F03 - Gaskets

SIGNIFICANCE AND USE
3.1 The gaskets covered by this practice can be used on, but are not limited to, equipment constructed of the following materials: (a) stoneware, (b) glass and glass-lined, (c) tantalum (solid and lined), (d) titanium (solid and lined or clad), (e) zirconium (solid and lined or clad), (f) silver (solid and lined), and (g) nickel and nickel alloys (solid and clad).  
3.2 The gaskets provided for herein are for the following: (a) pipe flanges (flat or raised face), (b) vessel nozzles, (c) circular openings in vessels in excess of 12 in. (305 mm) diameter, and (d) oval openings in vessels.
SCOPE
1.1 This practice covers the designs, sizes, classifications, and construction of enveloped gaskets for severe corrosive applications. The envelope serves as the corrosion resistant member of the composite gasket and is a nonmetallic material such as polytetrafluoroethylene, PTFE, or related materials. The inserts are nonmetallic gasketing materials with or without metal reinforcement. Other types of composite gaskets are covered in Classification F868.  
1.2 This standard is based directly upon ANSI B16.21–2011; for that reason units are as ANSI stated in inches.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 This test method is designed to compare related materials under controlled conditions and their ability to maintain a given compressive stress as a function of time. A portion of the torque loss on the bolted flange is a result of creep relaxation. Torque loss can also be caused by elongation of the bolts, distortion of the flanges, and vibration; therefore, the results obtained should be correlated with field results. This test method may be used as a routine test when agreed upon between the user and the producer.
SCOPE
1.1 This test method provides a means of measuring the amount of creep relaxation of a laminated composite gasket material at a predetermined time after a compressive stress has been applied.  
1.2 Creep relaxation is measured by means of a calibrated bolt with dial indicator.  
1.3 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 Gasket compressions produced by bolt loads in a flanged joint are important in the application engineering of a joint assembly. They are related to the ability of a gasket to seal, to maintain tightness on assembly bolts, and to a variety of other gasket properties that determine the service behavior of a joint assembly. Thus, being able to determine the degree of compression in a gasket under the bolt loading will permit one to make qualitative predictions of the behavior of a joint assembly when it comes in contact with the application or service environment. With the plug test, bending of a flange facing between bolt centers can be measured; however, in a few highly distortable flanges the maximum bending between bolt centers may not be detected.  
4.2 The variation in gasket compressions at selected points in a flat-face joint assembly reveals the degree of flange distortion or the ability of the flange to distribute satisfactorily the compressive forces from bolt loads throughout the gasket.
SCOPE
1.1 This practice permits measurement of gasket compression resulting from bolt loading on a flat-face joint assembly at ambient conditions.  
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
3.1 Gasket materials undergo several processing steps from point of manufacture to installation in a flange. Many applications require close control of dimensional change. An accurate test method for determining the relative stability of various materials is needed for design and quality assurance purposes. This test method is useful towards that end. It simulates the extreme storage conditions that a material may undergo prior to installation. Samples are allowed unrestricted expansion or contraction, and so this test method should not be used to predict behavior clamped in a flange or other applications, or during specific processing steps.  
3.2 This test method measures linear change, and may need to be modified if the test specimen is not flat, homogeneous, or free of voids.
SCOPE
1.1 This test method covers a procedure to determine the stability of a gasket material to linear dimensional change due to hygroscopic expansion and contraction. It subjects a sample to extremes, that is, oven drying and complete immersion in water, that have shown good correlation to low and high relative humidities.2  
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
5.1 This test method is designed to compare sealing characteristics of gasket materials under controlled conditions by providing a precise measure of leakage rate at different press loads up to 32 MPa (4640 psi).  
5.2 This test method is suitable for measuring leakage rates from 0.1 mL/min to as high as 5 L/min for gases.  
5.3 This test method evaluates leak rates after time periods (typically 30 min) that result in a steady state leakage rate condition. Holding gasket materials under load and internal fluid pressure until steady state is achieved is required to obtain reproducible results.  
5.4 If the fluid being used in the test causes changes, such as swelling, in the gasket material, it may affect results and diminish repeatability.
SCOPE
1.1 This test method covers a means of evaluating the sealing properties of sheet, composite, and solid form-in-place gasket materials (see Classification F104 or F868) at room temperature, and may be used for fluid (gas or liquid) leak rate measurements. It utilizes relatively short hold times and is not intended to predict long-term performance in application.  
1.2 This test method is suitable for evaluating the sealing characteristics of a gasket material under different press loads by measuring the leakage rate. This test method may be used as an acceptance test when the producer and user have agreed to specific test conditions for the following parameters: (1) test medium, (2) internal pressure of the medium, (3) press load on the gasket specimen, and (4) the surface finish of the platens.  
1.3 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This test method covers determination of the short-time compressibility and recovery at room temperature of sheet-gasket materials, form-in-place gaskets, and in certain cases, gaskets cut from sheets. The test shall be conducted with both specimen and apparatus at a required temperature. The compressibility and recovery shall be calculated.
SCOPE
1.1 This test method covers determination of the short-time compressibility and recovery at room temperature of sheet-gasket materials, form-in-place gaskets, and in certain cases, gaskets cut from sheets. It is not intended as a test for compressibility under prolonged stress application, generally referred to as “creep,” or for recovery following such prolonged stress application, the inverse of which is generally referred to as “compression set.” Also, it is not intended for tests at other than room temperature. A resiliency characteristic (the amount recovered expressed as a percentage of the compressed thickness) may also be calculated from the test data where desired.  
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 The gasket factors are a function of leak rate; therefore, this practice generates curves. Constants for use in the ASME Boiler and Pressure Vessel Code, Section VIII, Appendix 2 code calculations are selected from these data. Specific m and y values can be selected based on a maximum desired leak rate or derived from these data as described in this procedure. This practice addresses the influence of leak rate and gasket thickness on a gasket’s ability to provide a seal initially and in operation. This practice is performed at room temperature; therefore, this practice does not account for all conditions, such as high temperature or thermal cycling or both, that bolted flange connections may be subject to in field application.  
