All surfaces shall be machined prior to the cylinders being placed into service. The tensile strength of the cast irons shall be measured by tension testing while the thickness of the white cast iron shall be determined by ultrasonic testing.
SCOPE
1.1 This specification2 covers centrifugally cast cylinders with an outer layer of white cast iron and the remainder of the material of gray cast iron. These castings are suitable for pressure-containing parts, the design strength of which is based on the gray iron portion of the cylinder. These castings are suitable for service at temperatures up to 450 °F [230 °C].  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 The following safety hazards caveat pertains only to the test method portion, Section 8, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers gray iron castings intended for general engineering use where tensile strength is a major consideration. Castings are classified on the basis of the tensile strength of the iron in separately cast test bars. The surface of the casting shall be free of adhering sand, scale, cracks, and hot tears, as determined by visual examination. The test bars are designated into S, A, B, and C categories, according to the thickness of its controlling wall section. The casting shall be subjected to a tension test to determine its tensile strength.
SCOPE
1.1 This specification covers gray iron castings intended for general engineering use where tensile strength is a major consideration. Castings are classified on the basis of the tensile strength of the iron in separately cast test bars.  
1.1.1 This specification subordinates chemical composition to tensile strength.  
1.2 Castings produced to this specification are graded on the basis of minimum tensile strength obtained in special test coupons designed to standardize cooling rate. The tensile strength developed in certain casting sections may vary from test coupon values (see X1.2).  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.

ABSTRACT
This specification covers gray iron castings exposed to elevated temperatures for non-pressure containing parts such as grate bars, stoker links, stoker parts, oil still furnace parts, firebox parts, ingot molds, glass molds, caustic pots, and metal melting pots. The three classes of gray iron covered here are: Class I, possessing superior thermal shock resistance; Class II, possessing average thermal shock resistance and moderately good tensile strength; and Class III, possessing a higher tensile strength than either Classes I or II. It is the intention of this specification to classify the irons in accordance with their carbon content equivalent, wherein the equation for its calculation is given herein.
SCOPE
1.1 This specification covers three classes of gray iron suitable for castings exposed to temperatures encountered in such service as grate bars, stoker links, stoker parts, oil still furnace parts, firebox parts, ingot molds, glass molds, caustic pots, and metal melting pots.  
Note 1: This specification is general, covering cast irons normally used for the above types of service, at temperatures as high as 1400°F (760°C). It is not intended to imply that all three classes are suitable throughout this entire temperature range without regard to actual service stresses. Some are suitable for long service at the lower temperatures only, unless low stresses are involved.  
1.2 The three classes of gray iron covered by this specification are as follows:  
1.2.1 Class I,  possessing superior resistance to thermal shock,  
1.2.2 Class II,  possessing average resistance to thermal shock and a moderately good tensile strength (tensile strengths above 30 000 psi (207 MPa) may be expected), and  
1.2.3 Class III,  possessing a higher tensile strength than either Classes I or II (tensile strengths as high as 40 000 psi (276 MPa) may be expected).  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

ABSTRACT
This specification covers austenitic gray iron castings that are used primarily for their resistance to heat, corrosion, and wear. The types of castings covered here are: Type 1, Type 1b, Type 2, Type 2b, Type 3, Type 4, Type 5, and Type 6. The materials shall be manufactured by melting in any furnace that produces castings which includes cupolas, air furnaces, electric furnaces, crucible furnaces, and so forth. Heat and product analyses shall be performed wherein specimens shall conform to required chemical composition of carbon, silicon, manganese, nickel, copper, chromium, sulfur, and molybdenum. The materials shall undergo a nonmagnetic test which is based on the material's attraction to a small steel horseshoe-type magnet and a magnetic permeability test in the event that nonmagnetic castings are specified. Tension tests shall be performed wherein specimens shall conform to required tensile strength and Brinell hardness.
SCOPE
1.1 This specification covers austenitic gray iron castings that are used primarily for their resistance to heat, corrosion, and wear. Austenitic gray iron is characterized by uniformly distributed graphite flakes, some carbides, and the presence of sufficient alloy content to produce an austenitic structure.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

