Standard Practice for Butt Fusion Joining of PA12 Pipe and Fittings

Standard Practice for Butt Fusion Joining of PA12 Pipe and Fittings

SCOPE
1.1 This practice describes procedures for making butt fusion joints with Polyamide 12 (PA12) pipe and fittings by means of heat fusion joining in, but not limited to, a field environment. Procedure A is for environmental temperatures of 40 °F (4 °C) and higher. Procedure B is for site temperatures below 40 °F (4 °C). Other suitable heat fusion joining procedures are available from various sources including pipe and fitting manufacturers. This standard does not purport to address all possible heat fusion joining procedures, or to preclude the use of qualified procedures developed by other parties that have been proved to produce reliable heat fusion joints.  
1.2 The parameters and procedures are applicable only to joining PA12 pipe and fittings and are not applicable to other polyamide types. They are intended only for PA12 fuel gas pipe per Specification F2785 and PA12 butt heat fusion fittings in accordance with Specification F1733. Fusion to other polyamide types (that is, cross-fusion) is not permitted under this practice, and this practice does not not apply to other polyamide types. Consult with the pipe and fittings manufacturers to make sure they recommend this procedure for the pipe and fittings to be joined (also see Appendix X1).  
1.3 The procedures in this practice apply to the butt fusion of PA12 pipe and butt fusion fittings in accordance with 1.2 having like diameter and wall thickness.
Note 1: Refer to X1.5 for guidance regarding dissimilar wall thicknesses.  
1.4 Other suitable heat joining procedures are available from various sources including pipe and fitting manufacturers. Melt characteristics, average molecular weight and molecular weight distribution of PA12 compounds are influential factors in establishing suitable fusion parameters; therefore, consider the manufacturer’s recommendations in the use or development of a specific fusion procedure.  
1.5 The text of this practice references notes, footnotes, and appendixes which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the practice.  
1.6 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.6.1 Non-conformance with this specification is possible if values from the two systems are combined. Values in parentheses are conversions that are appropriately rounded for accuracy and precision; that are not exact equivalents, and that are for non-mandatory informational purposes.  
1.7 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.8 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

General Information

Status
Published
Publication Date
31-May-2020
ICS
25.160.10 - Welding processes
Technical Committee
F17 - Plastic Piping Systems
Drafting Committee
F17.20 - Joining
Current Stage
Ref Project

Relations

Refers
ASTM F412-20 - Standard Terminology Relating to Plastic Piping Systems
Effective Date
01-Apr-2020

Buy Standard

ASTM F3372-20 - Standard Practice for Butt Fusion Joining of PA12 Pipe and FittingsASTM F3372-20 - Standard Practice for Butt Fusion Joining of PA12 Pipe and Fittings
PreviousNext
Standard
ASTM F3372-20 - Standard Practice for Butt Fusion Joining of PA12 Pipe and Fittings
English language
11 pages
sale 15% off
Preview
sale 15% off
Preview

Standards Content (Sample)

