ASTM C286-22

(Terminology)

Standard Terminology Relating to Porcelain Enamel and Ceramic-Metal Systems

Standard Terminology Relating to Porcelain Enamel and Ceramic-Metal Systems

SCOPE
1.1 These definitions pertain to the terminology used in the porcelain enamel and ceramic-coated metal industries.  
1.2 Words adequately defined in standard dictionaries are not included. Included are words that are peculiar to these industries.  
1.3 Hyphenated words, double words, or phrases are listed alphabetically under the first word; additional important words are cross-referenced.  
1.4 When a word or phrase, listed as a synonym, is not separately defined, the defined word or phrase is the accepted or preferred form.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

General Information

Status
Published
Publication Date
30-Apr-2022
ICS
01.040.25 - Manufacturing engineering (Vocabularies)
25.220.50 - Enamels
Technical Committee
B08 - Metallic and Inorganic Coatings
Drafting Committee
B08.12 - Materials for Porcelain Enamel and Ceramic-Metal Systems
Current Stage
Ref Project

Buy Standard

ASTM C286-22 - Standard Terminology Relating to Porcelain Enamel and Ceramic-Metal SystemsASTM C286-22 - Standard Terminology Relating to Porcelain Enamel and Ceramic-Metal Systems
PreviousNext
Standard
ASTM C286-22 - Standard Terminology Relating to Porcelain Enamel and Ceramic-Metal Systems
English language
9 pages
sale 15% off
Preview
sale 15% off
Preview
REDLINE ASTM C286-22 - Standard Terminology Relating to Porcelain Enamel and Ceramic-Metal SystemsREDLINE ASTM C286-22 - Standard Terminology Relating to Porcelain Enamel and Ceramic-Metal Systems
PreviousNext
Standard
REDLINE ASTM C286-22 - Standard Terminology Relating to Porcelain Enamel and Ceramic-Metal Systems
English language
9 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the
Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
Designation: C286 − 22
Standard Terminology Relating to
1
Porcelain Enamel and Ceramic-Metal Systems
This standard is issued under the fixed designation C286; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the U.S. Department of Defense.
1. Scope C283 Test Methods for Resistance of Porcelain Enameled
Utensils to Boiling Acid
1.1 These definitions pertain to the terminology used in the
C285 Test Methods for Sieve Analysis of Wet-Milled and
porcelain enamel and ceramic-coated metal industries.
Dry-Milled Porcelain Enamel
1.2 Words adequately defined in standard dictionaries are
C346 Test Method for 45-deg Specular Gloss of Ceramic
not included. Included are words that are peculiar to these
Materials
industries.
C374 Test Methods for Fusion Flow of Porcelain Enamel
Frits (Flow-Button Methods)
1.3 Hyphenated words, double words, or phrases are listed
alphabetically under the first word; additional important words C385 Test Method for Thermal Shock Resistance of
Porcelain-Enameled Utensils
are cross-referenced.
C448 Test Methods for Abrasion Resistance of Porcelain
1.4 When a word or phrase, listed as a synonym, is not
Enamels
separately defined, the defined word or phrase is the accepted
C614 Test Method forAlkali Resistance of Porcelain Enam-
or preferred form.
els
1.5 This international standard was developed in accor-
C633 Test Method for Adhesion or Cohesion Strength of
dance with internationally recognized principles on standard-
Thermal Spray Coatings
ization established in the Decision on Principles for the
C743 Test Method for Continuity of Porcelain Enamel
Development of International Standards, Guides and Recom-
Coatings
mendations issued by the World Trade Organization Technical
C756 Test Method for Cleanability of Surface Finishes
Barriers to Trade (TBT) Committee.
C774 Test Method for Yield Strength of Enameling Steels
After Straining and Firing
2. Referenced Documents
D523 Test Method for Specular Gloss
2
2.1 ASTM Standards: D2244 Practice for Calculation of Color Tolerances and
A424 SpecificationforSteel,Sheet,forPorcelainEnameling
Color Differences from Instrumentally Measured Color
B487 Test Method for Measurement of Metal and Oxide Coordinates
Coating Thickness by Microscopical Examination of
D4060 Test Method for Abrasion Resistance of Organic
Cross Section Coatings by the Taber Abraser
B915 Test Method for Measuring Static Heat Resistance of
Self-Cleaning Oven Coating 3. Terminology
B916 Test Method for Adherence of Porcelain Enamel
abrasion resistance, n—the degree to which a porcelain
Coatings to Sheet Metal
enamel will resist attack by abrasive materials.
C282 Test Method for Acid Resistance of Porcelain Enam-
NOTE 1—See Test Methods C448 and D4060.
els(Citric Acid Spot Test)
acid resistance, n—the degree to which a porcelain enamel
will resist attack by acids.
1
This terminology is under the jurisdiction of ASTM Committee B08 on
NOTE 2—See Test Methods C283 and C282.
Metallic and Inorganic Coatings and is the direct responsibility of Subcommittee
B08.12 on Materials for Porcelain Enamel and Ceramic-Metal Systems.
adherence, n—(1) the degree of adhesion of a porcelain
Current edition approved May 1, 2022. Published May 2022. Originally
approvedin1951.Lastpreviouseditionapprovedin2017asC286 – 99(2017).DOI: enamel or other ceramic coating to a metal substrate.
10.1520/C0286-22.
2
NOTE 3—See Test Method B916.
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
(2) Stress necessary to cause separation of one material from
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
Standards volume information, refer to the standard’s Document Summary page on another at their interface.
the ASTM website. NOTE 4—See Test Method C633.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
C286 − 22
aging, n—the storing of porcelain enamel slips or powders black speck, n—a defect that appears in the fired cover coat as
before use. The change occurring in slips or powders with a small dark spot.
the lapse of time.
blank, n—the piece cut from metal sheet that is to be used in
air atomizing, n—air used to atomize powder and to control forming the finished article.
powder/air mix and powder cloud density.
blemish, n—in dry process enamel
...