ABSTRACT
This specification covers gray iron for castings suitable for pressure-containing parts at elevated temperatures. Castings shall be stress-relieved by placing them in a suitable furnace and heating them uniformly to the temperatures and for the times specified. Castings to be used at a particular temperature range shall undergo heat treatment and cooling. Chemical analysis shall be performed on each class of castings and shall meet the maximum requirement for carbon, phosphorus and sulfur. Iron used in supplying castings shall conform to the required tensile strength. Separately cast test bars having the required dimensions shall be poured from the same lot as the castings represented. The test bars shall be cast in dried siliceous sand molds maintained at approximately room temperature. Tension test shall be performed on each lot and materials shall conform to the tensile requirements specified.
SCOPE
1.1 This specification2 covers gray iron for castings suitable for pressure-containing parts for use at temperatures up to 650°F (350°C).  
1.2 Classes of Iron:  
1.2.1 Castings of all classes are suitable for use up to 450°F (230°C). For temperatures above 450°F and up to 650°F, only Class 40, 45, 50, 55, and 60 castings are suitable.  
1.2.2 Castings of all classes are suitable for use up to 230°C. For temperatures above 230°C and up to 350°C, only Class 275, 300, 325, 350, 380, and 415 castings are suitable.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.

ABSTRACT
This specification covers gray iron castings for products of the automobile, truck, tractor and allied industries. The materials shall be classified into eight grades (G1800, G2500, G3000, G3500, G4000, G2500a, G3500b and G3500c) based on the range of their casting hardness, chemical composition and microstructure. Grades G1800 and G2500 shall be annealed. Alloy gray iron automotive camshafts of grade designation G4000d shall conform to the required values of casting hardness, chemical compositions of chromium, molybdenum, and nickel and microstructure. The cam areas of camshaft casting shall undergo selective hardening by flame or induction hardening and shall conform to the required values of depth and surface hardness.
SCOPE
1.1 This specification applies to gray iron castings, cast in sand molds, used in the products of the automobile, truck, tractor, and allied industries.  
1.2 The values stated in inch-pound units are to be regarded as standard. No other units of measurement are included in this standard.

ABSTRACT
This specification covers the standard common requirements for iron castings to be used for general industrial applications. The castings shall be made in a workman-like manner and shall conform to the dimensions on drawings furnished by the purchaser before manufacture is started. A lot shall consist of one of the following: all the metal from a single heating in a batch-type melting furnace; all the metal poured from two or more batch-type melting furnaces into a single ladle or a single casting; or all the metal poured from a continuous melting furnace for a given period of time between changes in charge, processing conditions, or aim-for chemistry, whichever is the shorter period. Specimens shall undergo tension tests and shall conform to the specified tensile strength requirements. Chemical analysis such as spectrographic methods shall be performed to determine the chemical composition which shall be in accordance to the carbon content requirement of the specimen. Visual inspection shall also be done to ensure that the casting surface is free of adhering sand, scale, cracks, and hot tears.
SCOPE
1.1 This specification covers a group of requirements that are mandatory requirements when used in conjunction with the following iron casting specifications issued by ASTM:    
ASTM Specification2    
A47/A47M  
A48/A48M  
A197/A197M  
A220/A220M  
A278/A278M  
A319  
A395/A395M  
A436  
A439  
A518/A518M  
A532/A532M  
A536  
A571/A571M  
A823  
A842  
A874/A874M  
A897/A897M  
1.2 This specification also covers a group of supplementary requirements which may be applied to the above specifications as indicated herein. These are provided for use when additional testing or inspection is desired and apply only when specified individually by the purchaser in the order.  
1.3 The requirements of the individual material specification, and this general specification shall prevail in the sequence named.  
1.4 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

