IEC 60371-2:2004

Specification for insulating materials based on mica - Part 2: Methods of test

Defines the methods of test which are applicable to built-up mica materials, products based on them and mica paper. The main changes from the previous edition are as follows: a) All clauses re-numbered. b) Relevant template of ISO 67 has been added to this standard as Annex A. c) Clause 8: Tensile strength and elongation at break Procedure modified to give "rate of movement" instead of "time limit". Different rate of movement for raw mica as opposed to reinforced and/or impregnated mica. d) Clause 11: Stiffness Size of test specimen revised. Wording modified so that standard covers materials using carriers other than woven glass cloth and materials that are 3-ply. Revision of terms ""machine direction" and "transverse direction". (These were incorrect in second edition (1987).) e) Clause 13: Elastic compression and plastic compression Tolerance on measurement of height of stack changed to within 0,01 mm. Times for change in pressure in procedure changed to 1 min. f) Clause 16: Electric strength Modified in line with Amendment 1 (1994) to the second edition (1987). Changes relate to latest edition of IEC 60243-1. g) Clause 19: Detection of defects and conductive particles Revised subclause.

Spécification pour les matériaux isolants à base de mica - Partie 2: Méthodes d'essais

Définit les méthodes d'essais qui sont applicables aux matériaux à base de mica, aux produits qui en sont issus et au papier de mica. Les changements par rapport à l'édition précédente sont les suivants: a) Tous les articles ont été renumérotés b) Le modèle de l'ISO 67 a été ajouté à cette norme comme Annexe A c) Dans l'Article 8 : Résistance à la traction et allongement à la rupture La procédure modifiée indique " vitesse du mouvement " au lieu de " limite de temps ". La vitesse du mouvement pour le mica pur est différente de celle du mica renforcé et/ou imprégné. d) Dans l' Article 11: Rigidité La taille des éprouvettes a été revue. Certains termes ont été modifiés car cette norme couvre des matériaux utilisés pour d'autres fonctions comme les revêtements en laine de verre ou les matériaux triplex. Révision des termes " sens de fafrication " et " sens perpendiculaire ". (Ils étaient incorrects dans la deuxième édition (1987).) e) Article 13: Compressibilité élastique et compressibilité plastique La tolérances dans la mesure de la hauteur de la pile a été changée pour " à 0,01 mm près " Le temps de changement de la pression dans le mode opératoire a été changé en 1 min. f) Article 16: Rigidité diélectrique Insertion de l'Amendement 1 (1984) à la deuxième édition (1987). Modifications en relation avec la dernière édition de la CEI 60243-1. g) Article 19: Recherche des défauts et des particules conductrices Révision du paragraphe.

General Information

• Status: Published
• Publication Date: 22-Jun-2004
• ICS: 17.220.99 - Other standards related to electricity and magnetism
• ICS: 29.035.50 - Mica based materials
• Technical Committee: TC 15 - Solid electrical insulating materials
• Drafting Committee: MT 11 - TC 15/MT 11
• Current Stage: PPUB - Publication issued
• Start Date: 23-Jun-2004
• Completion Date: 31-Aug-2004

Overview

IEC 60371-2:2004 is an international standard developed by the International Electrotechnical Commission (IEC) that specifies detailed methods of test for insulating materials based on mica. This standard applies to built-up mica materials, products made from them, and mica paper. It is the third edition and introduces significant updates to testing procedures to ensure industry-wide consistency, quality assurance, and reliability in mica-based electrical insulating materials.

IEC 60371-2:2004 is integral for manufacturers and quality control professionals who require precise test methodologies for determining physical, mechanical, and electrical properties of mica insulation products. The document details specimen preparation, test apparatus, procedures, and result interpretation for a comprehensive suite of tests essential to material performance verification.

Key Topics

This standard covers a broad range of testing methods specific to mica insulation materials, including but not limited to:

• Specimen Preparation: Methods for preparing test samples from curable mica materials, ensuring uniformity and accuracy of test results.

• Physical Properties:

  • Thickness measurement with defined test apparatus and procedures.
  • Determination of density and calculated density.
  • Composition analysis including binder content, mica content, and size of mica splittings.