This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the
Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
Designation: F3372 − 20 An American National Standard
Standard Practice for
1
Butt Fusion Joining of PA12 Pipe and Fittings
This standard is issued under the fixed designation F3372; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (´) indicates an editorial change since the last revision or reapproval.
1. Scope 1.6 The values stated in inch-pound units are to be regarded
as standard. The values given in parentheses are mathematical
1.1 This practice describes procedures for making butt
conversions to SI units that are provided for information only
fusion joints with Polyamide 12 (PA12) pipe and fittings by
and are not considered standard.
means of heat fusion joining in, but not limited to, a field
1.6.1 Non-conformance with this specification is possible if
environment.ProcedureAisforenvironmentaltemperaturesof
values from the two systems are combined. Values in paren-
40 °F (4 °C) and higher. Procedure B is for site temperatures
theses are conversions that are appropriately rounded for
below 40 °F (4 °C). Other suitable heat fusion joining proce-
accuracy and precision; that are not exact equivalents, and that
dures are available from various sources including pipe and
are for non-mandatory informational purposes.
fittingmanufacturers.Thisstandarddoesnotpurporttoaddress
1.7 This standard does not purport to address all of the
all possible heat fusion joining procedures, or to preclude the
safety concerns, if any, associated with its use. It is the
use of qualified procedures developed by other parties that
responsibility of the user of this standard to establish appro-
have been proved to produce reliable heat fusion joints.
priate safety, health, and environmental practices and deter-
1.2 The parameters and procedures are applicable only to
mine the applicability of regulatory limitations prior to use.
joining PA12 pipe and fittings and are not applicable to other
1.8 This international standard was developed in accor-
polyamide types. They are intended only for PA12 fuel gas
dance with internationally recognized principles on standard-
pipe per Specification F2785 and PA12 butt heat fusion fittings
ization established in the Decision on Principles for the
in accordance with Specification F1733. Fusion to other
Development of International Standards, Guides and Recom-
polyamide types (that is, cross-fusion) is not permitted under
mendations issued by the World Trade Organization Technical
this practice, and this practice does not not apply to other
Barriers to Trade (TBT) Committee.
polyamide types. Consult with the pipe and fittings manufac-
turerstomakesuretheyrecommendthisprocedureforthepipe
2. Referenced Documents
and fittings to be joined (also see Appendix X1).
2
2.1 ASTM Standards:
1.3 The procedures in this practice apply to the butt fusion
F412 Terminology Relating to Plastic Piping Systems
of PA12 pipe and butt fusion fittings in accordance with 1.2
F1733 Specification for Butt Heat Fusion Polyamide(PA)
having like diameter and wall thickness.
Plastic Fitting for Polyamide(PA) Plastic Pipe and Tubing
NOTE 1—Refer to X1.5 for guidance regarding dissimilar wall thick- F2785 Specification for Polyamide 12 Gas Pressure Pipe,
nesses.
Tubing, and Fittings
1.4 Other suitable heat joining procedures are available
3. Terminology
from various sources including pipe and fitting manufacturers.
Melt characteristics, average molecular weight and molecular
3.1 General—Definitions and abbreviations are in accor-
weight distribution of PA12 compounds are influential factors
dance with Terminology F412, unless otherwise specified.
in establishing suitable fusion parameters; therefore, consider
3.2 Definitions of Terms Specific to This Standard:
the manufacturer’s recommendations in the use or develop-
3.2.1 drag force, n—the force required to overcome the
ment of a specific fusion procedure.
static and dynamic resistance to motion of the movable
1.5 The text of this practice references notes, footnotes, and
carriage.
appendixes which provide explanatory material. These notes
3.2.2 fusion force, n—the force applied between the melted
and footnotes (excluding those in tables and figures) shall not
polymer pipe ends.
be considered as requirements of the practice.
1 2
This test method is under the jurisdiction of ASTM Committee F17 on Plastic For referenced ASTM standards, visit the ASTM website, www.astm.org, or
Piping Systems and is the direct responsibility of Subcommittee F17.20 on Joining. contact ASTM Customer Service at service@astm.org. F
...

Questions, Comments and Discussion

Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.

This May Also Interest You

ASTM
ASTM E751/E751M-17(2022)(Practice)
Standard Practice for Acoustic Emission Monitoring During Resistance Spot-Welding

SIGNIFICANCE AND USE
5.1 The AE produced during the production of a spot-weld can be related to weld quality parameters such as the strength and size of the nugget, the amount of expulsion, and the amount of cracking. Therefore, in-process AE monitoring can be used both as an examination method, and as a means for providing feedback control.
SCOPE
1.1 This practice describes procedures for the measurement, processing, and interpretation of the acoustic emission (AE) response associated with selected stages of the resistance spot-welding process.  
1.2 This practice also provides recommendations for feedback control by utilizing the measured AE response signals during the spot-welding process.  
1.3 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    7 pages
    English language
    sale 15% off
ASTM
ASTM E749/E749M-17(2021)(Practice)
Standard Practice for Acoustic Emission Monitoring During Continuous Welding