ABSTRACT
This specification deals with abrasion-resistant cast irons used for mining, milling, earth-handling, and manufacturing industries. These alloys may be made by melting process and shall have microstructures that consist of carbides, martensite, bainite, austenite, and in exceptional cases, minor amounts of graphite or pearlite. The following conditions for casting will be supplied: as-cast, as-cast and stress relieved, hardened, hardened and stress relieved, or softened for machining. Heat treatment shall be done. The chemical composition of a class and type (that is, Class I, Type A) shall conform to the range of values specified for carbon, manganese, silicon, nickel, chromium, molybdenum, copper, phosphorus, and sulfur. Hardness test shall also be made.
SCOPE
1.1 This specification covers a group of white cast irons that have been alloyed to secure high resistance to abrasive wear in the applications of the mining, milling, earth-handling, and manufacturing industries.  
1.2 Simple and low-alloy white cast irons that consist essentially of iron carbides and pearlite are specifically excluded from this specification.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.

ABSTRACT
This guide covers standard specification for three classes of gray iron for castings intended for use as valve pressure retaining parts, pipe fittings, and flanges. Chemical analysis shall be performed in each lot and shall conform to the required chemical composition for phosphorous and sulfur. Tension test shall be conducted on each class of gray iron castings and shall conform to the specified values of tensile strength. Tension test specimens shall have threaded ends and shall conform to the prescribed dimensions.
SCOPE
1.1 This specification covers three classes of gray iron for castings intended for use as valve pressure retaining parts, pipe fittings, and flanges.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.Note 1—The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.

ABSTRACT
This specification covers double pour, centrifugally cast, abrasion-resistant roll shells for general application. The outer layer is white iron and the inner layer is gray iron and there shall be no gradient of mottled iron these layers. Both the white and the gray irons may be melted by any suitable melting process. The white iron portion of the casting shall be produced by chemistry rather than chilling. A chemical analysis of the white and gray irons shall be taken and the chemical compositions shall be controlled to obtain the required mechanical properties. The white iron (Types I, II, III, and IV) shall conform to the specified Brinell hardness and the gray iron (Class Nos. 20, 25, 30, and 35) shall conform to the specified tensile strength. The minimum thickness of the white iron layer is given. Hardness and tension tests of the cast dual metal shall be performed.
SCOPE
1.1 This specification covers double pour, centrifugally cast, abrasion-resistant roll shells for general application. The outer layer is white iron and the inner layer is gray iron. There shall be no gradient of mottled iron between the white iron and the gray iron.  
1.2 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with this specification.

ABSTRACT
This specification covers statically cast dual metal rolls with the outer layer of the roll body being chilled white iron of different chemical composition than the core and journals of the roll which is gray cast iron. The castings are suitable for pressure containing parts such as pressure vessels, the design strength of which is based on the gray iron portion of the cylinder, and for service at the specified temperatures. The melting procedure shall be optional with the foundry and the casting process shall be controlled to produce a metallurgical bond between the chilled white iron exterior and gray iron interior. The chilled white iron exterior shall be made to the specified minimum hardness and the gray iron portion of the roll shall conform to the applicable class as determined by design requirements. The roll shall conform to the tensile strength requirement to be determined by tensile test and shall meet the required thickness. All surfaces shall be machined or ground, or both, prior to the rolls being placed into service.
SCOPE
1.1 This specification covers statically cast dual metal rolls with the outer layer of the roll body being chilled white iron of different chemical composition than the core and journals of the roll which is gray cast iron. The castings are suitable for pressure containing parts, the design strength of which is based on the gray iron portion of the cylinder. The castings are suitable for service at temperatures up to 450°F [232°C].  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.3 The following safety hazards statement pertains only to the test method portion, 9, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SCOPE
1.1 This specification covers double pour, centrifugally cast, abrasion-resistant roll shells for general application. The outer layer is white iron and the inner layer is gray iron. There shall be no gradient of mottled iron between the white iron and the gray iron.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.2.1 Within the text, the SI units are shown in brackets.