4.2 This practice determines two general characteristics that are specific to the ASME design criteria. Caution should be exercised when comparing yield and maintenance factors between gasket materials, and it is recommended that the m and y curves be compared. Selecting a gasket material for use in an application should not be based exclusively on these two general characteristics. Gasket material selection for a given application should consider additional information not described in this practice, which includes, but is not limited to, chemical resistance, thermal resistance, creep relaxation, compressibility, and accommodation of thermal cycling.  
4.3 This practice builds upon work conducted in the Fluid Sealing Association (FSA G 605:11). The associated round robin data is provided for reference in Tables 1-4.   (A) BDL = below detection limit.  (A) BDL = below detection limit.
SCOPE
1.1 This practice will establish criteria for determining loading constants that are referenced in the American Society of Mechanical Engineers (ASME) pressure vessel design (Boiler and Pressure Vessel Code, Section VIII, Divs. 1 and 2). These constants are specific to this design criterion for metallic, semi-metallic, and nonmetallic gaskets.  
1.2 Units—The values stated in inch-pound units are to be regarded as the standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
5.1 The quantity of volatile components in FIPG silicone adhesive and sealant by-products can be established by this test method. This test method does not identify the components.
SCOPE
1.1 This practice covers the quantitative determination of the volatile matter evolved during the curing process of silicone adhesives and sealants for transportation applications.  
1.2 The values stated in SI units are to be regarded as the standard. The values in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
3.1 This classification system is intended to encourage uniformity in reporting properties; to provide a common language for communications between suppliers and consumers; to guide engineers and designers in the test methods commonly used for commercially available materials; and to be versatile enough to cover new materials and test methods as they are introduced.  
3.2 This system is based on the principle that nonmetallic gasket materials can be described in terms of specific physical and mechanical properties. This enables the user, or producer, to characterize a nonmetallic gasket based on properties that are important for the application.
SCOPE
1.1 This classification system2 provides a means for specifying or describing pertinent properties of commercial nonmetallic gasket materials. Materials composed of asbestos, cork, cellulose, and other organic or inorganic materials in combination with various binders or impregnants are included. Materials normally classified as rubber compounds are not included, since they are covered in Classification D2000. Gasket coatings are not covered, since details thereof are intended to be given on engineering drawings or in separate specifications. Facing materials for laminate composite gasket materials (LCGM) are included in Classification System F104. Assembled LCGMs are covered in Classification F868.  
1.2 Since all of the properties that contribute to gasket performance are not included, use of the classification system as a basis for selecting materials is limited.  
1.3 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

ABSTRACT
This specification covers preformed open-cell sponge rubber gaskets, for use in new or reconditioned pails or drums, of the following classes: Class A and Class B, each divided into Grade 1, Grade 2, and Grade 3. Cellular sponge rubber gaskets shall be made by incorporating a blowing agent into the compound, such as sodium bicarbonate, that gives off a gas which expands the mass during the vulcanization process, and shall be manufactured from natural rubber, synthetic rubber, or rubber-like materials, together with added compounding ingredients. Unless otherwise specified, gasket sponge rubber shall have a natural skin on both the top and bottom surfaces. Cellular rubber shall conform to the prescribed requirements as to physical properties such as (1) compression at deflection, (2) change in volume upon oil immersion, (3) change in compression value after heat aging, (4) compression set, and (5) color (tan or black). The following test methods shall be used: (1) compression deflection test, (2) oil immersion test, (3) heat oven aging test, and (4) compression set test under constant deflection. The formula for calculating the compression set is given. The requirements for sampling, test specimens and slabs, and measurements of test specimen such as width and thickness are detailed as well. The location from which standard test specimens are to be cut when testing standard test slabs or commercial flat sheets and the four-cavity frame for standard test slabs of cellular rubbers are illustrated.
SCOPE
1.1 This specification covers preformed open–cell sponge rubber gaskets of the following classes for use in new or reconditioned pails or drums.  
1.1.1 Class A—Non–Oil Resistant.  
1.1.2 Class B—Oil Resistant.  
1.2 The values stated in SI units are to be regarded as the standard.  
1.3 The following safety hazards caveat pertains only to Section 10, General Test Methods. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.
Note 1: ISO Equivalency Statement—This proposed specification was found to be not equivalent.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
5.1 This practice may be used to determine the viability of an RTV sealant to withstand pressure leak testing before cure at maximum gap conditions of a system. This practice may be used to indicate an RTV’s acceptability to undergo an assembly line leak check without causing a leak path due to material blow out.
SCOPE
1.1 This practice provides a means to determine the blowout resistance of a room-temperature vulcanized elastomer system (RTV) using a standard fixture.  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
3.1 This practice may be used to evaluate Classification F104 gasket materials using saturated steam and standard ASME RF (raised face) flanges. This practice is intended for use as quality control or material comparison tool and should not be used to predict performance.
SCOPE
1.1 This practice provides a means of comparing various nonmetallic flat gasket materials, Classification F104, in saturated steam service under controlled conditions. While the practice is designed primarily for flat gaskets, it also can be applied to various form-in-place gasket materials upon modification. The practice may be used for quality control or material comparison purposes as agreed upon between producer and user. This practice is consistent with Fluid Sealing Association test method, FSA-NMG-204-02, with regard to fixtures used and procedure.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
5.1 This practice is designed to compare related materials under controlled conditions and their ability to maintain a minimum amount of thermal conductance. Test results should be correlated with field results in order to predict heat transfer properties in particular applications.  
5.2 This practice may be used as a routine test when agreed upon by the user and the producer.
SCOPE
1.1 This practice covers a means of measuring the amount of heat transfer quantitatively through a material or system.  
1.2 This practice is similar to the Heat Flow Meter System of Test Method C518, but modified to accommodate small test samples of higher thermal conductance.  
1.3 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 This classification is intended to encourage uniformity in reporting properties of MLS and Metal Layer gaskets, to provide a common language for communications between producers and users, and to guide engineers and designers in the application and construction of commercially available gaskets. (A) This classification may also be used to classify Single Layer Steel (SLS) Gaskets.(B) Refer to Specification A666 or Specification A109/A109M for Stainless Steel and Low Carbon Steel, respectively. Other metals not referenced in the table or not covered by Specification A666 or Specification A109/A109M must be defined by the producer/user (that is, H – High Temperature Alloy).(C) Refer to Practice D1418 for general information regarding rubber coating types and use Classification D2000 to define the physical properties of the rubber. This physical property information is typically specified on the gasket drawing or the customer specification, or both.(D) Coated side as specified on part drawing.  