• Mechanical Properties:

  • Tensile strength and elongation at break, with modifications to procedures for different mica types.
  • Flexural strength and elastic modulus in bending.
  • Folding and stiffness measurements, including conditioning and atmosphere control.
  • Elastic and plastic compressibility tests with precise measurement tolerances.

• Electrical Properties:

  • Dielectric rigidity according to the latest IEC 60243-1 standard.
  • Dissipation factor characterization across specific frequency and temperature ranges.
  • Detection of defects and conductive particles within mica products to identify material faults.

• Additional Testing:

  • Resistance to exudation and displacement to assess material stability under stress.
  • Resin flow and consolidation for hardened mica materials.
  • Gelation time determination.

This edition of the IEC 60371-2 standard also incorporates a relevant testing template from ISO 67 as Annex A for enhanced harmonization.

Applications

IEC 60371-2:2004 applies primarily to:

• Electrical Equipment Manufacturers: Ensures that mica insulating materials used in transformers, electrical machines, and high-voltage equipment meet stringent quality and performance standards.

• Material Testing Laboratories: Provides standardized test methods for evaluation and certification of mica-based insulating materials.

• Research and Development: Assists in the development of new mica-based composites with optimized mechanical and electrical properties.

• Quality Assurance: Facilitates thorough verification of manufacturing processes and product conformity with international standards, reducing risks of insulation failure.

• Regulatory Compliance: Supports adherence to safety and performance regulations in electrical equipment certifications globally.

Related Standards

IEC 60371-2:2004 complements other international standards, including:

• IEC 60243-1 – Tests on electric strength of insulating materials, which IEC 60371-2 aligns with for dielectric testing.

• ISO 67 – Provides a template for test reporting included in Annex A of the standard.

• Additional parts of IEC 60371 series, specifying material characteristics and product requirements for mica insulation.

By following IEC 60371-2:2004, stakeholders in the electrical insulation field can ensure that mica-based materials undergo rigorous and internationally recognized testing procedures, guaranteeing high reliability, durability, and safety in their applications. This standard plays a vital role in supporting innovation and quality control across the mica insulation industry.

Standards Content (Sample)

