SIST EN ISO 16101:2005
(Main)Packaging - Transport packaging for dangerous goods - Plastics compatibility testing (ISO 16101:2004)
Packaging - Transport packaging for dangerous goods - Plastics compatibility testing (ISO 16101:2004)
This standard specifies the requirements and test methods for compatibility testing of polyethylene based plastics packagings and composite packagings with plastic inners containing liquids. The testing involves storage with the packaged substance, or with a standard liquid as defined in annex A. Annex B describes small scale laboratory tests, which may be used to determine the assimilation of those products to be carried with the standard liquids.
NOTE This standard should be used in conjunction with one or more of the International Regulations set out in the Bibliography
Verpackung - Verpackungen zur Beförderung gefährlicher Güter - Verträglicheitsprüfung für Kunststoffverpackungen (ISO 16101:2004)
Diese Europäische Norm enthält Anforderungen und Prüfverfahren für die chemische Verträglichkeitsprüfung von Kunststoffverpackungen und Kombinationsverpackungen mit Innenverpackungen aus Polyethylen, die für Flüssigkeiten vorgesehen sind. Die Prüfung schließt die Vorlagerung mit dem zu verpackenden Füllgut oder mit einer Standardflüssigkeit, wie sie in Anhang B definiert wird, ein. Anhang C beschreibt Labormethoden, die für die Zuordnung von zu befördernden Produkten und Standardflüssigkeiten verwendet werden können.
Emballages - Emballages pour le transport des marchandises dangereuses - Essais de compatibilité des matieres plastiques (ISO 16101:2004)
Le présent projet de norme européenne spécifie les exigences et méthodes d'essai pour l'essai de compatibilité des emballages en plastique a base de polyéthylene et les emballages composites avec récipients intérieurs en plastique contenant des liquides. L'essai implique le stockage avec la substance emballée ou avec un liquide standard tel que défini dans l'annexe B. L'annexe C décrit des essais en laboratoire sur éprouvette pouvant etre utilisés pour déterminer l'assimilation de ces produits aux liquides standard.
Embalaža - Transportna embalaža za nevarno blago - Preskušanje združljivosti plastike (ISO 16101:2004)
General Information
Relations
Standards Content (Sample)
SLOVENSKI STANDARD
SIST EN ISO 16101:2005
01-marec-2005
Embalaža - Transportna embalaža za nevarno blago - Preskušanje združljivosti
plastike (ISO 16101:2004)
Packaging - Transport packaging for dangerous goods - Plastics compatibility testing
(ISO 16101:2004)
Verpackung - Verpackungen zur Beförderung gefährlicher Güter - Verträglicheitsprüfung
für Kunststoffverpackungen (ISO 16101:2004)
Emballages - Emballages pour le transport des marchandises dangereuses - Essais de
compatibilité des matieres plastiques (ISO 16101:2004)
Ta slovenski standard je istoveten z: EN ISO 16101:2004
ICS:
13.300 Varstvo pred nevarnimi Protection against dangerous
izdelki goods
55.180.99 Drugi standardi v zvezi z Other standards related to
distribucijo blaga s prevozom freight distribution of goods
SIST EN ISO 16101:2005 en,fr,de
2003-01.Slovenski inštitut za standardizacijo. Razmnoževanje celote ali delov tega standarda ni dovoljeno.
---------------------- Page: 1 ----------------------
SIST EN ISO 16101:2005
---------------------- Page: 2 ----------------------
SIST EN ISO 16101:2005
EUROPEAN STANDARD
EN ISO 16101
NORME EUROPÉENNE
EUROPÄISCHE NORM
September 2004
ICS 13.300; 55.140
English version
Packaging - Transport packaging for dangerous goods - Plastics
compatibility testing (ISO 16101:2004)
Emballages - Emballages pour le transport des Verpackung - Verpackungen zur Beförderung gefährlicher
marchandises dangereuses - Essais de compatibilité des Güter - Verträglicheitsprüfung für Kunststoffverpackungen
matières plastiques (ISO 16101:2004) (ISO 16101:2004)
This European Standard was approved by CEN on 27 February 2004.
CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European
Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national
standards may be obtained on application to the Central Secretariat or to any CEN member.
This European Standard exists in three official versions (English, French, German). A version in any other language made by translation
under the responsibility of a CEN member into its own language and notified to the Central Secretariat has the same status as the official
versions.