4.2 Suffix Table 2 is provided to allow hardness designation for Active, Inactive, or Load Stoppers.  
4.2.1 If suffixes are not to be used, only the basic callout from Table 1 is required. If a suffix is used for 1 layer, it must be specified for all layers, even if a “0” is used. It cannot be assumed that hardnesses of like layers are the same; if used, all layers must be specified separately. The first layer specified must be indicated on the part drawing. To use a hardness call-out, at the end of the base callout leave a space followed by the “HR” suffix with a series of suffix numbers to specify the hardnesses for each layer.
4.2.1.1 Example: ASTM F2325, A32ANBW11 HR252—Example from Table 1 modified to add hardness requirement for the three metal layers. Active layers 1 and 3 are designated to be the same, 1/4 hard steel. Stopper layer 2 is designated to be full hard steel.
SCOPE
1.1 This classification covers a means for specifying Multi-Layer Steel (MLS) and other Metal Layer Gaskets for Transportation Applications by application and construction. These structures are composed of one or more steel or metal layers of material, which may have coatings or embossments. Commercial materials designated as composite or enveloped gaskets are excluded from this classification and are covered by Classification F868 and Practice F336, respectively.  
1.2 Since all of the properties that contribute to gasket performance are not included, use of this classification as a basis for selecting an MLS or Metal Layer gasket is limited.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 These test methods provide a standardized procedure to measure the effect of immersion in specified fluids under definite conditions of time and temperature. The results of these test methods are not intended to give any direct correlation with service conditions in view of the wide variations in temperature and special uses encountered in gasket applications. The specific test fluids and test conditions outlined were selected as typical for purposes of comparing different materials and can be used as a routine test when agreed upon between the purchaser and the manufacturer.
SCOPE
1.1 These test methods cover the determination of the effect on physical properties of nonmetallic gasketing materials after immersion in test fluids. The types of materials covered are Type 1, Type 2, Type 3, and Type 7 as described in Classification F104. These test methods are not applicable to the testing of vulcanized rubber, a procedure that is described in Test Method D471. It is designed for testing specimens cut from gasketing materials or from finished articles of commerce. These test methods may also be used as a pre-treatment for Multi-Layer Steel, MLS, or Metal Layer Gasket materials adhesion testing per Test Methods D3359. The pre-treatment of MLS or Metal Layer Gasket materials pertains only as a pre-cursor to the adhesion test. Other physical property tests described in this standard are not applicable to MLS or Metal Layer Gasket materials.  
1.2 The values stated in SI units are to be regarded as the standard. The inch-pound units in parentheses are for information only.  
1.3 Refer to the current Material Safety Data Sheet (MSDS) and any precautionary labeling provided by the supplier of any materials referred to in these test methods.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
2.1 Weight loss represents the amount of combustibles and volatiles of the material at various temperatures between 315°C (600°F) and 815°C (1499°F). This procedure should not be used to determine percent of binder content.
SCOPE
1.1 This test method covers the determination of gasket material weight loss upon exposure to elevated temperatures.  
1.2 This test method may include hazardous materials, operations, and equipment.  
1.3 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 This test method provides terms such as megapascals or pounds-force per square inch of gasket surface for expressing the extent of adhesion applicable to all materials within the scope of Classification System F104. Under certain conditions, adhesion develops when gasket materials are confined in a compressed state between metal flanges. Adhesion is important as an index of ease of removal of a gasket material. Since other variables may enter into the performance in an application, the results obtained should be correlated with field results. A typical set of conditions is described in this test method. This test method may be used as an acceptance test when agreed upon between the user and the producer.
SCOPE
1.1 This test method provides a means of determining the degree to which gasket materials under compressive load adhere to metal surfaces. The test conditions described are indicative of those frequently encountered in gasket applications. Test conditions may also be modified in accordance with the needs of specific applications as agreed upon between the user and the producer. The maximum temperature recommended for this test method is 205°C (400°F).  
1.2 The values stated in SI units are to be regarded as standard. The values in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 The purpose of this classification system is to provide a method of adequately identifying silicone adhesives and sealants through the use of a line call-out designation.  
4.2 This classification system was designed to permit the addition of property values for future silicone adhesives and sealants.
SCOPE
1.1 This classification covers silicone adhesives and sealants intended for but not limited to sealing and retaining metallic and nonmetallic component assemblies in transportation applications. The materials cure to an elastomeric state by their specified cure system and mechanism.
Note 1: The classification system may serve many of the needs of industries using silicone materials. This classification is subject to revision, as the need requires; therefore, the latest revision should always be used.  
1.2 This classification is intended to be a means of classifying silicone materials. It is not intended for engineering design purposes.  
1.3 It is not the intent of this classification to include pressure-sensitive or hot-melt adhesives.  
1.4 In all cases in which the provisions of this classification system would conflict with the referenced ASTM standard for a particular method, the latter shall take precedence.  
1.5 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.6 The following safety hazards caveat pertains only to the test methods portion, Section 7, of this classification. This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.7 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 These test methods are designed to compare gasket materials under controlled conditions and to provide a precise measure of leakage rate.  
4.2 These test methods are suitable for measuring leakage rates as high as 6 L/h and as low as 0.3 mL/h. In many cases, “zero” leakage may not be attainable.  
4.3 These test methods evaluate leakage rates after time periods that are typically 5 to 30 min under load. Holding a gasket material under load for extended time periods may give different results.  
4.4 If the fluid being used in the test causes changes, such as swelling, in the gasket material, then unpredictable results may be obtained.
SCOPE
1.1 These test methods provide a means of evaluating the sealing properties of sheet and solid form-in-place gasket materials at room temperature. Test Method A is restricted to liquid leakage measurements, whereas Test Method B may be used for both liquid and gas leakage measurements.  
1.2 These test methods are suitable for evaluating the sealing characteristics of a gasket material under different compressive flange loads. The test method may be used as an acceptance test when the producer and user have agreed to specific test conditions for the following parameters: test medium, internal pressure on medium, and flange load on gasket specimens.  