SIGNIFICANCE AND USE
4.1 Detection and location of AE sources in weldments during fabrication may provide information related to the integrity of the weld. Such information may be used to direct repair procedures on the weld or as a guide for application of other nondestructive evaluation (NDE) methods. A major attribute of applying AE for in-process monitoring of welds is the ability of the method to provide immediate real-time information on weld integrity. This feature makes the method useful to lower weld costs by repairing defects at the most convenient point in the production process. The AE activity from discontinuities in the weldment is stimulated by the thermal stresses from the welding process. The AE activity resulting from this stimulation is detected by AE sensors in the vicinity of the weldment, which convert the acoustic waves into electronic signals. The AE instrumentation processes signals and provides means for immediate display or indication of AE activity and for permanent recordings of the data.  
4.2 Items to be considered in preparation and planning for monitoring should include but not be limited to the following:  
4.2.1 Description of the system or object to be monitored or examined,  
4.2.2 Extent of monitoring, that is, entire weld, cover passes only, and so forth,  
4.2.3 Limitations or restrictions on the sensor mounting procedures, if applicable,  
4.2.4 Performance parameters to be established and maintained during the AE system verification procedure (sensitivity, location accuracy, and so forth),  
4.2.5 Maximum time interval between AE system verification checks,  
4.2.6 Performance criteria for purchased equipment,  
4.2.7 Requirements for permanent records of the AE response, if applicable,  
4.2.8 Content and format of test report, if required, and  
4.2.9 Operator qualification and certification, if required.
SCOPE
1.1 This practice provides recommendations for acoustic emission (AE) monitoring of weldments during and immediately following their fabrication by continuous welding processes.  
1.2 The procedure described in this practice is applicable to the detection and location of AE sources in weldments and in their heat-affected zone during fabrication, particularly in those cases where the time duration of welding is such that fusion and solidification take place while welding is still in progress.  
1.3 The effectiveness of acoustic emission to detect discontinuities in the weldment and the heat-affected zone is dependent on the design of the AE system, the AE system verification procedure, the weld process, and the material type. Materials that have been monitored include low-carbon steels, low-alloy steels, stainless steels, and some aluminum alloys. The system performance must be verified for each application by demonstrating that the defects of concern can be detected with the desired reliability.  
1.4 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    5 pages
    English language
    sale 15% off
ASTM
ASTM A370-23(Test Method)
Standard Test Methods and Definitions for Mechanical Testing of Steel Products

SIGNIFICANCE AND USE
4.1 The primary use of these test methods is testing to determine the specified mechanical properties of steel, stainless steel, and related alloy products for the evaluation of conformance of such products to a material specification under the jurisdiction of ASTM Committee A01 and its subcommittees as designated by a purchaser in a purchase order or contract.  
4.1.1 These test methods may be and are used by other ASTM Committees and other standards writing bodies for the purpose of conformance testing.  
4.1.2 The material condition at the time of testing, sampling frequency, specimen location and orientation, reporting requirements, and other test parameters are contained in the pertinent material specification or in a general requirement specification for the particular product form.  
4.1.3 Some material specifications require the use of additional test methods not described herein; in such cases, the required test method is described in that material specification or by reference to another appropriate test method standard.  
4.2 These test methods are also suitable to be used for testing of steel, stainless steel and related alloy materials for other purposes, such as incoming material acceptance testing by the purchaser or evaluation of components after service exposure.  
4.2.1 As with any mechanical testing, deviations from either specification limits or expected as-manufactured properties can occur for valid reasons besides deficiency of the original as-fabricated product. These reasons include, but are not limited to: subsequent service degradation from environmental exposure (for example, temperature, corrosion); static or cyclic service stress effects, mechanically-induced damage, material inhomogeneity, anisotropic structure, natural aging of select alloys, further processing not included in the specification, sampling limitations, and measuring equipment calibration uncertainty. There is statistical variation in all aspects of mechanical testin...
SCOPE
1.1 These test methods2 cover procedures and definitions for the mechanical testing of steels, stainless steels, and related alloys. The various mechanical tests herein described are used to determine properties required in the product specifications. Variations in testing methods are to be avoided, and standard methods of testing are to be followed to obtain reproducible and comparable results. In those cases in which the testing requirements for certain products are unique or at variance with these general procedures, the product specification testing requirements shall control.  
1.2 The following mechanical tests are described:    
Sections  
Tension  
7 to 14  
Bend  
15  
Hardness  
16  
Brinell  
17  
Rockwell  
18  
Portable  
19  
Impact  
20 to 30  
Keywords  
32  
1.3 Annexes covering details peculiar to certain products are appended to these test methods as follows:    
Annex  
Bar Products  
Annex A1  
Tubular Products  
Annex A2  
Fasteners  
Annex A3  
Round Wire Products  
Annex A4  
Significance of Notched-Bar Impact Testing  
Annex A5  
Converting Percentage Elongation of Round Specimens to
Equivalents for Flat Specimens  
Annex A6    
Testing Multi-Wire Strand  
Annex A7  
Rounding of Test Data  
Annex A8  
Methods for Testing Steel Reinforcing Bars  
Annex A9  
Procedure for Use and Control of Heat-cycle Simulation  
Annex A10  
1.4 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.5 When these test methods are referenced in a metric product specification, the yield and tensile values may be determined in inch-pound (ksi) units then converted into SI (MPa) units. The elongation determined in inch-pound gauge lengths of 2 in. or 8 in. may be report...