This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Because
it may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current version
of the standard as published by ASTM is to be considered the official document.
Designation: C286 − 99 (Reapproved 2017) C286 − 22
Standard Terminology Relating to
1
Porcelain Enamel and Ceramic-Metal Systems
This standard is issued under the fixed designation C286; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the U.S. Department of Defense.
1. Scope
1.1 These definitions pertain to the terminology used in the porcelain enamel and ceramic-coated metal industries.
1.2 Words adequately defined in standard dictionaries are not included. Included are words that are peculiar to these industries.
1.3 Hyphenated words, double words, or phrases are listed alphabetically under the first word; additional important words are
cross-referenced.
1.4 When a word or phrase, listed as a synonym, is not separately defined, the defined word or phrase is the accepted or preferred
form.
1.5 This international standard was developed in accordance with internationally recognized principles on standardization
established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued
by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
2. Referenced Documents
2
2.1 ASTM Standards:
A424 Specification for Steel, Sheet, for Porcelain Enameling
A919B487 Terminology Relating to Heat Treatment of MetalsTest Method for Measurement of Metal and Oxide Coating
Thickness by Microscopical Examination of Cross Section (Withdrawn 1999)
B915 Test Method for Measuring Static Heat Resistance of Self-Cleaning Oven Coating
B916 Test Method for Adherence of Porcelain Enamel Coatings to Sheet Metal
C282 Test Method for Acid Resistance of Porcelain Enamels(Citric Acid Spot Test)
C283 Test Methods for Resistance of Porcelain Enameled Utensils to Boiling Acid
C285 Test Methods for Sieve Analysis of Wet-Milled and Dry-Milled Porcelain Enamel
3
C313 Method of Test for Adherence of Porcelain Enamel and Ceramic Coatings to Sheet Metal (Withdrawn 1989)
3
C314 Test Method for Flatness of Porcelain Enameled Panels (Withdrawn 1979)
C346 Test Method for 45-deg Specular Gloss of Ceramic Materials
3
C347 Test Method for Reflectivity and Coefficient of Scatter of White Porcelain Enamels (Withdrawn 1990)
C374 Test Methods for Fusion Flow of Porcelain Enamel Frits (Flow-Button Methods)
1
This terminology is under the jurisdiction of ASTM Committee B08 on Metallic and Inorganic Coatings and is the direct responsibility of Subcommittee B08.12 on
Materials for Porcelain Enamel and Ceramic-Metal Systems.
Current edition approved May 1, 2017May 1, 2022. Published May 2017May 2022. Originally approved in 1951. Last previous edition approved in 20092017 as
C286–99(2017).C286 – 99(2017). DOI: 10.1520/C0286-99R17.10.1520/C0286-22.
2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM Standards
volume information, refer to the standard’s Document Summary page on the ASTM website.
Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
1