ABSTRACT
This specification covers standards for high-silicon iron castings of Grades 1, 2, and 3 intended for severe environment corrosion-resistant services. The alloy shall be produced by any melting and casting process, or combination of processes that will be capable of meeting the specified contents of carbon, manganese, silicon, chromium, molybdenum, and copper. Reference analysis methods are given for each chemical component. Transverse bend test and hydrostatic test shall be performed. Material shall conform to minimum load at center and minimum deflection at center requirements.
SCOPE
1.1 This specification covers high-silicon cast iron castings intended for corrosion-resistant service.  
1.2 This specification covers three grades as shown in Table 1. Selection of grade depends on the corrosive service to be experienced by the casting. All three grades are suited for application in severe corrosive environments. However, Grade 2 is particularly suited for application in strong chloride environments, and Grade 3 is recommended for impressed current anodes. TABLE 1 Chemical Composition    
Element
Composition, Weight %
Grade 1
Grade 2
Grade 3
Carbon  
0.65–1.10  
0.75–1.15  
0.70–1.10  
Manganese  
1.50, max  
1.50, max  
1.50, max  
Silicon  
14.20–14.75  
14.20–14.75  
14.20–14.75  
Chromium  
0.50, max  
3.25–5.00  
3.25–5.00  
Molybdenum  
0.50, max  
0.40–0.60  
0.20, max  
Copper  
0.50, max  
0.50, max  
0.50, max  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.4 The following safety hazards caveat pertains only to the test method portion, Section 9, of this specification:  This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ABSTRACT
This specification covers gray iron castings intended for general engineering use where tensile strength is a major consideration. Castings are classified on the basis of the tensile strength of the iron in separately cast test bars. The surface of the casting shall be free of adhering sand, scale, cracks, and hot tears, as determined by visual examination. The test bars are designated into S, A, B, and C categories, according to the thickness of its controlling wall section. The casting shall be subjected to a tension test to determine its tensile strength.
SCOPE
1.1 This specification covers gray iron castings intended for general engineering use where tensile strength is a major consideration. Castings are classified on the basis of the tensile strength of the iron in separately cast test bars.  
1.1.1 This specification subordinates chemical composition to tensile strength.  
1.2 Castings produced to this specification are graded on the basis of minimum tensile strength obtained in special test coupons designed to standardize cooling rate. The tensile strength developed in certain casting sections may vary from test coupon values (see X1.2).  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.

ABSTRACT
This specification covers centrifugally cast cylinders with an outer layer of white cast iron and the remainder of the material of gray cast iron. These castings are suitable for pressure containing parts of the design strength of which is based on the gray iron portion of the cylinder. The white iron portion of the cylinder shall be made to a minimum hardness and the casting process shall be controlled to produce a metallurgical bond between the two metal layers. All surfaces shall be machined prior to the cylinders being placed into service. The tensile strength of the cast irons shall be measured by tension testing while the thickness of the white cast iron shall be determined by ultrasonic testing.
SCOPE
1.1 This specification2 covers centrifugally cast cylinders with an outer layer of white cast iron and the remainder of the material of gray cast iron. These castings are suitable for pressure containing parts the design strength of which is based on the gray iron portion of the cylinder. These castings are suitable for service at temperatures up to 450°F [230°C].  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.3 The following safety hazards caveat pertains only to the test method portion, Section 8, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ABSTRACT
This specification covers gray iron castings that are statically cast in permanent molds. Castings under this specification are classified into a number of grades (A-SA, A-SB, A-SC, A-SS, A-CA, A-CB, A-CC, N-SA, N-SB, N-SC,N-SS, N-CA, N-CB and N-CC) based on the properties of separately cast test bars. The grades are designated A for annealed or N for normalized; followed by an S or a C to designate a solid or a cored casting; followed by an A, B, C, or S to designate the test bar to be poured with the castings. The cast test bar shall be selected on the basis of the controlling section size of the casting and shall have the specified dimensions (diameter and length). Castings may be produced in the as cast state provided the tensile strength and Brinell hardness requirements are met. The chemical composition and heat treatment shall be such as to produce these mechanical requirements as well. A suitable permanent mold design for separately cast test bars is described and the tension test requirements are detailed.
SCOPE
1.1 This specification covers gray iron castings that are statically cast in permanent molds.  
1.2 No precise quantitative relationship can be stated between the properties of the iron in various locations of the same casting or between the properties of a casting and those of a test specimen cast from the same iron (see Appendix X1).  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