CEN members are the national standards bodies of Austria, Belgium, Cyprus, Czech Republic, Denmark, Estonia, Finland, France,
Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Slovakia,
Slovenia, Spain, Sweden, Switzerland and United Kingdom.
EUROPEAN COMMITTEE FOR STANDARDIZATION
COMITÉ EUROPÉEN DE NORMALISATION
EUROPÄISCHES KOMITEE FÜR NORMUNG
Management Centre: rue de Stassart, 36 B-1050 Brussels
© 2004 CEN All rights of exploitation in any form and by any means reserved Ref. No. EN ISO 16101:2004: E
worldwide for CEN national Members.
---------------------- Page: 3 ----------------------
SIST EN ISO 16101:2005
EN ISO 16101:2004 (E)
Contents
page
Foreword.3
Introduction .4
1 Scope.5
2 Normative references.5
3 Terms and definitions .5
4 Test requirements.6
5 Selection and preparation of test packagings.7
6 Facilities for testing.9
7 Conditioning procedures.10
8 Permeability testing.12
Annex A (normative) Standard liquids and applicability to polyethylene types .13
Annex B (normative) Small scale laboratory tests to assess packaged substances against standard
liquids .16
Annex C (informative) Assimilation of packaged substance to standard liquids .34
Bibliography .71
2
---------------------- Page: 4 ----------------------
SIST EN ISO 16101:2005
EN ISO 16101:2004 (E)
Foreword
This document (EN ISO 16101:2004) has been prepared by CEN /TC 261, "Packaging", the secretariat of which is
held by AFNOR, in collaboration with ISO/TC 122 "Packaging".
This European Standard shall be given the status of a national standard, either by publication of an identical text or
by endorsement, at the latest by March 2005, and conflicting national standards shall be withdrawn at the latest by
March 2005.
This document has been prepared under a mandate given to CEN by the European Commission and the European
Free Trade Association, and supports the objectives of the framework Directives on Transport of Dangerous Goods.
This European Standard has been submitted for reference into the RID and/or in the technical annexes of the ADR.
Therefore in this context the standards listed in the normative references and covering basic requirements of the
RID/ADR not addressed within the present standard are normative only when the standards themselves are
referred to in the RID and/or in the technical annexes of the ADR.
According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following
countries are bound to implement this European Standard: Austria, Belgium, Cyprus, Czech Republic, Denmark,
Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta,
Netherlands, Norway, Poland, Portugal, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.
3
---------------------- Page: 5 ----------------------
SIST EN ISO 16101:2005
EN ISO 16101:2004 (E)
Introduction
This standard was developed to provide requirements and test procedures to meet the compatibility provisions for
plastics packagings to contain liquids as set out in:
The European Agreement concerning the International Carriage of Dangerous Goods by Road (ADR)
(covering most of Europe) [2] and
Regulations concerning the International Carriage of Dangerous Goods by Rail (RID) (covering most of Europe,
parts of North Africa and the Middle East) [5].
This procedure is an alternative option to that set out in the UN Recommendations on the Transport of Dangerous
Goods [1].
Plastics packaging material can be attacked by the chemical contents of the package. Such effects are caused by
different mechanisms such as environmental stress cracking (ESC) chemical degradation and swelling.
The UN Recommendations and the associated modal regulations require that all packagings shall be assessed for
compatibility with the substances which they are to contain. The UN text makes special reference to plastics
packagings for liquids. The procedure therein contains details of testing for six months at ambient temperature with
the liquid to be carried. RID/ADR permits as an alternative the use of standard liquids to which this document refers.
The UN Recommendations are given legal entity not only to ADR and RID but also to:
The International Civil Aviation Organisations Technical Instructions for the SafeTransport of Dangerous
Goods by Air (ICAO Tis) (worldwide) [3] and
The International Maritime Dangerous Goods Code (IMDG Code) (worldwide) [4].
These two modal rules do not refer to the standard liquid tests but they may still be acceptable as the UN
provisions do not make the six month test a mandatory requirement.
The application of this standard will need to take account of the requirements of these international agreements
and the relevant national regulations [6] [7] for domestic transport of dangerous goods.
Although not stipulated in the UN Recommendations or the modal regulations, these tests may be applied, where
deemed appropriate, to inner packagings of combination packagings. However, for this purpose, the standard liquid
tests may not be applicable to all types of plastics materials, since the tests were originally created for high
molecular weight high density polyethylene (PE-HD-HMW).