---------------------- Page: 1 ----------------------
C286 − 22
C385 Test Method for Thermal Shock Resistance of Porcelain-Enameled Utensils
C448 Test Methods for Abrasion Resistance of Porcelain Enamels
C614 Test Method for Alkali Resistance of Porcelain Enamels
C633 Test Method for Adhesion or Cohesion Strength of Thermal Spray Coatings
C743 Test Method for Continuity of Porcelain Enamel Coatings
C756 Test Method for Cleanability of Surface Finishes
C774 Test Method for Yield Strength of Enameling Steels After Straining and Firing
D523 Test Method for Specular Gloss
D2244 Practice for Calculation of Color Tolerances and Color Differences from Instrumentally Measured Color Coordinates
D4060 Test Method for Abrasion Resistance of Organic Coatings by the Taber Abraser
3. Terminology
abrasion resistance—resistance, n—the degree to which a porcelain enamel will resist attack by abrasive materials.
NOTE 1—See Test Methods C448 and D4060.
acid annealing—an annealing process in which ferrous metal shapes are coated with acid before and in conjunction with the
annealing.
acid resistance—resistance, n—the degree to which a porcelain enamel will resist attack by acids.
NOTE
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM A370-23(Test Method)
Standard Test Methods and Definitions for Mechanical Testing of Steel Products

SIGNIFICANCE AND USE
4.1 The primary use of these test methods is testing to determine the specified mechanical properties of steel, stainless steel, and related alloy products for the evaluation of conformance of such products to a material specification under the jurisdiction of ASTM Committee A01 and its subcommittees as designated by a purchaser in a purchase order or contract.  
4.1.1 These test methods may be and are used by other ASTM Committees and other standards writing bodies for the purpose of conformance testing.  
4.1.2 The material condition at the time of testing, sampling frequency, specimen location and orientation, reporting requirements, and other test parameters are contained in the pertinent material specification or in a general requirement specification for the particular product form.  
4.1.3 Some material specifications require the use of additional test methods not described herein; in such cases, the required test method is described in that material specification or by reference to another appropriate test method standard.  
4.2 These test methods are also suitable to be used for testing of steel, stainless steel and related alloy materials for other purposes, such as incoming material acceptance testing by the purchaser or evaluation of components after service exposure.  
4.2.1 As with any mechanical testing, deviations from either specification limits or expected as-manufactured properties can occur for valid reasons besides deficiency of the original as-fabricated product. These reasons include, but are not limited to: subsequent service degradation from environmental exposure (for example, temperature, corrosion); static or cyclic service stress effects, mechanically-induced damage, material inhomogeneity, anisotropic structure, natural aging of select alloys, further processing not included in the specification, sampling limitations, and measuring equipment calibration uncertainty. There is statistical variation in all aspects of mechanical testin...
SCOPE
1.1 These test methods2 cover procedures and definitions for the mechanical testing of steels, stainless steels, and related alloys. The various mechanical tests herein described are used to determine properties required in the product specifications. Variations in testing methods are to be avoided, and standard methods of testing are to be followed to obtain reproducible and comparable results. In those cases in which the testing requirements for certain products are unique or at variance with these general procedures, the product specification testing requirements shall control.  
1.2 The following mechanical tests are described:    
Sections  
Tension  
7 to 14  
Bend  
15  
Hardness  
16  
Brinell  
17  
Rockwell  
18  
Portable  
19  
Impact  
20 to 30  
Keywords  
32  
1.3 Annexes covering details peculiar to certain products are appended to these test methods as follows:    
Annex  
Bar Products  
Annex A1  
Tubular Products  
Annex A2  
Fasteners  
Annex A3  
Round Wire Products  
Annex A4  
Significance of Notched-Bar Impact Testing  
Annex A5  
Converting Percentage Elongation of Round Specimens to
Equivalents for Flat Specimens  
Annex A6    
Testing Multi-Wire Strand  
Annex A7  
Rounding of Test Data  
Annex A8  
Methods for Testing Steel Reinforcing Bars  
Annex A9  
Procedure for Use and Control of Heat-cycle Simulation  
Annex A10  
1.4 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.5 When these test methods are referenced in a metric product specification, the yield and tensile values may be determined in inch-pound (ksi) units then converted into SI (MPa) units. The elongation determined in inch-pound gauge lengths of 2 in. or 8 in. may be report...