1.3 These test methods use a small-diameter narrow-width gasket as the test specimen under relatively low gasket loads and relatively low pressures. Test Method F2378 is another sealability test method that uses a larger gasket specimen and higher internal pressures and flange loads.  
1.4 The values stated in SI units are to be regarded as the standard. The values in parentheses are for information only.  
1.5 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. (For specific hazard or warning statements, or both, see 5.2.11, Section 6, 6.3, 8.2.4, 11.3.2, and 11.4.2.)  
1.6 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 This test method is designed to evaluate all types of enveloped gaskets under controlled conditions with respect to leakage and to provide measurable leakage rates.  
4.2 Determining torque required to seal a given gasket is also part of this test method. By converting the torque at sealing to total bolt load, useful design information may be obtained for other standard and nonstandard openings.  
4.3 This test method may be used as an incoming quality control test to evaluate similar gaskets from different suppliers. This test method may also be used as a quality control test when parameters are agreed upon between the producer and the user.  
4.4 Leakage through the gasket or over the gasket, or both, is determined by this test method.
SCOPE
1.1 This test method covers the evaluation of the sealing properties of enveloped gaskets for use with corrosion-resistant process equipment.2 Enveloped gaskets are described as gaskets having some corrosion-resistant covering over the internal area normally exposed to the corrosive environment. The shield material may be plastic (such as polytetrafluoroethylene) or metal (such as tantalum). A resilient conformable filler is usually used inside the envelope. The design and construction of nonmetallic gaskets is covered in Practice F336.  
1.2 The values stated in SI units are to be regarded as standard. The values given in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. For specific precautionary statements, see Section 6.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
5.1 This practice is a screening tool and should be used in conjunction with other more accurate real-time load-measuring techniques.  
5.2 This practice covers the use of PIF, which is available in several load ranges. This practice also covers the use of a manual or automatic scanning device to read indicated load.  
5.3 Limitations include those applications in which the PIF may be kinked, twisted, or buckled. PIF does not withstand elevated temperature, low temperature, or fluid aging and does not take into account any relaxation of bolts, gasket materials, or flange twisting, as it provides only the maximum attained pressure.
SCOPE
1.1 This practice covers a standard means for measuring initial static sealing pressure in transportation applications.  
1.2 It uses a pressure-indicating film (PIF) that will record the maximum load imprint of the seal-to-flange interfaces. The imprints will vary in intensity based on load across and along the interface.  
1.3 These imprints can be used to determine if initial load on the gasket is adequate to attain a seal. These imprints may also indicate correct bolt torque sequence. These imprints may also be used to determine if the mating surface waviness or local flatness meets gasket requirements. Roughness is rarely found by PIFs because peak-to-peak wavelengths are too short. PIF is very good at finding waviness (peak to peak > 2.5 mm) and local flatness dips. PIFs provide an approximation of maximum pressures, and do not take into account relaxation of the joint after the torque sequence. Other methods involving dynamic measurement should be used if flange loading after relaxation is desired.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
5.1 This test method is designed to measure the chemical cure of the binder used in the manufacture of cork compositions. The results of this test method can be used only as a guide for its intended service in elevated temperature and environmental conditions.
SCOPE
1.1 This test method covers three procedures for determination of the binder durability of cork-containing materials.  
1.2 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.3 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
5.1 This practice determines the room temperature gasket constants Gb and a for initial seating and Gs for operating conditions as related to the tightness behavior of pressurized bolted flanged connections. These constants are used in determining the design bolt load for gasketed bolted joints.  
5.2 This practice is suitable for all the types of gaskets and facings as are considered by the ASME Division 1 Code. This includes ASME B16.5 raised facings, nubbin-type facings, O-ring grooves, and a wide variety of gaskets including spiral wound, flat sheet, solid metal, jacketed, and other types of gaskets common to process and power industry pressurized equipment.  
5.3 These constants are intended for direct use in determining ASME Code design calculations for bolted flanged joints. An appendix of the ASME Boiler and Pressure Vessel Code, Section VIII, Division 1 will refer to the gasket constants Gb, a, and Gs produced by this practice. The user and bolted joint designer are cautioned that gasket constants Gb, a, and Gs and any gasket design stresses calculated from these may not be conservative for design stresses below S1 or beyond S13 as indicated in Table 3.  
5.4 When required, this practice evaluates both the mechanical and leakage resistance of gaskets to excessive compression to determine their maximum assembly stress, Sc.  
5.5 This test procedure is a gasket tightness characterization test and is not considered as a gasket manufacturing quality control test.
SCOPE
1.1 This practice determines room temperature gasket tightness design constants for pressurized bolted flanged connections such as those designed in accordance with the ASME Boiler and Pressure Vessel Code.  
1.2 This practice applies mainly to all types of circular gasket products and facings typically used in process or power plant pressure vessels, heat exchangers, and piping including solid metal, jacketed, spiral wound, and sheet-type gaskets. As an optional extension of this practice, the maximum assembly stress for those gaskets may also be determined by this procedure.  
1.3 Units—The values stated in SI units are to be regarded as the standard, but other units may be included.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
5.1 The hot compression properties of a gasket material, including creep resistance and compression set, are a major factor with regard to the selection of a given material for use in a particular sealing application. The significance of the test method is based, in part; on the assumption that if a material exhibits too much creep at elevated temperature that it will no longer function as effectively as a seal. This assumption can only be used as a guide; however, since exact yield or failure points are difficult to define for gasket materials (which are usually viscoelastic in nature). Two or more materials can be compared to determine differences in their hot compression properties. A sample of material can be compared to an established standard or previously determined characteristics on original lots of the same material, for quality assurance purposes.  
5.2 Samples are to be tested with a raised profile insert or calibration ring described in 6.3 and Fig. 1 so that the area (2042 mm2  (3.17 in.2)) remains constant during the test.
FIG. 1 Test Assembly for Determining Hot Compression
SCOPE
1.1 This test method covers a means of measuring the hot compression properties of a gasket material by measuring its creep under a constant load at both room temperature and while increasing the temperature. Short term creep properties including both cold and hot creep, total creep and compression set of a gasket material can be determined.  