NORME CEI
INTERNATIONALE
IEC
60371-2
INTERNATIONAL
Troisième édition
STANDARD
Third edition
2004-06
Spécification pour les matériaux isolants
à base de mica –
Partie 2:
Méthodes d'essais
Specification for insulating materials
based on mica –
Part 2:
Methods of test
Numéro de référence
Reference number
CEI/IEC 60371-2:2004
Numérotation des publications Publication numbering
Depuis le 1er janvier 1997, les publications de la CEI As from 1 January 1997 all IEC publications are
sont numérotées à partir de 60000. Ainsi, la CEI 34-1 issued with a designation in the 60000 series. For
devient la CEI 60034-1. example, IEC 34-1 is now referred to as IEC 60034-1.
Editions consolidées Consolidated editions
Les versions consolidées de certaines publications de la The IEC is now publishing consolidated versions of its
CEI incorporant les amendements sont disponibles. Par publications. For example, edition numbers 1.0, 1.1
exemple, les numéros d’édition 1.0, 1.1 et 1.2 indiquent and 1.2 refer, respectively, to the base publication,
respectivement la publication de base, la publication de the base publication incorporating amendment 1 and
base incorporant l’amendement 1, et la publication de the base publication incorporating amendments 1
base incorporant les amendements 1 et 2. and 2.
Informations supplémentaires Further information on IEC publications
sur les publications de la CEI
Le contenu technique des publications de la CEI est The technical content of IEC publications is kept
constamment revu par la CEI afin qu'il reflète l'état under constant review by the IEC, thus ensuring that
actuel de la technique. Des renseignements relatifs à the content reflects current technology. Information
cette publication, y compris sa validité, sont dispo- relating to this publication, including its validity, is
nibles dans le Catalogue des publications de la CEI available in the IEC Catalogue of publications
(voir ci-dessous) en plus des nouvelles éditions, (see below) in addition to new editions, amendments
amendements et corrigenda. Des informations sur les and corrigenda. Information on the subjects under
sujets à l’étude et l’avancement des travaux entrepris consideration and work in progress undertaken by the
par le comité d’études qui a élaboré cette publication, technical committee which has prepared this
ainsi que la liste des publications parues, sont publication, as well as the list of publications issued,
également disponibles par l’intermédiaire de: is also available from the following:
• Site web de la CEI (www.iec.ch) • IEC Web Site (www.iec.ch)
• Catalogue des publications de la CEI • Catalogue of IEC publications
Le catalogue en ligne sur le site web de la CEI The on-line catalogue on the IEC web site
(www.iec.ch/searchpub) vous permet de faire des (www.iec.ch/searchpub) enables you to search by a
recherches en utilisant de nombreux critères, variety of criteria including text searches,
comprenant des recherches textuelles, par comité technical committees and date of publication. On-
d’études ou date de publication. Des informations en line information is also available on recently
ligne sont également disponibles sur les nouvelles issued publications, withdrawn and replaced
publications, les publications remplacées ou retirées, publications, as well as corrigenda.
ainsi que sur les corrigenda.
• IEC Just Published • IEC Just Published
Ce résumé des dernières publications parues This summary of recently issued publications
(www.iec.ch/online_news/justpub) est aussi dispo- (www.iec.ch/online_news/justpub) is also available
nible par courrier électronique. Veuillez prendre by email. Please contact the Customer Service
contact avec le Service client (voir ci-dessous) Centre (see below) for further information.
pour plus d’informations.
• Service clients • Customer Service Centre
Si vous avez des questions au sujet de cette If you have any questions regarding this
publication ou avez besoin de renseignements publication or need further assistance, please
supplémentaires, prenez contact avec le Service contact the Customer Service Centre:
clients:
Email: [e-mail] Email: [e-mail]
Tél: [phone] Tel: [phone]
Fax: [phone] Fax: [phone]
.
NORME CEI
INTERNATIONALE
IEC
60371-2
INTERNATIONAL
Troisième édition
STANDARD
Third edition
2004-06
Spécification pour les matériaux isolants
à base de mica –
Partie 2:
Méthodes d'essais
Specification for insulating materials
based on mica –
Part 2:
Methods of test
 IEC 2004 Droits de reproduction réservés  Copyright - all rights reserved
Aucune partie de cette publication ne peut être reproduite ni No part of this publication may be reproduced or utilized in any
utilisée sous quelque forme que ce soit et par aucun procédé, form or by any means, electronic or mechanical, including
électronique ou mécanique, y compris la photocopie et les photocopying and microfilm, without permission in writing from
microfilms, sans l'accord écrit de l'éditeur. the publisher.
International Electrotechnical Commission, 3, rue de Varembé, PO Box 131, CH-1211 Geneva 20, Switzerland
Telephone: [phone] Telefax: [phone] E-mail: [e-mail] Web: www.iec.ch
CODE PRIX
U
PRICE CODE
Commission Electrotechnique Internationale
International Electrotechnical Commission
МеждународнаяЭлектротехническаяКомиссия
Pour prix, voir catalogue en vigueur
For price, see current catalogue

– 2 – 60371-2  CEI:2004
SOMMAIRE
AVANT-PROPOS.6
INTRODUCTION.10

1 Domaine d’application.12
2 Références normatives.12
3 Méthodes de préparation des éprouvettes pour matériaux durcissables.12
3.1 Généralités.12
3.2 Méthode 1.12
3.3 Méthode 2.14
4 Epaisseur.16
4.1 Appareillage d’essai.16
4.2 Eprouvette.16
4.3 Mode opératoire.18
4.4 Expression des résultats.20
5 Masse volumique.20
6 Masse volumique calculée.20
7 Composition.20
7.1 Eprouvette.20
7.2 Masse surfacique à l’état de réception .20
7.3 Teneur en matières volatiles et masse surfacique du matériau séché.20
7.4 Teneur en liant.22
7.5 Masse surfacique du matériau de renforcement (m′ ) .24
r
7.6 Teneur en mica .26
7.7 Dimension des clivures.26
8 Résistance à la traction et allongement à la rupture .28
8.1 Appareillage d’essai.28
8.2 Eprouvette.28
8.3 Mode opératoire.28
8.4 Expression des résultats.28
9 Résistance à la flexion et module d’élasticité en flexion.30
9.1 Eprouvette.30
9.2 Mode opératoire.30
10 Pliage.30
11 Rigidité.30
11.1 Conditionnement des éprouvettes et atmosphère d’essai .30
11.2 Eprouvettes.30
11.3 Mode opératoire.30
11.4 Expression des résultats.32
12 Résistance à l’exsudation et au glissement .32
12.1 Appareillage d’essai.32
12.2 Eprouvette.32
12.3 Mode opératoire.32
12.4 Expression des résultats.34