ABSTRACT
This specification covers the standard common requirements for iron castings to be used for general industrial applications. The castings shall be made in a workman-like manner and shall conform to the dimensions on drawings furnished by the purchaser before manufacture is started. A lot shall consist of one of the following: all the metal from a single heating in a batch-type melting furnace; all the metal poured from two or more batch-type melting furnaces into a single ladle or a single casting; or all the metal poured from a continuous melting furnace for a given period of time between changes in charge, processing conditions, or aim-for chemistry, whichever is the shorter period. Specimens shall undergo tension tests and shall conform to the specified tensile strength requirements. Chemical analysis such as spectrographic methods shall be performed to determine the chemical composition which shall be in accordance to the carbon content requirement of the specimen. Visual inspection shall also be done to ensure that the casting surface is free of adhering sand, scale, cracks, and hot tears.
SCOPE
1.1 This specification covers a group of requirements that are mandatory requirements when used in conjunction with the following iron casting specifications issued by ASTM: ASTM Specification2
  A47/A47M A48/A48M A197/A197M A220/A220M A278/A278M A319 A395/A395M A436 A439 A518/A518M A532/A532M A536 A571/A571M A823 A842 A874/A874M A897/A897M  
1.2 This specification also covers a group of supplementary requirements which may be applied to the above specifications as indicated herein. These are provided for use when additional testing or inspection is desired and apply only when specified individually by the purchaser in the order.  
1.3 The requirements of the individual material specification, and this general specification shall prevail in the sequence named.  
1.4 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

ABSTRACT
This specification covers austenitic gray iron castings that are used primarily for their resistance to heat, corrosion, and wear. The types of castings covered here are: Type 1, Type 1b, Type 2, Type 2b, Type 3, Type 4, Type 5, and Type 6. The materials shall be manufactured by melting in any furnace that produces castings which includes cupolas, air furnaces, electric furnaces, crucible furnaces, and so forth. Heat and product analyses shall be performed wherein specimens shall conform to required chemical composition of carbon, silicon, manganese, nickel, copper, chromium, sulfur, and molybdenum. The materials shall undergo a nonmagnetic test which is based on the material's attraction to a small steel horseshoe-type magnet and a magnetic permeability test in the event that nonmagnetic castings are specified. Tension tests shall be performed wherein specimens shall conform to required tensile strength and Brinell hardness.
SCOPE
1.1 This specification covers austenitic gray iron castings that are used primarily for their resistance to heat, corrosion, and wear. Austenitic gray iron is characterized by uniformly distributed graphite flakes, some carbides, and the presence of sufficient alloy content to produce an austenitic structure.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

ABSTRACT
This specification covers gray iron for castings suitable for pressure-containing parts at elevated temperatures. Castings shall be stress-relieved by placing them in a suitable furnace and heating them uniformly to the temperatures and for the times specified. Castings to be used at a particular temperature range shall undergo heat treatment and cooling. Chemical analysis shall be performed on each class of castings and shall meet the maximum requirement for carbon, phosphorus and sulfur. Iron used in supplying castings shall conform to the required tensile strength. Separately cast test bars having the required dimensions shall be poured from the same lot as the castings represented. The test bars shall be cast in dried siliceous sand molds maintained at approximately room temperature. Tension test shall be performed on each lot and materials shall conform to the tensile requirements specified.
SCOPE
p id="s00002">1.1 This specification covers gray iron for castings suitable for pressure-containing parts for use at temperatures up to 650°F (350°C).
1.2 Classes of Iron:
1.2.1 Castings of all classes are suitable for use up to 450°F (230°C). For temperatures above 450°F and up to 650°F, only Class 40, 45, 50, 55, and 60 castings are suitable.
1.2.2 Castings of all classes are suitable for use up to 230°C. For temperatures above 230°C and up to 350°C, only Class 275, 300, 325, 350, 380, and 415 castings are suitable.
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.