WARNING — The use of this International Standard may involve hazardous materials and equipment. This
International Standard does not purport to address all of the safety problems associated with its use. It is
the responsibility of the user of this International Standard to establish appropriate safety and health
practices and determine the applicability of regulatory limitations prior to use.
4
---------------------- Page: 6 ----------------------
SIST EN ISO 16101:2005
EN ISO 16101:2004 (E)
1 Scope
This standard specifies the requirements and test methods for compatibility testing of polyethylene based plastics
packagings and composite packagings with plastic inners containing liquids. The testing involves storage with the
packaged substance, or with a standard liquid as defined in annex A. Annex B describes small scale laboratory
tests, which may be used to determine the assimilation of those products to be carried with the standard liquids.
NOTE This standard should be used in conjunction with one or more of the International Regulations set out in the
Bibliography
2 Normative references
The following referenced documents are indispensable for the application of this document. For dated references,
only the edition cited applies. For undated references, the latest edition of the referenced document (including any
amendments) applies.
EN ISO 291, Plastics - Standard atmospheres for conditioning and testing
EN ISO 527-2, Plastics - Determination of tensile properties - Part 2: Test conditions for moulding and extrusion
plastics (ISO 527-2:1993)
EN ISO 1133, Plastics - Determination of the melt mass-flow rate (MFR) and the melt volume-flow rate (MVR) of
thermoplastics (ISO 1133:1997)
EN ISO 1183-1, Plastics - Methods for determining the density of non-cellular plastics – Part 1: Immersion method,
liquid pyknometer method and titration method (ISO 1183-1:2004)
EN ISO 1628-3, Plastics - Determination of the viscosity of polymers in dilute solution using capillary viscometers -
Part 3: Polyethylenes and polypropylenes (ISO 1628-3:2001)
EN ISO 1872-2, Plastics — Polyethylene (PE) moulding and extrusion materials — Part 2: Preparation of test
specimens and determination of properties (ISO 1872-2:1997)
EN ISO 2818, Plastics – Preparation of test specimens by machining (ISO 2818:1994)
EN ISO 11403-3 Plastics - Acquisition and presentation of comparable multipoint data - Part 3: Environmental
influences on properties (ISO 11403-3:1999)
EN ISO 11542-2:1998, Plastics - Ultra-high-molecular-weight polyethylene (PE-UHMW) moulding and extrusion
materials - Part 2: Preparation of test specimens and determination of properties (ISO 11542-2:1998)
EN ISO 16104:2003, Packaging – Transport packaging for dangerous goods – Test methods (ISO 16104:2002)
EN ISO/IEC 17025, General requirements for the competence of testing and calibration laboratories (ISO/IEC
17025:1999)
ISO 16770, Plastics - Determination of environmental stress crack (ESC ) of polyethylene – Full-notch creep test
(FNCT)
3 Terms and definitions
For the purposes of this European Standard, the following terms and definitions apply.
5
---------------------- Page: 7 ----------------------
SIST EN ISO 16101:2005
EN ISO 16101:2004 (E)
3.1
competent authority
any national regulatory body or authority designated or otherwise recognised as such for any purpose in connection
with the regulations specified in the Bibliography
3.2
plastics packagings
drums, jerricans and composite packagings with inner plastics receptacle made from certain types of plastics
NOTE Certain types of polyethylene are listed in A.3.
3.3
packaged substance (chemical product)
dangerous liquid with which the packaging is to be filled for transport
NOTE Packagings used for solid packaged substances, which can become liquid at temperatures encountered during
transport, should also meet the requirements of packagings for liquids.
3.4
standard liquids
defined liquids that are representative in their effect for a specific kind of interaction between a packaged substance
and the plastics packaging
NOTE A full description of the standard liquids can be found in A.2.
4 Test requirements
4.1 General
Plastics packagings selected in accordance with clause 5 shall be conditioned with the packaged substance or a
standard liquid with which it is to be assimilated. Annex C contains a list of substances assigned to standard liquids
For other chemicals not listed in annex C, small scale laboratory tests (see annex B) shall be used to prove
assimilation with standard liquids. The standard liquid chosen shall be at least as aggressive as the substance to
be transported. Where the packaged substance to be filled cannot be assimilated with one of the standard liquids,
the packaged substance itself shall be used and its specification recorded. In the event that the effect is more
aggressive than that of the standard liquids, the six month procedure shall be followed, as given in 7.2, or
alternatively, and with the exception of nitric acid > 55%, the accelerated procedure, as given in 7.3.
NOTE When the standard liquid is water, proof of chemical compatibility is not required.