60371-2  IEC:2004 – 3 –
CONTENTS
FOREWORD.7
INTRODUCTION.11

1 Scope.13
2 Normative references.13
3 Preparation methods of test specimens for curable materials .13
3.1 General.13
3.2 Method 1.13
3.3 Method 2.15
4 Thickness.17
4.1 Test apparatus.17
4.2 Test specimen.17
4.3 Procedure.19
4.4 Statement of results.21
5 Density.21
6 Calculated density.21
7 Composition.21
7.1 Test specimen.21
7.2 Mass per unit area in the "as received" condition .21
7.3 Content of volatiles and mass per unit area of dried material.21
7.4 Binder content.23
’
7.5 Mass per unit area of reinforcement material (m′ ) .25
r
7.6 Mica content.27
7.7 Size of splittings.27
8 Tensile strength and elongation at break .29
8.1 Test apparatus.29
8.2 Test specimen.29
8.3 Procedure.29
8.4 Statement of results.29
9 Flexural strength and elastic modulus in bend .31
9.1 Test specimen.31
9.2 Procedure.31
10 Folding.31
11 Stiffness.31
11.1 Conditioning and test atmosphere .31
11.2 Test specimens.31
11.3 Procedure.31
11.4 Statement of results.33
12 Resistance to exudation and displacement .33
12.1 Test apparatus.33
12.2 Test specimen.33
12.3 Procedure.33
12.4 Statement of results.35

– 4 – 60371-2  CEI:2004
13 Compressibilité élastique et compressibilité plastique.34
13.1 Appareil d'essai.34
13.2 Eprouvette.34
13.3 Mode opératoire.34
13.4 Expression des résultats.36
14 Ecoulement de résine et consolidation.36
14.1 Eprouvette.36
14.2 Mode opératoire.36
14.3 Expression des résultats.38
15 Temps de gélification .38
16 Rigidité diélectrique.38
16.1 Electrodes.38
16.2 Eprouvettes.40
16.3 Mode opératoire.40
16.4 Expression des résultats.40
17 Caractéristique du facteur de dissipation/température aux fréquences de 48 Hz à 62 Hz .40
17.1 Eprouvette.40
17.2 Conditions d’essai.40
17.3 Electrodes.40
17.4 Mode opératoire.40
17.5 Expression des résultats.42
18 Caractéristique du facteur de dissipation/tension aux fréquences de 48 Hz à 62 Hz .42
18.1 Eprouvette.42
18.2 Conditions d’essai.42
18.3 Electrodes.42
18.4 Mode opératoire.42
18.5 Expression des résultats.42
19 Recherche des défauts et des particules conductrices.42
20 Pénétration.42
20.1 Appareillage d’essai.42
20.2 Eprouvettes.44
20.3 Méthode d’essais.44
20.4 Rapport d’essai.44
21 Endurance thermique.44

Annexe A (normative) .54

Figure 1 – Montage des empilages pour la préparation des éprouvettes stratifiées .46
Figure 2 – Conditions pour la méthode de pressage .46
Figure 3 – Appareil pour mesurer la rigidité (Vue de profil) .48
Figure 4 – Appareil pour mesurer la rigidité .48
Figure 5 – Compressibilité élastique, compressibilité plastique .50
Figure 6 – Pénétromètre Williams de modèle standard .52

60371-2  IEC:2004 – 5 –
13 Elastic compression and plastic compression .35
13.1 Test apparatus.35
13.2 Test specimen.35
13.3 Procedure.35
13.4 Statement of results.37
14 Resin flow and consolidation .37
14.1 Test specimen.37
14.2 Procedure.37
14.3 Statement of results.39
15 Gel time.39
16 Electric strength.39
16.1 Electrodes.39
16.2 Test specimen.41
16.3 Procedure.41
16.4 Statement of results.41
17 Dissipation factor/temperature characteristics at frequencies of between 48 Hz
and 62 Hz.41
17.1 Test specimen.41
17.2 Test conditions.41
17.3 Electrodes.41
17.4 Procedure.41
17.5 Statement of results.43
18 Dissipation factor/voltage characteristics at frequencies of between 48 Hz and
62 Hz .43
18.1 Test specimen.43
18.2 Test conditions.43
18.3 Electrodes.43
18.4 Procedure.43
18.5 Statement of results.43
19 Detection of defects and conductive particles .43
20 Penetration.43
20.1 Test apparatus.43
20.2 Test specimens.45
20.3 Method of test .45
20.4 Statement of results.45
21 Thermal endurance.45