ABSTRACT
This specification covers gray iron castings for products of the automobile, truck, tractor and allied industries. The materials shall be classified into eight grades (G1800, G2500, G3000, G3500, G4000, G2500a, G3500b and G3500c) based on the range of their casting hardness, chemical composition and microstructure. Grades G1800 and G2500 shall be annealed. Alloy gray iron automotive camshafts of grade designation G4000d shall conform to the required values of casting hardness, chemical compositions of chromium, molybdenum, and nickel and microstructure. The cam areas of camshaft casting shall undergo selective hardening by flame or induction hardening and shall conform to the required values of depth and surface hardness.
SCOPE
1.1 This specification applies to gray iron castings, cast in sand molds, used in the products of the automobile, truck, tractor, and allied industries.  
1.2 The values stated in inch-pound units are to be regarded as standard. No other units of measurement are included in this standard.

ABSTRACT
This specification covers gray iron castings exposed to elevated temperatures for non-pressure containing parts such as grate bars, stoker links, stoker parts, oil still furnace parts, firebox parts, ingot molds, glass molds, caustic pots, and metal melting pots. The three classes of gray iron covered here are: Class I, possessing superior thermal shock resistance; Class II, possessing average thermal shock resistance and moderately good tensile strength; and Class III, possessing a higher tensile strength than either Classes I or II. It is the intention of this specification to classify the irons in accordance with their carbon content equivalent, wherein the equation for its calculation is given herein.
SCOPE
1.1 This specification covers three classes of gray iron suitable for castings exposed to temperatures encountered in such service as grate bars, stoker links, stoker parts, oil still furnace parts, firebox parts, ingot molds, glass molds, caustic pots, and metal melting pots.
Note 1—This specification is general, covering cast irons normally used for the above types of service, at temperatures as high as 1400°F (760°C). It is not intended to imply that all three classes are suitable throughout this entire temperature range without regard to actual service stresses. Some are suitable for long service at the lower temperatures only, unless low stresses are involved.  
1.2 The three classes of gray iron covered by this specification are as follows:  
1.2.1 Class I,  possessing superior resistance to thermal shock,  
1.2.2 Class II,  possessing average resistance to thermal shock and a moderately good tensile strength (tensile strengths above 30 000 psi (207 MPa) may be expected), and  
1.2.3 Class III,  possessing a higher tensile strength than either Classes I or II (tensile strengths as high as 40 000 psi (276 MPa) may be expected).  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

ABSTRACT
This specification deals with abrasion-resistant cast irons used for mining, milling, earth-handling, and manufacturing industries. These alloys may be made by melting process and shall have microstructures that consist of carbides, martensite, bainite, austenite, and in exceptional cases, minor amounts of graphite or pearlite. The following conditions for casting will be supplied: as-cast, as-cast and stress relieved, hardened, hardened and stress relieved, or softened for machining. Heat treatment shall be done. The chemical composition of a class and type (that is, Class I, Type A) shall conform to the range of values specified for carbon, manganese, silicon, nickel, chromium, molybdenum, copper, phosphorus, and sulfur. Hardness test shall also be made.
SCOPE
1.1 This specification covers a group of white cast irons that have been alloyed to secure high resistance to abrasive wear in the applications of the mining, milling, earth-handling, and manufacturing industries.  
1.2 Simple and low-alloy white cast irons that consist essentially of iron carbides and pearlite are specifically excluded from this specification.
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.