1.2 The values stated in SI units are to be regarded as standard. The values given in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 These test methods are designed to compare related materials under controlled conditions and their ability to maintain a given compressive stress as a function of time. A portion of the torque loss on the bolted flange is a result of creep relaxation. Torque loss can also be caused by elongation of the bolts, distortion of the flanges, and vibration; therefore, the results obtained should be correlated with field results. These test methods may be used as a routine test when agreed upon between the consumer and the producer.
Note 1: Test Method B was developed using asbestos gasket materials and at issuance substantiating data were not available for other gasket materials.
SCOPE
1.1 These test methods provide a means of measuring the amount of creep relaxation of a gasket material at a predetermined time after a compressive stress has been applied.  
1.1.1 Test Method A—Creep relaxation measured by means of a calibrated strain gauge on a bolt.  
1.1.2 Test Method B—Creep relaxation measured by means of a calibrated bolt with dial indicator.  
1.2 The values stated in SI units are to be regarded as standard. The values given in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
3.1 This test method is designed to compare all types of gaskets under simulated field operating conditions. Performance of a gasket can thus be measured prior to the start-up of chemical processes.5 The design of the test unit provides maximum range of corrosion resistance so that meaningful results are possible. This test method may be used as a routine test when agreed upon between the purchaser and the seller.
SCOPE
1.1 This test method covers the evaluation of gaskets under corrosive conditions at varying temperature and pressure levels. The test unit may be glass lined if the flanges are sufficiently plane (industry accepted), thus providing resistance to all chemicals, except hydrofluoric acid, from cryogenic temperatures to 260°C (500°F) at pressures from full vacuum to the allowable pressure rating of the unit, or made of other suitable material. The test unit described (Fig. 1) has an internal design pressure rating of 1034 kPa (150 psi) at 260°C (500°F).
FIG. 1 Test Unit  
1.2 The values stated in SI units are to be regarded as the standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. For specific hazards statements, see Section 5.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 Use of this practice in conjunction with realistic maximum volatility tolerance level can help minimize the risk of oxygen sensor dysfunction from formed-in-place-sealants in transportation applications. This practice provides a method for determination of percentage volatiles in silicone elastomers. The volatile silicones from a commercial silicone are primarily cyclo dimethyl-siloxane. Other species present having GC retention times similar to those of the cyclics are assumed to be silicone as well.
SCOPE
1.1 This practice covers a means to determine the percent silicone-producing volatiles present in heat-cured silicone rubber and room temperature-cured silicones (RTV).  
1.2 Silicone-producing volatiles contribute to fouling of oxygen sensor systems used in the control of vehicle emissions.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
5.1 The load versus thickness properties of a gasket material are an important factor with regard to the selection of a given material for use in a particular sealing application. Additionally, compression/load behavior data are a common request from users. The test allows comparison of materials at room temperature or elevated temperatures or both. Additionally, properties can be evaluated while loading and unloading the material at room temperature or elevated temperatures or both. The significance of the test method is based, in part, on the assumption that, if a material exhibits too much compression at either room temperatures or elevated temperatures, it will no longer function as effectively as a seal. The results may be used in certain flange design methods to characterize properties for design such as finite element analysis (FEA). The results may be used to confirm adequate assembly loading based on measured gasket compression in the field. Two or more materials can be compared to determine differences in their compression properties. A sample of material can be compared to an established standard or previously determined characteristics on original lots of the same material for quality assurance purposes.  
5.2 If desired, samples may be tested with a raised profile flange, insert, or calibration ring described in 6.3 and Fig. 1 so that the area (2042 mm2 [3.18 in.2]) remains constant during the test.
FIG. 1 Test Assembly for Determining Load versus Compression
SCOPE
1.1 This practice measures the compression properties of a gasket material by measuring gasket deflection while it is subjected to an increasing compressive load until a target load is reached. The load and change in thickness are recorded at a defined loading rate as a function of time for the duration of the test.  
1.2 Suggested loading rates are 0.5 MPa/s [72.52 psi/s] for all types of gaskets except for expanded polytetrafluoroethylene (PTFE), elastomer, and cork/elastomer gaskets when 0.1 MPa/s [14.5 psi/s] is used.  
1.3 The Part A test is performed that measures the compression properties of a gasket material by measuring gasket thickness while it is subjected to an increasing compressive load until a target load is reached. This test is performed at room temperature but may be performed at an elevated temperature if desired or when agreed upon by producer and user.  
1.4 The Part B test may be performed that measures the compression properties of a gasket material by measuring gasket thickness while it is subjected to increasing compressive loads that includes a sequence or sequences in which the gasket is unloaded followed by a resumption of the compressive load until a target load is reached. The unloading rate is the same as the loading rate unless different loading and unloading rates are desired or when agreed upon by producer and user. This test is performed at room temperature but may be performed at an elevated temperature if desired or when agreed upon by producer and user.  
1.5 The testing parameters for both Parts A and B including the gasket material type, gasket dimensions, platen type (RF or FF), target load, loading time, recording interval used during the test, loading and unloading rates, and temperature are to be reported with the results.  
1.6 Units—The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard.  
1.7 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.  
1.8 This internation...

SIGNIFICANCE AND USE
3.1 This test method is designed to compare related laminated composite gasket materials under controlled conditions and their short-time compressibility and recovery at room temperature. It measures compressibility with a matched pair of opposing upper and lower penetrators which provide better precision and bias than methods using an upper penetrator and a lower anvil. It is difficult to prepare undistorted test specimens from laminated composite gasket materials which will lay flat on an anvil. Also, with many composites having rigid inner layers the load on the upper penetrator is distributed over the bottom anvil area resulting in a lower than actual compressibility reading. This test method may be used as a routine test method when agreed upon between the purchaser and the producer.
SCOPE
1.1 This test method covers determination of the short-time compressibility and recovery at room temperature of laminated composite gasket materials.  
1.2 This test method is not intended as a test for compressibility under prolonged stress application, that is “creep,” or for recovery following such prolonged stress application, the inverse of which is generally referred to as “compression set.” Also, it is only intended for tests at room temperature.  
1.3 The values stated in SI units are to be regarded as the standard. The inch-pound units given in parentheses are for information only.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 These test methods are described in order to standardize procedures for determining the tensile strength of nonmetallic gasket materials. The measurement of this property characterizes various classes and grades of materials of a given type and in so doing, it will give the manufacturer a measurement of the quality of his product. It also will aid the purchaser of the gasketing materials to be able to determine whether the gasket material that he has approved for a given application is being manufactured in acceptable quality.  