Annex A (normative) .55

Figure 1 – Assembly of stacks for preparing test laminates.47
Figure 2 – Conditions for press procedure .47
Figure 3 – Apparatus for measurement of stiffness .49
Figure 4 – Apparatus for measurement of stiffness .49
Figure 5 – Elastic compression, plastiac compression.51
Figure 6 – Standard Williams type penetrometer.53

– 6 – 60371-2  CEI:2004
COMMISSION ÉLECTROTECHNIQUE INTERNATIONALE
___________
SPÉCIFICATION POUR LES MATÉRIAUX ISOLANTS
À BASE DE MICA –
Partie 2: Méthodes d’essais
AVANT-PROPOS
1) La Commission Electrotechnique Internationale (CEI) est une organisation mondiale de normalisation
composée de l'ensemble des comités électrotechniques nationaux (Comités nationaux de la CEI). La CEI a
pour objet de favoriser la coopération internationale pour toutes les questions de normalisation dans les
domaines de l'électricité et de l'électronique. A cet effet, la CEI – entre autres activités – publie des Normes
internationales, des Spécifications techniques, des Rapports techniques, des Spécifications accessibles au
public (PAS) et des Guides (ci-après dénommés "Publication(s) de la CEI"). Leur élaboration est confiée à des
comités d'études, aux travaux desquels tout Comité national intéressé par le sujet traité peut participer. Les
organisations internationales, gouvernementales et non gouvernementales, en liaison avec la CEI, participent
également aux travaux. La CEI collabore étroitement avec l'Organisation Internationale de Normalisation (ISO),
selon des conditions fixées par accord entre les deux organisations.
2) Les décisions ou accords officiels de la CEI concernant les questions techniques représentent, dans la mesure
du possible, un accord international sur les sujets étudiés, étant donné que les Comités nationaux de la CEI
intéressés sont représentés dans chaque comité d’études.
3) Les Publications de la CEI se présentent sous la forme de recommandations internationales et sont agréées
comme telles par les Comités nationaux de la CEI. Tous les efforts raisonnables sont entrepris afin que la CEI
s'assure de l'exactitude du contenu technique de ses publications; la CEI ne peut pas être tenue responsable
de l'éventuelle mauvaise utilisation ou interprétation qui en est faite par un quelconque utilisateur final.
4) Dans le but d'encourager l'uniformité internationale, les Comités nationaux de la CEI s'engagent, dans toute la
mesure possible, à appliquer de façon transparente les Publications de la CEI dans leurs publications
nationales et régionales. Toutes divergences entre toutes Publications de la CEI et toutes publications
nationales ou régionales correspondantes doivent être indiquées en termes clairs dans ces dernières.
5) La CEI n’a prévu aucune procédure de marquage valant indication d’approbation et n'engage pas sa
responsabilité pour les équipements déclarés conformes à une de ses Publications.
6) Tous les utilisateurs doivent s'assurer qu'ils sont en possession de la dernière édition de cette publication.
7) Aucune responsabilité ne doit être imputée à la CEI, à ses administrateurs, employés, auxiliaires ou
mandataires, y compris ses experts particuliers et les membres de ses comités d'études et des Comités
nationaux de la CEI, pour tout préjudice causé en cas de dommages corporels et matériels, ou de tout autre
dommage de quelque nature que ce soit, directe ou indirecte, ou pour supporter les coûts (y compris les frais
de justice) et les dépenses découlant de la publication ou de l'utilisation de cette Publication de la CEI ou de
toute autre Publication de la CEI, ou au crédit qui lui est accordé.
8) L'attention est attirée sur les références normatives citées dans cette publication. L'utilisation de publications
référencées est obligatoire pour une application correcte de la présente publication.
9) L’attention est attirée sur le fait que certains des éléments de la présente Publication de la CEI peuvent faire
l’objet de droits de propriété intellectuelle ou de droits analogues. La CEI ne saurait être tenue pour
responsable de ne pas avoir identifié de tels droits de propriété et de ne pas avoir signalé leur existence.
La Norme internationale CEI 60371-2 a été établie par le sous-comité 15C: Spécifications, du
comité d’études 15 de la CEI: Matériaux isolants.
Cette troisième édition de la CEI 60371-2 annule et remplace la deuxième édition parue en