ABSTRACT
This guide covers standard specification for three classes of gray iron for castings intended for use as valve pressure retaining parts, pipe fittings, and flanges. Chemical analysis shall be performed in each lot and shall conform to the required chemical composition for phosphorous and sulfur. Tension test shall be conducted on each class of gray iron castings and shall conform to the specified values of tensile strength. Tension test specimens shall have threaded ends and shall conform to the prescribed dimensions.
SCOPE
1.1 This specification covers three classes of gray iron for castings intended for use as valve pressure retaining parts, pipe fittings, and flanges.
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.
Note 1—The text of this standard references notes and footnotes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the standard.

ABSTRACT
This specification covers centrifugally cast cylinders with an outer layer of white cast iron and the remainder of the material of gray cast iron. These castings are suitable for pressure containing parts of the design strength of which is based on the gray iron portion of the cylinder. The white iron portion of the cylinder shall be made to a minimum hardness and the casting process shall be controlled to produce a metallurgical bond between the two metal layers. All surfaces shall be machined prior to the cylinders being placed into service. The tensile strength of the cast irons shall be measured by tension testing while the thickness of the white cast iron shall be determined by ultrasonic testing.
SCOPE
1.1 This specification covers centrifugally cast cylinders with an outer layer of white cast iron and the remainder of the material of gray cast iron. These castings are suitable for pressure containing parts the design strength of which is based on the gray iron portion of the cylinder. These castings are suitable for service at temperatures up to 450°F [230°C].
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.
1.3 The following safety hazards caveat pertains only to the test method portion, Section 8, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ABSTRACT
This specification covers gray iron castings intended for general engineering use where tensile strength is a major consideration. Castings are classified on the basis of the tensile strength of the iron in separately cast test bars. The surface of the casting shall be free of adhering sand, scale, cracks, and hot tears, as determined by visual examination. The test bars are designated into S, A, B, and C categories, according to the thickness of its controlling wall section. The casting shall be subjected to a tension test to determine its tensile strength.
SCOPE
1.1 This specification covers gray iron castings intended for general engineering use where tensile strength is a major consideration. Castings are classified on the basis of the tensile strength of the iron in separately cast test bars.  
1.1.1 This specification subordinates chemical composition to tensile strength.  
1.2 Castings produced to this specification are graded on the basis of minimum tensile strength obtained in special test coupons designed to standardize cooling rate. The tensile strength developed in certain casting sections may vary from test coupon values (see X1.2).  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.

ABSTRACT
This specification covers standards for high-silicon iron castings of Grades 1, 2, and 3 intended for severe environment corrosion-resistant services. The alloy shall be produced by any melting and casting process, or combination of processes that will be capable of meeting the specified contents of carbon, manganese, silicon, chromium, molybdenum, and copper. Reference analysis methods are given for each chemical component. Transverse bend test and hydrostatic test shall be performed. Material shall conform to minimum load at center and minimum deflection at center requirements.
SCOPE
1.1 This specification covers high-silicon cast iron castings intended for corrosion-resistant service.  
1.2 This specification covers three grades as shown in Table 1. Selection of grade depends on the corrosive service to be experienced by the casting. All three grades are suited for application in severe corrosive environments. However, Grade 2 is particularly suited for application in strong chloride environments, and Grade 3 is recommended for impressed current anodes.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.
1.4 The following safety hazards caveat pertains only to the test method portion, Section 9, of this specification:  This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
TABLE 1 Chemical Composition   Element
Composition, Weight %
  Grade 1
Grade 2
Grade 3
  Carbon 0.65–1.10 0.75–1.15 0.70–1.10 Manganese 1.50, max 1.50, max 1.50, max Silicon14.20–14.7514.20–14.7514.20–14.75 Chromium 0.50, max 3.25–5.00 3.25–5.00 Molybdenum 0.50, max 0.40–0.60 0.20, max Copper 0.50, max 0.50, max 0.50, max