4.2 The measurement of this property should not be misconstrued as to give the purchaser of the gasket material an indication of the performance of that material in application.  
4.3 The property may be useful in establishing material specifications.  
4.4 Various procedures are given for the different types of materials, and in order to compare the results from one laboratory to another, it is imperative that the applicable procedure be selected.  
4.5 Various types of tension-testing apparatus are allowed to be used. These types of equipment can produce different indicated results. Laboratories having different equipment may have to establish correlations between each other; otherwise, misinterpretation of the test data could result.
SCOPE
1.1 These test methods cover the determination of tensile strength of certain nonmetallic gasketing materials at room temperature. The types of materials covered are those containing asbestos and other inorganic fibers (Type 1), cork (Type 2), cellulose or other organic fiber (Type 3), and flexible graphite (Type 5) as described in Classification F104. These test methods are not applicable to the testing of vulcanized rubber, a method for which is described in Test Methods D412 nor for rubber O-rings, a method for which is described in Test Methods D1414.  
1.2 The values stated in SI units are to be regarded as the standard. The values in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 This classification is intended to encourage uniformity in reporting properties; to provide a common language for communications between producers and users; to guide engineers and designers in the use, construction, and properties of commercially available materials; and to be versatile enough to cover new materials and test methods as they are introduced.
SCOPE
1.1 This classification covers a means for specifying or describing pertinent properties of commercial laminate composite gasket materials (LCGM). These structures are composed of two or more chemically different layers of material. These materials may be organic or inorganic, or combinations with various binders or impregnants. Gasket coatings are not covered since details thereof are intended to be given on engineering drawings, or as separate specifications. Commercial materials designated as enveloped gaskets are excluded from this classification; they are covered in Practice F336. This classification system does not cover multilayer steel (MLS) gaskets currently used for some automotive exhaust and head gaskets. MLS gaskets are classified under Classification F2325.  
1.2 Since all of the properties that contribute to gasket performance are not included, use of this classification as a basis for selecting LCGM is limited.  
1.3 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.  
1.5 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 This test method is designed to measure the ability of non-metallic gasket materials to withstand handling, as would be encountered before and during installation of cut gaskets.
SCOPE
1.1 This test method covers the determination of the flexibility of non-metallic gasket materials. It is designed for testing specimens cut from sheet goods or from the gasket in the finished form, as supplied for commercial use. Materials normally classified as rubber compounds are excluded since they are covered in Classification D2000.  
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 The compressive strength or crush-extrusion resistance of a gasket material is a major factor with regard to the selection of a given material for use in a particular sealing application. The significance of the test method is based, in part, on the assumption that a material, once it has been crushed or extruded, will no longer function as effectively as a seal. This assumption can only be used as a guide, however, since exact yield or failure points are difficult to define for gasket materials (which are usually viscoelastic in nature). Two or more materials can be compared to determine differences in their resistance to compressive stress. A sample of material can be compared to an established standard or previously determined characteristics on original lots of the same material, for quality assurance purposes. See 6.2 for discussion of specimen area and geometry effects.
SCOPE
1.1 This test method covers the determination of compressive strength characteristics (crush-extrusion resistance) of gasket materials at elevated temperature.  
1.2 The values stated in SI units are to be regarded as the standard. The values in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
3.1 This test method is designed to compare all types of preformed gaskets under controlled conditions with respect to blow-out resistance. This test method may be used as a routine test when agreed upon between the purchaser and the seller.
SCOPE
1.1 This test method covers the determination of the resistance against blow-out of preformed gaskets. The test is conducted under ambient conditions and should be used for comparison purposes only to select suitable designs and constructions for specific applications.  
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.  
1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.

SIGNIFICANCE AND USE
4.1 Density is an important property of a gasket material, since it has an inverse relationship to the void volume of the material. Density is often used in a specification, since relationships to sealability, compressibility, creep relaxation, and tensile strength can be found for a given gasket grade.  
4.2 Density is a measurement of the mass to the volume ratio and therefore easily determined with a weight scale and thickness measuring device. This test method requires from 1 h to two days of sample conditioning, which is necessary to achieve a high level of precision, but which detracts from its usefulness as a production test method. Where it must be modified for manufacturing control, it is recommended that thickness and weight measurement methods be adhered to strictly.
SCOPE
1.1 This test method covers a procedure for determining the density of a gasket material.  
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SIGNIFICANCE AND USE
4.1 Gasket compressions produced by bolt loads in a flanged joint are important in the application engineering of a joint assembly. They are related to the ability of a gasket to seal, to maintain tightness on assembly bolts, and to a variety of other gasket properties that determine the service behavior of a joint assembly. Thus, being able to determine the degree of compression in a gasket under the bolt loading will permit one to make qualitative predictions of the behavior of a joint assembly when it comes in contact with the application or service environment. With the plug test, bending of a flange facing between bolt centers can be measured; however, in a few highly distortable flanges the maximum bending between bolt centers may not be detected.  
4.2 The variation in gasket compressions at selected points in a flat-face joint assembly reveals the degree of flange distortion or the ability of the flange to distribute satisfactorily the compressive forces from bolt loads throughout the gasket.
SCOPE
1.1 This practice permits measurement of gasket compression resulting from bolt loading on a flat-face joint assembly at ambient conditions.  
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SIGNIFICANCE AND USE
5.1 This test method is designed to compare sealing characteristics of gasket materials under controlled conditions by providing a precise measure of leakage rate at different press loads up to 32 MPa (4640 psi).  
5.2 This test method is suitable for measuring leakage rates from 0.1 mL/min to as high as 5 L/min for gases.  
5.3 This test method evaluates leak rates after time periods (typically 30 min) that result in a steady state leakage rate condition. Holding gasket materials under load and internal fluid pressure until steady state is achieved is required to obtain reproducible results.  
5.4 If the fluid being used in the test causes changes, such as swelling, in the gasket material, it may affect results and diminish repeatability.
SCOPE
1.1 This test method covers a means of evaluating the sealing properties of sheet, composite, and solid form-in-place gasket materials (see Classification F104 or F868) at room temperature, and may be used for fluid (gas or liquid) leak rate measurements. It utilizes relatively short hold times and is not intended to predict long-term performance in application.  