4.2 Conditioning
Plastics packagings shall be conditioned in accordance with clause 7 of this standard.
4.3 Post-conditioning inspection
At the end of the conditioning period the packagings shall be inspected for leakage. Where no leakage is apparent
testing in accordance with clause 7 of EN ISO 16104:2003 shall commence within 21 days of the end of the
conditioning period (see 7.4).
4.4 Drop test
When tested in accordance with 7.1 of EN ISO 16104:2003, the plastics packaging:
a) shall be leakproof, subsequent to any slight discharge that may be apparent at the moment of impact and
subsequent to the equalization of internal and external pressures (except for inner packagings of combination
packagings, when it is not necessary for the pressure to be equalized);
6
---------------------- Page: 8 ----------------------
SIST EN ISO 16101:2005
EN ISO 16101:2004 (E)
b) shall not exhibit any damage liable to affect safety during transport, for example if the package cannot be used
without leaking.
4.5 Stacking test
When tested in accordance with 7.2 of EN ISO 16104:2003, the packaging shall not:
a) show any sign of leakage ;
b) show any deterioration which could adversely affect transport safety, nor any distortion liable to reduce its
strength or stability in stacks of packages.
4.6 Leakproofness test
When tested in accordance with 7.3 of EN ISO 16104:2003, plastics packagings shall be leakproof.
4.7 Hydraulic pressure test
When tested in accordance with 7.4 of EN ISO 16104:2003, plastics packagings shall be leakproof.
4.8 Permeability testing
With the exception of composite packagings having a plastics receptacle with outer steel drum, when tested in
accordance with 8 of this standard, plastics packaging shall have a permeability not exceeding 0,008 g/l.h.
4.9 Equivalent testing
The test methods described in this standard shall be considered to be the reference test methods.
NOTE Alternative methods may be used to demonstrate compliance with relevant regulations provided that:
- their equivalency to the reference test method can be demonstrated;
- their use is recorded in the test report;
- prior approval is obtained from the competent authority.
4.10 Test report
All packaging tests in conformity with this standard shall be the subject of a test report prepared in accordance with
annex E of EN ISO 16104:2003. It shall be possible to specifically identify the packaging relative to each test report,
either by the retention of uniquely numbered specimens or by inclusion of sufficient photographs and/or drawings
with unique references.
5 Selection and preparation of test packagings
5.1 Selection of packagings
A minimum of 15 packagings of each design type (or 18 in the case of a requirement to carry out the tests in 8), for
each chemical to be tested, shall be selected at random from normal production and submitted for testing.
NOTE 1 For box shaped composite packagings a different number of samples, 14 or 17, may be required.
Packagings shall be:
a) at least 48 h old;
7
---------------------- Page: 9 ----------------------
SIST EN ISO 16101:2005
EN ISO 16101:2004 (E)
b) marked with a test reference number which shall also be entered on the test record and later used on the test
report;
c) individually weighed to establish the tare or the filled mass;
NOTE 2 The form of such weighing may be varied to fit in with whether the packagings have been supplied full or empty to
the test station. Where the masses of individual empty packagings are recorded, it is necessary to record only a typical filled
mass (or vice-versa).
d) examined for damage etc. which might invalidate the tests;
NOTE 3 The tests set out below should be applied to every design type of packaging, by polymer type and grade.
NOTE 4 For selective testing see EN ISO 16104:2003, annex F.
NOTE 5 For testing with a lesser number of packagings see EN ISO 16104:2003, 4.1 NOTE.
5.2 Information to be provided with packagings
Each packaging type shall be accompanied by specification(s) for that design type (in the appropriate format set
out in annex G of EN ISO 16104:2003 and by the following additional information as relevant.
The packaging user (with the assistance, where appropriate, of the packaging manufacturer and the test
laboratory) shall identify the packaged substance. In the first instance this process shall consist of identifying the
plastics material concerned and its possible interactions, such as swelling, environmental stress cracking (ESC),
and molecular degradation.
NOTE 1 The specification forms for plastics packagings should identify the material by polymer type and grade.
NOTE 2 Where tests are carried out using the packaged substance the test report may be applicable for other substances
having equivalent or lesser chemical effects.
5.3 Filling of packaging prior to testing
5.3.1 Determination of brimful capacity
A packaging intended to contain liquids shall be filled to not less than 98% of the brimful capacity. The brimful
(overflow) capacity is determined for example by:
weighing the empty packaging including closures (mass empty = m kg) and
weighing the packaging full (mass m kgs brimful = W kg ).