ABSTRACT
This specification covers gray iron castings that are statically cast in permanent molds. Castings under this specification are classified into a number of grades (A-SA, A-SB, A-SC, A-SS, A-CA, A-CB, A-CC, N-SA, N-SB, N-SC,N-SS, N-CA, N-CB and N-CC) based on the properties of separately cast test bars. The grades are designated A for annealed or N for normalized; followed by an S or a C to designate a solid or a cored casting; followed by an A, B, C, or S to designate the test bar to be poured with the castings. The cast test bar shall be selected on the basis of the controlling section size of the casting and shall have the specified dimensions (diameter and length). Castings may be produced in the as cast state provided the tensile strength and Brinell hardness requirements are met. The chemical composition and heat treatment shall be such as to produce these mechanical requirements as well. A suitable permanent mold design for separately cast test bars is described and the tension test requirements are detailed.
SCOPE
1.1 This specification covers gray iron castings that are statically cast in permanent molds.  
1.2 No precise quantitative relationship can be stated between the properties of the iron in various locations of the same casting or between the properties of a casting and those of a test specimen cast from the same iron (see Appendix X1).  
1.3 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.

ABSTRACT
This specification covers statically cast dual metal rolls with the outer layer of the roll body being chilled white iron of different chemical composition than the core and journals of the roll which is gray cast iron. The castings are suitable for pressure containing parts such as pressure vessels, the design strength of which is based on the gray iron portion of the cylinder, and for service at the specified temperatures. The melting procedure shall be optional with the foundry and the casting process shall be controlled to produce a metallurgical bond between the chilled white iron exterior and gray iron interior. The chilled white iron exterior shall be made to the specified minimum hardness and the gray iron portion of the roll shall conform to the applicable class as determined by design requirements. The roll shall conform to the tensile strength requirement to be determined by tensile test and shall meet the required thickness. All surfaces shall be machined or ground, or both, prior to the rolls being placed into service.
SCOPE
1.1 This specification covers statically cast dual metal rolls with the outer layer of the roll body being chilled white iron of different chemical composition than the core and journals of the roll which is gray cast iron. The castings are suitable for pressure containing parts, the design strength of which is based on the gray iron portion of the cylinder. The castings are suitable for service at temperatures up to 450°F [232°C].
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.
1.3 The following safety hazards statement pertains only to the test method portion, 9, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ABSTRACT
This specification deals with abrasion-resistant cast irons used for mining, milling, earth-handling, and manufacturing industries. These alloys may be made by melting process and shall have microstructures that consist of carbides, martensite, bainite, austenite, and in exceptional cases, minor amounts of graphite or pearlite. The following conditions for casting will be supplied: as-cast, as-cast and stress relieved, hardened, hardened and stress relieved, or softened for machining. Heat treatment shall be done. The chemical composition of a class and type (that is, Class I, Type A) shall conform to the range of values specified for carbon, manganese, silicon, nickel, chromium, molybdenum, copper, phosphorus, and sulfur. Hardness test shall also be made.
SCOPE
1.1 This specification covers a group of white cast irons that have been alloyed to secure high resistance to abrasive wear in the applications of the mining, milling, earth-handling, and manufacturing industries.  
1.2 Simple and low-alloy white cast irons that consist essentially of iron carbides and pearlite are specifically excluded from this specification.
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.

ABSTRACT
This specification covers double pour, centrifugally cast, abrasion-resistant roll shells for general application. The outer layer is white iron and the inner layer is gray iron and there shall be no gradient of mottled iron these layers. Both the white and the gray irons may be melted by any suitable melting process. The white iron portion of the casting shall be produced by chemistry rather than chilling. A chemical analysis of the white and gray irons shall be taken and the chemical compositions shall be controlled to obtain the required mechanical properties. The white iron (Types I, II, III, and IV) shall conform to the specified Brinell hardness and the gray iron (Class Nos. 20, 25, 30, and 35) shall conform to the specified tensile strength. The minimum thickness of the white iron layer is given. Hardness and tension tests of the cast dual metal shall be performed.
SCOPE
1.1 This specification covers double pour, centrifugally cast, abrasion-resistant roll shells for general application. The outer layer is white iron and the inner layer is gray iron. There shall be no gradient of mottled iron between the white iron and the gray iron.
1.2 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with this specification.