1987 et son amendement 1 (1994), et constitue une révision technique.
Les changements par rapport à l’édition précédente sont les suivants:
a) Tous les articles ont été renumérotés.
b) Le modèle de l’ISO 67 a été ajouté à cette norme comme Annexe A.
c) Dans l’Article 8 : Résistance à la traction et allongement à la rupture
La procédure modifiée indique « vitesse du mouvement » au lieu de « limite de temps ».
La vitesse du mouvement pour le mica pur est différente de celle du mica renforcé et/ou
imprégné
60371-2  IEC:2004 – 7 –
INTERNATIONAL ELECTROTECHNICAL COMMISSION
____________
SPECIFICATION FOR INSULATING MATERIALS
BASED ON MICA –
Part 2: Methods of test
FOREWORD
1) The International Electrotechnical Commission (IEC) is a worldwide organization for standardization comprising
all national electrotechnical committees (IEC National Committees). The object of IEC is to promote
international co-operation on all questions concerning standardization in the electrical and electronic fields. To
this end and in addition to other activities, IEC publishes International Standards, Technical Specifications,
Technical Reports, Publicly Available Specifications (PAS) and Guides (hereafter referred to as “IEC
Publication(s)”). Their preparation is entrusted to technical committees; any IEC National Committee interested
in the subject dealt with may participate in this preparatory work. International, governmental and non-
governmental organizations liaising with the IEC also participate in this preparation. IEC collaborates closely
with the International Organization for Standardization (ISO) in accordance with conditions determined by
agreement between the two organizations.
2) The formal decisions or agreements of IEC on technical matters express, as nearly as possible, an international
consensus of opinion on the relevant subjects since each technical committee has representation from all
interested IEC National Committees.
3) IEC Publications have the form of recommendations for international use and are accepted by IEC National
Committees in that sense. While all reasonable efforts are made to ensure that the technical content of IEC
Publications is accurate, IEC cannot be held responsible for the way in which they are used or for any
misinterpretation by any end user.
4) In order to promote international uniformity, IEC National Committees undertake to apply IEC Publications
transparently to the maximum extent possible in their national and regional publications. Any divergence
between any IEC Publication and the corresponding national or regional publication shall be clearly indicated in
the latter.
5) IEC provides no marking procedure to indicate its approval and cannot be rendered responsible for any
equipment declared to be in conformity with an IEC Publication.
6) All users should ensure that they have the latest edition of this publication.
7) No liability shall attach to IEC or its directors, employees, servants or agents including individual experts and
members of its technical committees and IEC National Committees for any personal injury, property damage or
other damage of any nature whatsoever, whether direct or indirect, or for costs (including legal fees) and
expenses arising out of the publication, use of, or reliance upon, this IEC Publication or any other IEC
Publications.
8) Attention is drawn to the Normative references cited in this publication. Use of the referenced publications is
indispensable for the correct application of this publication.
9) Attention is drawn to the possibility that some of the elements of this IEC Publication may be the subject of
patent rights. IEC shall not be held responsible for identifying any or all such patent rights.
International Standard IEC 60371-2 has been prepared by subcommittee 15C: Specifications,
of IEC technical committee 15: Insulating materials. prescription
This third edition of IEC 60371-2 cancels and replaces the second edition, published in 1987,
and its amendment 1 (1994), and constitutes a technical revision.
The main changes from the previous edition are as follows:
a) All clauses re-numbered.
b) Relevant template of ISO 67 has been added to this standard as Annex A.
c) Clause 8: Tensile strength and elongation at break
Procedure modified to give “rate of movement” instead of "time limit". Different rate of
movement for raw mica as opposed to reinforced and/or impregnated mica.