The packaging shall be filled with water until the water just overflows and then fitting the closure and any surplus
mopped up. No steps shall be taken, e.g. by tilting or tapping the packaging, to enable water to penetrate into a
hollow handle or other design feature above the closure.
W - m
b =
d
where
b is the brimful capacity in litres
W is the mass of the packaging when brimful with water in kilograms (kg)
m is the mass of the empty packaging in kilograms (kg)
d is the density of water (1,0 kg/l)
NOTE When the brimful capacity has already been determined by testing to EN ISO 16104:2003, this procedure is not
necessary.
8
---------------------- Page: 10 ----------------------
SIST EN ISO 16101:2005
EN ISO 16101:2004 (E)
5.3.2 Filling of packaging
Filling of packagings shall be carried out in accordance with the following:
a) The packaging shall be filled to not less than 98 % of the brimful capacity (see 5.3.1).
b) When filling test packagings, at least one packaging shall have its capacity and filling level determined as in c).
Further specimens of that design type may be filled using a dipstick calibrated on the first specimen or, in the
case of small packagings, by mass or volume. When test specimens are filled by mass with a liquid other than
water (e.g. anti-freeze solution), the density of that liquid shall be taken into account, in order to obtain the
correct volume of fill (≥ 98 %). Determination shall be made of the total empty packaging mass including the
closure(s). This facilitates calculation of stacking loads.
c) The calculation of required volume for testing shall be:
(W − m)x98
C =
100d
where
C is the required volume of water in litres (l)
W is the mass of packaging when brimful with water in kilograms (kg)
m is the mass of the empty packaging in kilograms (kg)
d is the relative density of water (1,0 kg/l)
5.4 Closing packagings
Screw type closures shall be tightened to the torque recommended by the applicant where appropriate, which shall
be recorded in the test report.
Closure torque shall not differ from one test to another in the test report. If it is necessary to revise a closure torque
following a failure in one test, then all tests shall be completed using that torque setting.
All tests for a particular liquid shall be carried out at the same torque.
NOTE 1 The closure torque may vary for different seals.
NOTE 2 It is not necessary to apply the specified torque during the conditioning period if this affects the subsequent
performance of the seal during the packaging testing.
Where vented closures are intended for use in the packaging they shall be fitted for testing. Packagings fitted with
vented closures shall be inverted after closing and observed for leakage for a period of 5 min. Leakage from the
closure vent shall be regarded as a failure. An alternative method of test instead of inversion is shown in Figure 1,
clause 7.1.
6 Facilities for testing
6.1 General requirements
Tests shall be carried out at a testing facility capable of meeting the operational provisions of EN ISO/IEC 17025.
NOTE 1 This does not imply a requirement for the test laboratory to have attained third party certification or accreditation, but
if appropriate such external approval may be obtained from either a national accreditation body or from the competent authority.
NOTE 2 Testing staff should have a knowledge of the principles of the dangerous goods regulations, as set out in the UN
Recommendations.
9
---------------------- Page: 11 ----------------------
SIST EN ISO 16101:2005
EN ISO 16101:2004 (E)
6.2 Accuracy of measurement equipment
The accuracy of measuring equipment shall be more precise than the accuracy of the measurements in testing, as
specified in 6.3, unless otherwise approved by the competent authority. The measuring equipment shall be
calibrated in accordance with the relevant provisions of EN ISO/IEC 17025.
6.3 Accuracy of measurements in testing
Measurement equipment shall be selected such that individual measurement results including errors in reading and
calibration shall not exceed the following tolerances:
Mass in kilograms (kg): ± 2 %
Pressure in kilopascals (kPa): ± 3 %
Distance / length in millimetres (mm): ± 2 %
Temperature in degrees Celsius (ºC): ± 1 °C
Humidity in percentage (%): tolerances are as specified in particular
test methods
Time in minutes (min): ± 3 %
Torque in newton·metres (N·m): ± 3 N m or 10 %, whichever is the greater
NOTE For some measurements, the tolerances may be lower in order to have meaningful measurements e.g. when
measuring masses or dimensions of empty packagings.
Where only maximum or minimum values are specified in the text, tolerances are one sided e.g. in 7.3 the
conditioning temperature may exceed 40°C, but shall not be less.
6.4 Climatic conditions
There shall be adequate climatic facilities to meet the requirements in Table 1 of EN ISO 16104:2003.