  • Standard
    51 pages
    English language
    sale 15% off
  • Standard
    51 pages
    English language
    sale 15% off
ASTM
ASTM F3565-23(Practice)
Standard Practice for Electrofusion Joining Polyethylene (PE) Pipe and Fittings for Pressure Pipe Service

SIGNIFICANCE AND USE
4.1 Using the procedures and apparatus in Sections 8 and 9 and the manufacturer's instructions, pressure-tight joints as strong as the pipe itself can be made between manufacturer-recommended combinations of pipe and fittings. See Specification F1055 for performance requirements of polyethylene electrofusion fittings.
SCOPE
1.1 This practice describes procedures for making joints suitable for pressure service with polyethylene (PE) pipe and fittings by means of electrofusion joining techniques in, but not limited to, a field environment. Other suitable electrofusion joining procedures are available from various sources including fitting manufacturers. This standard does not purport to address all possible electrofusion joining procedures, or to preclude the use of qualified procedures developed by other parties that have been proven to produce reliable electrofusion joints. (Note 1)
Note 1: Reference to the manufacturer in this practice refers to the electrofusion fitting manufacturer.  
1.2 The parameters and procedure are applicable only to joining polyethylene pipe and fittings (Note 2) which are intended for PE fuel gas pipe per Specification D2513 and PE potable water, sewer and industrial pipe manufactured per Specification F714, Specification D3035, Specification F2619, and AWWA C901 and C906.
Note 2: Commercially available materials classified with a thermoplastic pipe material designation code beginning with PE 14, PE 23, PE 24, PE 27, PE 33, PE 34, PE 36, and PE 46, and PE 47 in accordance with Specification D3350 and Terminology F412 are generally acceptable for electrofusion joining using this practice. Consult with the pipe or fitting manufacturer for specific compatibility information.  
1.3 Parts that are within the dimensional tolerances given in present ASTM specifications are required to produce sound joints between polyethylene pipe and fittings when using the joining techniques described in this practice.  
1.4 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.5 The text of this practice references notes, footnotes, and appendices which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the practice.  
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    7 pages
    English language
    sale 15% off
ASTM
ASTM D5141-23(Test Method)
Standard Test Method for Determining Filtering Efficiency and Flow Rate of the Filtration Component of a Sediment Retention Device

SIGNIFICANCE AND USE
5.1 This test method is used to determine the filtering efficiency and flow rate of the filtration component of a sediment retention device, such as a silt fence, a silt barrier, or a silt curtain, for specific soil tested.  
5.2 This test method may be used for the design of the filtration component of a sediment retention device to meet requirements of regulatory agencies in filtering efficiency or flow rate for the specific soil tested.  
5.2.1 The designer can use this test method to determine the spacing between sediment retention devices.  
5.3 This test method is intended for performance evaluation, as the results will depend on the specific soil evaluated. Unless testing with the default soil is desired, it is recommended that the user or representative perform the test to pre-approve products, as sediment retention device manufacturers are not typically equipped to handle or test soil requirements.  
5.4 This test method provides a means of evaluating the filtration component of sediment retention devices with different soils under various conditions that simulate the conditions that exist in a sediment retention device installation. This test method may be used to simulate several storm events on the same sediment retention device specimen. Therefore, the number of times this test is repeated per specimen is dependent upon the user and the site conditions.
SCOPE
1.1 This test method is used to determine the filtering efficiency and the flow rate of the filtration component of a sediment retention device, such as a silt fence, silt barrier, or inlet protector.  
1.1.1 The results are shown as a percentage for filtering efficiency and cubic metres per square metre per minute (m3/m2/min) or gallons per square foot per minute (gal/ft2/min) for flow rate.  
1.1.2 The filtering efficiency indicates the percent of sediment removed from sediment-laden water.  
1.1.3 The flow rate is the average rate of passage of the sediment-laden water through the filtration component of a sediment retention device.  
1.2 This test method requires several specialized pieces of equipment, such as an integrated water sampler and an analytical balance, or a vacuum filtration system. At the client’s discretion, the test soil is either a site-specific soil or a soil that is representative of a target default gradation.  
1.3 The values stated in SI units are the standard, while the inch-pound units are provided for information. The values expressed in each system may not be exact equivalents; therefore, each system must be used independently of the other, without combining values in any way.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    5 pages
    English language
    sale 15% off
  • Standard
    5 pages
    English language
    sale 15% off
ASTM
ASTM F2647-07(2023)(Guide)
Standard Guide for Approved Methods of Installing a CVS (Central Vacuum System)