  • Standard
    51 pages
    English language
    sale 15% off
  • Standard
    51 pages
    English language
    sale 15% off
ASTM
ASTM F3565-23(Practice)
Standard Practice for Electrofusion Joining Polyethylene (PE) Pipe and Fittings for Pressure Pipe Service

SIGNIFICANCE AND USE
4.1 Using the procedures and apparatus in Sections 8 and 9 and the manufacturer's instructions, pressure-tight joints as strong as the pipe itself can be made between manufacturer-recommended combinations of pipe and fittings. See Specification F1055 for performance requirements of polyethylene electrofusion fittings.
SCOPE
1.1 This practice describes procedures for making joints suitable for pressure service with polyethylene (PE) pipe and fittings by means of electrofusion joining techniques in, but not limited to, a field environment. Other suitable electrofusion joining procedures are available from various sources including fitting manufacturers. This standard does not purport to address all possible electrofusion joining procedures, or to preclude the use of qualified procedures developed by other parties that have been proven to produce reliable electrofusion joints. (Note 1)
Note 1: Reference to the manufacturer in this practice refers to the electrofusion fitting manufacturer.  
1.2 The parameters and procedure are applicable only to joining polyethylene pipe and fittings (Note 2) which are intended for PE fuel gas pipe per Specification D2513 and PE potable water, sewer and industrial pipe manufactured per Specification F714, Specification D3035, Specification F2619, and AWWA C901 and C906.
Note 2: Commercially available materials classified with a thermoplastic pipe material designation code beginning with PE 14, PE 23, PE 24, PE 27, PE 33, PE 34, PE 36, and PE 46, and PE 47 in accordance with Specification D3350 and Terminology F412 are generally acceptable for electrofusion joining using this practice. Consult with the pipe or fitting manufacturer for specific compatibility information.  
1.3 Parts that are within the dimensional tolerances given in present ASTM specifications are required to produce sound joints between polyethylene pipe and fittings when using the joining techniques described in this practice.  
1.4 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.5 The text of this practice references notes, footnotes, and appendices which provide explanatory material. These notes and footnotes (excluding those in tables and figures) shall not be considered as requirements of the practice.  
1.6 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    7 pages
    English language
    sale 15% off
ASTM
ASTM D5141-23(Test Method)
Standard Test Method for Determining Filtering Efficiency and Flow Rate of the Filtration Component of a Sediment Retention Device

SIGNIFICANCE AND USE
5.1 This test method is used to determine the filtering efficiency and flow rate of the filtration component of a sediment retention device, such as a silt fence, a silt barrier, or a silt curtain, for specific soil tested.  
5.2 This test method may be used for the design of the filtration component of a sediment retention device to meet requirements of regulatory agencies in filtering efficiency or flow rate for the specific soil tested.  
5.2.1 The designer can use this test method to determine the spacing between sediment retention devices.  
5.3 This test method is intended for performance evaluation, as the results will depend on the specific soil evaluated. Unless testing with the default soil is desired, it is recommended that the user or representative perform the test to pre-approve products, as sediment retention device manufacturers are not typically equipped to handle or test soil requirements.  
5.4 This test method provides a means of evaluating the filtration component of sediment retention devices with different soils under various conditions that simulate the conditions that exist in a sediment retention device installation. This test method may be used to simulate several storm events on the same sediment retention device specimen. Therefore, the number of times this test is repeated per specimen is dependent upon the user and the site conditions.
SCOPE
1.1 This test method is used to determine the filtering efficiency and the flow rate of the filtration component of a sediment retention device, such as a silt fence, silt barrier, or inlet protector.  
1.1.1 The results are shown as a percentage for filtering efficiency and cubic metres per square metre per minute (m3/m2/min) or gallons per square foot per minute (gal/ft2/min) for flow rate.  
1.1.2 The filtering efficiency indicates the percent of sediment removed from sediment-laden water.  
1.1.3 The flow rate is the average rate of passage of the sediment-laden water through the filtration component of a sediment retention device.  
1.2 This test method requires several specialized pieces of equipment, such as an integrated water sampler and an analytical balance, or a vacuum filtration system. At the client’s discretion, the test soil is either a site-specific soil or a soil that is representative of a target default gradation.  
1.3 The values stated in SI units are the standard, while the inch-pound units are provided for information. The values expressed in each system may not be exact equivalents; therefore, each system must be used independently of the other, without combining values in any way.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    5 pages
    English language
    sale 15% off
  • Standard
    5 pages
    English language
    sale 15% off
ASTM
ASTM F2647-07(2023)(Guide)
Standard Guide for Approved Methods of Installing a CVS (Central Vacuum System)