6.5 Impact surfaces for drop tests
The drop test area shall be horizontal and flat, massive enough to be immovable and rigid enough to be non-
deformable under test conditions and sufficiently large to ensure that the test package falls entirely on the surface.
7 Conditioning procedures
7.1 General
After filling, the packagings shall be inverted for 24 h (unless fitted with a vented closure, see following), and then
restored to the normal standing position. For the last 24 h of the conditioning period as defined in 7.2 and 7.3, the
packagings shall be inverted again.
For packagings that have vented closures, invert the packagings for a period of 5 min after filling and then restore
the packagings to their normal standing position. At the end of the conditioning period, invert the packagings again
for a period of 5 min.
NOTE As an alternative to complete inversion the packaging may be laid on its side such that all closures are below the
level of the substance being tested (see Figure 1).
10
---------------------- Page: 12 ----------------------
SIST EN ISO 16101:2005
EN ISO 16101:2004 (E)
Acceptable Unacceptable
Key
1 Liquid level
2 Closure
Figure 1 — Explanatory diagram of alternative inversion method
7.2 Six months ambient conditioning
This test shall be carried out at ambient temperature for a period of 6 months.
For the purposes of this standard, ambient temperature, which shall be monitored and recorded, is considered to
be not less than 15 °C.
NOTE The competent authority may, however, allow an extended period of test for temperatures below 15 °C.
7.3 Accelerated conditioning procedure
The packagings for test shall be conditioned for 21 days at a minimum of 40 °C with each standard liquid required.
The procedure shall be applied for polyethylene types as defined in the A.3.1 and A.3.2. For other types of
polyethylene such as those defined in A 3.3 and A.3.4, the approval of the competent authority shall be obtained
7.4 Procedure at the end of the conditioning period
At the end of the conditioning period, all packagings, except those intended to withstand the stack test, shall be
emptied, rinsed, inspected for damage and prepared for test in accordance with the test procedures for plastics
packagings for liquids (EN ISO 16104). Testing shall commence within 21 days of the end of the conditioning
period. If emptied the packaging shall be kept closed until testing commences.
Packagings which have been conditioned with standard liquid, n-butyl acetate, shall be emptied and refilled with a
mixture of 1 %–10 % aqueous wetting agent solution and 2 % of n-butyl acetate for the stacking test.
NOTE 1 Where the closure elements (for example heat or induction seals) would have to be destroyed to empty the
packaging after conditioning; the packaging should be emptied through an additional opening drilled into the package. Such an
opening should not affect the results of the other tests (drop, hydraulic pressure and leakproofness tests).
NOTE 2 This does not apply to composite packagings where the outer non-plastics packaging withstands the stacking load,
e.g. steel.
11
---------------------- Page: 13 ----------------------
SIST EN ISO 16101:2005
EN ISO 16101:2004 (E)
NOTE 3 For substances presenting a danger at 40°C it may be necessary to replace the filling substance by another
substance where at least the same chemical interaction has been demonstrated and the agreement of the competent authority
has been obtained.
The same closures and gaskets used during the conditioning of the packagings shall be used for the rest of the
tests; i.e. gaskets and closures shall not be replaced.
7.5 Reuse of standard liquids
The standard liquids shall be checked periodically in accordance with Table 1 as their effectiveness can be reduced
over a period of time.
Table 1 — Reuse of standard liquids
Standard Liquid Specification
Wetting solution New solution for each test or check surface
tension (see annex A )
Acetic acid Concentration 99 ± 1%
a)
Normal butyl acetate
≥ 98 %
a)
Mixture of hydrocarbons 16%–21% aromatic content
Nitric acid
Concentration ≥ 55 %
a)
It is recommended that the absorption of these standard liquids is periodically checked with a control
specimen of polyethylene of defined type and grade, in accordance with B.4.1 The used standard liquid is no
longer fit for purpose when the determined absorption deviates by more than 5 % from the original determined
value.
Tests to monitor the quality of the standard liquids shall be done by appropriate means at intervals according to the
frequency of usage.
8 Permeability testing
8.1 Applicability
This test is required only for packagings for benzene, toluene, xylene or mixtures and preparations containing those
substances.
8.2 Test preparation
Three packagings shall be preconditioned according to 7.2 of this standard for original filling substance or
according to 7.3 of this standard for the standard liquid mix
...
Questions, Comments and Discussion
Ask us and Technical Secretary will try to provide an answer. You can facilitate discussion about the standard in here.