– 8 – 60371-2  CEI:2004
d) Dans l’ Article 11: Rigidité
La taille des éprouvettes a été revue. Certains termes ont été modifiés car cette norme
couvre des matériaux utilisés pour d’autres fonctions comme les revêtements en laine de
verre ou les matériaux triplex. Révision des termes « sens de fafrication » et « sens
perpendiculaire ». (Ils étaient incorrects dans la deuxième édition (1987).)
e) Article 13: Compressibilité élastique et compressibilité plastique
La tolérances dans la mesure de la hauteur de la pile a été changée pour « à 0,01 mm
près »
Le temps de changement de la pression dans le mode opératoire a été changé en 1 min.
f) Article 16: Rigidité diélectrique
Insertion de l’Amendement 1 (1984) à la deuxième édition (1987). Modifications en
relation avec la dernière édition de la CEI 60243-1.
g) Article 19: Recherche des défauts et des particules conductrices
Révision du paragraphe.
Le texte de cette norme est issu des documents suivants:
FDIS Rapport de vote
15C/1610/FDIS 15C/1643/RVD
Le rapport de vote indiqué dans le tableau ci-dessus donne toute information sur le vote ayant
abouti à l'approbation de cette norme.
Cette publication a été rédigée selon les Directives ISO/CEI, Partie 2.
Le comité a décidé que le contenu de cette publication ne sera pas modifié avant la date de
maintenance indiquée sur le site web de la CEI sous «http://webstore.iec.ch» dans les
données relatives à la publication recherchée. A cette date, la publication sera
• reconduite;
• supprimée;
• remplacée par une édition révisée, ou
• amendée.
60371-2  IEC:2004 – 9 –
d) Clause 11: Stiffness
Size of test specimen revised. Wording modified so that standard covers materials using
carriers other than woven glass cloth and materials that are 3-ply. Revision of terms
"“machine direction” and “transverse direction”. (These were incorrect in second edition
(1987).)
e) Clause 13: Elastic compression and plastic compression
Tolerance on measurement of height of stack changed to within 0,01 mm.
Times for change in pressure in procedure changed to 1 min.
f) Clause 16: Electric strength
Modified in line with Amendment 1 (1994) to the second edition (1987). Changes relate to
latest edition of IEC 60243-1.
g) Clause 19: Detection of defects and conductive particles
Revised subclause.
The text of this standard is based on the following documents:
FDIS Report on voting
15C/1610/FDIS 15C/1643/RVD
Full information on the voting for the approval of this standard can be found in the report on
voting indicated in the above table.
This publication has been drafted in accordance with the ISO/IEC Directives, Part 2.
The committee has decided that the contents of this publication will remain unchanged until
the maintenance result date indicated on the IEC web site under "http://webstore.iec.ch" in
the data related to the specific publication. At this date, the publication will be
• reconfirmed;
• withdrawn;
• replaced by a revised edition, or
• amended.
– 10 – 60371-2  CEI:2004
INTRODUCTION
La présente partie de la CEI 60371 fait partie d'une série traitant de matériaux isolants à base
de clivures de mica ou de papier mica, avec ou sans renforcement qui sont utilisés dans
l'équipement électrique, ainsi que du papier mica à l'état pur.
La CEI 60371 comprend trois parties présentées sous le titre général Spécification pour les
matériaux isolants à base de mica:
Partie 1: Définitions et exigences générales
Partie 2: Méthodes d'essais
Partie 3: Spécifications pour matériaux particuliers

60371-2  IEC:2004 – 11 –
INTRODUCTION
This part of IEC 60371 is one of a series which deals with insulating materials for use in
electrical equipment built up from mica splittings or mica paper, with or without reinforcement,
and with mica paper in its pure state.
IEC 60371 consists of three parts under the main title Specification for insulating materials
based on mica:
Part 1 Definitions and general requirements
Part 2 Methods of test
Part 3 Specifications for individual materials