SIGNIFICANCE AND USE
4.1 The suggestions of this guide are intended to provide proper installation materials and practices to be used during the installation of a central-vacuum system.
SCOPE
1.1 This guide demonstrates proper methods for installing a central-vacuum system.  
1.2 Appendix X1 contains additional sources of information that may be helpful to the user of this guide.  
1.3 The values stated in inch-pound units are to be regarded as the standard. The values given in parentheses are for information only.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Guide
    7 pages
    English language
    sale 15% off
ASTM
ASTM F2886-17(2023)(Specification)
Standard Specification for Metal Injection Molded Cobalt-28Chromium-6Molybdenum Components for Surgical Implant Applications

ABSTRACT
This specification covers chemical, mechanical, and metallurgical general requirements for metal injection molded (MIM) cobalt-28chromium-6molybddenum components to be used in manufacturing surgical implants. In this specification, the MIM components covered may have been densified beyond their as-sintered density by post-sinter processing. For the chemical requirements, the components supplied in this specification must conform in accordance to the chemical requirements specified herein in Table 1. The product analysis tolerances must also conform to the product tolerances presented in Table 2. The specification also enumerates the mechanical requirements for MIM components wherein the tensile properties of the MIM must conform to the mechanical properties in Table 3. The microstructural requirements and specimen preparation shall be in accordance with Guide E3 and Practice E407.
SCOPE
1.1 This specification covers chemical, mechanical, and metallurgical requirements for metal injection molded (MIM) cobalt-28chromium-6molybdenum components to be used in the manufacture of surgical implants  
1.2 The MIM components covered by this specification may have been densified beyond their as-sintered density by post-sinter processing.  
1.3 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    5 pages
    English language
    sale 15% off
ASTM
ASTM A480/A480M-23a(Specification)
Standard Specification for General Requirements for Flat-Rolled Stainless and Heat-Resisting Steel Plate, Sheet, and Strip

ABSTRACT
This specification covers general requirements for flat-rolled stainless and heat-resisting steel plate, sheet, and strip. The steel shall be made by one of the following processes: electric-arc, electric-induction, or other suitable processes. Heat and product analyses shall conform to the chemical requirements for each of the specific elements. The material shall undergo mechanical tests such as tension test, hardness test, and bend test. Special tests like intergranular corrosion test, permeability test, Charpy impact testing and tests for detrimental intermetallic phases in wrought duplex stainless steels shall be also be performed when required.
SCOPE
1.1 This specification2 covers a group of general requirements that, unless otherwise specified in the purchase order or in an individual specification, shall apply to rolled steel plate, sheet, and strip, under each of the following specifications issued by ASTM: Specifications A240/A240M, A263, A264, A265, A666, A693, A793, and A895.  
1.2 In the case of conflict between a requirement of a product specification and a requirement of this specification, the product specification shall prevail. In the case of conflict between a requirement of the product specification or a requirement of this specification and a more stringent requirement of the purchase order, the purchase order shall prevail. The purchase order requirements shall not take precedence if they, in any way, violate the requirements of the product specification or this specification; for example, by waiving a test requirement or by making a test requirement less stringent.  
1.3 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The SI units are shown in brackets, except that when A480M is specified, Annex A3 shall apply for the dimensional tolerances and not the bracketed SI values in Annex A2. The values stated in each system are not necessarily exact equivalents; therefore, to ensure conformance with the standard, each system shall be used independently of the other, and values from the two systems shall not be combined.  
1.4 This specification and the applicable material specifications are expressed in both inch-pound and SI units. However, unless the order specifies the applicable “M” specification designation [SI units], the material shall be furnished in inch-pound units.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Technical specification
    26 pages
    English language
    sale 15% off
  • Technical specification
    26 pages
    English language
    sale 15% off
ASTM
ASTM E2552-23(Guide)
Standard Guide for Assessing the Environmental and Human Health Impacts of New Compounds for Military Use