SIGNIFICANCE AND USE
4.1 The suggestions of this guide are intended to provide proper installation materials and practices to be used during the installation of a central-vacuum system.
SCOPE
1.1 This guide demonstrates proper methods for installing a central-vacuum system.  
1.2 Appendix X1 contains additional sources of information that may be helpful to the user of this guide.  
1.3 The values stated in inch-pound units are to be regarded as the standard. The values given in parentheses are for information only.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Guide
    7 pages
    English language
    sale 15% off
ASTM
ASTM F2886-17(2023)(Specification)
Standard Specification for Metal Injection Molded Cobalt-28Chromium-6Molybdenum Components for Surgical Implant Applications

ABSTRACT
This specification covers chemical, mechanical, and metallurgical general requirements for metal injection molded (MIM) cobalt-28chromium-6molybddenum components to be used in manufacturing surgical implants. In this specification, the MIM components covered may have been densified beyond their as-sintered density by post-sinter processing. For the chemical requirements, the components supplied in this specification must conform in accordance to the chemical requirements specified herein in Table 1. The product analysis tolerances must also conform to the product tolerances presented in Table 2. The specification also enumerates the mechanical requirements for MIM components wherein the tensile properties of the MIM must conform to the mechanical properties in Table 3. The microstructural requirements and specimen preparation shall be in accordance with Guide E3 and Practice E407.
SCOPE
1.1 This specification covers chemical, mechanical, and metallurgical requirements for metal injection molded (MIM) cobalt-28chromium-6molybdenum components to be used in the manufacture of surgical implants  
1.2 The MIM components covered by this specification may have been densified beyond their as-sintered density by post-sinter processing.  
1.3 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    5 pages
    English language
    sale 15% off
ASTM
ASTM A480/A480M-23a(Specification)
Standard Specification for General Requirements for Flat-Rolled Stainless and Heat-Resisting Steel Plate, Sheet, and Strip

ABSTRACT
This specification covers general requirements for flat-rolled stainless and heat-resisting steel plate, sheet, and strip. The steel shall be made by one of the following processes: electric-arc, electric-induction, or other suitable processes. Heat and product analyses shall conform to the chemical requirements for each of the specific elements. The material shall undergo mechanical tests such as tension test, hardness test, and bend test. Special tests like intergranular corrosion test, permeability test, Charpy impact testing and tests for detrimental intermetallic phases in wrought duplex stainless steels shall be also be performed when required.
SCOPE
1.1 This specification2 covers a group of general requirements that, unless otherwise specified in the purchase order or in an individual specification, shall apply to rolled steel plate, sheet, and strip, under each of the following specifications issued by ASTM: Specifications A240/A240M, A263, A264, A265, A666, A693, A793, and A895.  
1.2 In the case of conflict between a requirement of a product specification and a requirement of this specification, the product specification shall prevail. In the case of conflict between a requirement of the product specification or a requirement of this specification and a more stringent requirement of the purchase order, the purchase order shall prevail. The purchase order requirements shall not take precedence if they, in any way, violate the requirements of the product specification or this specification; for example, by waiving a test requirement or by making a test requirement less stringent.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The SI units are shown in brackets, except that when A480M is specified, Annex A3 shall apply for the dimensional tolerances and not the bracketed SI values in Annex A2. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.4 This specification and the applicable material specifications are expressed in both inch-pound and SI units. However, unless the order specifies the applicable “M” specification designation [SI units], the material shall be furnished in inch-pound units.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    26 pages
    English language
    sale 15% off
  • Technical specification
    26 pages
    English language
    sale 15% off
ASTM
ASTM E2552-23(Guide)
Standard Guide for Assessing the Environmental and Human Health Impacts of New Compounds for Military Use