1.2 This test method is suitable for evaluating the sealing characteristics of a gasket material under different press loads by measuring the leakage rate. This test method may be used as an acceptance test when the producer and user have agreed to specific test conditions for the following parameters: (1) test medium, (2) internal pressure of the medium, (3) press load on the gasket specimen, and (4) the surface finish of the platens.  
1.3 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and to determine the applicability of regulatory limitations prior to use.

SIGNIFICANCE AND USE
3.1 Gasket materials undergo several processing steps from point of manufacture to installation in a flange. Many applications require close control of dimensional change. An accurate test method for determining the relative stability of various materials is needed for design and quality assurance purposes. This test method is useful towards that end. It simulates the extreme storage conditions that a material may undergo prior to installation. Samples are allowed unrestricted expansion or contraction, and so this test method should not be used to predict behavior clamped in a flange or other applications, or during specific processing steps.  
3.2 This test method measures linear change, and may need to be modified if the test specimen is not flat, homogeneous, or free of voids.
SCOPE
1.1 This test method covers a procedure to determine the stability of a gasket material to linear dimensional change due to hygroscopic expansion and contraction. It subjects a sample to extremes, that is, oven drying and complete immersion in water, that have shown good correlation to low and high relative humidities.2  
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SIGNIFICANCE AND USE
4.1 This test method is designed to compare related materials under controlled conditions and their ability to maintain a given compressive stress as a function of time. A portion of the torque loss on the bolted flange is a result of creep relaxation. Torque loss can also be caused by elongation of the bolts, distortion of the flanges, and vibration; therefore, the results obtained should be correlated with field results. This test method may be used as a routine test when agreed upon between the user and the producer.
SCOPE
1.1 This test method provides a means of measuring the amount of creep relaxation of a laminated composite gasket material at a predetermined time after a compressive stress has been applied.  
1.2 Creep relaxation is measured by means of a calibrated bolt with dial indicator.  
1.3 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SIGNIFICANCE AND USE
3.1 The gaskets covered by this practice can be used on, but are not limited to, equipment constructed of the following materials: (a) stoneware, (b) glass and glass-lined, (c) tantalum (solid and lined), (d) titanium (solid and lined or clad), (e) zirconium (solid and lined or clad), (f) silver (solid and lined), and (g) nickel and nickel alloys (solid and clad).  
3.2 The gaskets provided for herein are for the following: (a) pipe flanges (flat or raised face), (b) vessel nozzles, (c) circular openings in vessels in excess of 12 in. (305 mm) diameter, and (d) oval openings in vessels.
SCOPE
1.1 This practice covers the designs, sizes, classifications, and construction of enveloped gaskets for severe corrosive applications. The envelope serves as the corrosion resistant member of the composite gasket and is a nonmetallic material such as polytetrafluoroethylene, PTFE, or related materials. The inserts are nonmetallic gasketing materials with or without metal reinforcement. Other types of composite gaskets are covered in Classification F868.  
1.2 This standard is based directly upon ANSI B16.21–2011; for that reason units are as ANSI stated in inches.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SIGNIFICANCE AND USE
4.1 The gasket factors are a function of leak rate; therefore, this practice generates curves. Constants for use in the ASME Boiler and Pressure Vessel Code, Section VIII, Appendix 2 code calculations are selected from these data. Specific m and y values can be selected based on a maximum desired leak rate or derived from these data as described in this procedure. This practice addresses the influence of leak rate and gasket thickness on a gasket’s ability to provide a seal initially and in operation. This practice is performed at room temperature; therefore, this practice does not account for all conditions, such as high temperature or thermal cycling or both, that bolted flange connections may be subject to in field application.  
4.2 This practice determines two general characteristics that are specific to the ASME design criteria. Caution should be exercised when comparing yield and maintenance factors between gasket materials, and it is recommended that the m and y curves be compared. Selecting a gasket material for use in an application should not be based exclusively on these two general characteristics. Gasket material selection for a given application should consider additional information not described in this practice, which includes, but is not limited to, chemical resistance, thermal resistance, creep relaxation, compressibility, and accommodation of thermal cycling.  
4.3 This practice builds upon work conducted in the Fluid Sealing Association (FSA G 605:11). The associated round robin data is provided for reference in Tables 1-4.   (A) BDL = below detection limit.  (A) BDL = below detection limit.
SCOPE
1.1 This practice will establish criteria for determining loading constants that are referenced in the American Society of Mechanical Engineers (ASME) pressure vessel design (Boiler and Pressure Vessel Code, Section VIII, Divs. 1 and 2). These constants are specific to this design criterion for metallic, semi-metallic, and nonmetallic gaskets.  
1.2 Units—The values stated in inch-pound units are to be regarded as the standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

ABSTRACT
This test method covers determination of the short-time compressibility and recovery at room temperature of sheet-gasket materials, form-in-place gaskets, and in certain cases, gaskets cut from sheets. The test shall be conducted with both specimen and apparatus at a required temperature. The compressibility and recovery shall be calculated.
SCOPE
1.1 This test method covers determination of the short-time compressibility and recovery at room temperature of sheet-gasket materials, form-in-place gaskets, and in certain cases, gaskets cut from sheets. It is not intended as a test for compressibility under prolonged stress application, generally referred to as “creep,” or for recovery following such prolonged stress application, the inverse of which is generally referred to as “compression set.” Also, it is not intended for tests at other than room temperature. A resiliency characteristic (the amount recovered expressed as a percentage of the compressed thickness) may also be calculated from the test data where desired.  
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SIGNIFICANCE AND USE
4.1 This classification is intended to encourage uniformity in reporting properties of MLS and Metal Layer gaskets, to provide a common language for communications between producers and users, and to guide engineers and designers in the application and construction of commercially available gaskets. (A) This classification may also be used to classify Single Layer Steel (SLS) Gaskets.(B) Refer to Specification A666 or Specification A109/A109M for Stainless Steel and Low Carbon Steel, respectively. Other metals not referenced in the table or not covered by Specification A666 or Specification A109/A109M must be defined by the producer/user (that is, H – High Temperature Alloy).(C) Refer to Practice D1418 for general information regarding rubber coating types and use Classification D2000 to define the physical properties of the rubber. This physical property information is typically specified on the gasket drawing or the customer specification, or both.(D) Coated side as specified on part drawing.  