SIGNIFICANCE AND USE
5.1 The purpose of this guide is to provide a logical, tiered approach in the development of environmental health criteria coincident with level and effort in the research, development, testing, and evaluation of new materials for military use. Various levels of uncertainty are associated with data collected from previous stages. Following the recommendation in the guide should reduce the relative uncertainty of the data collected at each developmental stage. At each stage, a general weight of evidence qualifier shall accompany each exposure/effect relationship. They may be simple (for example, low, medium, or high confidence) or sophisticated using a numerical value for each predictor as a multiplier to ascertain relative confidence in each step of risk characterization. The specific method used will depend on the stage of development, quantity and availability of data, variation in the measurement, and general knowledge of the dataset. Since specific formulations, conditions, and use scenarios may not be known until the later stages, exposure estimates can be determined when practical (for example, Engineering and Manufacturing Development; see 6.6). Exposure data can then be used with other toxicological data collected from previous stages in a quantitative risk assessment to determine the relative degree of hazard.  
5.2 Data developed from the use of this guide are designed to be consistent with criteria required in weapons and weapons system development (for example, programmatic environment, safety and occupational health evaluations, environmental assessments/environmental impact statements, toxicity clearances, and technical data sheets).  
5.3 Information shall be evaluated in a flexible manner consistent with the needs of the authorizing program. This requires proper characterization of the current problem. For example, compounds may be ranked relative to the environmental criteria of the prospective alternatives, the replacement compound, and within bo...
SCOPE
1.1 This guide is intended to determine the relative environmental influence of new substances, consistent with the research and development (R&D) level of effort and is intended to be applied in a logical, tiered manner that parallels both the available funding and the stage of research, development, testing, and evaluation. Specifically, conservative assumptions, relationships, and models are recommended early in the research stage, and as the technology is matured, empirical data will be developed and used. Munition constituents are included and may include propellants, oxidizers, explosives, binders, stabilizers, metals, dyes, and other compounds used in the formulation to produce a desired effect. Munition systems range from projectiles, grenades, rockets/missiles, training simulators, to smokes and obscurants. Given the complexity of issues involved in the assessment of environmental fate and effects and the diversity of the systems used, this guide is broad in scope and not intended to address every factor that may be important in an environmental context. Rather, it is intended to reduce uncertainty at minimal cost by considering the most important factors related to human health and environmental impacts of energetic materials. This guide provides an outline for collecting data useful in a relative ranking procedure to provide the systems scientist with a sound basis for prospectively determining a selection of candidates based on environmental and human health criteria. The general principles in this guide are applicable to substances other than energetics if intended to be used in a similar manner with similar exposure profiles.  
1.2 The scope of this guide includes:  
1.2.1 Energetic and other new/novel materials and compositions in all stages of research, development, test and evaluation.  
1.2.2 Environmental assessment, including:
1.2.2.1 Human and ecological effects of the unexploded energetics and ...

  • Guide
    9 pages
    English language
    sale 15% off
  • Guide
    9 pages
    English language
    sale 15% off
ASTM
ASTM D8042-18(2023)(Test Method)
Test Method for Shrinkage Temperature of Wet Blue and Wet White

SIGNIFICANCE AND USE
5.1 This test method is designed to determine the temperature at which the Wet Blue or Wet White specimen experiences shrinkage. In this test method, shrinkage occurs as a result of hydrothermal denaturation of the collagen protein molecules which make up the fiber structure of the Wet Blue or Wet White. The shrinkage temperature of Wet Blue or Wet White is influenced by many different factors, most of which appear to affect the number and nature of crosslinking interactions between adjacent polypeptide chains of the collagen protein molecules. The value of the shrinkage temperature of Wet Blue or Wet White is commonly used as an indicator of the type of tannage or the degree of tannage, or both, of that particular Wet Blue or Wet White (especially for the more hydrothermally stable tannages such as chrome tannage).
SCOPE
1.1 This test method covers the determination of the shrinkage temperature of all types of Wet Blue and Wet White. The heating medium is water when the shrinkage temperature is at or below 98 °C. The heating medium is a glycerine-water solution when the shrinkage temperature is above 98 °C.  
1.2 The values stated in SI units are to be regarded as the standard. The values in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

  • Standard
    3 pages
    English language
    sale 15% off