SIGNIFICANCE AND USE
5.1 The purpose of this guide is to provide a logical, tiered approach in the development of environmental health criteria coincident with level and effort in the research, development, testing, and evaluation of new materials for military use. Various levels of uncertainty are associated with data collected from previous stages. Following the recommendation in the guide should reduce the relative uncertainty of the data collected at each developmental stage. At each stage, a general weight of evidence qualifier shall accompany each exposure/effect relationship. They may be simple (for example, low, medium, or high confidence) or sophisticated using a numerical value for each predictor as a multiplier to ascertain relative confidence in each step of risk characterization. The specific method used will depend on the stage of development, quantity and availability of data, variation in the measurement, and general knowledge of the dataset. Since specific formulations, conditions, and use scenarios may not be known until the later stages, exposure estimates can be determined when practical (for example, Engineering and Manufacturing Development; see 6.6). Exposure data can then be used with other toxicological data collected from previous stages in a quantitative risk assessment to determine the relative degree of hazard.  
5.2 Data developed from the use of this guide are designed to be consistent with criteria required in weapons and weapons system development (for example, programmatic environment, safety and occupational health evaluations, environmental assessments/environmental impact statements, toxicity clearances, and technical data sheets).  
5.3 Information shall be evaluated in a flexible manner consistent with the needs of the authorizing program. This requires proper characterization of the current problem. For example, compounds may be ranked relative to the environmental criteria of the prospective alternatives, the replacement compound, and within bo...
SCOPE
1.1 This guide is intended to determine the relative environmental influence of new substances, consistent with the research and development (R&D) level of effort and is intended to be applied in a logical, tiered manner that parallels both the available funding and the stage of research, development, testing, and evaluation. Specifically, conservative assumptions, relationships, and models are recommended early in the research stage, and as the technology is matured, empirical data will be developed and used. Munition constituents are included and may include propellants, oxidizers, explosives, binders, stabilizers, metals, dyes, and other compounds used in the formulation to produce a desired effect. Munition systems range from projectiles, grenades, rockets/missiles, training simulators, to smokes and obscurants. Given the complexity of issues involved in the assessment of environmental fate and effects and the diversity of the systems used, this guide is broad in scope and not intended to address every factor that may be important in an environmental context. Rather, it is intended to reduce uncertainty at minimal cost by considering the most important factors related to human health and environmental impacts of energetic materials. This guide provides an outline for collecting data useful in a relative ranking procedure to provide the systems scientist with a sound basis for prospectively determining a selection of candidates based on environmental and human health criteria. The general principles in this guide are applicable to substances other than energetics if intended to be used in a similar manner with similar exposure profiles.  
1.2 The scope of this guide includes:  
1.2.1 Energetic and other new/novel materials and compositions in all stages of research, development, test and evaluation.  
1.2.2 Environmental assessment, including:
1.2.2.1 Human and ecological effects of the unexploded energetics and ...

  • Guide
    9 pages
    English language
    sale 15% off
  • Guide
    9 pages
    English language
    sale 15% off
ASTM
ASTM D8042-18(2023)(Test Method)
Test Method for Shrinkage Temperature of Wet Blue and Wet White