– 12 – 60371-2  CEI:2004
SPÉCIFICATION POUR LES MATÉRIAUX ISOLANTS
À BASE DE MICA –
Partie 2: Méthodes d’essais
1 Domaine d’application
La présente partie de la CEI 60371 définit les méthodes d'essais qui sont applicables aux
matériaux à base de mica, aux produits qui en sont issus et au papier de mica.
2 Références normatives
Les documents de référence suivants sont indispensables pour l'application du présent
document. Pour les références datées, seule l'édition citée s'applique. Pour les références
non datées, la dernière édition du document de référence s'applique (y compris les éventuels
amendements).
CEI 60216 (toutes les parties), Matériaux isolants électriques – Propriétés d'endurance
thermique
CEI 60243-1:1998, Rigidité diélectrique des matériaux isolants – Méthodes d'essais –
Partie 1: Essais aux fréquences industrielles
CEI 60250:1969, Méthodes recommandées pour la détermination de la permittivité et du
facteur de dissipation des isolants électriques aux fréquences industrielles, audibles et
radioélectriques (ondes métriques comprises)
CEI 60371-3 (toutes les parties), Spécification pour les matériaux isolants à base de mica –
Partie 3: Spécifications pour matériaux particuliers
ISO 178:2001, Plastiques – Détermination des propriétés en flexion
3 Méthodes de préparation des éprouvettes pour matériaux durcissables
3.1 Généralités
Les éprouvettes sont préparées conformément aux méthodes suivantes qui ne sont
applicables qu’aux matériaux durcissables.
3.2 Méthode 1
Nettoyer assez de matériau pour avoir les éprouvettes nécessaires à l’essai envisagé en le
débarrassant des particules libres et des fibres protubérantes.
Découper et empiler les morceaux nécessaires pour constituer le stratifié d'essai. Pour les
matériaux en ruban, amener l’empilage à l’épaisseur voulue en plaçant des morceaux se
chevauchant à demi, en couches successivement croisées à angle droit, en coupant, si
nécessaire, les bords de manière à obtenir les dimensions requises.
Régler la température de la presse à 160 °C ± 5 K, sauf spécification contraire

60371-2  IEC:2004 – 13 –
SPECIFICATION FOR INSULATING MATERIALS
BASED ON MICA –
Part 2: Methods of test
1 Scope
This part of IEC 60371 defines the methods of test which are applicable to built-up mica
materials, products based on them and mica paper.
2 Normative references
The following referenced documents are indispensable for the application of this document.
For dated references, only the edition cited applies. For undated references, the latest edition
of the referenced document (including any amendments) applies.
IEC 60216 (all parts), Electrical insulating materials − Thermal endurance properties
IEC 60243-1:1998, Electrical strength of insulating materials – Part 1: Tests at power
frequencies
IEC 60250:1969, Recommended methods for the determination of the permittivity and
dielectric dissipation factor of electric insulating materials at power, audio and radio
frequencies including metre wavelengths
IEC.60371-3 (all parts), Specification for insulating materials based on mica – Part 3:
Specifications for individual materials
ISO 178:2001, Plastics – Determination of flexural properties
3 Preparation methods of test specimens for curable materials
3.1 General
Test specimens are prepared in accordance with the following methods which are applicable
only to curable materials.
3.2 Method 1
Clean off all loose particles and projecting fibres from sufficient material to provide the test
pieces required for the particular test.
Cut and stack the pieces required to form the test laminate. For tape material, build up the
laminate to the required thickness using half-lapped layers with successive layers at right
angles, where necessary cutting the sides to obtain the required dimensions.
Adjust the press temperature to 160 °C ± 5 K, unless otherwise specified.

– 14 – 60371-2  CEI:2004
Placer l'éprouvette stratifiée au centre de deux plaques compensatrices dont l'épaisseur ne
dépasse pas 1,5 mm et à une température de 15 °C à 35 °C.
Installer des cales destinées à assurer l’épaisseur voulue de l’éprouvette stratifiée.
Introduire l’ensemble formé par l’éprouvette et ses plaques au centre de la presse
préchauffée.
Fermer immédiatement la presse et appliquer une pression suffisante pour venir sur les cales.
Traiter l’éprouvette pendant 30 min au minimum.
Enlever l'éprouvette et continuer le durcissement pendant le temps voulu à la température
indiquée dans la CEI 60371-3, ou suivant les recommandations du fournisseur.
Sauf spécification contraire, conditionner l'éprouvette pendant 24 h en atmosphère régulée à
(50 ± 5) % d'humidité relative et à 23 °C ± 2 K avant l'essai.
3.3 Méthode 2
Nettoyer assez de matériau pour avoir les éprouvettes nécessaires à l’essai envisagé en le
débarrassant des particules libres et des fibres protubérantes.
Pour les matériaux pleine largeur ou en feuille, découper et empiler les morceaux nécessaires
pour former l’éprouvette str
...