4.2 Suffix Table 2 is provided to allow hardness designation for Active, Inactive, or Load Stoppers.  
4.2.1 If suffixes are not to be used, only the basic callout from Table 1 is required. If a suffix is used for 1 layer, it must be specified for all layers, even if a “0” is used. It cannot be assumed that hardnesses of like layers are the same; if used, all layers must be specified separately. The first layer specified must be indicated on the part drawing. To use a hardness call-out, at the end of the base callout leave a space followed by the “HR” suffix with a series of suffix numbers to specify the hardnesses for each layer.
4.2.1.1 Example: ASTM F2325, A32ANBW11 HR252—Example from Table 1 modified to add hardness requirement for the three metal layers. Active layers 1 and 3 are designated to be the same, 1/4 hard steel. Stopper layer 2 is designated to be full hard steel.
SCOPE
1.1 This classification covers a means for specifying Multi-Layer Steel (MLS) and other Metal Layer Gaskets for Transportation Applications by application and construction. These structures are composed of one or more steel or metal layers of material, which may have coatings or embossments. Commercial materials designated as composite or enveloped gaskets are excluded from this classification and are covered by Classification F868 and Practice F336, respectively.  
1.2 Since all of the properties that contribute to gasket performance are not included, use of this classification as a basis for selecting an MLS or Metal Layer gasket is limited.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory requirements prior to use.

SIGNIFICANCE AND USE
5.1 This practice is designed to compare related materials under controlled conditions and their ability to maintain a minimum amount of thermal conductance. Test results should be correlated with field results in order to predict heat transfer properties in particular applications.  
5.2 This practice may be used as a routine test when agreed upon by the user and the producer.
SCOPE
1.1 This practice covers a means of measuring the amount of heat transfer quantitatively through a material or system.  
1.2 This practice is similar to the Heat Flow Meter System of Test Method C518, but modified to accommodate small test samples of higher thermal conductance.  
1.3 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.4 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SIGNIFICANCE AND USE
4.1 This test method provides terms such as megapascals or pounds-force per square inch of gasket surface for expressing the extent of adhesion applicable to all materials within the scope of Classification System F104. Under certain conditions, adhesion develops when gasket materials are confined in a compressed state between metal flanges. Adhesion is important as an index of ease of removal of a gasket material. Since other variables may enter into the performance in an application, the results obtained should be correlated with field results. A typical set of conditions is described in this test method. This test method may be used as an acceptance test when agreed upon between the user and the producer.
SCOPE
1.1 This test method provides a means of determining the degree to which gasket materials under compressive load adhere to metal surfaces. The test conditions described are indicative of those frequently encountered in gasket applications. Test conditions may also be modified in accordance with the needs of specific applications as agreed upon between the user and the producer. The maximum temperature recommended for this test method is 205°C (400°F).  
1.2 The values stated in SI units are to be regarded as standard. The values in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SIGNIFICANCE AND USE
3.1 This practice may be used to evaluate Classification F104 gasket materials using saturated steam and standard ASME RF (raised face) flanges. This practice is intended for use as quality control or material comparison tool and should not be used to predict performance.
SCOPE
1.1 This practice provides a means of comparing various nonmetallic flat gasket materials, Classification F104, in saturated steam service under controlled conditions. While the practice is designed primarily for flat gaskets, it also can be applied to various form-in-place gasket materials upon modification. The practice may be used for quality control or material comparison purposes as agreed upon between producer and user. This practice is consistent with Fluid Sealing Association test method, FSA-NMG-204-02, with regard to fixtures used and procedure.  
1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SIGNIFICANCE AND USE
4.1 These test methods are designed to compare related materials under controlled conditions and their ability to maintain a given compressive stress as a function of time. A portion of the torque loss on the bolted flange is a result of creep relaxation. Torque loss can also be caused by elongation of the bolts, distortion of the flanges, and vibration; therefore, the results obtained should be correlated with field results. These test methods may be used as a routine test when agreed upon between the consumer and the producer.Note 1—Test Method B was developed using asbestos gasket materials and at issuance substantiating data were not available for other gasket materials.
SCOPE
1.1 These test methods provide a means of measuring the amount of creep relaxation of a gasket material at a predetermined time after a compressive stress has been applied.  
1.1.1 Test Method A—Creep relaxation measured by means of a calibrated strain gauge on a bolt.  
1.1.2 Test Method B—Creep relaxation measured by means of a calibrated bolt with dial indicator.  
1.2 The values stated in SI units are to be regarded as standard. The values given in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SIGNIFICANCE AND USE
4.1 Density is an important property of a gasket material, since it has an inverse relationship to the void volume of the material. Density is often used in a specification, since relationships to sealability, compressibility, creep relaxation, and tensile strength can be found for a given gasket grade.  
4.2 Density is a measurement of the mass to the volume ratio and therefore easily determined with a weight scale and thickness measuring device. This test method requires from 1 h to two days of sample conditioning, which is necessary to achieve a high level of precision, but which detracts from its usefulness as a production test method. Where it must be modified for manufacturing control, it is recommended that thickness and weight measurement methods be adhered to strictly.
SCOPE
1.1 This test method covers a procedure for determining the density of a gasket material.  
1.2 The values stated in SI units are to be regarded as the standard. The values given in parentheses are for information only.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SIGNIFICANCE AND USE
5.1 This practice may be used to determine the viability of an RTV sealant to withstand pressure leak testing before cure at maximum gap conditions of a system. This practice may be used to indicate an RTV’s acceptability to undergo an assembly line leak check without causing a leak path due to material blow out.
SCOPE
1.1 This practice provides a means to determine the blowout resistance of a room-temperature vulcanized elastomer system (RTV) using a standard fixture.  
1.2 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.  
1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

SIGNIFICANCE AND USE
5.1 This test method is designed to measure the chemical cure of the binder used in the manufacture of cork compositions. The results of this test method can be used only as a guide for its intended service in elevated temperature and environmental conditions.
SCOPE
1.1 This test method covers three procedures for determination of the binder durability of cork-containing materials.  
1.2 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.