SIGNIFICANCE AND USE
5.1 This test method is designed to determine the temperature at which the Wet Blue or Wet White specimen experiences shrinkage. In this test method, shrinkage occurs as a result of hydrothermal denaturation of the collagen protein molecules which make up the fiber structure of the Wet Blue or Wet White. The shrinkage temperature of Wet Blue or Wet White is influenced by many different factors, most of which appear to affect the number and nature of crosslinking interactions between adjacent polypeptide chains of the collagen protein molecules. The value of the shrinkage temperature of Wet Blue or Wet White is commonly used as an indicator of the type of tannage or the degree of tannage, or both, of that particular Wet Blue or Wet White (especially for the more hydrothermally stable tannages such as chrome tannage).
SCOPE
1.1 This test method covers the determination of the shrinkage temperature of all types of Wet Blue and Wet White. The heating medium is water when the shrinkage temperature is at or below 98 °C. The heating medium is a glycerine-water solution when the shrinkage temperature is above 98 °C.  
1.2 The values stated in SI units are to be regarded as the standard. The values in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off
ASTM
ASTM D8530/D8530M-23(Guide)
Standard Guide for the Selection and Use of Waterstops

SIGNIFICANCE AND USE
4.1 This guide is intended to be used in the selection and installation of waterstops in cast-in-place concrete construction. This guide is intended to assist the building owner, owner’s representative, architect, engineer, contractor, and/or authorized inspector during the specification and installation of waterstops.  
4.2 This guide is applicable to cast-in-place concrete construction. The use of this guide may not be appropriate for installation of waterstops in other types of concrete construction, including but not limited to, pneumatically applied (that is, shotcrete) and precast concrete construction.
SCOPE
1.1 This guide covers the use of waterstops within cast-in-place concrete construction. Waterstops are generally placed within static, non-moving construction joints in concrete to close off the joint to water, which may be under significant hydrostatic pressure. They are used as part of the overall waterproofing strategy for a building or other structure. Expansion and other types of moving joints may require the use of waterstops, which can accommodate the anticipated movement of the structure and are beyond the scope of this guide.  
1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents: therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Guide
    4 pages
    English language
    sale 15% off
ASTM
ASTM E2956-23(Guide)
Standard Guide for Monitoring the Neutron Exposure of LWR Reactor Pressure Vessels

SIGNIFICANCE AND USE
4.1 Regulatory Requirements—The USA Code of Federal Regulations (10CFR Part 50, Appendix H) requires the implementation of a reactor vessel materials surveillance program for all operating LWRs. Other countries have similar regulations. The purpose of the program is to (1) monitor changes in the fracture toughness properties of ferritic materials in the reactor vessel beltline6 resulting from exposure to neutron irradiation and the thermal environment, and (2) make use of the data obtained from surveillance programs to determine the conditions under which the vessel can be operated with adequate margins of safety throughout its service life. Practice E185, derived mechanical property data, and (r, θ, z) physics-dosimetry data (derived from the calculations and reactor cavity and surveillance capsule measurements (1) using physics-dosimetry standards) can be used together with information in Guide E900 and Refs. 4, 11-18 to provide a relation between property degradation and neutron exposure, commonly called a “trend curve.” To obtain this trend curve at all points in the pressure vessel wall requires that the selected trend curve be used together with the appropriate (r, θ, z) neutron field information derived by use of this guide to accomplish the necessary interpolations and extrapolations in space and time.  
4.2 Neutron Field Characterization—The tasks required to satisfy the second part of the objective of 4.1 are complex and are summarized in Practice E853. In doing this, it is necessary to describe the neutron field at selected (r, θ, z) points within the pressure vessel wall. The description can be either time dependent or time averaged over the reactor service period of interest. This description can best be obtained by combining neutron transport calculations with plant measurements such as reactor cavity (ex-vessel) and surveillance capsule or RPV cladding (in-vessel) measurements, benchmark irradiations of dosimeter sensor materials, and knowledge of th...
SCOPE
1.1 This guide establishes the means and frequency of monitoring the neutron exposure of the LWR reactor pressure vessel throughout its operating life.  
1.2 The physics-dosimetry relationships determined from this guide may be used to estimate reactor pressure vessel damage through the application of Practice E693 and Guide E900, using fast neutron fluence (E > 1.0 MeV and E > 0.1 MeV), displacements per atom (dpa), or damage-function-correlated exposure parameters as independent exposure variables. Supporting the application of these standards are the E853, E944, E1005, and E1018 standards, identified in 2.1.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Guide
    12 pages
    English language
    sale 15% off
  • Guide
    12 pages
    English language
    sale 15% off